Effect of Strain Ratio on Fatigue Model of Ultra-fine Grained Pure Titanium

The ultra-fine grained(UFG)pure titanium was prepared by equal channel angular pressing(ECAP)and rotary swaging(RS).The strain controlled low cycle fatigue(LCF)test was carried out at room temperature.The fatigue life prediction model and mean stress relaxation model under asymmetrical stress load were discussed.The results show that the strain ratio has a significant effect on the low cycle fatigue performance of the UFG pure titanium,and the traditional Manson-coffin model can not accurately predict the fatigue life under asymmetric stress load.Therefore,the SWT mean stress correction model and three-parameter power curve model are proposed,and the test results are verified.The final research shows that the threeparameter power surface model has better representation.By studying the mean stress relaxation phenomenon under the condition of R≠-1,it is revealed that the stress ratio and the strain amplitude are the factors that significantly afiect the mean stress relaxation rate,and the mean stress relaxation model with the two variables is calculated to describe the mean stress relaxation phenomenon of the UFG pure titanium under different strain ratios.The fracture morphology of the samples was observed by SEM,and it was concluded that the final fracture zone of the fatigue fracture of the UFG pure titanium was a mixture of ductile fracture and quasi cleavage fracture.The toughness of the material increases with the increase of strain ratio at the same strain amplitude.

DYNAMIC RHEOLOGICAL BEHAVIOR OF POLYPROPYLENE FILLED WITH ULTRA-FINE POWDERED RUBBER PARTICLES

Dynamic rheological characteristics of polypropylene (PP) filled with ultra-fine full-vulcanized powdered rubber (UFPR) composed of styrene-butadiene copolymer were studied through dynamic rheological measurements on an Advanced Rheometric Expansion System (ARES). A specific viscoelastic phenomenon, i.e. 'the second plateau', appeared at low frequencies, and exhibits a certain dependence on the amount of rubber particles and the dispersion state in the matrix. This phenomenon is attributed to the formation of aggregation structure of rubber particles. The analyses of Cole-Cole diagrams of the dynamic viscoelastic functions suggest that the heterogeneity of the composites is enhanced on increasing both particle content and temperature.

Optimal Conditions for Preparing Ultra-Fine CeO_2 Powders in A Submerged Circulative Impinging Stream Reactor

Cerium carbonate powders were produced in a submerged circulation impinging stream reactor （SCISR） from Ce（NO3）3· 6H2O. NH4HCO3 was used as a precipitant in the reaction. Cerium carbonate powders were roasted to produce ultra-fine cerium dioxide （CeO2） powders. The optimal conditions of such production process were obtained by orthogonal and one-factor experiments. The results showed that ultra-fine and narrowly distributed cerium carbonate powders were produced under the optimal flowing conditions. The concentrations of Ce（NO3）3 and NH4HCO3 solutions were 02,5 and 0.3 mol · L^-1, respectively. The concentration of PEG4000 added in these two solutions was 4 g · L^-1. The stirring ratio, reaction temperature, feeding time, solution pH, reaction time and digestion time were 900 r · min^- 1,80 ℃, 20 min, 5 - 6, 5 min and 1 h, respectively. The final product, CeO2 powders, was obtained by roasting the produced cerium carbonate in air for 3 h at 500 ℃. The finally produced CeO2 powders were torispherical particles with a narrow size distribution of 0.8 -2.5 μm. The crystal structure of CeO2 powders belonged to cubic crystal system and its space point 5 group was OH^5-FM3M. Under optimal conditions, powders produced by SCISR were finer and more narrowly distributed than that by Stirred Tank Reactor （STR）.

