Effect of Crystallographic Orientation on Quenching Stress during Martensitic Phase Transformation of Carbon Steel Plate

During quenching, the residual stresses are affected by the crystallographic orientation of martensite, because the nonuniform thermal stresses affect the crystallographic orientation of the lathshaped martensite and induce the anisotropic expansion. To simulate this process, the model of anisotropic transformation induced plasticity（TRIP） was built using the WLR-BM phenomenological theory. The equivalent expansion coefficient was introduced considering the thermal and plastic strains, which simplified the numerical simulation. Furthermore, the quenching residual stresses in carbon steel plates were calculated using the finite element method under ANSYS Workbench simulation environment. To evaluate the simulative results, distributions of residual stresses from the surface to the interior at the center of specimen were measured using the layer-by-layer hole-drilling method. Compared to the measured results, the simulative results considering the anisotropic expansion induced by the crystallographic orientation of martenstic laths were found to be more accurate than those without considering it.

Quantitative Analysis of the Crystallographic Orientation Relationship Between the Martensite and Austenite in Quenching–Partitioning–Tempering Steels

The orientation relationships（ORs）between the martensite and the retained austenite in low-and medium-carbon steels after quenching–partitioning–tempering process were studied in this work.The ORs in the studied steels are identified by selected-area electron diffraction（SAED）as either K–S or N–W ORs.Meanwhile,the ORs were also studied based on numerical fitting of electron backscatter diffraction data method suggested by Miyamoto.The simulated K–S and N–W ORs in the low-index directions generally do not well coincide with the experimental pole figure,which may be attributed to both the orientation spread from the ideal variant orientations and high symmetry of the low-index directions.However,the simulated results coincide well with experimental pole figures in the high-index directions{123}_（bcc）.A modified method with simplicity based on Miyamoto’s work was proposed.The results indicate that the ORs determined by modified method are similar to those determined by Miyamoto’method,that is,the OR is near K–S OR for the low-carbon Q–P–T steel,and with the increase of carbon content,the OR is closer to N–W OR in medium-carbon Q–P–T steel.