Titanium(Ti)alloys are widely used in high-tech fields like aerospace and biomedical engineering.Laser additive manufacturing(LAM),as an innovative technology,is the key driver for the development of Ti alloys.Despite...Titanium(Ti)alloys are widely used in high-tech fields like aerospace and biomedical engineering.Laser additive manufacturing(LAM),as an innovative technology,is the key driver for the development of Ti alloys.Despite the significant advancements in LAM of Ti alloys,there remain challenges that need further research and development efforts.To recap the potential of LAM high-performance Ti alloy,this article systematically reviews LAM Ti alloys with up-to-date information on process,materials,and properties.Several feasible solutions to advance LAM Ti alloys are reviewed,including intelligent process parameters optimization,LAM process innovation with auxiliary fields and novel Ti alloys customization for LAM.The auxiliary energy fields(e.g.thermal,acoustic,mechanical deformation and magnetic fields)can affect the melt pool dynamics and solidification behaviour during LAM of Ti alloys,altering microstructures and mechanical performances.Different kinds of novel Ti alloys customized for LAM,like peritecticα-Ti,eutectoid(α+β)-Ti,hybrid(α+β)-Ti,isomorphousβ-Ti and eutecticβ-Ti alloys are reviewed in detail.Furthermore,machine learning in accelerating the LAM process optimization and new materials development is also outlooked.This review summarizes the material properties and performance envelops and benchmarks the research achievements in LAM of Ti alloys.In addition,the perspectives and further trends in LAM of Ti alloys are also highlighted.展开更多
Titanium alloys are excellent structural materials in engineering fields,but their poor tribological properties limit their further applications.Electroless plating is an effective method to enhance the tribological p...Titanium alloys are excellent structural materials in engineering fields,but their poor tribological properties limit their further applications.Electroless plating is an effective method to enhance the tribological performance of alloys,but it is difficult to efficiently apply to titanium alloys,due to titanium alloy’s strong chemical activity.In this work,the electroless Nickel-Boron(Ni-B)coating was successfully deposited on the surface of titanium alloy(Ti-6AL-4V)via a new pre-treatment process.Then,linearly reciprocating sliding wear tests were performed to evaluate the tribological behaviors of titanium alloy and its electroless Ni-B coatings.It was found that the Ni-B coatings can decrease the wear rate of the titanium alloy from 19.89×10^(−3)mm^(3)to 0.41×10^(−3)mm^(3),which attributes to the much higher hardness of Ni-B coatings.After heat treatment,the hardness of Ni-B coating further increases corresponding to coating crystallization and hard phase formation.However,heat treatment does not improve the tribological performance of Ni-B coating,due to the fact that higher brittleness and more severe oxidative wear exacerbate the damage of heat-treated coatings.Furthermore,the Ni-B coatings heat-treated both in air and nitrogen almost present the same tribological performance.The finding of this work on electroless coating would further extend the practical applications of titanium alloys in the engineering fields.展开更多
Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titaniu...Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titanium alloy plates were prepared by cold press-ing sintering combined with high-temperature hot rolling.The microstructure and mechanical properties under different process paramet-ers were investigated.Optical microscope,electron backscatter diffraction,and others were applied to characterize the microstructure evolution and mechanical properties strengthening mechanism.The results showed that the chemical compositions were uniformly dif-fused without segregation during sintering,and the closing of the matrix craters was accelerated by increasing the sintering temperature.The block was hot rolled at 1200℃ with an 80%reduction under only two passes without annealing.The strength and elongation of the plate at 20–25℃ after solution and aging were 1247 MPa and 14.0%,respectively,which were increased by 24.5%and 40.0%,respect-ively,compared with the as-sintered alloy at 1300℃.The microstructure was significantly refined by continuous dynamic recrystalliza-tion,which was completed by the rotation and dislocation absorption of the substructure surrounded by low-angle grain boundaries.After hot rolling combined with heat treatment,the strength and plasticity of PM-TA15 were significantly improved,which resulted from the dense,uniform,and fine recrystallization structure and the synergistic effect of multiple slip systems.展开更多
The Ti-5Al-2Sn-4Zr-4Mo-2Cr-1Fe(β-CEZ)alloy is considered as a potential structural material in the aviation industry due to its outstanding strength and corrosion resistance.Electrochemical machining(ECM)is an effici...The Ti-5Al-2Sn-4Zr-4Mo-2Cr-1Fe(β-CEZ)alloy is considered as a potential structural material in the aviation industry due to its outstanding strength and corrosion resistance.Electrochemical machining(ECM)is an efficient and low-cost technology for manufacturing theβ-CEZ alloy.In ECM,the machining parameter selection and tool design are based on the electrochemical dissolution behavior of the materials.In this study,the electrochemical dissolution behaviors of theβ-CEZ and Ti-6Al-4V(TC4)alloys in NaNO3solution are discussed.The open circuit potential(OCP),Tafel polarization,potentiodynamic polarization,electrochemical impedance spectroscopy(EIS),and current efficiency curves of theβ-CEZ and TC4 alloys are analyzed.The results show that,compared to the TC4 alloy,the passivation film structure is denser and the charge transfer resistance in the dissolution process is greater for theβ-CEZ alloy.Moreover,the dissolved surface morphology of the two titanium-based alloys under different current densities are analyzed.Under low current densities,theβ-CEZ alloy surface comprises dissolution pits and dissolved products,while the TC4 alloy surface comprises a porous honeycomb structure.Under high current densities,the surface waviness of both the alloys improves and the TC4 alloy surface is flatter and smoother than theβ-CEZ alloy surface.Finally,the electrochemical dissolution models ofβ-CEZ and TC4 alloys are proposed.展开更多
