The 18%Ni alloy steels provide high strength and toughness, while age-hardenable or PH stainless steels also have good corrosion resistance. This paper focuses on an investigation of the heat treatment, mechanical pro...The 18%Ni alloy steels provide high strength and toughness, while age-hardenable or PH stainless steels also have good corrosion resistance. This paper focuses on an investigation of the heat treatment, mechanical properties and microstructural development of a new maraging stainless steel. It is reported that the heat treatment process should consist of solution treatment and cryogenic cooling to attain a fully martensitic structure, followed by aging at 813 K. This heat treatment resulted in an ultimate tensile strength of over 1900 MPa combined with good impact toughness. Transmission electron microscopy is used to show that, for the peak-aged condition (813 K/4 h), nano-sized precipitates, e.g. Ni3Mo and/or R-phase, and a high density of dislocations were uniformly dispersed in the lath martensite matrix. The calculated yield strength, based on a revised Orowan mechanism, is in good agreement with the test data. The steel studied has an ultimate tensile strength over 1900 MPa, excellent fracture toughness, and good resistance against over-aging and relatively good corrosion resistance as well.展开更多
The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite (CFB/M) complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrason...The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite (CFB/M) complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of "soft structure". It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.展开更多
The corrosion behaviors of ultra-high strength steel 30CrMnSiNi2A in sodium chloride solution were studied by weight loss and electrochemical methods. The morphology of corrosion products was observed using scanning e...The corrosion behaviors of ultra-high strength steel 30CrMnSiNi2A in sodium chloride solution were studied by weight loss and electrochemical methods. The morphology of corrosion products was observed using scanning electron microscopy(SEM) and the composition was analyzed using an energy dispersive spectroscopy(EDS) and X-Ray diffraction (XRD). The experimental results showed that the corrosion came from pitting corrosion and the rust layer was composed of outer rust layer γ-FeOOH and inner rust layer Fe_2O_3 with a little β-FeOOH. The correlation between corrosion rate and test time accorded with exponential rule. The corrosion current measured by polarization methods was higher than that calculated by weight loss method after a long-time immersion, the main reason was that,β-FeOOH and γ-Fe_2O_3 transformed by γ-FeOOH led to overestimating corrosion rate. The processes of corrosion prophase were obtained from XRD and EIS results. The corrosion product, Fe(OH)_2 formed at the initial stage stayed at a non-steady state and then consequently transferred to γ-FeOOH, γ-Fe_2O_3 or β-FeOOH.展开更多
AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding jo...AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.展开更多
This paper studied the spot welding structure of ultra-high strength steel 22MnB5.ANSYS software was adopted to simulate its static strength;BS5400 algorithm was used to calculate the fatigue life;and the grouping met...This paper studied the spot welding structure of ultra-high strength steel 22MnB5.ANSYS software was adopted to simulate its static strength;BS5400 algorithm was used to calculate the fatigue life;and the grouping method was used to test the fatigue performance of tensile shear spot weld specimens.The simulation results were in good agreement with the experimental values.Based on the validation of the simulation method,influences of different structural parameters on static strength and fatigue life were explored by adopting single factor.The results showed that within the selected structure parameter range,increase of the sheet thickness,nugget diameter,sheet width and overlapping length can lead to longer fatigue life.Besides,the fatigue life of spot weld took on a linear relationship with the overlapping length,a DoseResp relationship with the sheet thickness,and a single exponential decay relationship with the sheet width and the nugget diameter.Moreover,in order to estimate the impact from various parameters on the fatigue life of the specimens,the Taguchi orthogonal design method was applied in the simulation design.The simulating result indicated that influence of the sheet thickness on fatigue life was the most significant.In addition,the effects of nugget diameter,sheet width and overlapping length on fatigue life were reduced in turn.展开更多
