Pore-filling Three-dimensionally Ordered Macroporous Polyimide Composite Proton Conducting Membranes

The silica opal templates were prepared from three silica colloids of different diameters of 230 nm, 500 nm and 1.5 mm by a filtration route. The large-scale stable opal template membranes after sintering the deposited SiO2 opal template can be successfully obtained by optimizing the pH value and NaCl concentration in silica colloidal solutions. The three-dimensionally ordered macroporous（3DOM） polyimide membranes without crack were fabricated by reproducing the structure of silica opal template. We prepared the pore-filling composite proton exchange membranes by filling the 3DOM structure with proton conducting organosilane sol. The result indicates that the composite membranes exhibit higher water uptake than pure filling organosilane gel. The proton conductivity increased with the increasing of pore cell in composite membranes.

Three-dimensional ordered macroporous perovskite-type La_(1-x)K_xNiO_3 catalysts with enhanced catalytic activity for soot combustion: the Effect of K-substitution

Three-dimensional ordered macroporous (3DOM) La1?xKxNiO3 perovskite-type catalysts were successfully prepared by a colloidal crystal template method and characterized by scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, energy-dispersive X-ray scattering elemental mapping, X-ray diffraction, Raman and X-ray photoelectron spectroscopy, and temperature-programmed reduction of H2. Further, their catalytic activity in soot combustion was determined by temperature-programmed oxidation reaction. K substitution into the LaNiO3 lattice led to remarkably improved catalytic activity of this catalyst in soot combustion. Amongst various catalysts, La0.95K0.05NiO3 exhibited the highest activity in soot combustion (with its T50 and CO2 S values being 338 °C and 98.2%, respectively), which is comparable to the catalytic activities of Pt-based catalysts under the condition of poor contact between the soot and the catalyst. K-substitution improves the valence state of Ni and increases the number of oxygen vacancies, thereby leading to increased density of surface-active oxygen species. The active oxygen species play a vital role in catalyzing the elimination of soot. The perovskite-type La1?xKxNiO3 nanocatalysts with 3DOM structure without noble metals have potential for practical applications in the catalytic combustion of diesel soot particles.

Color tunable upconversion emission in CeO_2:Yb,Er three-dimensional ordered macroporous materials

The three-dimensional ordered macroporous CeO2：Yb,Er materials were prepared, and the influence of doping concentra- tion of Yb3＋ or Er3＋ ions on upconversion property was investigated. Green and red upconversion emissions were observed under the excitation of 980 nm at room temperature. It was found that the ratio of red to green upconversion emission intensity increased with increasing of concentration of the Yb3＋ or Er3＋ ions in the three-dimensional ordered macroporous CeO2：Yb,Er materials. When the concentration of Yb3＋ was 10 mol%, pure red upconversion emission was obtained. The varied mechanism of ratio of red to green upconversion emission intensity was discussed with the concentration of Yb3＋ or Er3＋ ions.

Immobilization of Glucose Oxidase on Ordered Macroporous Silicas Functionalized with Amino Group

A novel glucose oxidase immobilized on three-dimensionally ordered macroporous （3DOM） material has been prepared by firstly preparation of hybrid 3DOM SiO2-NH2 materials using colloidal crystal method, and following covalent immobilization of glucose oxidase on the pore walls of the 3DOM materials. The materials were characterized by SEM, FTIR, DSC and BET techniques. SEM observation shows that the macropores are highly ordered and are interconnected by small windows. FTIR measurement shows that there are amino and organic groups in the pore walls. The surface area of the 3DOM SiO2-NH2 material is about 10.2 m2/g. The loaded amount of enzyme is increased with amino content in the materials. The immobilized enzyme has high activity, thermal stability and can be reused.

