Ultra high molar mass polyethylene(UHPE)powder as polymerized in a slurry process has been studied,in its nascent state,after recrystallization on rapid cooling from the melt and after hot compression molding to a fil...Ultra high molar mass polyethylene(UHPE)powder as polymerized in a slurry process has been studied,in its nascent state,after recrystallization on rapid cooling from the melt and after hot compression molding to a film,by DSC,effect of annealing the recrystallized specimen at 120 similar to 130 degreesC,morphology by polarizing optical microscopy and small angle X-ray scattering.Based on the experimental results obtained the macromolecular condensed state of the nascent UHPE powder is a rare case of a multi-chain condensed state of non-interpenetrating chains,involving interlaced extended chain crystalline layers and relaxed parallel chain amorphous layers.On melting,a nematic rubbery state of nanometer size domain resulted.The nematic-isotropic transition temperature was judged from literature data to be at least 220 degreesC,possibly higher than 300 ℃,the exact temperature is however not sue because of chain degradation at such high temperatures.The recrystallization process from the melt is a crystallization from a nematic rubbery state.The drop of remelting peak temperature by 10 K of the specimen recrystallized from its melt as compared to the nascent state has its origin in the decrease both of the crystalline chain stem length and of the degree of crystallinity.The remelting peak temperature could be returned close to that of the nascent state by annealing at 120~130 ℃.展开更多
Ultra-high molecular weight polyethylene (UHMWPE) with a microporous structure was prepared via thermally induced phase separation (TIPS).Liquid paraffin (LP) was used as a diluent in the preparation of microporous UH...Ultra-high molecular weight polyethylene (UHMWPE) with a microporous structure was prepared via thermally induced phase separation (TIPS).Liquid paraffin (LP) was used as a diluent in the preparation of microporous UHMWPE. Small angle laser light scattering (SALLS) and differential scanning calorimetry (DSC) were used to determine the phase separation temperatures,i.e.the cloud points and the dynamic crystallization temperatures,respectively.It was found that the cloudI points were coincident with the cryst...展开更多
High-strength and high-modulus ultra-high molecular weight polyethylene(UHMWPE), named self-reinforced material, was obtained by the elongation of UHMWPE-montmorillonite nanocomposite at melting temperature. According...High-strength and high-modulus ultra-high molecular weight polyethylene(UHMWPE), named self-reinforced material, was obtained by the elongation of UHMWPE-montmorillonite nanocomposite at melting temperature. According to the scanning electron microscope(SEM) analysis, a great deal of fibrillar texture formed in the direction of elongation, and the tensile fractured surface was similar to that of highly oriented fiber. The transmission electron microscope(TEM) and selective area electron diffraction(SAED) analyses reveal that the reinforced phase of the self-reinforced material is an extended chain crystal and its size is about 50_200 nm wide and several microns long, and the montmorillonite layers are broken up to pieces in the size from 100 to 10 nm. The broken layers which have a huge surface area interacting strongly with macromolecules reduces the entanglement density of UHMWPE and induces the chain orientation in flow field. It is supposed that the astriction of montmorillonite layers to polyethylene chains is not only end-tethered but also side-tethered. The differential scan calorimetry(DSC) analysis shows that there are two endothermal peaks for the self-reinforced material, of which the peak at a higher temperature(136.4 ℃) is ascribed to the melting of the reinforced phase.展开更多
Managing fractures of distal humerus in patients with rheumatoid arthritis (RA) is technically challenging. Total elbow arthroplasty (TEA) is one of the treatment options for these fractures. While elbow motion is lar...Managing fractures of distal humerus in patients with rheumatoid arthritis (RA) is technically challenging. Total elbow arthroplasty (TEA) is one of the treatment options for these fractures. While elbow motion is largely regained by TEA, comminuted condyle fragments are often ignored. Although numerous approaches for repair of condylar fragments around TEA are described, any universal fixation strategy for these fractures has not been established. This report describes, for the first time, application of an ultra-high molecular weight polyethylene (UHMWPE) tape for the treatment of distal humerus fracture in 2 patients with rheumatic elbow arthropathy. The post-operative clinical courses were good. Radiographs showed bony union of the condylar fragments without loosening in two cases. Because of its flat configuration, softness, and flexibility, UHMWPE tape is a promising material for stabilizing fracture of the distal humerus associated with TEA.展开更多
Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-...Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-lar Weight Polyethylene(UHMWPE)fiber reinforcedPE tape prepared with the method of powder impregnat-ion was studied.The effect of impregnate length and thetensile force of the yarn on the fiber content as well as on the strength and modulus of the tape were discussed.Calculation shows that the strength and the modulus ofthe ULMWPE fiber can keep about 85% after it undergothe process.展开更多
This paper reports the spinning and drawing behavior of Ultra-high Molecular Weight polyethylene Terephthalate) (UHMW-PET) fibers. The as-spun fibers were produced by dry-jet wet spinning of a 15%-17% solution in 50:5...This paper reports the spinning and drawing behavior of Ultra-high Molecular Weight polyethylene Terephthalate) (UHMW-PET) fibers. The as-spun fibers were produced by dry-jet wet spinning of a 15%-17% solution in 50:50(v:v) trifluroroacetic acid and dichloromethane. Both molecular weight and polymer solution concentration have marked effect on the drawability of the as-spun-fibers. The maximum extension drawing ratio (EDRmax) of as-spun fiber increases with increasing molecular weight, whereas optimal concentration to achieve the EDRmax of as-spun fibers decreases with increasing molecular weight. Drawing speed and temperature during the first step have remarkable effect on the drawability of these fiber during the second step. Relatively lower drawing temperature and drawing speed (19 ℃ , 60 mm/min) during the first drawing step was beneficial to mechanical properties of ultimate fibers. At the range of 210 ℃ to 230 ℃, the draw ratio (DR) during the second step increases with increasing temperature.展开更多
Clinical two-dimensional linear wear rate data for acetabular cup liners fabricated using approved brands of highly cross-linked ultra-high-molecular-weight polyethylene, as reported in 39 articles in the literature, ...Clinical two-dimensional linear wear rate data for acetabular cup liners fabricated using approved brands of highly cross-linked ultra-high-molecular-weight polyethylene, as reported in 39 articles in the literature, were analyzed using a statistical technique called response surface methodology. The output was a series comprising16 acceptable combinations of femoral head diameter (HD), femoral head material (HM), and HXLPE brand (PB), each of which would yield the optimum wear rate (herein taken to be a wear rate of practically zero). An example of such a combination is 28- mm-diameter Oxinium? femoral head articulated against an acetabular cup liner fabricated from ReflectionTM HXLPE. The findings in this work may guide an orthopaedic surgeon’s selection of the combination of HD, HM, and PB to use in a primary total hip joint replacement.展开更多
采用M80弹(7.62 mm×51 mm NATO)分别对常温和高温(55℃)下的防弹插板进行实弹射击试验,以研究高温环境对防弹插板抗弹性能的影响。通过分析试验时防弹插板弹击瞬间凹陷值,同时结合聚氨酯树脂的剥离强度、超高分子量聚乙烯纤维层压...采用M80弹(7.62 mm×51 mm NATO)分别对常温和高温(55℃)下的防弹插板进行实弹射击试验,以研究高温环境对防弹插板抗弹性能的影响。通过分析试验时防弹插板弹击瞬间凹陷值,同时结合聚氨酯树脂的剥离强度、超高分子量聚乙烯纤维层压板剥离强度和弯曲强度的测试结果对高温下抗弹性能变化原因进行了研究。结果表明:高温下防弹插板抗弹性能明显下降,相对于常温下每发弹的弹击瞬间凹陷值增加了2~5 mm。其主要原因是超高分子量聚乙烯纤维层压板在高温下抵抗变形的能力发生明显下降,从而导致防弹插板的弹击瞬间凹陷值增大。展开更多
基金This work was supported by the National Key Projects for Fundamental Research-“Macromoleular Condensed State”,Ministry of Science and Technology,China
文摘Ultra high molar mass polyethylene(UHPE)powder as polymerized in a slurry process has been studied,in its nascent state,after recrystallization on rapid cooling from the melt and after hot compression molding to a film,by DSC,effect of annealing the recrystallized specimen at 120 similar to 130 degreesC,morphology by polarizing optical microscopy and small angle X-ray scattering.Based on the experimental results obtained the macromolecular condensed state of the nascent UHPE powder is a rare case of a multi-chain condensed state of non-interpenetrating chains,involving interlaced extended chain crystalline layers and relaxed parallel chain amorphous layers.On melting,a nematic rubbery state of nanometer size domain resulted.The nematic-isotropic transition temperature was judged from literature data to be at least 220 degreesC,possibly higher than 300 ℃,the exact temperature is however not sue because of chain degradation at such high temperatures.The recrystallization process from the melt is a crystallization from a nematic rubbery state.The drop of remelting peak temperature by 10 K of the specimen recrystallized from its melt as compared to the nascent state has its origin in the decrease both of the crystalline chain stem length and of the degree of crystallinity.The remelting peak temperature could be returned close to that of the nascent state by annealing at 120~130 ℃.
基金supported by Special Funds for Major State Basic Research Projects,China (No.2003CB615705).
文摘Ultra-high molecular weight polyethylene (UHMWPE) with a microporous structure was prepared via thermally induced phase separation (TIPS).Liquid paraffin (LP) was used as a diluent in the preparation of microporous UHMWPE. Small angle laser light scattering (SALLS) and differential scanning calorimetry (DSC) were used to determine the phase separation temperatures,i.e.the cloud points and the dynamic crystallization temperatures,respectively.It was found that the cloudI points were coincident with the cryst...
