The purpose of this multicenter study was to evaluate the clinical performance of an ultrahigh molecular weight polyethylene (UHMWPE) fiber cable for re-attachment of the osteotomized greater trochanter in hip surgery...The purpose of this multicenter study was to evaluate the clinical performance of an ultrahigh molecular weight polyethylene (UHMWPE) fiber cable for re-attachment of the osteotomized greater trochanter in hip surgery. Included in the study were 85 hips that had undergone surgery with greater trochanter osteotomy, including 50 hip arthroplasty procedures and 35 hip osteotomies. The osteotomized greater trochanter was reattached using one or more UHMWPE fiber cables. The bone union and displacement of the greater trochanter were assessed in radiographs for up to 12 months after surgery. Non-union of the osteotomy site occurred in 4.7% of the cases. In approximately 90% of the cases, displacement was less than 2 mm at up to 12 months after surgery. The UHMWPE fiber cable was a good biomaterial for reattaching the osteotomized greater trochanter and may also be an option for osteosynthesis procedures.展开更多
Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-...Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-lar Weight Polyethylene(UHMWPE)fiber reinforcedPE tape prepared with the method of powder impregnat-ion was studied.The effect of impregnate length and thetensile force of the yarn on the fiber content as well as on the strength and modulus of the tape were discussed.Calculation shows that the strength and the modulus ofthe ULMWPE fiber can keep about 85％ after it undergothe process.展开更多
In this paper, statistical optimization method was used to optimize the flash-spinning process conditions. Ultra-high molecular weight polyethylene （UHMWPE） superfine fiber was fabricated by flash-spinning method us...In this paper, statistical optimization method was used to optimize the flash-spinning process conditions. Ultra-high molecular weight polyethylene （UHMWPE） superfine fiber was fabricated by flash-spinning method using UHMWPE as the fiberforming polymer, 1, 2-dichloroethane as the main solvent. The important parameters of the flash-spinning were filtered by Plackett-Burman experimental design based on the single factor experiments. After determining the best regions of the fiber properties, the optimum level of the important parameters were determined by Box-Behnken design. The results of the design showed that the important parameters influencing on the properties of the flash.spinning fiber were spinning temperature, spinning pressure, and spinning solution concentration. The optimum technical parameters were： spinning temperature 186. 4 ~C, spinning pressure 6. 16 MPa, spinning solution concentration 3.06 %. The highest combination property of the flash-spinning fiber was 86.39 under this condition.展开更多
Ultrahigh molecular weight polyethylene (UHMWPE)/WS2 nanoparticle fibers were prepared by adding WS2 nanoparticles treated by coupling agent in the precursor solution of UHMWPE. The influence of WS2 nanoparticles on t...Ultrahigh molecular weight polyethylene (UHMWPE)/WS2 nanoparticle fibers were prepared by adding WS2 nanoparticles treated by coupling agent in the precursor solution of UHMWPE. The influence of WS2 nanoparticles on the microstructure and properties of UHMWPE fibers was characterized by SEM, TGA, mechanical property measurement and bullet-shock test. The results showed that WS2 nanoparticles can be uniformly dispersed in the UHMWPE fiber. After incorporating of WS2 nanoparticles, UHMWPE fibers became stiffer and tougher than the pristine ones. Particularly, the modulus of the fiber increased from 1203 to 1326cN/dtex. Furthermore, UHMWPE/WSfibers showed an improved thermal stability.展开更多
采用M80弹(7.62 mm×51 mm NATO)分别对常温和高温(55℃)下的防弹插板进行实弹射击试验,以研究高温环境对防弹插板抗弹性能的影响。通过分析试验时防弹插板弹击瞬间凹陷值,同时结合聚氨酯树脂的剥离强度、超高分子量聚乙烯纤维层压...采用M80弹(7.62 mm×51 mm NATO)分别对常温和高温(55℃)下的防弹插板进行实弹射击试验,以研究高温环境对防弹插板抗弹性能的影响。通过分析试验时防弹插板弹击瞬间凹陷值,同时结合聚氨酯树脂的剥离强度、超高分子量聚乙烯纤维层压板剥离强度和弯曲强度的测试结果对高温下抗弹性能变化原因进行了研究。结果表明:高温下防弹插板抗弹性能明显下降,相对于常温下每发弹的弹击瞬间凹陷值增加了2~5 mm。其主要原因是超高分子量聚乙烯纤维层压板在高温下抵抗变形的能力发生明显下降,从而导致防弹插板的弹击瞬间凹陷值增大。展开更多
文摘The purpose of this multicenter study was to evaluate the clinical performance of an ultrahigh molecular weight polyethylene (UHMWPE) fiber cable for re-attachment of the osteotomized greater trochanter in hip surgery. Included in the study were 85 hips that had undergone surgery with greater trochanter osteotomy, including 50 hip arthroplasty procedures and 35 hip osteotomies. The osteotomized greater trochanter was reattached using one or more UHMWPE fiber cables. The bone union and displacement of the greater trochanter were assessed in radiographs for up to 12 months after surgery. Non-union of the osteotomy site occurred in 4.7% of the cases. In approximately 90% of the cases, displacement was less than 2 mm at up to 12 months after surgery. The UHMWPE fiber cable was a good biomaterial for reattaching the osteotomized greater trochanter and may also be an option for osteosynthesis procedures.
