To reuse roller waste as a raw material of high performance green ceramic balls, three kinds of white alumina ceramic balls whose wear resistance were 2-3 times of the best high alumina ceramic ball with 90% Al2O3 wer...To reuse roller waste as a raw material of high performance green ceramic balls, three kinds of white alumina ceramic balls whose wear resistance were 2-3 times of the best high alumina ceramic ball with 90% Al2O3 were prepared, and the Al2O3 content of the prepared balls was 75%. It is found that the effect of calcia and magnesia on the wear resistance of ceramic balls is contrast to the accepted one： the wear rate of the ceramic balls prepared in CaO-Al2O3-SiO2 system is the lowest and the wear rate of the ceramic balls prepared in MgO-Al2O3-SiO2 is the highest. The main crystal phase of the ceramic ball is mullite and corundum. The ceramic ball granular is uniform and fine with 4-5 μm average size. The pore diameter is about 2 μm. The wear way of the ceramic balls is mainly transcrystalline fracture.展开更多
基金the National Natural Science Fundation of China(No.50272016),Guangxi 2003 Degree Authorzation Office academic Construction Fun,and Natural Science Fund of Guangxi Education Department(No.[2004]4)
文摘To reuse roller waste as a raw material of high performance green ceramic balls, three kinds of white alumina ceramic balls whose wear resistance were 2-3 times of the best high alumina ceramic ball with 90% Al2O3 were prepared, and the Al2O3 content of the prepared balls was 75%. It is found that the effect of calcia and magnesia on the wear resistance of ceramic balls is contrast to the accepted one： the wear rate of the ceramic balls prepared in CaO-Al2O3-SiO2 system is the lowest and the wear rate of the ceramic balls prepared in MgO-Al2O3-SiO2 is the highest. The main crystal phase of the ceramic ball is mullite and corundum. The ceramic ball granular is uniform and fine with 4-5 μm average size. The pore diameter is about 2 μm. The wear way of the ceramic balls is mainly transcrystalline fracture.