Microstructures of ultra-fine grained FeCoV alloys processed by ECAP plus cold rolling and their evolutions during tempering

A new processing method,equal channel angular pressing(ECAP)plus cold rolling(CR),was applied to producing ultra-fine grained FeCoV alloy.The microstructures of ultra-fine grained FeCoV alloy after ECAP,ECAP plus CR,and the effect of tempering treatment on the microstructure of FeCoV alloy produced by ECAP plus CR were investigated.The results show that an elongated substructure with a width of about 0.3μm is obtained after four-pass ECAP using Route A.Cold rolling after ECAP cannot change the morphologies of elongated substructure,and it results in higher fraction of high-angle boundaries and higher dislocation density compared with the identical ECAP without rolling.Subsequent tempering for 30 min at 853 K brings about many nano-phases precipitating at subgrain boundaries and insides the grains,and the size of precipitated phase is measured to be about 10 nm.Nano-phases grow up with increasing tempering temperature and equiaxed structure forms at 883 K.

Weld formation and heating mechanism in ultra-narrow gap withconstricted arc by ultra-fine granular flux

Ultra-narrow gap welding （UNGW） process with high stabilization, reliability and without spatter can be achieved with constricted arc by molten slag wall, which is made from melted flux. The experiments are carried out by changing voltage under different currents. The results indicate voltage range being fit for UNGW is about 22 -31 V under the current range of 200 -320 A. With the increasing of voltage, weld formation of UNGW has the law of lack of fusion on sidewall, good weld and undercut in turn under a certain current. In addition, the action relationships among arc, molten slag wall and sidewalls can be improved by properly adjusting voltage and current of arc, which makes cathode spot properly distribute in ultra-narrow gap. Therefore, the effective control of weld formation of UNGW has been achieved.

Isothermal Growth Kinetics of Ultra-fine Austenite Grains in a Nb-V-Ti Microalloyed Steel

Ultra-fine austenite grains with size of i-3 μm were prepared in a Nb-V-Ti steel through repetitive treatment of rapid heating and quenching. A model for the growth kinetics of these ultra-fine austenite grains was successfully created through successive 2 processes, and the activation energy Q for growth was estimated to be about 693.2 kJ/mol, which directly shows the inhibition effect of microalloy elements on the growth of ultra-fine austenite grains.

Influence of Ultra-Fine B_4C and Nano-SiO_2 on the Properties of Alumina-Graphite Refractories

The role of nano-SiO 2 and ultra-fine boron carbide on the properties of alumina-graphite materials was investigated. The study showed that the ultra-fine boron carbide added modified the microstructure of residual carbon and promoted the chemical bond between residual carbon from phenolic resin and flake graphite. The carbon white could strengthen the residual carbon from phenolic resin. These two additives improved the mechanical properties of AG refractories at both room temperature and high temperature, and thermal shock resistance was improved noticeably. When the two additives were doped together, carbon white could retard the evaporation of B 2O 3. Thermal shock resistance was guaranteed with a smaller amount of ultra-fine boron carbide.

Preparation of Well Dispersed and Ultra-Fine Ce(Zr)O_2 Mixed Oxide by Mechanochemical Processing

Ultra-fine CeO_2-ZrO_2 mixed oxide was successfully synthesized by wet-solid phase mechanochemical processing, Ce_2(CO_3)_3·8H_2O, ZrOCl_2·xH_2O and ammonia were used as reactants. It is found that the crystalline Ce_2(CO_3)_3·8H_2O and ZrOCl_2·xH_2O are changed to amorphous cerium and zirconium hydroxide precursor after milling with ammonia, and Ce_(0.15)Zr_(0.85)O_2 mixed oxide with pure tetragonal phase structure and medium particle size(D_(50))less than 1μm is formed by calcining precursor over 673 K. The XRD patterns indicate that the crystal unite size increases with rising calcining temperature due to crystal growth. However, the particle size and BET surface area of the Ce(Zr)O_2 mixed oxide decreases with rising calcining temperature, which may be attributed to the contract of particles and the vanish of holes inside grains.

