Micro-mechanical properties of 2219 welded joints with twin wire welding

Nanoindentation method was adopted to investigate the distribution regularities of micro-mechanical properties of 2219 twin wire welded joints, thus providing the necessary theoretical basis and guidance for joint strengthening and improvement of welding procedure. Experimental results show that in weld zone, micro-mechanical properties are seriously uneven. Both hardness and elastic modulus distribute as uneven sandwich layers, while micro-mechanical properties in bond area are much more uniform than weld zone;In heat-affected zone of 2219 twin wire welded joint, distribution regularity of hardness is similar to elastic modulus. The average hardness in quenching zone is higher than softening zone, and the average elastic modulus in solid solution zone is slightly higher than softening zone. As far as the whole welded joint is concerned, metal in weld possesses the lowest hardness. For welded specimens without reinforcement, fracture position is the weld when tensioning. While for welded specimens with reinforcement, bond area is the poorest position with joint strength coefficient of 61%. So, it is necessary to strengthen the poor positions--weld and bond area of 2219 twin wire welded joint in order to solve joint weakening of welding this kind of alloy.

Prediction of cooling time t8/5 in twin wire submerged arc welding of intermediate thickness plate

Twin wire submerged arc welding （SAW） is widely used in oil or gas line pipe fabrication because of its high productivity. To investigate the strength and toughness of the heat-affected zone （HAZ） in twin wire SAW, the cooling time t8/5 of the coarse grained zone must be studied. The authors presented a method of predicting the cooling time in twin wire SAW of intermediate thickness plate. Based on Rosenthal analytical solutions, an energy factor was introduced to describe the energy contribution of the two wires, equations of thermal cycle and cooling time in twin wire SAW of both thick, and thin, plates were developed. Weighting factors determined by actual thickness and critical thickness were adopted to represent the thermal cycle and cooling time of intermediate thickness plate through linear interpolation with thick, and thin, plate solutions. The predicted cooling time for an intermediate thickness plate was verified experimentally, and the predicted results agreed therewith.

Microstructures of 2219 twin wire welded joints

With thick plates of 2219 high-strength alloy, the microstructures of welded joints with twin wire MIG welding were analyzed. Experimental results show that no hot crack was found in the weld due to discontinuous distribution of cocrystallization with low melting temperature, but porosity is serious in the first weld seam that is mainly composed of equiaxial grains with uneven sizes. As the poor position of the whole welded joint, fusion zone has big and coarse grains, uneven microstructures ; In quenching zone, there exist a lot of soaked microstructures that cocrystallizntion with low melting temperature solute into matrix, thus strengthening the metal in this zone; In excessive aging zone, much more phases that distribute evenly will be separated from the matrix; Ontside this zone, properties and microstructures of the metal are basically similar to matrix due to the relatively low temperature or unaffected heat in the zone during welding.

TANDEM and GMAW Twin Wire Welding of Q690 Steel Used in Hydraulic Support

Compared with using semi-automatic gas shielded arc welding, using automatic TANDEM twin wire welding and twin wire gas metal arc welding （GMAW） to weld Q690 steel, a low-alloy high-strength structural steel used in the hydraulic support in the fully-mechanized mining face, the welding speed, deposition rate, production environment and welding quality can be obviously improved. Compared with GMAW twin wire welding, a refined micro- structure in the weld and heat-affected zone （HAZ）, narrow HAZ and improved joint strength were achieved with TANDEM on Q690. Also, due to the push-pull pulsed way in TANDEM welding, the droplet transfer, distribution on heat flow and interaction between two arcs were completely different from those in GMAW twin wire system. The heat input of TANDEM is only about 76.6% of GMAW, and correspondingly, the welding speed and welding seam can be obviously improved. The complete oscillation caused by TANDEM pulsed current occurred in the welding pool, which refined the grains in the microstructure. The results show that TANDEM twin wire welding is very suitable in the welding of Q690 used in the hydraulic support.