Effect of low-temperature tempering on the mechanical properties of cold-rolled martensitic steel

Cold-rolled martensitic steel is an important type of advanced high-strength steel for automobile production.With martensite as its primary microstructure constituent, martensitic steel possesses exceptional high strength despite its low alloy content.As the strength of cold-rolled martensitic steel increases, the martensite and carbon content also increases, leading to a decrease in bending properties and toughness.In this paper, the effect of various tempering parameters on the bending property and impact toughness of a quenched cold-rolled martensitic steel sheet was studied.It is found that after quenching, the ductility and impact toughness of the experimental steel are improved using low-temperature heat treatment.The optimal tempering conditions for ductility and toughness are analyzed.

Effect of Microstructure Refinement on the Strength and Toughness of Low Alloy Martensitic Steel

Martensitic microstructure in quenched and tempered 17CrNiMo6 steel with the prior austenite grain size ranging from 6 μm to 199 μm has been characterized by optical metallography （OM）, scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The yield strength and the toughness of the steel with various prior austenite grain sizes were tested and correlated with microstructure characteristics. Results show that both the prior austenite grain size and the martensitic packet size in the 17CrNiMo6 steel follow a HalI-Petch relation with the yield strength. When the prior austenite grain size was refined from 199 μm to 6 μm , the yield strength increased by 235 MPa, while the Charpy U-notch impact energy at 77 K improved more than 8 times, indicating that microstructure refinement is more effective in improving the resistance to cleavage fracture than in increasing the strength. The fracture surfaces implied that the unit crack path for cleavage fracture is identified as being the packet.

Design of a low-alloy high-strength and high-toughness martensitic steel

To develop a high strength low alloy （HSLA） steel with high strength and high toughness, a series of martensitic steels were studied through alloying with various elements and thermodynamic simulation. The microstructure and mechanical properties of the designed steel were investigated by optical microscopy, scanning electron microscopy, tensile testing and Charpy impact test. The results show that cementite exists between 500℃ and 700℃, M7C3 exits below 720℃, and they are much lower than the austenitizing temperature of the designed steel. Furthermore, the Ti（C,N） precipitate exists until 1280℃, which refines the microstructure and increases the strength and toughness. The optimal alloying components are 0.19% C, 1.19% Si, 2.83% Mn, 1.24% Ni, and 0.049% Ti; the tensile strength and the V notch impact toughness of the designed steel are more than 1500 MPa and 100 J, respectively.

Ultra-high cycle fatigue behavior of high strength steel with carbide-free bainite/martensite complex microstructure

The ultra-high cycle fatigue behavior of a novel high strength steel with carbide-free bainite/martensite （CFB/M） complex microstructure was studied. The ultra-high cycle fatigue properties were measured by ultrasonic fatigue testing equipment at a frequency of 20 kHz. It is found that there is no horizontal part in the S-N curve and fatigue fracture occurs when the life of specimens exceeds 10^7 cycles. In addition, the origination of fatigue cracks tends to transfer from the surface to interior of specimens as the fatigue cycle exceeds 10^7, and the fatigue crack originations of many specimens are not induced by inclusions, but by some kind of ＂soft structure＂. It is shown that the studied high strength steel performs good ultra-high cycle fatigue properties. The ultra-high fatigue mechanism was discussed and it is suggested that specific CFB/M complex microstructure of the studied steel contributes to its superior properties.

Effect of microstructure on corrosion behavior of high strength martensite steel-A literature review

The high strength martensite steels are widely used in aerospace,ocean engineering,etc.,due to their high strength,good ductility and acceptable corrosion resistance.This paper provides a review for the influence of microstructure on corrosion behavior of high strength martensite steels.Pitting is the most common corrosion type of high strength stainless steels,which always occurs at weak area of passive film such as inclusions,carbide/intermetallic interfaces.Meanwhile,the chromium carbide precipitations in the martensitic lath/prior austenite boundaries always result in intergranular corrosion.The precipitation,dislocation and grain/lath boundary are also used as crack nucleation and hydrogen traps,leading to hydrogen embrittlement and stress corrosion cracking for high strength martensite steels.Yet,the retained/reversed austenite has beneficial effects on the corrosion resistance and could reduce the sensitivity of stress corrosion cracking for high strength martensite steels.Finally,the corrosion mechanisms of additive manufacturing high strength steels and the ideas for designing new high strength martensite steel are explored.