Titanium alloy has been applied in the field of aerospace manufacturing for its high specific strength and hardness.Nonetheless,these properties also cause general problems in the machining,such as processing ineffici...Titanium alloy has been applied in the field of aerospace manufacturing for its high specific strength and hardness.Nonetheless,these properties also cause general problems in the machining,such as processing inefficiency,serious wear,poor workpiece face quality,etc.Aiming at the above problems,this paper carried out a comparative experimental study on titanium alloy milling based on the CAMCand BEMC.The variation law of cutting force and wear morphology of the two tools were obtained,and the wear mechanism and the effect of wear on machining quality were analyzed.The conclusion is that in contrast with BEMC,under the action of cutting thickness thinning mechanism,the force of CAMC was less,and its fluctuation was more stable.The flank wear was uniform and near the cutting edge,and the wear rate was slower.In the early period,the wear mechanism of CAMC was mainly adhesion.Gradually,oxidative wear also occurred with milling.Furthermore,the surface residual height of CAMC was lower.There is no obvious peak and trough accompanied by fewer surface defects.展开更多
Acetabular cups,which are among themost important implants in total hip arthroplasty,are usually made from titanium alloys with high porosity and adequate mechanical properties.The current three-dimensional(3D)printin...Acetabular cups,which are among themost important implants in total hip arthroplasty,are usually made from titanium alloys with high porosity and adequate mechanical properties.The current three-dimensional(3D)printing approaches to fabricate customized acetabular cups have some inherent disadvantages such as high cost and energy consumption,residual thermal stress,and relatively low efficiency.Thus,in this work,a direct ink writing method was developed to print a cup structure at room temperature,followed by multi-step heat treatment to form microscale porous structure within the acetabular cup.Our method is facilitated by the development of a self-supporting titanium-6 aluminum-4 vanadium(Ti64)ink that is composed of Ti64 particles,bentonite yield-stress additive,ultraviolet curable polymer,and photo-initiator.The effects of Ti64 and bentonite concentrations on the rheological properties and printability of inks were systematically investigated.Moreover,the printing conditions,geometrical limitations,and maximum curing depth were explored.Finally,some complex 3D structures,including lattices with different gap distances,honeycomb with a well-defined shape,and an acetabular cup with uniformly distributed micropores,were successfully printed/fabricated to validate the effectiveness of the proposed method.展开更多
An accurate flow stress model was established by considering the parameters of strain rate,strain and temperature as well asβ→a+βphase transformation in order to develop the plastic forming theory of TC18 titanium ...An accurate flow stress model was established by considering the parameters of strain rate,strain and temperature as well asβ→a+βphase transformation in order to develop the plastic forming theory of TC18 titanium alloy.Firstly,the phase transition kinetics of TC18 titanium alloy during isothermal and continuous cooling at 1073 and 1273 K was studied by thermodynamic calculation,meanwhile,the relationship of volume fraction of phase transition with temperature and time was obtained.Constitutive models were calculated by investigating flow behaviors under hot compression tests with the strain rates of 0.001-1s^(-1) and temperatures of 973-1223 K in the singleβand a+βregions in TC18 titanium alloy,respectively.By combining the phase transformation dynamic kinetics with constitutive models,an accurate flow stress model was established,providing theoretical basis and data support for the hot forging of TC18 titanium alloy.展开更多
The microstructure and mechanical properties of the TB8 titanium alloy were controlled by a secondary processing technology of solution-equal channel angular pressing(ECAP)-aging treatment,which combined strong plasti...The microstructure and mechanical properties of the TB8 titanium alloy were controlled by a secondary processing technology of solution-equal channel angular pressing(ECAP)-aging treatment,which combined strong plastic deformation with heat treatment. The effects of ECAP and heat treatment on the microstructure and properties of the titanium alloy were systematically investigated by optical microscopy(OM), scanning electron microscopy(SEM), hardness tests, and tensile property analysis. The results indicate that the metallographic structure without ECAP treatment is mainly equiaxed β-phase, while that after ECAP treatment is equiaxed β-phase with grain fragmentation, slip bands, and new small grains. After 850 ℃ solutionECAP-520 ℃ aging treatment, the titanium alloy has the smallest grain size, while the directionality of tissue growth along the ECAP direction is the most apparent. Under the same solution-aging conditions, the hardness of the titanium alloy increases from 431.5 to 531.2 HV compared to that without ECAP treatment, i e, increases by 23.11%, and the tensile strength increases from 1 045.30 to 1 176.25 MPa, i e, increases by 12.5%.展开更多
Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot ...Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot isostatic pressing parameters on defects,composition uniformity,microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in detail.Results show that increasing temperature and pressure of hot isostatic pressing can reduce defects,especially,the internal defects are substantially eliminated when the temperature exceeds 920℃or the pressure exceeds 125 MPa.The higher temperature and pressure can improve the microstructure uniformity.Besides,the higher pressure can promote the composition uniformity.With the temperature increases from 880℃to 960℃,α-laths are coarsened.But with increasing pressure,the grain size of prior-βphase,the widths ofα-laths andα-colony are reduced.The tensile strength of Ti60 alloy is 949 MPa,yield strength is 827 MPa,and the elongation is 11%when the hot isostatic pressing parameters are 960℃/125 MPa/2 h,which exhibits the best match between the strength and plasticity.展开更多
As an important green manufacturing process,dry grinding has problems such as high grinding temperature and insufficient cooling capacity.Aiming at the problems of sticking and burns in dry grinding of titanium alloys...As an important green manufacturing process,dry grinding has problems such as high grinding temperature and insufficient cooling capacity.Aiming at the problems of sticking and burns in dry grinding of titanium alloys,grinding performance evaluation of molybdenum disulfide(MoS_(2))solid lubricant coated brazed cubic boron carbide(CBN)grinding wheel(MoS_(2)-coated CBN wheel)in dry grinding titanium alloys was carried out.The lubrication mechanism of MoS_(2)in the grinding process is analyzed,and the MoS_(2)-coated CBN wheel is prepared.The results show that the MoS_(2)solid lubricant can form a lubricating film on the ground surface and reduce the friction coefficient and grinding force.Within the experimental parameters,normal grinding force decreased by 42.5%,and tangential grinding force decreased by 28.1%.MoS_(2)lubricant can effectively improve the heat dissipation effect of titanium alloy grinding arc area.Compared with common CBN grinding wheel,MoS_(2)-coated CBN wheel has lower grinding temperature.When the grinding depth reaches 20μm,the grinding temperature decreased by 30.5%.The wear of CBN grains of grinding wheel were analyzed by mathematical statistical method.MoS_(2)lubricating coating can essentially decrease the wear of grains,reduce the adhesion of titanium alloy chip,prolong the service life of grinding wheel,and help to enhance the surface quality of workpiece.This research provides high-quality and efficient technical support for titanium alloy grinding.展开更多
Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Fi...Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.展开更多
Titanium cermets were successfully synthesized on the surface of biomedical grade titanium alloys by using sequential carburization method. The mechanical properties such as hardness, fracture toughness and plasticity...Titanium cermets were successfully synthesized on the surface of biomedical grade titanium alloys by using sequential carburization method. The mechanical properties such as hardness, fracture toughness and plasticity were measured to estimate the potential application of titanium cermets. The results show that after carburization the surface hardness of titanium cermets was 778 HV, with a significant improvement of 128% compared with that of titanium alloys. In addition, the fracture toughness of titanium cermets was 21.5 × 10^6 Pa.m^1/2, much higher than that of other ceramics. Furthermore, the analysis of the loading-unloading curve in the nanoindentation test also indicates that the plasticity of titanium cermet reached 32.1%, a relatively high value which illustrates the combination of the metal and ceramics properties. The results suggest that sequential carburization should be an efficient way to produce titanium cermets with hard surface, high toughness and plasticity.展开更多
The aim of this paper was to study the reaction between a Ti-6Al-4V alloy and boron nitride based investment shell molds used for investment casting titanium. In BN based investment shell molds, the face coatings are ...The aim of this paper was to study the reaction between a Ti-6Al-4V alloy and boron nitride based investment shell molds used for investment casting titanium. In BN based investment shell molds, the face coatings are made of pretreated hexagonal boron nitride (hBN) with a few yttria (Y2O3) and colloidal yttria as binder. The Ti-6Al-4V alloy was melted in a controlled atmosphere induction furnace with a segment water-cooled copper crucible. The cross-section of reaction interface between Ti alloys and shell mold was investigated by electron probe micro-analyzer (EPMA) and microhardness tester. The results show that the reaction is not serious, the thickness of the reacting layer is about 30-50 μm, and the thickness of α-case is about 180-200 pro. Moreover the α-case formation mechanism was also discussed.展开更多
The Ti-Al-Sn-Zr-Cr-Mo-V-Si (Ti-62A) alloy, an alpha-beta alloy with high strength and fracture toughness, is currently used as an advanced structural material in aerospace and non-aerospace applications. Thermo-mech...The Ti-Al-Sn-Zr-Cr-Mo-V-Si (Ti-62A) alloy, an alpha-beta alloy with high strength and fracture toughness, is currently used as an advanced structural material in aerospace and non-aerospace applications. Thermo-mechanical processes can be used to optimize the relationship between its strength and fracture toughness. A Ti-62A alloy bar can be machined through a transus β-forged plus α+β solution treated and aged specimen with a lamellar alpha microstructure. The effects of heat treatment on the mechanical properties were discussed. Heat treatment provided a practical balance of strength, fracture toughness, and fatigue crack growth resistance. A comparison of the Ti-62A alloy with the Ti-62222S alloy under the same thermo-mechanical processing conditions showed that their properties are at the same level.展开更多