Microstructural Evolution and Thermal Stability of Ultra-fine Grained Al-4Mg Alloy by Equal Channel Angular Pressing

Experiments were conducted to evaluate the grain refinement and thermal stability of ultra-fine grained Al-4Mgalloy introduced by equal-channel angular pressing (ECAP) at 473 K. The results show that the intensities of X-ray(111/222) and (200/400) peaks for the alloy processed by ECAP decrease significantly and the peak widths of halfheight become broadening compared with the corresponding value in the annealed alloy. The microstructure of 2passes ECAPed alloy consists of both elongated and equiaxed subgrains. The residual strain in the alloy increaseswith increasing passes numbers, that appears as increasing dislocation density and lattice constant of matrix. Anequiaxed ultra-fine grained structure of～0.2μm is obtained in the present alloy after 8 passes. The ultra-fine grainsare stable below 523 K, because the alloy retains extremely fine grain size of～1μm after static annealing at 523 Kfor 1 h.

Strengthening of HT250 by modified ultra-fine ceramic powders

In this study, three kinds of modified ultra-fine ceramic powders marked A, B and C, which were prepared by each of three different modifiers mixing with a commercial SiC, were added to HT250 cast iron, respectively, and the effects of the modified ultra-fine ceramic powders on microstructure, mechanical properties and wear resistance were studied. Metallographic examination, tensile test, scanning electron microscopy, and three-dimensional surface topography were applied to analyze and compare the samples containing modified powder with the original samples. The results showed that the most obvious modification effect among the powders was seen in the sample containing powder A, with the graphite and eutectic cells being refined, the tensile strength being increased by 36.9%, and the wear resistance being improved by 45.5% and 47.2% under loads of 150 N and 300 N, respectively. The improvements of mechanical properties and wear resistance in the HT250 cast iron with the modified ultra-fine ceramic powders were attributed to the synergistic effect of the grain refinement with the powder acting as a hard particle phase and the lubrication by the graphite.

Ultra-fine ferrite grains obtained in the TSDR process

By careful design of rolling schedule,ultra-fine （～2μm） ferrite grains in a low carbon high niobium （0.09wt%Nb） microalloying steel with average austenite grain sizes above 800 μm can be achieved in the simulated thin slab direct rolling process. The 5-pass deformation was divided into two stages： the refinement of austenite through complete recrystallization and the refinement of ferrite through dynamic strain-induced transformation. The effects of Nb in solution and strain-induced NbCN precipitates on the ferrite transformation were also extensively discussed.

Hydrogen Reduction:A Novel Method of Synthesizing Ultra-fine Chromic Oxide Powder

The ultra-fine chromic oxide powder was prepared by a novel gas-solid reduction reaction.Na2CrO4 was firstly reduced with hydrogen at 400-600 ℃.The obtained reduction products,mainly the mixture of NaCrO2 and sodium hydroxide（NaOH）,were converted into chromic oxide through hydrolysis followed by calcination.The obtained chromic oxide product was characterized by powder X-ray diffraction（XRD） and SEM.The results show that the hydrolysis process of sodium chromite is the key step and lower reduction temperature helps intensify the hydrolysis process.

The Rheological Properties of Ultra-fine High Performance Grouting Cement

The material properties of surface and powder, rheological property, and mineral composition were investigated by means of SEM, XRD, Malvern laser granulometer and rotary, viscometer. The influence of a admixture on ultra-fine cement rheological properties and its mechanism, were studied in material theories. The results show that the ultra-fine fly ash has a higher zeta potential, and improves flowability of ultra-fine cement paste, decreases flowability loss as time prolonging, improves compatibility between superplasticizers and cement because of the electrostatic repulsion, ball bearing effect, filling and dispersing effect of admixtures and delay-releasing effect of superplasticizers.

Effect of upsetting force on microstructure of welds in resistance spot welding of 400 MPa ultra-fine grain steel

The ultra-fine grain （UFG） steel is welded by using resistance spot welding technique with or without requirement of upsetting force. Metallographic inspection shows that the grain size of weld nugget is larger than that of the base metal and the microstructure is altered significantly. In addition, contracting defects such as air holes can be found in the nugget center. The experiments show that the defects can be effectively avoided by the technique of adding upsetting force during the nugget cooling and crystallizing processes. In tensile shear tests, the welding joint starts to crack from the inner edge of the corona bond. The results of micro-hardness tests show that the newly born martensite structure dramatically improves the hardness of the joint. Under the interactions between residual stresses and regenerated fine grains, the micro-hardness of the heat-affected zone （ HAZ ） is lower than that of the nugget, but evidently higher than that of the base metal.