Synthesis of 3D ordered macroporous indium tin oxide using polymer colloidal crystal template

Three-dimensional (3D) ordered macroporous indium tin oxide (ITO) is pre- pared using a polymer colloidal crystal template that is formed by self-assembly of the monodisperse poly(methyl methacrylate) (PMMA) microspheres. The morphologies and BET surface area of the macroporous material is examined by scanning electron micro- scope, transmission electron microscopy and N2 adsorption/desorption. Results indicate that the macroporous material has highly ordered arrays of the uniform pores replicated from the PMMA colloidal crystal template when the polymer colloidal crystal template is removed by calcinations at 500℃. The pore diameter (about 450 nm) of macroporous ITO slightly shrank to the PMMA microspheres. The BET surface area and pore volume of the macroporous material are 389 m2·g-1 and 0.36 cm3·g-1, respectively. Moreover, the macroporous ITO, containing 5 mol% Sn and after annealing under vacuum, shows the minimum resistivity of ρ = 8.2×10-3 Ω· cm. The conductive mechanism of macroporous ITO is discussed, and it is believed that the oxygen vacancies are the major factor for excellent electrical properties.

Synthesis of 3D ordered porous polystyrene using silica template

A rigid colloidal silica template was formed by self-assembly of the monodispersed silica spheres prepared according to Stober method. The silica template is highly ordered, which was verified by bright color effect due to Bragg diffraction and the results of SEM. The free radical polymerization of styrene was allowed within the interstices of the rigid template to result in the formation of the three-dimensional periodic silica/polystyrene nano-composites. The titled porous polystyrene was prepared by chemical decomposition of the template with concentrated aqueous hydrofluoric acid. Scanning electron microscopy characterization showed that the macroporous polystyrene has ordered arrays of the uniform pores replicated from the template. Moreover, it was found that the morphology of the as-synthesized macroporous polystyrene was greatly affected by the connectivity of the silica spheres treated under different conditions.

三维有序大孔硅材料载体固定化脂肪酶研究

以聚苯乙烯胶体晶体为模板制备三维有序大孔硅材料（3DOM-SiO_2）,以其作为载体来固定脂肪酶。分别考察了脂肪酶加入量、反应体系pH、固定反应时间对固定化效果的影响。结果表明,3DOM-SiO_2材料固定脂肪酶的最佳酶液加入量为200 mL/g,固定化最适宜pH为7.0,最佳反应时间为5 h。固定化的脂肪酶在催化性能上与游离脂肪酶相比优势明显,最适宜反应温度提高到40℃左右,并且酶活随温度变化率低,热稳定性明显提高;脂肪酶固定化后对pH的敏感度降低,适应范围更宽,催化反应的最适pH为8.0;固定化脂肪酶重复使用8次后,相对酶活保持在62%。由此可见,3DOMSiO_2材料是固定脂肪酶的优良载体,在酶固定化领域应用前景广阔。

Effects of Au-Ce strong interactions on catalytic activity of Au/CeO_2/3DOM Al_2O_3 catalyst for soot combustion under loose contact conditions

Au/3DOM（three-dimensionally ordered macroporous） Al2O3 and Au/CeO2/3DOM Al2O3 were prepared using a reduction-deposition method and characterized using scanning electron microscopy,N2 adsorption-desorption,X-ray diffraction,transmission electron microscopy,ultraviolet-visible spectroscopy,temperature-programmed hydrogen reduction,and X-ray photoelectron spectroscopy.Au nanoparticles of similar sizes were well dispersed and supported on the inner walls of uniform macropores.The norminal Au loading is 2%.Al-Ce-O solid solution in CeO2/3DOM Al2O3 catalysts can be formed due to the incorporation of Al^3＋ ions into the ceria lattice,which causes the creation of extrinsic oxygen vacancies.The extrinsic oxygen vacancies improved the oxygen-transport properties.The strong metal-support interactions between Au and CeO2 increased the amount of active oxygen on the Au nanoparticle surfaces,and this promoted soot oxidation.The activities of the Au-based catalysts were higher than those of the supports（Al2O3 or CeO2/3DOM Al2O3） at low temperature.Au/CeO2/3DOM Al2O3 had the highest catalytic activity for soot combustion,with T（10）,T（50）,and T（90） values of 273,364,and 412℃,respectively.