Microporous titanium carbide coating was successfully synthesized on medical grade titanium alloy by using sequential carburization.Changes in the surface morphology of titanium alloy occasioned by sequential carburiz...Microporous titanium carbide coating was successfully synthesized on medical grade titanium alloy by using sequential carburization.Changes in the surface morphology of titanium alloy occasioned by sequential carburization were characterized and the wettability characteristics were quantified.Furthermore,the dispersion forces were calculated and discussed.The results indicate that sequential carburization is an effective way to modify the wettability of titanium alloy.After the carburization the surface dispersion force of titanium alloy increased from 76.5×10^(-3)J·m^(-2) to 105.5×10^(-3) J·m^(-2),with an enhancement of 37.9 %.Meanwhile the contact angle of titanium alloy decreased from 83° to 71.5°,indicating a significant improvement of wettability,which is much closer to the optimal water contact angle for cell adhesion of 70°.展开更多
The fine-grained microstructure of TA15 titanium alloy was prepared through two-step forging technology combined with high and low temperatures, and a transnormal superplastic elongation of more than 2000% was obtaine...The fine-grained microstructure of TA15 titanium alloy was prepared through two-step forging technology combined with high and low temperatures, and a transnormal superplastic elongation of more than 2000% was obtained. The superplastic behaviour and microstructure evolution were systematically researched at different temperatures and strain rates through superplastic tensile test. The results indicate that the fine-grained TA15 alloy exhibits superplasticity at temperatures of 760-980°C and initial strain rates from 1.1 × 10^-2 to 5.5 × 10^-5 s^-1. The optimal superplastic conditions are 940°C and 3.3 × 10^-4 s^-1, in which the average elongation is 2526% and the maximum elongation is 2743%. During superplastic deformation, dynamic recovery and recrystallization occur obviously, and the corporate effect of strain hardening and recrystallization softening decides the superplastic ability directly.展开更多
Anodic oxide films of the titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate electrolyte without hydrofluoric acid or fluoride were fabricated. The morphology, components, and microstructure of the films were characte...Anodic oxide films of the titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate electrolyte without hydrofluoric acid or fluoride were fabricated. The morphology, components, and microstructure of the films were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and Raman spectroscopy. The results showed that the films were thick, uniform, and nontransparent. Such films exhibited sedimentary morphology, with a thickness of about 3 μm, and the pore diameters of the deposits ranged from several hundred nanometers to 1.5 μm. The films were mainly titanium dioxide. Some coke-like deposits, which may contain or be changed by OH, NH, C-C, C-O, and C=O groups, were doped in the films. The films were mainly amorphous with a small amount of anatase and rutile phase.展开更多
The development of microstructure during the aging of Ti-10V-2Fe-3A1 alloy in the 13 and (α+β) solution-treated and quenched conditions was investigated. The results showed that the isothermal holding below 400℃...The development of microstructure during the aging of Ti-10V-2Fe-3A1 alloy in the 13 and (α+β) solution-treated and quenched conditions was investigated. The results showed that the isothermal holding below 400℃ yielded homogeneously distributed, spherical ω-phase particles. Fine α aggregates are formed uniformly within 13 grains by nucleating at at particles or β/ω interfaces. At higher temperatures, thin martensite plates decomposed in water-quenched condition. The formation of ω phase was avoided and coarse coarse α-phase plates directly precipitated from the 13 matrix. The highest hardness values were found when the alloys were aged at 400℃ for 8 h. The significance of the observations was discussed in terms of the effect of aging on the precipitations and property.展开更多
基金financially supported by the Young Individual Research Grants(Grant No:M22K3c0097)Singapore RIE 2025 plan and Singapore Aerospace Programme Cycle 16(Grant No:M2215a0073)led by C Tan+2 种基金supported by the Singapore A*STAR Career Development Funds(Grant No:C210812047)the National Natural Science Foundation of China(52174361 and 52374385)the support by US NSF DMR-2104933。
文摘Titanium(Ti)alloys are widely used in high-tech fields like aerospace and biomedical engineering.Laser additive manufacturing(LAM),as an innovative technology,is the key driver for the development of Ti alloys.Despite the significant advancements in LAM of Ti alloys,there remain challenges that need further research and development efforts.To recap the potential of LAM high-performance Ti alloy,this article systematically reviews LAM Ti alloys with up-to-date information on process,materials,and properties.Several feasible solutions to advance LAM Ti alloys are reviewed,including intelligent process parameters optimization,LAM process innovation with auxiliary fields and novel Ti alloys customization for LAM.The auxiliary energy fields(e.g.thermal,acoustic,mechanical deformation and magnetic fields)can affect the melt pool dynamics and solidification behaviour during LAM of Ti alloys,altering microstructures and mechanical performances.Different kinds of novel Ti alloys customized for LAM,like peritecticα-Ti,eutectoid(α+β)-Ti,hybrid(α+β)-Ti,isomorphousβ-Ti and eutecticβ-Ti alloys are reviewed in detail.Furthermore,machine learning in accelerating the LAM process optimization and new materials development is also outlooked.This review summarizes the material properties and performance envelops and benchmarks the research achievements in LAM of Ti alloys.In addition,the perspectives and further trends in LAM of Ti alloys are also highlighted.