The effects of the composition and cooling process on the microstructures and properties of hot-rolled ultra-high strength low alloy (HSLA) steel, complex phase steel and martensite steel were studied in the laborat...The effects of the composition and cooling process on the microstructures and properties of hot-rolled ultra-high strength low alloy (HSLA) steel, complex phase steel and martensite steel were studied in the laboratory. And S700MC and MP1200 ultra-high strength steels were trial produced at the 1 880 mm hot-rolling line of Baosteel. Compared with conventional hot-rolled high strength products,the idea that water is alloy was applied in the newly developed hot-rolled ultra-high strength steel. By the use of the economical composition design and controlled cooling after hot-rolling effectively,ultra-high strength steel of different steel grades can be obtained.展开更多
In this study,the scale and internal oxidation of hot-rolled ultra-high strength steel sheets were characterized.It was found that both the formation of the scale and the internal oxidation of Si and Mn depended on th...In this study,the scale and internal oxidation of hot-rolled ultra-high strength steel sheets were characterized.It was found that both the formation of the scale and the internal oxidation of Si and Mn depended on the coiling temperature and position of the steel sample on the strip coil.At a relatively high coiling temperature,a large amount of internal oxidation was observed on the samples cut from the middle of the coil.The depth of the internal oxidation zone exceeded 10 μm and a thin iron layer covering the scale was observed in some cases.Pickling and cold-rolling experiments were conducted on selected samples.Scale pickling was found to be greatly delayed by the formation of an iron layer,which frequently resulted in under-pickled defects.In addition,pickling of the entire internal oxidation zone was difficult,except at the grain boundaries,where the degree of internal Si and Mn oxidation was enriched.The surface of the cold-rolled steel sheet was ruined by the remaining oxidation zone in the subsurface of the pickled steel.The internal oxidation of hot-rolled ultra-high strength steel must be precisely controlled to improve the subsequent surface quality of cold-rolled steel.展开更多
Corrosion behavior of 300M in neutralcorrosion environments containing Na Clsimulated by totalimmersion(TI),salt spraying(SS)and periodic immersion(PI),was investigated by surface analysis techniques,corrosion w...Corrosion behavior of 300M in neutralcorrosion environments containing Na Clsimulated by totalimmersion(TI),salt spraying(SS)and periodic immersion(PI),was investigated by surface analysis techniques,corrosion weight-loss method,and electrochemicalmeasurements.In totalimmersion environment,rust on the steelconsisted of a porous outer rust layer with main constituent of γ-Fe OOH,and an inner rust layer of dense Fe_3O_4 film with network broad cracks.In salt spraying environment,outer rust with main composition of γ-Fe OOH/α-Fe OOH/Fe_3O_4 was compact,and inner rust showed dense Fe_3O_4 film.Rust formed by periodic immersion exhibited a compact outer rust layer with constituent of α-Fe OOH/γ-Fe OOH/Fe_3O_4 and an inner rust layer with composition of α-Fe OOH/α-Fe_2O_3;inner rust showed a ultra-dense film adherent to the steel.The corrosion rate showed a rule of vss(salt spraying)〉vti(totalimmersion)〉〉vpi(periodic immersion)in 0-240 h,and vss≈vti?vpiin 240-720 h.The rust formed by periodic immersion was dense and compact,with stable electrochemicalproperties,and had excellent protection on the steel.Humidity and oxygen concentration in allthe environments played major roles in rust formation.展开更多
Ultra-high strength special steels and wrought Ni-base superalloys are been ever increasingly applied in aircraft and aerospace,power generation,oil-gas and other industries.The development of those materials is drive...Ultra-high strength special steels and wrought Ni-base superalloys are been ever increasingly applied in aircraft and aerospace,power generation,oil-gas and other industries.The development of those materials is driven by tougher working conditions,higher efficiency,environment consideration,resource limitation and cost reduction. This presentation will focus on the development of ultra high strength special steels and wrought Ni-base superalloys in aircraft industry. The examples of ultra-high strength steels include: (1) Ultra-high strength stainless steels for landing gear and other structures; (2)High speed and high temperature main shaft bearing steels; (3) Ultra-high strength steels for jet engine main shaft. New and modified Ni-base superalloys will be discussed by examples of (1 )Low cost,process-friendly superalloys with higher performance; (2)Modification of hard-to-processed superalloys. Future development of those materials will be addressed.展开更多