文摘Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-lar Weight Polyethylene(UHMWPE)fiber reinforcedPE tape prepared with the method of powder impregnat-ion was studied.The effect of impregnate length and thetensile force of the yarn on the fiber content as well as on the strength and modulus of the tape were discussed.Calculation shows that the strength and the modulus ofthe ULMWPE fiber can keep about 85％ after it undergothe process.
基金Key Project of Chinese Ministry of Education( No. 208005)Instructional Technology Project of National Textile andApparel Council, China ( No.2009076)Application Fundamental and Advanced Technology Research Proposal Project of Tianjin, China(No.10 JCYBJC03100)
文摘In this paper, statistical optimization method was used to optimize the flash-spinning process conditions. Ultra-high molecular weight polyethylene （UHMWPE） superfine fiber was fabricated by flash-spinning method using UHMWPE as the fiberforming polymer, 1, 2-dichloroethane as the main solvent. The important parameters of the flash-spinning were filtered by Plackett-Burman experimental design based on the single factor experiments. After determining the best regions of the fiber properties, the optimum level of the important parameters were determined by Box-Behnken design. The results of the design showed that the important parameters influencing on the properties of the flash.spinning fiber were spinning temperature, spinning pressure, and spinning solution concentration. The optimum technical parameters were： spinning temperature 186. 4 ~C, spinning pressure 6. 16 MPa, spinning solution concentration 3.06 %. The highest combination property of the flash-spinning fiber was 86.39 under this condition.
基金supported by the National Natural Science Foundation of China (51002184 and 50972018)
文摘Ultrahigh molecular weight polyethylene (UHMWPE)/WS2 nanoparticle fibers were prepared by adding WS2 nanoparticles treated by coupling agent in the precursor solution of UHMWPE. The influence of WS2 nanoparticles on the microstructure and properties of UHMWPE fibers was characterized by SEM, TGA, mechanical property measurement and bullet-shock test. The results showed that WS2 nanoparticles can be uniformly dispersed in the UHMWPE fiber. After incorporating of WS2 nanoparticles, UHMWPE fibers became stiffer and tougher than the pristine ones. Particularly, the modulus of the fiber increased from 1203 to 1326cN/dtex. Furthermore, UHMWPE/WSfibers showed an improved thermal stability.
文摘采用M80弹(7.62 mm×51 mm NATO)分别对常温和高温(55℃)下的防弹插板进行实弹射击试验,以研究高温环境对防弹插板抗弹性能的影响。通过分析试验时防弹插板弹击瞬间凹陷值,同时结合聚氨酯树脂的剥离强度、超高分子量聚乙烯纤维层压板剥离强度和弯曲强度的测试结果对高温下抗弹性能变化原因进行了研究。结果表明:高温下防弹插板抗弹性能明显下降,相对于常温下每发弹的弹击瞬间凹陷值增加了2~5 mm。其主要原因是超高分子量聚乙烯纤维层压板在高温下抵抗变形的能力发生明显下降,从而导致防弹插板的弹击瞬间凹陷值增大。