基金Supported by Sichuan Provincial Science and Technology Program of China(Grant No.2018JY0245)National Natural Science Foundation of China(Grant No.51975492)Natural Science Foundation of Southwest University of Science and Technology of China(Grant No.19xz7163).
文摘Titanium alloys are excellent structural materials in engineering fields,but their poor tribological properties limit their further applications.Electroless plating is an effective method to enhance the tribological performance of alloys,but it is difficult to efficiently apply to titanium alloys,due to titanium alloy’s strong chemical activity.In this work,the electroless Nickel-Boron(Ni-B)coating was successfully deposited on the surface of titanium alloy(Ti-6AL-4V)via a new pre-treatment process.Then,linearly reciprocating sliding wear tests were performed to evaluate the tribological behaviors of titanium alloy and its electroless Ni-B coatings.It was found that the Ni-B coatings can decrease the wear rate of the titanium alloy from 19.89×10^(−3)mm^(3)to 0.41×10^(−3)mm^(3),which attributes to the much higher hardness of Ni-B coatings.After heat treatment,the hardness of Ni-B coating further increases corresponding to coating crystallization and hard phase formation.However,heat treatment does not improve the tribological performance of Ni-B coating,due to the fact that higher brittleness and more severe oxidative wear exacerbate the damage of heat-treated coatings.Furthermore,the Ni-B coatings heat-treated both in air and nitrogen almost present the same tribological performance.The finding of this work on electroless coating would further extend the practical applications of titanium alloys in the engineering fields.
基金supported by the National Natural Science Foundation of China(No.52274359)Guangdong Basic and Applied Basic Research Foundation,China(No.2022A1515110406)+3 种基金Beijing Natural Science Foundation,China(No.2212035)the Fundamental Research Funds for the Central Universities,China(Nos.FRF-TP-19005C1Z and 00007718)the Aeroengine Group University Research Cooperation Project,China(No.HFZL2021CXY021)the State Key Lab of Advanced Metals and Materials,University of Science and Technology Beijing,China(Nos.2021Z-03 and 2022Z-14).
文摘Hot deformation of sintered billets by powder metallurgy(PM)is an effective preparation technique for titanium alloys,which is more significant for high-alloying alloys.In this study,Ti–6.5Al–2Zr–Mo–V(TA15)titanium alloy plates were prepared by cold press-ing sintering combined with high-temperature hot rolling.The microstructure and mechanical properties under different process paramet-ers were investigated.Optical microscope,electron backscatter diffraction,and others were applied to characterize the microstructure evolution and mechanical properties strengthening mechanism.The results showed that the chemical compositions were uniformly dif-fused without segregation during sintering,and the closing of the matrix craters was accelerated by increasing the sintering temperature.The block was hot rolled at 1200℃ with an 80%reduction under only two passes without annealing.The strength and elongation of the plate at 20–25℃ after solution and aging were 1247 MPa and 14.0%,respectively,which were increased by 24.5%and 40.0%,respect-ively,compared with the as-sintered alloy at 1300℃.The microstructure was significantly refined by continuous dynamic recrystalliza-tion,which was completed by the rotation and dislocation absorption of the substructure surrounded by low-angle grain boundaries.After hot rolling combined with heat treatment,the strength and plasticity of PM-TA15 were significantly improved,which resulted from the dense,uniform,and fine recrystallization structure and the synergistic effect of multiple slip systems.