SCC evaluation of ultra-high strength steel in acidic chloride solution

The stress corrosion crack （SCC） susceptibility of ultra-high strength steel AerMet 100 was investigated by slow strain rate technique （SSRT）, tensile with polarization and surface analysis technique. The curves of tf^Cl/tf^W -strain rate are divided into three regions： stress-dominated region, SCC-dominated region, and corrosion-dominated region, so as the curves of εf^Cl/εf^W - strain rate and tm/tf-strain rate. The results of tensile tests with polarization show that the main SCC mechanism of AerMet 100 is anodic dissolution, which controls the corrosion process. The three regions have been discussed according to the relationship between the rate of slip-step formation and the rate of dissolution. Fracture appearances in different environments were analyzed by scanning electron microscopy （SEM）. SCC fracture appears as a mixture of intergranular and dimples, while it is totally dimples in the inert environment. The εf becomes the parameter to predict tf because the relationship between εf^Cl/εf^W and tf^Cl/tf^w is a straight line for AerMet 100.

Microstructure and Mechanical Properties of Aer Met 100 Ultra-high Strength Steel Joints by Laser Welding

AerMet100 ultra-high strength steel plates with a thickness of 2 mm were welded using a COz laser welding system. The influences of the welding process parameters on the morphology and microstructure of the welding joints were investigated, and the mechanical property of the welding joints was analyzed. The experimental results showed that the fusion zone of welding joint mainly consisted of columnar grains and a fine dendrite substructure grew epitaxially from the matrix. With the other conditions remaining unchanged, a finer weld microstructure was along with the scanning speed increase. The solidification microstructure gradually transformed from cellular crystal into dendrite crystal and the spaces of dendrite secondary arms rose from the fusion line to the center of the fusion zone. In the fusion zone of the weld, the rapid cooling caused the formation of martensite, which led the microhardness of the fusion zone higher than that of the matrix and the heat affected zone. The tensile strength of the welding joints was tested as 1 700 MPa, which was about 87% of the matrix. However, the tensile strength of the welding joints without defects existed was tested as 1832 MPa, which was about 94% of the matrix.

Manifestations in Corrosion Prophase of Ultra-high Strength Steel 30CrMnSiNi2 A in Sodium Chloride Solutions

The corrosion behaviors of ultra-high strength steel 30CrMnSiNi2A in sodium chloride solution were studied by weight loss and electrochemical methods. The morphology of corrosion products was observed using scanning electron microscopy（SEM） and the composition was analyzed using an energy dispersive spectroscopy（EDS） and X-Ray diffraction （XRD）. The experimental results showed that the corrosion came from pitting corrosion and the rust layer was composed of outer rust layer γ-FeOOH and inner rust layer Fe_2O_3 with a little β-FeOOH. The correlation between corrosion rate and test time accorded with exponential rule. The corrosion current measured by polarization methods was higher than that calculated by weight loss method after a long-time immersion, the main reason was that,β-FeOOH and γ-Fe_2O_3 transformed by γ-FeOOH led to overestimating corrosion rate. The processes of corrosion prophase were obtained from XRD and EIS results. The corrosion product, Fe（OH）_2 formed at the initial stage stayed at a non-steady state and then consequently transferred to γ-FeOOH, γ-Fe_2O_3 or β-FeOOH.

