Narrow gap welding has merits of lower residual stress and distortion, and superior mechanical properties of joints. A major problem of this process is the lack of fusion in sidewalls, hence many methods of weaving ar...Narrow gap welding has merits of lower residual stress and distortion, and superior mechanical properties of joints. A major problem of this process is the lack of fusion in sidewalls, hence many methods of weaving arc have been developed to increase heating effect of arc to the sidewalls. In this work, a new approach Without weaving arc is attempted to ensure the penetration of sidewall, and ultra-narrow gap welding with the gap of less than 5 mm was executed successfully. In this approach, the width of gap is decreased further, so that the sidewalls are made within range of arc heating to obtain the enough heat. In order to prevent the arc from being attracted by sidewall and going up along the sidewalls, two pieces of flux bands consisting of the specified aggregates are adhered to the sidewalls to constrain the arc. In addition, when flux band being heated by the arc, slag and gases are formed to shield the arc and the weld pool. This technique was tested on the welding experiment of pipeline steel with thickness of 20 mm. The involved welding parameters were obtained, that is, the width of gap is 4 mm, the welding current 250 A, and the heat input 0. 5 kJ/mm, the width of heat-affected zone is 1 -2 mm.展开更多
Ultra-narrow gap welding (UNGW) process with high stabilization, reliability and without spatter can be achieved with constricted arc by molten slag wall, which is made from melted flux. The experiments are carried ...Ultra-narrow gap welding (UNGW) process with high stabilization, reliability and without spatter can be achieved with constricted arc by molten slag wall, which is made from melted flux. The experiments are carried out by changing voltage under different currents. The results indicate voltage range being fit for UNGW is about 22 -31 V under the current range of 200 -320 A. With the increasing of voltage, weld formation of UNGW has the law of lack of fusion on sidewall, good weld and undercut in turn under a certain current. In addition, the action relationships among arc, molten slag wall and sidewalls can be improved by properly adjusting voltage and current of arc, which makes cathode spot properly distribute in ultra-narrow gap. Therefore, the effective control of weld formation of UNGW has been achieved.展开更多
文摘Narrow gap welding has merits of lower residual stress and distortion, and superior mechanical properties of joints. A major problem of this process is the lack of fusion in sidewalls, hence many methods of weaving arc have been developed to increase heating effect of arc to the sidewalls. In this work, a new approach Without weaving arc is attempted to ensure the penetration of sidewall, and ultra-narrow gap welding with the gap of less than 5 mm was executed successfully. In this approach, the width of gap is decreased further, so that the sidewalls are made within range of arc heating to obtain the enough heat. In order to prevent the arc from being attracted by sidewall and going up along the sidewalls, two pieces of flux bands consisting of the specified aggregates are adhered to the sidewalls to constrain the arc. In addition, when flux band being heated by the arc, slag and gases are formed to shield the arc and the weld pool. This technique was tested on the welding experiment of pipeline steel with thickness of 20 mm. The involved welding parameters were obtained, that is, the width of gap is 4 mm, the welding current 250 A, and the heat input 0. 5 kJ/mm, the width of heat-affected zone is 1 -2 mm.
基金The work was supported by National Natural Science Foundation of China (51105185) and Advanced Project Foundation of Jinchuan Company(420032).
文摘Ultra-narrow gap welding (UNGW) process with high stabilization, reliability and without spatter can be achieved with constricted arc by molten slag wall, which is made from melted flux. The experiments are carried out by changing voltage under different currents. The results indicate voltage range being fit for UNGW is about 22 -31 V under the current range of 200 -320 A. With the increasing of voltage, weld formation of UNGW has the law of lack of fusion on sidewall, good weld and undercut in turn under a certain current. In addition, the action relationships among arc, molten slag wall and sidewalls can be improved by properly adjusting voltage and current of arc, which makes cathode spot properly distribute in ultra-narrow gap. Therefore, the effective control of weld formation of UNGW has been achieved.