基金supported by the National Natural Science Foundation of China(No.92160301)the Industrial Technology Development Program,China(No.JCKY2021605 B026)。
文摘The Ti-5Al-2Sn-4Zr-4Mo-2Cr-1Fe(β-CEZ)alloy is considered as a potential structural material in the aviation industry due to its outstanding strength and corrosion resistance.Electrochemical machining(ECM)is an efficient and low-cost technology for manufacturing theβ-CEZ alloy.In ECM,the machining parameter selection and tool design are based on the electrochemical dissolution behavior of the materials.In this study,the electrochemical dissolution behaviors of theβ-CEZ and Ti-6Al-4V(TC4)alloys in NaNO3solution are discussed.The open circuit potential(OCP),Tafel polarization,potentiodynamic polarization,electrochemical impedance spectroscopy(EIS),and current efficiency curves of theβ-CEZ and TC4 alloys are analyzed.The results show that,compared to the TC4 alloy,the passivation film structure is denser and the charge transfer resistance in the dissolution process is greater for theβ-CEZ alloy.Moreover,the dissolved surface morphology of the two titanium-based alloys under different current densities are analyzed.Under low current densities,theβ-CEZ alloy surface comprises dissolution pits and dissolved products,while the TC4 alloy surface comprises a porous honeycomb structure.Under high current densities,the surface waviness of both the alloys improves and the TC4 alloy surface is flatter and smoother than theβ-CEZ alloy surface.Finally,the electrochemical dissolution models ofβ-CEZ and TC4 alloys are proposed.
基金Supported by National Natural Science Foundation of China(Grant No.51975168).
文摘Titanium alloy has been applied in the field of aerospace manufacturing for its high specific strength and hardness.Nonetheless,these properties also cause general problems in the machining,such as processing inefficiency,serious wear,poor workpiece face quality,etc.Aiming at the above problems,this paper carried out a comparative experimental study on titanium alloy milling based on the CAMCand BEMC.The variation law of cutting force and wear morphology of the two tools were obtained,and the wear mechanism and the effect of wear on machining quality were analyzed.The conclusion is that in contrast with BEMC,under the action of cutting thickness thinning mechanism,the force of CAMC was less,and its fluctuation was more stable.The flank wear was uniform and near the cutting edge,and the wear rate was slower.In the early period,the wear mechanism of CAMC was mainly adhesion.Gradually,oxidative wear also occurred with milling.Furthermore,the surface residual height of CAMC was lower.There is no obvious peak and trough accompanied by fewer surface defects.
基金supported by the Micro Grant (PG20473) at the University of Nevada, Reno, USA
文摘Acetabular cups,which are among themost important implants in total hip arthroplasty,are usually made from titanium alloys with high porosity and adequate mechanical properties.The current three-dimensional(3D)printing approaches to fabricate customized acetabular cups have some inherent disadvantages such as high cost and energy consumption,residual thermal stress,and relatively low efficiency.Thus,in this work,a direct ink writing method was developed to print a cup structure at room temperature,followed by multi-step heat treatment to form microscale porous structure within the acetabular cup.Our method is facilitated by the development of a self-supporting titanium-6 aluminum-4 vanadium(Ti64)ink that is composed of Ti64 particles,bentonite yield-stress additive,ultraviolet curable polymer,and photo-initiator.The effects of Ti64 and bentonite concentrations on the rheological properties and printability of inks were systematically investigated.Moreover,the printing conditions,geometrical limitations,and maximum curing depth were explored.Finally,some complex 3D structures,including lattices with different gap distances,honeycomb with a well-defined shape,and an acetabular cup with uniformly distributed micropores,were successfully printed/fabricated to validate the effectiveness of the proposed method.
基金Funded by the National Natural Science Foundation of China(No.52075058)the Natural Science Foundation of Chongqing(No.cstc2021jcyj-msxmX1112)the Research and Demonstration of Key Technologies for Forging High-performance Aluminum Alloys for Aerospace Applications(No.Z20210348)。
文摘An accurate flow stress model was established by considering the parameters of strain rate,strain and temperature as well asβ→a+βphase transformation in order to develop the plastic forming theory of TC18 titanium alloy.Firstly,the phase transition kinetics of TC18 titanium alloy during isothermal and continuous cooling at 1073 and 1273 K was studied by thermodynamic calculation,meanwhile,the relationship of volume fraction of phase transition with temperature and time was obtained.Constitutive models were calculated by investigating flow behaviors under hot compression tests with the strain rates of 0.001-1s^(-1) and temperatures of 973-1223 K in the singleβand a+βregions in TC18 titanium alloy,respectively.By combining the phase transformation dynamic kinetics with constitutive models,an accurate flow stress model was established,providing theoretical basis and data support for the hot forging of TC18 titanium alloy.
基金the Key R&D Plan of Zhenjiang in 2018 (No.GY2018021)。
文摘The microstructure and mechanical properties of the TB8 titanium alloy were controlled by a secondary processing technology of solution-equal channel angular pressing(ECAP)-aging treatment,which combined strong plastic deformation with heat treatment. The effects of ECAP and heat treatment on the microstructure and properties of the titanium alloy were systematically investigated by optical microscopy(OM), scanning electron microscopy(SEM), hardness tests, and tensile property analysis. The results indicate that the metallographic structure without ECAP treatment is mainly equiaxed β-phase, while that after ECAP treatment is equiaxed β-phase with grain fragmentation, slip bands, and new small grains. After 850 ℃ solutionECAP-520 ℃ aging treatment, the titanium alloy has the smallest grain size, while the directionality of tissue growth along the ECAP direction is the most apparent. Under the same solution-aging conditions, the hardness of the titanium alloy increases from 431.5 to 531.2 HV compared to that without ECAP treatment, i e, increases by 23.11%, and the tensile strength increases from 1 045.30 to 1 176.25 MPa, i e, increases by 12.5%.