Analysis of the effect of geometrical parameters on fatigue performance of spot-weld joint for ultra-high strength steel

This paper studied the spot welding structure of ultra-high strength steel 22MnB5.ANSYS software was adopted to simulate its static strength;BS5400 algorithm was used to calculate the fatigue life;and the grouping method was used to test the fatigue performance of tensile shear spot weld specimens.The simulation results were in good agreement with the experimental values.Based on the validation of the simulation method,influences of different structural parameters on static strength and fatigue life were explored by adopting single factor.The results showed that within the selected structure parameter range,increase of the sheet thickness,nugget diameter,sheet width and overlapping length can lead to longer fatigue life.Besides,the fatigue life of spot weld took on a linear relationship with the overlapping length,a DoseResp relationship with the sheet thickness,and a single exponential decay relationship with the sheet width and the nugget diameter.Moreover,in order to estimate the impact from various parameters on the fatigue life of the specimens,the Taguchi orthogonal design method was applied in the simulation design.The simulating result indicated that influence of the sheet thickness on fatigue life was the most significant.In addition,the effects of nugget diameter,sheet width and overlapping length on fatigue life were reduced in turn.

Research and development of hot-rolled ultra-high strength steel at Baosteel

The effects of the composition and cooling process on the microstructures and properties of hot-rolled ultra-high strength low alloy （HSLA） steel, complex phase steel and martensite steel were studied in the laboratory. And S700MC and MP1200 ultra-high strength steels were trial produced at the 1 880 mm hot-rolling line of Baosteel. Compared with conventional hot-rolled high strength products,the idea that water is alloy was applied in the newly developed hot-rolled ultra-high strength steel. By the use of the economical composition design and controlled cooling after hot-rolling effectively,ultra-high strength steel of different steel grades can be obtained.

Effect of anions on stress corrosion cracking behaviors of ultra-high strength steel 23Co14Ni12Cr3Mo

The effects of chloride,sulfate and carbonate anions on stress corrosion behaviors of ultra-high strength steel 23Co14Ni12Cr3Mo were studied by stress corrosion cracking(SCC)test method using double cantilever beam(DCB)specimens.The SCC morphology was observed by using scanning electron microscopy(SEM)and the composition of corrosion products was analyzed by using energy dispersive spectrometer(EDS).The results show that the crack propagates to bifurcation in NaCl and Na2SO4 solution,while the crack in Na2CO3 solution propagates along the load direction.The SCC rate in NaCl solution is the highest,while lower in Na2SO4 solution and little in Na2CO3 solution.From the SEM morphologies,quasi-cleavage fracture was observed in NaCl and Na2SO4 solutions,but intergranular features in Na2CO3 solution.The mechanism of anion effect on SCC of steel 23Co14Ni12Cr3Mo was studied by using full immersion test and electrochemical measurements.

Influence of rapid heating process on the microstructure and tensile properties of high-strength ferrite–martensite dual-phase steel

Three low-carbon dual-phase （DP） steels with almost constant martensite contents of 20vo1% were produced by intercritical annealing at different heating rates and soaking temperatures. Microstructures prepared at low temperature （1043 K, FH1） with fast-heating （300 K/s） show banded ferrite/martensite structure, whereas those soaked at high temperature （1103 K, FH2） with fast heating reveal blocky martensite uniformly distributed in the fine-grained ferrite matrix. Their mechanical properties were tested under tensile conditions and compared to a slow-heated （5 K/s） reference material （SH0）. The tensile tests indicate that for a given martensite volume fraction, the yield strength and total elongation values are noticeably affected by the refinement of ferrite grains and the martensite morphology. Metallographic observations reveal the formation of microvoids at the ferrite/martensite interface in the SH0 and FH2 samples, whereas microvoids nucleate via the fracture of banded martensite particles in the FH1 specimen. In addition, analyses of the work-hardening behaviors of the DP microstructures using the differential Crussard-Jaoul technique demonstrate two stages of work hardening for all samples.