In this paper, the performance of HG70D welded joint of ultra-high strength steel plates is presented, and the performance of HG70D and Q345B welded joints is studied. The high strength steel plate HG70D showed excell...In this paper, the performance of HG70D welded joint of ultra-high strength steel plates is presented, and the performance of HG70D and Q345B welded joints is studied. The high strength steel plate HG70D showed excellent weldability. Through the X-ray inspection of welded joints, tensile strength, impact test and bending performance test, the comprehensive performance of the joint was excellent. The macroscopic and microscopic metallographic analysises of the welded joints show that the welding seams included pearlite, sorbite, ferrite, etc. The influence of stress annealing temperature on HG70D of high strength steel plate was analyzed by heat treatment.展开更多
As the aircraft and aerospace industry and the automobile industry are developed, the demand of reliable materials with high strength and high toughness is steadily increased. The grain miniature method which improves...As the aircraft and aerospace industry and the automobile industry are developed, the demand of reliable materials with high strength and high toughness is steadily increased. The grain miniature method which improves the ductility and the toughness simultaneously under high strength is the miniature of the casting microstructure. In this paper, the Nb which affects the austenite grain miniature is added by 0.00%, 0.03% and 0.06% in this steel and the ingot is manufactured in a vacuum induction melting furnace (VIM). The casting microstructure and the mechanical property of the maraging steel according to Nb contents are analyzed by conducting the solution annealing and the age hardening after hot rolling. In this result, a specimen containing 0.03% Nb is most miniature. When it does the long time age hardening, the precipitation estimated as the carbide is appeared. The mechanical properties are excellent if a specimen containing 0.06% Nb does the age hardening during 8 h in 482℃.展开更多
The effect of quenching temperature on the stress corrosion cracking of 30Cr3SiNiMoV ultra-high strength steel in 3.5% NaCl aqueous solution has been studied.The threshold K_(ISCC) may continuously increase with the q...The effect of quenching temperature on the stress corrosion cracking of 30Cr3SiNiMoV ultra-high strength steel in 3.5% NaCl aqueous solution has been studied.The threshold K_(ISCC) may continuously increase with the quenching temperature raised from 870 to 1200℃ . All of the fractures are intergranular.The analyses of the segregation along prior austenitic grain boundaries,grain size and other microstructural factors reveal that the inerease of K_(ISCC) is mainly due to the coarsening of prior austenitic grains.展开更多
The microstructure and properties of a combined precipitation hardening ultrahigh strength steel with nano-sized carbides and intermetallics were studied systematically.The results show that after tempering at 300℃lo...The microstructure and properties of a combined precipitation hardening ultrahigh strength steel with nano-sized carbides and intermetallics were studied systematically.The results show that after tempering at 300℃lots ofε-carbides are precipitated in the martensite,the strength rises and the toughness falls slightly.After tempering at 430℃,much coarser cementite lamina are precipitated in martensitic laths,which causes the impact toughness falls to the minimum value.With temperature further increasing the cementites are dissolved and M_2C carbides,β-NiAl intermetallics and reverse austenite begin to precipitate.The tensile strength and yield strength achieve the peak value at 470℃,490℃respectively.The tested steel achieve a tensile strength of 2 120 MPa,a yield strength of 1 950 MPa and impact energy of 54 J/cm^2 after optimum tempering at 510℃.When tempering temperature is above 530℃the M_2C carbides and reverse austenite is coarsening.After tempering at 560℃the reverse austenite reaches the maximum volume fraction in present work.展开更多
Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel prod...Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel products.Some milestones achieved by Baosteel automotive steel sheet were briefly reviewed.The current challenges in producing ultra-high strength steel(UHSS),especially hot-dip galvanized UHSS,were summarized.The most current advancements in UHSS and the corresponding hot-dip galvanizing processes were discussed.The galvanizability of Si-Mn-added QP steel and DP steel, Mn-added TWIP steel, and Al-added low-density steel has been improved by different techniques in Baosteel.展开更多
