In this paper, the effect of of flank wear polycrystalline cubic boron nitride （PCBN） tools on residual stresses, white layer and roughness of machined workpiece surfaces is studied. Experimental results indicate th...In this paper, the effect of of flank wear polycrystalline cubic boron nitride （PCBN） tools on residual stresses, white layer and roughness of machined workpiece surfaces is studied. Experimental results indicate that with the increase of the tool wear, the surface of the machined workpiece tends to generate tensile residual stresses, and white layer becomes clearly thicker and uneven on the workpiece surface. The effect of the flank wear on the surface roughness is less within some range of flank wear value. The results show that it is possible to produce ideal surface integrality levels by controlling the tool flank wear.展开更多
This paper discusses experimental results of turnin g experiments on GCr15 bearing steel hardened to 60～64 HRC. The objective was to d etermine the effect of the cutting parameters on cutting force, chip morphology a...This paper discusses experimental results of turnin g experiments on GCr15 bearing steel hardened to 60～64 HRC. The objective was to d etermine the effect of the cutting parameters on cutting force, chip morphology and resultant workpiece surface quality, more specifically surface texture, micr ostructure alterations, changes in microhardness and residual stresses distribut ion. The changing rules of the main cutting force was shown in this paper which feature a increasing tendency with the improvement of the workpiece hardness wit hin the cutting parameter scope. The rule of cutting force changing with the wor kpiece hardness is accord to the traditional metal cutting theory. Stress value decrease with increasing cutting speed and workpiece hardness. The comparison of the machined surface roughness and harden layer depth of machined surface for d ifferent hardness is shown in Fig.1. The machined surface roughness is the worst when the workpiece hardness is around 50HRC. When the workpiece hardness is ove r 50HRC, the surface roughness value shows a descending tendency with the additi on hardness. The machined superficial harden layer depth shows an increasing ten dency with the improvement of the workpiece hardness. When the workpiece hardnes s is 50HRC the machined superficial harden layer depth is tiptop. When the workp iece hardness is over 50HRC the depth changes little with the addition of workpi ece hardness. The remnant stress status of the machined surface is shown in Fig. 2, which is press stress status both in surface and in base for less cutting par ameters under two kinds of cutting condition. But experiment results show that t ensile stress can be produced under uncomfortable cutting conditions. The deform ation created by the chip formation is reduced whereduce with [TPP126A,+35mm77mm,Z,PY#]Depth from surface (μm) ■ v=200m/min,f=0.24mm/r,ap=0.8mm,60HRC ● v=200m/min,f=0.15mm/r,ap=0.5mm,60HRC Fig.1 The subsurface residual stress between the two experimentsHardness (HRC) Fig.2 The surface finish vs. workpiece hardness the workpiece hardness is improved.展开更多
基金Supported by the National Natural Science Foundation of China（No.50875068）,and the National High Technology Research and Development Programme of China（No.2009AA044302）.
文摘In this paper, the effect of of flank wear polycrystalline cubic boron nitride （PCBN） tools on residual stresses, white layer and roughness of machined workpiece surfaces is studied. Experimental results indicate that with the increase of the tool wear, the surface of the machined workpiece tends to generate tensile residual stresses, and white layer becomes clearly thicker and uneven on the workpiece surface. The effect of the flank wear on the surface roughness is less within some range of flank wear value. The results show that it is possible to produce ideal surface integrality levels by controlling the tool flank wear.
文摘This paper discusses experimental results of turnin g experiments on GCr15 bearing steel hardened to 60～64 HRC. The objective was to d etermine the effect of the cutting parameters on cutting force, chip morphology and resultant workpiece surface quality, more specifically surface texture, micr ostructure alterations, changes in microhardness and residual stresses distribut ion. The changing rules of the main cutting force was shown in this paper which feature a increasing tendency with the improvement of the workpiece hardness wit hin the cutting parameter scope. The rule of cutting force changing with the wor kpiece hardness is accord to the traditional metal cutting theory. Stress value decrease with increasing cutting speed and workpiece hardness. The comparison of the machined surface roughness and harden layer depth of machined surface for d ifferent hardness is shown in Fig.1. The machined surface roughness is the worst when the workpiece hardness is around 50HRC. When the workpiece hardness is ove r 50HRC, the surface roughness value shows a descending tendency with the additi on hardness. The machined superficial harden layer depth shows an increasing ten dency with the improvement of the workpiece hardness. When the workpiece hardnes s is 50HRC the machined superficial harden layer depth is tiptop. When the workp iece hardness is over 50HRC the depth changes little with the addition of workpi ece hardness. The remnant stress status of the machined surface is shown in Fig. 2, which is press stress status both in surface and in base for less cutting par ameters under two kinds of cutting condition. But experiment results show that t ensile stress can be produced under uncomfortable cutting conditions. The deform ation created by the chip formation is reduced whereduce with [TPP126A,+35mm77mm,Z,PY#]Depth from surface (μm) ■ v=200m/min,f=0.24mm/r,ap=0.8mm,60HRC ● v=200m/min,f=0.15mm/r,ap=0.5mm,60HRC Fig.1 The subsurface residual stress between the two experimentsHardness (HRC) Fig.2 The surface finish vs. workpiece hardness the workpiece hardness is improved.