基金financially supported by the National Key Research and Development Program of China(Grant No.2020YFB2008300)。
文摘Hot isostatic pressing parameters are critical to Ti60 high temperature titanium alloy castings which have wide application perspective in aerospace.In order to obtain optimal processing parameters,the effects of hot isostatic pressing parameters on defects,composition uniformity,microstructure and mechanical properties of Ti60 cast high temperature titanium alloy were investigated in detail.Results show that increasing temperature and pressure of hot isostatic pressing can reduce defects,especially,the internal defects are substantially eliminated when the temperature exceeds 920℃or the pressure exceeds 125 MPa.The higher temperature and pressure can improve the microstructure uniformity.Besides,the higher pressure can promote the composition uniformity.With the temperature increases from 880℃to 960℃,α-laths are coarsened.But with increasing pressure,the grain size of prior-βphase,the widths ofα-laths andα-colony are reduced.The tensile strength of Ti60 alloy is 949 MPa,yield strength is 827 MPa,and the elongation is 11%when the hot isostatic pressing parameters are 960℃/125 MPa/2 h,which exhibits the best match between the strength and plasticity.
基金Supported by National Natural Science Foundation of China(Grant Nos.92160301,92060203,52175415,52205475)Science Center for Gas Turbine Project of China(Grant Nos.P2022-AB-IV-002-001,P2023-B-IV-003-001)+1 种基金Jiangsu Provincial Natural Science Foundation of China(Grant No.BK20210295)Graduate Research and Innovation Projects in Jiangsu Province of China(Grant No.KYCX22_0339).
文摘As an important green manufacturing process,dry grinding has problems such as high grinding temperature and insufficient cooling capacity.Aiming at the problems of sticking and burns in dry grinding of titanium alloys,grinding performance evaluation of molybdenum disulfide(MoS_(2))solid lubricant coated brazed cubic boron carbide(CBN)grinding wheel(MoS_(2)-coated CBN wheel)in dry grinding titanium alloys was carried out.The lubrication mechanism of MoS_(2)in the grinding process is analyzed,and the MoS_(2)-coated CBN wheel is prepared.The results show that the MoS_(2)solid lubricant can form a lubricating film on the ground surface and reduce the friction coefficient and grinding force.Within the experimental parameters,normal grinding force decreased by 42.5%,and tangential grinding force decreased by 28.1%.MoS_(2)lubricant can effectively improve the heat dissipation effect of titanium alloy grinding arc area.Compared with common CBN grinding wheel,MoS_(2)-coated CBN wheel has lower grinding temperature.When the grinding depth reaches 20μm,the grinding temperature decreased by 30.5%.The wear of CBN grains of grinding wheel were analyzed by mathematical statistical method.MoS_(2)lubricating coating can essentially decrease the wear of grains,reduce the adhesion of titanium alloy chip,prolong the service life of grinding wheel,and help to enhance the surface quality of workpiece.This research provides high-quality and efficient technical support for titanium alloy grinding.
文摘Titanium alloy (Ti-Al-V alloy) substrate was brazed with stainless steel (STS304) using filler metal.At an optimized brazing condition,various filler metals were used.Microstructures were observed at each condition.Filler metals were titanium based 40Ti-20Zr-20Cu-20Ni,silver based Ag 5Pd,and nickel based Ni-7Cr-3.1B-4.5Si-3Fe-0.06C (BNi2) and Ni-14Cr-10P-0.06C (BNi7).To select a good filler metal for brazing process,wetting test was performed at 880-1050 °C.It was not brazed using silver based filler metals,but at the conditions using titanium and nickel based filler metals had brazed zone between titanium alloy and stainless steel.However,titanium alloy was eroded during brazing using titanium based filler metals.Nickel based filler metal has a good brazed zone between titanium alloy and stainless steel among the filler metals.
基金Acknowledgments The authors wish to thank the National Natural Science Foundation of China (Grant No. 51005234 and 50905180), the Foundation of China University of Mining and Technology (Grant No. 2009A056) and the Natural Science Foundation of Jiangsu Province (Grant No. BK2008005).
文摘Titanium cermets were successfully synthesized on the surface of biomedical grade titanium alloys by using sequential carburization method. The mechanical properties such as hardness, fracture toughness and plasticity were measured to estimate the potential application of titanium cermets. The results show that after carburization the surface hardness of titanium cermets was 778 HV, with a significant improvement of 128% compared with that of titanium alloys. In addition, the fracture toughness of titanium cermets was 21.5 × 10^6 Pa.m^1/2, much higher than that of other ceramics. Furthermore, the analysis of the loading-unloading curve in the nanoindentation test also indicates that the plasticity of titanium cermet reached 32.1%, a relatively high value which illustrates the combination of the metal and ceramics properties. The results suggest that sequential carburization should be an efficient way to produce titanium cermets with hard surface, high toughness and plasticity.