The development of ultrastrong maraging stainless steels(MSSs)is always in high demand.However,traditional high-strength MSSs generally exhibit early plastic instability with a low uniform strain since the precipitate...The development of ultrastrong maraging stainless steels(MSSs)is always in high demand.However,traditional high-strength MSSs generally exhibit early plastic instability with a low uniform strain since the precipitated nanoparticles are non-coherent with the body-centered-cubic(BCC)lath martensitic matrix.Here,we design a novel ultrahigh strength MSS(Fe-5.30 Cr-13.47 Ni-3.10 Al-1.22 Mo-0.50 W-0.23 Nb-0.03 C-0.005 B,wt.%)using a cluster formula approach.A fabulous microstructure consisting of a uniform distribution of high-density coherent B2-Ni Al nanoprecipitates(3-5 nm)in BCC martensitic matrix was successfully obtained.This alloy has not only an exceedingly high ultimate tensile strength of 2.0 GPa,but also a decent uniform elongation of 4.2%-5.1%,which is almost triple of the value observed in existing MSSs.We present an in-depth discussion on the origins of ultrahigh strength and uniform plastic strain in the new alloy to validate our design strategy and further offer a new pathway to exploit highperformance MSSs.展开更多
The use of ultra-high strength steels through sheet metal forming process offers a practical solution to the lightweight design of vehicles.However,sheet metal forming process not only produces desirable changes in ma...The use of ultra-high strength steels through sheet metal forming process offers a practical solution to the lightweight design of vehicles.However,sheet metal forming process not only produces desirable changes in material properties but also causes material damage that may adversely influence the service performance of the material formed.Thus,an investigation is conducted to experimentally quantify such influence for a commonly used steel(the 22MnB5 steel) based on the hot and cold forming processes.For each process,a number of samples are used to conduct a uniaxial tensile test to simulate the forming process.After that,some of the samples are trimmed into a standard shape and then uniaxially extended until fracture to simulate the service stage.Finally,a microstructure test is conducted to analyze the microdefects of the remaining samples.Based on the results of the first two tests,the effect of material damage on the service performance of 22MnB5 steel is analyzed.It is found that the material damages of both the hot and cold forming processes cause reductions in the service performance,such as the failure strain,the ultimate stress,the capacity of energy absorption and the ratio of residual strain.The reductions are generally lower and non-linear in the former process but higher and linear in the latter process.Additionally,it is found from the microstructure analysis that the difference in the reductions of the service performance of 22MnB5 by the two forming processes is driven by the difference in the micro damage mechanisms of the two processes.The findings of this research provide a useful reference in terms of the selection of sheet metal forming processes and the determination of forming parameters for 22MnB5.展开更多
The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between...The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between the bainitic ferrite lathes was found in the steel after isothermally quenched at 300℃ for 1h.In comparison with the martensite structure obtained by isothermally quenching in martensite range,the meta-bainite has more excellent strength and plasticity,lower notch sensitivity,stronger strain harden ability,higher fatigue strength, longer strain or impact fatigue life,slower crack propagation rate and more remarkable overload effect on increasing fatigue life.展开更多
The hierarchical martensitic features in ultra-high strength stainless steel(UHSSS),including the prior austenite grains,martensite packets,blocks and laths with the descending size,were refined to various extents by ...The hierarchical martensitic features in ultra-high strength stainless steel(UHSSS),including the prior austenite grains,martensite packets,blocks and laths with the descending size,were refined to various extents by employing different thermomechanical processes and then carefully characterized.Their relation to yield strength and impact toughness was analyzed.We conclude that the refinement of martensitic structures could lead to the significant increase of yield strength,which follows the Hall-Petch relation with the effect grain size defined by high angle boundaries(HABs).Impact toughness of UHSSS depends on the frequency and capability for retained austenite(RA)grains at both HABs and martensite lath boundaries to trap the propagating cracks via strain-induced transformation,in which the film-like RA grains at lath boundaries appear to make the greater contribution.展开更多
