High uniformity and forming-free ZnO-based transparent RRAM with HfO_x inserting layer

The impacts of HfOx inserting layer thickness on the electrical properties of the ZnO-based transparent resistance random access memory （TRRAM） device were investigated in this paper. The bipolar resistive switching behavior of a single ZnO film and bilayer HfOx/ZnO films as active layers for TRRAM devices was demonstrated. It was revealed that the bilayer TRRAM device with a 10-nm HfOx inserted layer had a more stable resistive switching behavior than other devices including the single layer device, as well as being forming free, and the transmittance was more than 80% in the visible region. For the HfOx/ZnO devices, the current conduction behavior was dominated by the space-charge-limited current mechanism in the low resistive state （LRS） and Schottky emission in the high resistive state （HRS）, while the mechanism for single layer devices was controlled by ohmic conduction in the LRS and Poole-Frenkel emission in the HRS.

Enhanced resistance switching stability of transparent ITO/TiO_2/ITO sandwiches

We report that fully transparent resistive random access memory （TRRAM） devices based on ITO/TiO2/ITO sandwich structure, which are prepared by the method of RF magnetron sputtering, exhibit excellent switching stability. In the visible region （400 800 nm in wavelength） the TRRAM device has a transmittance of more than 80%. The fabricated TRRAM device shows a bipolar resistance switching behaviour at low voltage, while the retention test and rewrite cycles of more than 300,000 indicate the enhancement of switching capability. The mechanism of resistance switching is further explained by the forming and rupture processes of the filament in the TiO2 layer with the help of more oxygen vacancies which are provided by the transparent ITO electrodes.

Bipolar resistance switching in the fully transparent BaSnO_3-based memory device

The fully transparent indium-tin-oxide/BaSnO3/F-doped SnO2 devices that show a stable bipolar resistance switching effect are successfully fabricated. In addition to the transmittance being above 87% for visible light, an initial forming process is unnecessary for the production of transparent memory. Fittings to the current-voltage curves reveal the interfacial conduction in the devices. The first-principles calculation indicates that the oxygen vacancies in cubic BaSnO3 will form the defective energy level below the bottom of conduction band. The field-induced resistance change can be explained based on the change of the interracial Schottky barrier, due to the migration of oxygen vacancies in the vicinity of the interface. This work presents a candidate material BaSnO3 for the application of resistive random access memory to transparent electronics.