文摘High-strength and high-modulus ultra-high molecular weight polyethylene(UHMWPE), named self-reinforced material, was obtained by the elongation of UHMWPE-montmorillonite nanocomposite at melting temperature. According to the scanning electron microscope(SEM) analysis, a great deal of fibrillar texture formed in the direction of elongation, and the tensile fractured surface was similar to that of highly oriented fiber. The transmission electron microscope(TEM) and selective area electron diffraction(SAED) analyses reveal that the reinforced phase of the self-reinforced material is an extended chain crystal and its size is about 50_200 nm wide and several microns long, and the montmorillonite layers are broken up to pieces in the size from 100 to 10 nm. The broken layers which have a huge surface area interacting strongly with macromolecules reduces the entanglement density of UHMWPE and induces the chain orientation in flow field. It is supposed that the astriction of montmorillonite layers to polyethylene chains is not only end-tethered but also side-tethered. The differential scan calorimetry(DSC) analysis shows that there are two endothermal peaks for the self-reinforced material, of which the peak at a higher temperature(136.4 ℃) is ascribed to the melting of the reinforced phase.
文摘Managing fractures of distal humerus in patients with rheumatoid arthritis (RA) is technically challenging. Total elbow arthroplasty (TEA) is one of the treatment options for these fractures. While elbow motion is largely regained by TEA, comminuted condyle fragments are often ignored. Although numerous approaches for repair of condylar fragments around TEA are described, any universal fixation strategy for these fractures has not been established. This report describes, for the first time, application of an ultra-high molecular weight polyethylene (UHMWPE) tape for the treatment of distal humerus fracture in 2 patients with rheumatic elbow arthropathy. The post-operative clinical courses were good. Radiographs showed bony union of the condylar fragments without loosening in two cases. Because of its flat configuration, softness, and flexibility, UHMWPE tape is a promising material for stabilizing fracture of the distal humerus associated with TEA.
文摘Due to the low density and excellent mechanical proper-ties,high performance fiber reinforced materials have aconsiderable application in the area of high technologyand dally usage.In this paper,the Ultra-high Molecu-lar Weight Polyethylene(UHMWPE)fiber reinforcedPE tape prepared with the method of powder impregnat-ion was studied.The effect of impregnate length and thetensile force of the yarn on the fiber content as well as on the strength and modulus of the tape were discussed.Calculation shows that the strength and the modulus ofthe ULMWPE fiber can keep about 85% after it undergothe process.
文摘This paper reports the spinning and drawing behavior of Ultra-high Molecular Weight polyethylene Terephthalate) (UHMW-PET) fibers. The as-spun fibers were produced by dry-jet wet spinning of a 15%-17% solution in 50:50(v:v) trifluroroacetic acid and dichloromethane. Both molecular weight and polymer solution concentration have marked effect on the drawability of the as-spun-fibers. The maximum extension drawing ratio (EDRmax) of as-spun fiber increases with increasing molecular weight, whereas optimal concentration to achieve the EDRmax of as-spun fibers decreases with increasing molecular weight. Drawing speed and temperature during the first step have remarkable effect on the drawability of these fiber during the second step. Relatively lower drawing temperature and drawing speed (19 ℃ , 60 mm/min) during the first drawing step was beneficial to mechanical properties of ultimate fibers. At the range of 210 ℃ to 230 ℃, the draw ratio (DR) during the second step increases with increasing temperature.
文摘Clinical two-dimensional linear wear rate data for acetabular cup liners fabricated using approved brands of highly cross-linked ultra-high-molecular-weight polyethylene, as reported in 39 articles in the literature, were analyzed using a statistical technique called response surface methodology. The output was a series comprising16 acceptable combinations of femoral head diameter (HD), femoral head material (HM), and HXLPE brand (PB), each of which would yield the optimum wear rate (herein taken to be a wear rate of practically zero). An example of such a combination is 28- mm-diameter Oxinium? femoral head articulated against an acetabular cup liner fabricated from ReflectionTM HXLPE. The findings in this work may guide an orthopaedic surgeon’s selection of the combination of HD, HM, and PB to use in a primary total hip joint replacement.
文摘采用M80弹(7.62 mm×51 mm NATO)分别对常温和高温(55℃)下的防弹插板进行实弹射击试验,以研究高温环境对防弹插板抗弹性能的影响。通过分析试验时防弹插板弹击瞬间凹陷值,同时结合聚氨酯树脂的剥离强度、超高分子量聚乙烯纤维层压板剥离强度和弯曲强度的测试结果对高温下抗弹性能变化原因进行了研究。结果表明:高温下防弹插板抗弹性能明显下降,相对于常温下每发弹的弹击瞬间凹陷值增加了2~5 mm。其主要原因是超高分子量聚乙烯纤维层压板在高温下抵抗变形的能力发生明显下降,从而导致防弹插板的弹击瞬间凹陷值增大。