文摘The 18%Ni alloy steels provide high strength and toughness, while age-hardenable or PH stainless steels also have good corrosion resistance. This paper focuses on an investigation of the heat treatment, mechanical properties and microstructural development of a new maraging stainless steel. It is reported that the heat treatment process should consist of solution treatment and cryogenic cooling to attain a fully martensitic structure, followed by aging at 813 K. This heat treatment resulted in an ultimate tensile strength of over 1900 MPa combined with good impact toughness. Transmission electron microscopy is used to show that, for the peak-aged condition (813 K/4 h), nano-sized precipitates, e.g. Ni3Mo and/or R-phase, and a high density of dislocations were uniformly dispersed in the lath martensite matrix. The calculated yield strength, based on a revised Orowan mechanism, is in good agreement with the test data. The steel studied has an ultimate tensile strength over 1900 MPa, excellent fracture toughness, and good resistance against over-aging and relatively good corrosion resistance as well.
基金supported by the National Key Fundamental Research and Development Program of China (No.2004CB619105)
文摘The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite (CFB/M) complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of "soft structure". It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.
基金Funded by the National Natural Science Foundation of China(No.51171011)
文摘The corrosion behaviors of ultra-high strength steel 30CrMnSiNi2A in sodium chloride solution were studied by weight loss and electrochemical methods. The morphology of corrosion products was observed using scanning electron microscopy(SEM) and the composition was analyzed using an energy dispersive spectroscopy(EDS) and X-Ray diffraction (XRD). The experimental results showed that the corrosion came from pitting corrosion and the rust layer was composed of outer rust layer γ-FeOOH and inner rust layer Fe_2O_3 with a little β-FeOOH. The correlation between corrosion rate and test time accorded with exponential rule. The corrosion current measured by polarization methods was higher than that calculated by weight loss method after a long-time immersion, the main reason was that,β-FeOOH and γ-Fe_2O_3 transformed by γ-FeOOH led to overestimating corrosion rate. The processes of corrosion prophase were obtained from XRD and EIS results. The corrosion product, Fe(OH)_2 formed at the initial stage stayed at a non-steady state and then consequently transferred to γ-FeOOH, γ-Fe_2O_3 or β-FeOOH.
基金Funded by the National Natural Science Foundation of China(Nos.51201087,51165038)the Project of Jiangxi Province of Education(No.GJJ13493)+1 种基金the State Key Laboratory of Solidification Processing in NWPU(No.SKLSP201306)the China Postdoctoral Science Foundation(No.2014M552485)
文摘AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.
基金financially supported by the Beijing Natural Science Foundation(3122004)
文摘This paper studied the spot welding structure of ultra-high strength steel 22MnB5.ANSYS software was adopted to simulate its static strength;BS5400 algorithm was used to calculate the fatigue life;and the grouping method was used to test the fatigue performance of tensile shear spot weld specimens.The simulation results were in good agreement with the experimental values.Based on the validation of the simulation method,influences of different structural parameters on static strength and fatigue life were explored by adopting single factor.The results showed that within the selected structure parameter range,increase of the sheet thickness,nugget diameter,sheet width and overlapping length can lead to longer fatigue life.Besides,the fatigue life of spot weld took on a linear relationship with the overlapping length,a DoseResp relationship with the sheet thickness,and a single exponential decay relationship with the sheet width and the nugget diameter.Moreover,in order to estimate the impact from various parameters on the fatigue life of the specimens,the Taguchi orthogonal design method was applied in the simulation design.The simulating result indicated that influence of the sheet thickness on fatigue life was the most significant.In addition,the effects of nugget diameter,sheet width and overlapping length on fatigue life were reduced in turn.