Internal oxidation of hot-rolled ultra-high strength steel and its effect on the surface quality of cold-rolled sheets

In this study,the scale and internal oxidation of hot-rolled ultra-high strength steel sheets were characterized.It was found that both the formation of the scale and the internal oxidation of Si and Mn depended on the coiling temperature and position of the steel sample on the strip coil.At a relatively high coiling temperature,a large amount of internal oxidation was observed on the samples cut from the middle of the coil.The depth of the internal oxidation zone exceeded 10 μm and a thin iron layer covering the scale was observed in some cases.Pickling and cold-rolling experiments were conducted on selected samples.Scale pickling was found to be greatly delayed by the formation of an iron layer,which frequently resulted in under-pickled defects.In addition,pickling of the entire internal oxidation zone was difficult,except at the grain boundaries,where the degree of internal Si and Mn oxidation was enriched.The surface of the cold-rolled steel sheet was ruined by the remaining oxidation zone in the subsurface of the pickled steel.The internal oxidation of hot-rolled ultra-high strength steel must be precisely controlled to improve the subsequent surface quality of cold-rolled steel.

Corrosion Behavior of Ultra-high Strength Steel 300M in Different Simulated Marine Environments

Corrosion behavior of 300M in neutralcorrosion environments containing Na Clsimulated by totalimmersion（TI）,salt spraying（SS）and periodic immersion（PI）,was investigated by surface analysis techniques,corrosion weight-loss method,and electrochemicalmeasurements.In totalimmersion environment,rust on the steelconsisted of a porous outer rust layer with main constituent of γ-Fe OOH,and an inner rust layer of dense Fe_3O_4 film with network broad cracks.In salt spraying environment,outer rust with main composition of γ-Fe OOH/α-Fe OOH/Fe_3O_4 was compact,and inner rust showed dense Fe_3O_4 film.Rust formed by periodic immersion exhibited a compact outer rust layer with constituent of α-Fe OOH/γ-Fe OOH/Fe_3O_4 and an inner rust layer with composition of α-Fe OOH/α-Fe_2O_3;inner rust showed a ultra-dense film adherent to the steel.The corrosion rate showed a rule of vss（salt spraying）〉vti（totalimmersion）〉〉vpi（periodic immersion）in 0-240 h,and vss≈vti？vpiin 240-720 h.The rust formed by periodic immersion was dense and compact,with stable electrochemicalproperties,and had excellent protection on the steel.Humidity and oxygen concentration in allthe environments played major roles in rust formation.

Interaction of Hydrogen and Retained Austenite in Bainite/Martensite Dual-Phase High Strength Steel

The hydrogen trapping phenomena in two bainite/martensite dual-phase high strength steels(U20Si and U20DSi)were investigated by electrochemical permeation technique.The hydrogen diffusivity was calculated from data of permeation delay time,and the diffusion coefficient in U20 Si is far less than that in U20 DSi.Moreover,the hydrogen diffusivity decreases as the volume percent of retained austenite increases.The experiment results show that there are different hydrogen trappings and different volume percents of retained austenite in U20 Si and U20 DSi.The retained austenite is precipitated as films.The trap binding energy for the retained austenite and hydrogen is calculated to be 40.4kJ·mol-1.

Simulation about hot stamping of ultra-high strength steel on the basis of lightweight technology

With the development of automobile lightweight,it is very necessary to apply the ultra-high strength steel parts manufactured by hot stamping,which offers the possibility to reduce the weight of automobiles and maintain the safety requirement.In order to complete hot stamping,it is important to design the structure of parts reasonably,which is related with reasonable matching of strength.The objective of this paper is to guide the design of parts manufactured by hot stamping and find the forming technical requirements of vehicle performance.Through experiments,the paper obtains the stress and strain curves at different deformation temperatures and strain rates.Based on experimental data, the constitutive relationship model is established which can reflect the deformation capacity of ultra-high strength steel during the process of hot stamping.Combined with finite element simulation results of hot stamping by commercial software AUTOFORM,transfer path of load and matching law of strength,the paper determines the design criteria and forming technical requirements of parts manufactured by hot stamping.At the same time,the impact performance of front cross member internal plate is taken into consideration.

