Ultra-fine-grained commercial purity aluminum was produced by severe cold rolling, annealing and then strain- ing at ultra-high rate by a single pass laser shock. Resulted microstructure was investigated by transmissi...Ultra-fine-grained commercial purity aluminum was produced by severe cold rolling, annealing and then strain- ing at ultra-high rate by a single pass laser shock. Resulted microstructure was investigated by transmission electron microscopy. Microhardness of annealed 0.6μm ultra-fine grained aluminum increased by 67% from 24 to 40 HV. Many 0.3 μm sub-grains appeared at the shock wave center after a single pass laser shock, while high density dislocation networks were observed in some grains at the shock wave edges. Accordingly, microhardness at the impact center increased by 37.5% from 40 to 55 HV. From the impact center to the edge, microhardness decreased by 22% from 55 to 45 HV.展开更多
基金support from the National Natural Science Foundation of China (No. 50801021)
文摘Ultra-fine-grained commercial purity aluminum was produced by severe cold rolling, annealing and then strain- ing at ultra-high rate by a single pass laser shock. Resulted microstructure was investigated by transmission electron microscopy. Microhardness of annealed 0.6μm ultra-fine grained aluminum increased by 67% from 24 to 40 HV. Many 0.3 μm sub-grains appeared at the shock wave center after a single pass laser shock, while high density dislocation networks were observed in some grains at the shock wave edges. Accordingly, microhardness at the impact center increased by 37.5% from 40 to 55 HV. From the impact center to the edge, microhardness decreased by 22% from 55 to 45 HV.