The stoichiometric alloy MlB5.0 and the hypo-stoichiometric alloy MlB4.85 were prepared by twin-roller rapid quenching process, and their structure and electrochemical properties were studied. The results of XRD show ...The stoichiometric alloy MlB5.0 and the hypo-stoichiometric alloy MlB4.85 were prepared by twin-roller rapid quenching process, and their structure and electrochemical properties were studied. The results of XRD show that both of the alloys have a typical single-phase hexagonal CaCus-type structure. The cell volume of the hylpo-stoichiometric alloy M1B4.85 is slightly larger than that of the stoichiometric alloy M1B5.0, although its lattice constant cla is smaller. Under 2 C discharging rate, i.e. 640 mA/g, the M1B4.85 has a discharge capacity of 320 mAh/g, which is higher than that of the M1Bs.o, 312 mAh/g. Nevertheless, the capacities of the M1B4.85 and the M1Bs.o decline 24.7% and 20.2% after 400 cycles, respectively. The relationship of electrochemical performances of the alloys with their structures is discussed.展开更多
基金[This project was supported by the National Natural Science Foundation of China (No. 20373016), the Key Project of In-ternational Science and Technology Cooperation of MOST of China (No. 2005DFA60580), the Key Project of Guangdong Province (No. 2005B50101003), and the Excellent Young Teachers Program of MOE of China.]
文摘The stoichiometric alloy MlB5.0 and the hypo-stoichiometric alloy MlB4.85 were prepared by twin-roller rapid quenching process, and their structure and electrochemical properties were studied. The results of XRD show that both of the alloys have a typical single-phase hexagonal CaCus-type structure. The cell volume of the hylpo-stoichiometric alloy M1B4.85 is slightly larger than that of the stoichiometric alloy M1B5.0, although its lattice constant cla is smaller. Under 2 C discharging rate, i.e. 640 mA/g, the M1B4.85 has a discharge capacity of 320 mAh/g, which is higher than that of the M1Bs.o, 312 mAh/g. Nevertheless, the capacities of the M1B4.85 and the M1Bs.o decline 24.7% and 20.2% after 400 cycles, respectively. The relationship of electrochemical performances of the alloys with their structures is discussed.