Effect of welding heat input on HAZ character in ultra-fine grain steel welding

In this essay, we studied how heat input affected the microstructure, hardness, grain size and heat-affected zone(HAZ) dimension of WCX355 ultra-fine grain steel which was welded respectively by the ultra narrow-gap welding (UNGW) process and the overlaying process with CO 2 as protective atmosphere and laser welding process. The experimental results show when the heat input changed from 1.65 kJ/cm to 5.93 kJ/cm, the width of its HAZ ranged from 0.6 mm to 2.1 mm.The average grain size grew up from 2～5 μm of base metal to 20～70 μm and found no obvious soften phenomenon in overheated zone. The width of normalized zone was generally wide as 2/3 as that of the whole HAZ, and the grain size in this zone is smaller than that in base metal. Under the circumstance of equal heat input, the HAZ width of UNGW is narrower than that of the laser welding.

Manufacturing of High-efficiency Air Filter Paper Using Ultra-fine Fibers

In this paper,the manufacturing of high-efficiency air filter paper is reported.The air filter paper was produced using ultra-fine fibers and wateroat fibers mercerized by alkali,using an electrospinning apparatus with multiple rings.The high efficiency air filter paper has an antibacterial effect after adding a chitosan-copper complex which is harmless to humans.As a result of the measurement,the filtering efficiency of the air filter paper is approximately 99.998%and its antibacterial efficiency is approximately 99.5%.

Hydraulicity of Wet-milling Ultra-fine Grouting Cement

The physical and mechanical properties of wet-milling ultra-fine grouting cement were studied,and its microstructure was observed through modern instrumentation analysis such as scanning electronic microscopy(SEM),X-ray diffraction and Hg-intrusion micromeritics.The experimental results indicate that wet-milling ultra-fine cement possesses high rheological properties and groutability.It can be filled densely in cracks of rock and hydrate fully,which may endow hydrated cement with high mechanical strength.Main hydration products of wet-milling ultra-fine cement are poorly crystalline C-S-H(Ⅰ),acicular AFt and plank-shape Ca(OH)_2.The dense crystal-network structure can be formed in the rock gaps filled with cement paste,but some weak regions exist owing to Ca(OH)_2.The features of micro-pore structure of hydrated wet-milling ultra-fine cement are few big harmful pores,abundant harmless micro pores and little most possible pore radius.

Study on Ultra-fine Microstructure of Cast Iron under Rapid Solidification

The ultra-fine microstructrue of cast iron has been studied under rapid solidification by laser rapid meltingand solidifying method and SEM and TEM technology and results show cementite, martensite, austenite and ultra-fineperlite phases can be obtained under rapid solidification and many dislocations have been the found in cementite.

Synthesis and Characterization of Ultra-fine Cr_2O_3 from Hydrogen Reduction of K_2CrO_4

As a part of the green process for manufacturing chromium compounds, two steps are involved in the synthesis of ultra-fine Cr2O3 powders： the first is the hydrogen reduction of K2CrO4 into intermediate trivalent （Cr^3＋） or tetravalent （Cr^4＋） chromium compounds; the second is the decomposing of the intermediate into Cr2O3 by heat treating. The intermediate is well characterized by means of SEM, XRD, and XPS. The possible reaction mechanism of the process is analyzed.

Surface Cracking Behaviors of Ultra-Fine Grained Tungsten Under Edge Plasma Loading in the HT-7 Tokamak

Tests of the candidate plasma facing materials（PFMs） used in experimental fusion devices are essential due to the direct influence of in-situ plasma loading.A type of ultrafine grained（UFG） tungsten sintered by resistance sintering under ultra-high pressure（RSUHP） method has been exposed in the edge plasma of the HT-7 tokamak to investigate its performance under plasma loading.Under cychc edge plasma loading,the UFG tungsten develops both macro and micro cracks.The macro cracks are attributed to the low temperature brittleness of the tungsten material itself,while the micro cracks are generated from local intense power flux deposition.