This work explored the way to improve hot modulus q/＇ rupture （HMOR） and refractoriness under load （RUL） by adding mild-calcined coal gangue （MCG） in Al2O3 -SiO2 ultra low cement （ULC） castables, making use o...This work explored the way to improve hot modulus q/＇ rupture （HMOR） and refractoriness under load （RUL） by adding mild-calcined coal gangue （MCG） in Al2O3 -SiO2 ultra low cement （ULC） castables, making use of the in-situ effect of the MCG during heating-up. The influence of respective additions of 5%, 10% and 1.5% of the MCG powders calcined at 700℃ was investigated on HMOR at 1400 ℃ and RUL of the castables. With increased addition of the MCG, HMOR and RUL become significantly enhanced. At 10% of the MCG addition, HMOR reaches 3 MPa, as compared to 0. 3 MPa in the case of no MCG addition. RUL of the specimens dried at 110 ℃for 24 h can be increased by some 270 ℃ with 10% of the MCG addition. RUL 0.11 the specimens preheated at 1 500℃ for 3 h maintains the growth trend with the MCG addition increasing. The microstructure of the heated castable samples was investigated by means of SEM. The in-situ formed needle-like and interlaced mullite in the matrix is contributive to the tmprovement.展开更多
磁性铁是超贫磁铁矿勘查中的基本分析项目之一,为准确测定磁性铁的含量,首先需要实现磁性铁的定量分离。目前常用的手工内磁选法由于所用磁铁的有效磁场强度难以保证,而且受人为操作的影响较大,导致分析结果的重现性差。本文应用50 m L...磁性铁是超贫磁铁矿勘查中的基本分析项目之一,为准确测定磁性铁的含量,首先需要实现磁性铁的定量分离。目前常用的手工内磁选法由于所用磁铁的有效磁场强度难以保证,而且受人为操作的影响较大,导致分析结果的重现性差。本文应用50 m L滴定管、电磁铁和三相异步电动机,研制了一种新型磁选装置——电磁式磁性铁分选装置,实现了超贫磁铁矿中磁性铁与非磁性铁的定量分离,结合重铬酸钾容量法建立了超贫磁铁矿中磁性铁的分析方法。在选定的磁选条件下(电流2.5 A,磁选管运动频率40 r/min,磁选时间5 min)分析铁矿石标准物质,磁性铁的测定值与标准值的相对误差小于1.0%;分析采自实际矿区的超贫磁铁矿样品,磁性铁的测定结果与手工内磁选法一致,且相对标准偏差(RSD,n=5)小于1.0%,优于手工内磁选法的精密度。本方法采用的电磁式磁性铁分选装置有效地控制了磁场强度的强弱,避免永磁铁出现磁损失,同时可以量化磁性铁分离的参数,提高了磁性铁的分析精度。展开更多
文摘This work explored the way to improve hot modulus q/＇ rupture （HMOR） and refractoriness under load （RUL） by adding mild-calcined coal gangue （MCG） in Al2O3 -SiO2 ultra low cement （ULC） castables, making use of the in-situ effect of the MCG during heating-up. The influence of respective additions of 5%, 10% and 1.5% of the MCG powders calcined at 700℃ was investigated on HMOR at 1400 ℃ and RUL of the castables. With increased addition of the MCG, HMOR and RUL become significantly enhanced. At 10% of the MCG addition, HMOR reaches 3 MPa, as compared to 0. 3 MPa in the case of no MCG addition. RUL of the specimens dried at 110 ℃for 24 h can be increased by some 270 ℃ with 10% of the MCG addition. RUL 0.11 the specimens preheated at 1 500℃ for 3 h maintains the growth trend with the MCG addition increasing. The microstructure of the heated castable samples was investigated by means of SEM. The in-situ formed needle-like and interlaced mullite in the matrix is contributive to the tmprovement.