文摘The effects of the composition and cooling process on the microstructures and properties of hot-rolled ultra-high strength low alloy (HSLA) steel, complex phase steel and martensite steel were studied in the laboratory. And S700MC and MP1200 ultra-high strength steels were trial produced at the 1 880 mm hot-rolling line of Baosteel. Compared with conventional hot-rolled high strength products,the idea that water is alloy was applied in the newly developed hot-rolled ultra-high strength steel. By the use of the economical composition design and controlled cooling after hot-rolling effectively,ultra-high strength steel of different steel grades can be obtained.
文摘In this study,the scale and internal oxidation of hot-rolled ultra-high strength steel sheets were characterized.It was found that both the formation of the scale and the internal oxidation of Si and Mn depended on the coiling temperature and position of the steel sample on the strip coil.At a relatively high coiling temperature,a large amount of internal oxidation was observed on the samples cut from the middle of the coil.The depth of the internal oxidation zone exceeded 10 μm and a thin iron layer covering the scale was observed in some cases.Pickling and cold-rolling experiments were conducted on selected samples.Scale pickling was found to be greatly delayed by the formation of an iron layer,which frequently resulted in under-pickled defects.In addition,pickling of the entire internal oxidation zone was difficult,except at the grain boundaries,where the degree of internal Si and Mn oxidation was enriched.The surface of the cold-rolled steel sheet was ruined by the remaining oxidation zone in the subsurface of the pickled steel.The internal oxidation of hot-rolled ultra-high strength steel must be precisely controlled to improve the subsequent surface quality of cold-rolled steel.
基金Funded by the National Natural Science Foundation of China(No.51171011)
文摘Corrosion behavior of 300M in neutralcorrosion environments containing Na Clsimulated by totalimmersion(TI),salt spraying(SS)and periodic immersion(PI),was investigated by surface analysis techniques,corrosion weight-loss method,and electrochemicalmeasurements.In totalimmersion environment,rust on the steelconsisted of a porous outer rust layer with main constituent of γ-Fe OOH,and an inner rust layer of dense Fe_3O_4 film with network broad cracks.In salt spraying environment,outer rust with main composition of γ-Fe OOH/α-Fe OOH/Fe_3O_4 was compact,and inner rust showed dense Fe_3O_4 film.Rust formed by periodic immersion exhibited a compact outer rust layer with constituent of α-Fe OOH/γ-Fe OOH/Fe_3O_4 and an inner rust layer with composition of α-Fe OOH/α-Fe_2O_3;inner rust showed a ultra-dense film adherent to the steel.The corrosion rate showed a rule of vss(salt spraying)〉vti(totalimmersion)〉〉vpi(periodic immersion)in 0-240 h,and vss≈vti?vpiin 240-720 h.The rust formed by periodic immersion was dense and compact,with stable electrochemicalproperties,and had excellent protection on the steel.Humidity and oxygen concentration in allthe environments played major roles in rust formation.
文摘Ultra-high strength special steels and wrought Ni-base superalloys are been ever increasingly applied in aircraft and aerospace,power generation,oil-gas and other industries.The development of those materials is driven by tougher working conditions,higher efficiency,environment consideration,resource limitation and cost reduction. This presentation will focus on the development of ultra high strength special steels and wrought Ni-base superalloys in aircraft industry. The examples of ultra-high strength steels include: (1) Ultra-high strength stainless steels for landing gear and other structures; (2)High speed and high temperature main shaft bearing steels; (3) Ultra-high strength steels for jet engine main shaft. New and modified Ni-base superalloys will be discussed by examples of (1 )Low cost,process-friendly superalloys with higher performance; (2)Modification of hard-to-processed superalloys. Future development of those materials will be addressed.