文摘The aim of this paper was to study the reaction between a Ti-6Al-4V alloy and boron nitride based investment shell molds used for investment casting titanium. In BN based investment shell molds, the face coatings are made of pretreated hexagonal boron nitride (hBN) with a few yttria (Y2O3) and colloidal yttria as binder. The Ti-6Al-4V alloy was melted in a controlled atmosphere induction furnace with a segment water-cooled copper crucible. The cross-section of reaction interface between Ti alloys and shell mold was investigated by electron probe micro-analyzer (EPMA) and microhardness tester. The results show that the reaction is not serious, the thickness of the reacting layer is about 30-50 μm, and the thickness of α-case is about 180-200 pro. Moreover the α-case formation mechanism was also discussed.
文摘The Ti-Al-Sn-Zr-Cr-Mo-V-Si (Ti-62A) alloy, an alpha-beta alloy with high strength and fracture toughness, is currently used as an advanced structural material in aerospace and non-aerospace applications. Thermo-mechanical processes can be used to optimize the relationship between its strength and fracture toughness. A Ti-62A alloy bar can be machined through a transus β-forged plus α+β solution treated and aged specimen with a lamellar alpha microstructure. The effects of heat treatment on the mechanical properties were discussed. Heat treatment provided a practical balance of strength, fracture toughness, and fatigue crack growth resistance. A comparison of the Ti-62A alloy with the Ti-62222S alloy under the same thermo-mechanical processing conditions showed that their properties are at the same level.
基金supported by the National Nature Science Foundation of China (Grant No.50535050)the Vital Foundational 973 Program of Chinafoundation of China Scholarship Council (Project 2007CB607605).
文摘Microporous titanium carbide coating was successfully synthesized on medical grade titanium alloy by using sequential carburization.Changes in the surface morphology of titanium alloy occasioned by sequential carburization were characterized and the wettability characteristics were quantified.Furthermore,the dispersion forces were calculated and discussed.The results indicate that sequential carburization is an effective way to modify the wettability of titanium alloy.After the carburization the surface dispersion force of titanium alloy increased from 76.5×10^(-3)J·m^(-2) to 105.5×10^(-3) J·m^(-2),with an enhancement of 37.9 %.Meanwhile the contact angle of titanium alloy decreased from 83° to 71.5°,indicating a significant improvement of wettability,which is much closer to the optimal water contact angle for cell adhesion of 70°.
文摘The fine-grained microstructure of TA15 titanium alloy was prepared through two-step forging technology combined with high and low temperatures, and a transnormal superplastic elongation of more than 2000% was obtained. The superplastic behaviour and microstructure evolution were systematically researched at different temperatures and strain rates through superplastic tensile test. The results indicate that the fine-grained TA15 alloy exhibits superplasticity at temperatures of 760-980°C and initial strain rates from 1.1 × 10^-2 to 5.5 × 10^-5 s^-1. The optimal superplastic conditions are 940°C and 3.3 × 10^-4 s^-1, in which the average elongation is 2526% and the maximum elongation is 2743%. During superplastic deformation, dynamic recovery and recrystallization occur obviously, and the corporate effect of strain hardening and recrystallization softening decides the superplastic ability directly.
文摘Anodic oxide films of the titanium alloy Ti-10V-2Fe-3Al in ammonium tartrate electrolyte without hydrofluoric acid or fluoride were fabricated. The morphology, components, and microstructure of the films were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD), and Raman spectroscopy. The results showed that the films were thick, uniform, and nontransparent. Such films exhibited sedimentary morphology, with a thickness of about 3 μm, and the pore diameters of the deposits ranged from several hundred nanometers to 1.5 μm. The films were mainly titanium dioxide. Some coke-like deposits, which may contain or be changed by OH, NH, C-C, C-O, and C=O groups, were doped in the films. The films were mainly amorphous with a small amount of anatase and rutile phase.
文摘The development of microstructure during the aging of Ti-10V-2Fe-3A1 alloy in the 13 and (α+β) solution-treated and quenched conditions was investigated. The results showed that the isothermal holding below 400℃ yielded homogeneously distributed, spherical ω-phase particles. Fine α aggregates are formed uniformly within 13 grains by nucleating at at particles or β/ω interfaces. At higher temperatures, thin martensite plates decomposed in water-quenched condition. The formation of ω phase was avoided and coarse coarse α-phase plates directly precipitated from the 13 matrix. The highest hardness values were found when the alloys were aged at 400℃ for 8 h. The significance of the observations was discussed in terms of the effect of aging on the precipitations and property.