Microstructural Transformation and Precipitation of an Ultra-high Strength Steel under Continuous Cooling

We investigated phase transition and precipitation of ultra-high strength steel（UHSS）in a new ＂short process＂ with controlled rolling and controlled cooling.Thermalexpansion test combined with metallographic observation was used to research the continuous cooling transformation（CCT）curve.Moreover,the microstructuraltransformation and precipitation law was revealed by morphologicalobservation and alloying elements by electron probe micro-analyzer（EPMA）.Transmission electron microscopy（TEM）was utilized to analyze the composition and grain orientation of microstructure.The study showed that the measured criticaltransformation temperatures of Ac1 and Ac3 were 746 and 868 ℃,respectively.The CCT curve indicated that the undercooled austenite was transformed into proeutectoid ferrite and bainite with HV 520 in a broad range of cooling rate 0.1^（-1） ℃·s^（-1）.When subjected to a cooling rate of 1 ℃·s^（-1）,the undercooled austenite was divided into small-sized blocks by formed martensite.With further increase of cooling rate,micro-hardness increased dramatically,the microstructure of specimen was mainly lathe bainite（LB）,granular bainite（GB）,lath martensite（LM）and residualaustenite.By diffraction test analysis,it was identified that there was K-S orientation relationship between martensite and austenite for {110}_α//{111}_γ,{111}_α//{101}_γ.EPMA clearly showed that carbon diffused adequately due to staying for a long time at high temperature with a lower cooling rate of 2 ℃·s-1.Phase transition drive force was lower and the residualaustenite existed in the block form of Martensite austenite island（M-A）.With the increase of cooling rate to 10 ℃·s^（-1）,the block residualaustenite reduced,the carbon content of residualaustenite increased and α phase around the residualaustenite formed into a low carbon bainite form.

Effect of short-time low-temperature austenitizing on microstructure and mechanical properties of DT300 ultra-high strength steel fabricated by laser powder bed fusion

To address the inhomogeneous microstructure and improve the mechanical properties of DT300 ultra-high strength steel specimens fabricated by laser powder bed fusion,different post-heat treatment schedules are performed.With the increase in austenitizing temperature and time,the migration rate of austenite grain boundaries continuously increases with the dissolution of nano-carbides,and the formation of nano-oxides and twin martensite is also inhibited accordingly.The rapid growth in the size of prior austenite grains and martensite laths,as well as the decrease in the content of nano-oxides and twin martensite,led to a rapid decrease in the strength(yield strength and ultimate tensile strength)from HT2 to HTF specimens.The HT1 specimens(austenitizing at 830℃for 30 min,then oil quenching and tempering at 300℃for 120 min and finally air cooling)display excellent mechanical properties of yield strength of 1572 MPa,ultimate tensile strength of 1847 MPa,elongation of 9.84%,and fracture toughness of 106 MPa m^(1/2),which are counterparts to those of conventional DT300 steel forgings after heat treatment.

Study on welding process performance of HG70D high strength steel plate

In this paper, the performance of HG70D welded joint of ultra-high strength steel plates is presented, and the performance of HG70D and Q345B welded joints is studied. The high strength steel plate HG70D showed excellent weldability. Through the X-ray inspection of welded joints, tensile strength, impact test and bending performance test, the comprehensive performance of the joint was excellent. The macroscopic and microscopic metallographic analysises of the welded joints show that the welding seams included pearlite, sorbite, ferrite, etc. The influence of stress annealing temperature on HG70D of high strength steel plate was analyzed by heat treatment.

Microstructure evolution of an ultra-high strength metal alloy with tempering temperature

Optical microscopy (OM) and transmission electron microscopy (TEM) were used to investigate the effect of tempering temperature on the experimental extra-high carbon steels. It is found that tempering reaction can reduce austenite content and influence the stability of the austenite. As-normalized microstructure is a mixture of twinned martensite and retained austenite. Tempered at 250 °C for 2 h, lath martensite can occasionally be found nearby the diffusionally decomposed austenite area. It also is found that tempering at 650 °C for 2 h, nanoparticles of carbides precipitate in the martensite and decomposed austenite. © The Nonferrous Metals Society of China and Springer-Verlag Berlin Heidelberg 2012.