文摘In this paper, the performance of HG70D welded joint of ultra-high strength steel plates is presented, and the performance of HG70D and Q345B welded joints is studied. The high strength steel plate HG70D showed excellent weldability. Through the X-ray inspection of welded joints, tensile strength, impact test and bending performance test, the comprehensive performance of the joint was excellent. The macroscopic and microscopic metallographic analysises of the welded joints show that the welding seams included pearlite, sorbite, ferrite, etc. The influence of stress annealing temperature on HG70D of high strength steel plate was analyzed by heat treatment.
基金supported by Research Funds from Chosun University,2007.
文摘As the aircraft and aerospace industry and the automobile industry are developed, the demand of reliable materials with high strength and high toughness is steadily increased. The grain miniature method which improves the ductility and the toughness simultaneously under high strength is the miniature of the casting microstructure. In this paper, the Nb which affects the austenite grain miniature is added by 0.00%, 0.03% and 0.06% in this steel and the ingot is manufactured in a vacuum induction melting furnace (VIM). The casting microstructure and the mechanical property of the maraging steel according to Nb contents are analyzed by conducting the solution annealing and the age hardening after hot rolling. In this result, a specimen containing 0.03% Nb is most miniature. When it does the long time age hardening, the precipitation estimated as the carbide is appeared. The mechanical properties are excellent if a specimen containing 0.06% Nb does the age hardening during 8 h in 482℃.
文摘The effect of quenching temperature on the stress corrosion cracking of 30Cr3SiNiMoV ultra-high strength steel in 3.5% NaCl aqueous solution has been studied.The threshold K_(ISCC) may continuously increase with the quenching temperature raised from 870 to 1200℃ . All of the fractures are intergranular.The analyses of the segregation along prior austenitic grain boundaries,grain size and other microstructural factors reveal that the inerease of K_(ISCC) is mainly due to the coarsening of prior austenitic grains.
文摘The microstructure and properties of a combined precipitation hardening ultrahigh strength steel with nano-sized carbides and intermetallics were studied systematically.The results show that after tempering at 300℃lots ofε-carbides are precipitated in the martensite,the strength rises and the toughness falls slightly.After tempering at 430℃,much coarser cementite lamina are precipitated in martensitic laths,which causes the impact toughness falls to the minimum value.With temperature further increasing the cementites are dissolved and M_2C carbides,β-NiAl intermetallics and reverse austenite begin to precipitate.The tensile strength and yield strength achieve the peak value at 470℃,490℃respectively.The tested steel achieve a tensile strength of 2 120 MPa,a yield strength of 1 950 MPa and impact energy of 54 J/cm^2 after optimum tempering at 510℃.When tempering temperature is above 530℃the M_2C carbides and reverse austenite is coarsening.After tempering at 560℃the reverse austenite reaches the maximum volume fraction in present work.
文摘Baosteel has excelled in automotive steel sheets in the past three decades.It has made a significant contribution to the development of China’s automotive industry by producing a wide range of high-quality steel products.Some milestones achieved by Baosteel automotive steel sheet were briefly reviewed.The current challenges in producing ultra-high strength steel(UHSS),especially hot-dip galvanized UHSS,were summarized.The most current advancements in UHSS and the corresponding hot-dip galvanizing processes were discussed.The galvanizability of Si-Mn-added QP steel and DP steel, Mn-added TWIP steel, and Al-added low-density steel has been improved by different techniques in Baosteel.
基金supported by the National Natural Science Foundation of China[grant numbers 91860108,U1867201]Natural Science Foundation of Liaoning Province of China[grant number 2019-KF-05-01]the Fundamental Research Funds for the Central Universities[grant number DUT19LAB01]。
文摘The development of ultrastrong maraging stainless steels(MSSs)is always in high demand.However,traditional high-strength MSSs generally exhibit early plastic instability with a low uniform strain since the precipitated nanoparticles are non-coherent with the body-centered-cubic(BCC)lath martensitic matrix.Here,we design a novel ultrahigh strength MSS(Fe-5.30 Cr-13.47 Ni-3.10 Al-1.22 Mo-0.50 W-0.23 Nb-0.03 C-0.005 B,wt.%)using a cluster formula approach.A fabulous microstructure consisting of a uniform distribution of high-density coherent B2-Ni Al nanoprecipitates(3-5 nm)in BCC martensitic matrix was successfully obtained.This alloy has not only an exceedingly high ultimate tensile strength of 2.0 GPa,but also a decent uniform elongation of 4.2%-5.1%,which is almost triple of the value observed in existing MSSs.We present an in-depth discussion on the origins of ultrahigh strength and uniform plastic strain in the new alloy to validate our design strategy and further offer a new pathway to exploit highperformance MSSs.
基金Supported by National Natural Science Foundation of China(Grant No.51375201)CSAE(Beijing)Automotive Lightweight Technology Research Institute Development Fund Project of China
文摘The use of ultra-high strength steels through sheet metal forming process offers a practical solution to the lightweight design of vehicles.However,sheet metal forming process not only produces desirable changes in material properties but also causes material damage that may adversely influence the service performance of the material formed.Thus,an investigation is conducted to experimentally quantify such influence for a commonly used steel(the 22MnB5 steel) based on the hot and cold forming processes.For each process,a number of samples are used to conduct a uniaxial tensile test to simulate the forming process.After that,some of the samples are trimmed into a standard shape and then uniaxially extended until fracture to simulate the service stage.Finally,a microstructure test is conducted to analyze the microdefects of the remaining samples.Based on the results of the first two tests,the effect of material damage on the service performance of 22MnB5 steel is analyzed.It is found that the material damages of both the hot and cold forming processes cause reductions in the service performance,such as the failure strain,the ultimate stress,the capacity of energy absorption and the ratio of residual strain.The reductions are generally lower and non-linear in the former process but higher and linear in the latter process.Additionally,it is found from the microstructure analysis that the difference in the reductions of the service performance of 22MnB5 by the two forming processes is driven by the difference in the micro damage mechanisms of the two processes.The findings of this research provide a useful reference in terms of the selection of sheet metal forming processes and the determination of forming parameters for 22MnB5.
文摘The microstructure,strength,toughness and fatigue properties of an ultra-high strength steel 40CrMnSiMoVA have been investigated.The so-called meta-bainite,composed of thin re- tained austenite films within or between the bainitic ferrite lathes was found in the steel after isothermally quenched at 300℃ for 1h.In comparison with the martensite structure obtained by isothermally quenching in martensite range,the meta-bainite has more excellent strength and plasticity,lower notch sensitivity,stronger strain harden ability,higher fatigue strength, longer strain or impact fatigue life,slower crack propagation rate and more remarkable overload effect on increasing fatigue life.
基金the support from the National Key Research and Development Program of China(2016YFB0300202 and 2016YFB0300102)the Fundamental Research Funds for the Central Universities(No.FRF-TP-18-002C2)。
文摘The hierarchical martensitic features in ultra-high strength stainless steel(UHSSS),including the prior austenite grains,martensite packets,blocks and laths with the descending size,were refined to various extents by employing different thermomechanical processes and then carefully characterized.Their relation to yield strength and impact toughness was analyzed.We conclude that the refinement of martensitic structures could lead to the significant increase of yield strength,which follows the Hall-Petch relation with the effect grain size defined by high angle boundaries(HABs).Impact toughness of UHSSS depends on the frequency and capability for retained austenite(RA)grains at both HABs and martensite lath boundaries to trap the propagating cracks via strain-induced transformation,in which the film-like RA grains at lath boundaries appear to make the greater contribution.