The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.O...The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.展开更多
Using yttriu m nitrate as the m other salt , synthesis of ultrafine yttria po w der through w et che mical route w as investigated . Choice of precipitant has dra m atic effects on co m position ,particle size distrib...Using yttriu m nitrate as the m other salt , synthesis of ultrafine yttria po w der through w et che mical route w as investigated . Choice of precipitant has dra m atic effects on co m position ,particle size distribution and particle m orphology of the precipitates . When a m m onia solutionw as used as the precipitant , the precursor precipitate w as m ainly Y2( O H) 5 14( N O3) 0 86· H2 O with co m paratively large particle size , broad size distribution and co m plex particleshapes . When sodiu m hydroxide solution w as used , roughly spherical α Y( O H)3·3 H2 Opre cipitate w ith sm all particle size and narro w size distribution w as obtained . The transfor m a tion sequence of dry α Y( O H)3 ·3 H2 O gel during calcination w as determ ined to be α Y( O H) 3·3 H2 O→ Y O O H→ Y2 O3 . After calcining at 600 ℃ for 1 hour , both Y2( O H) 5 14( N O3) 0 86· H2 O and α Y( O H) 3·3 H2 O transfor m to well crystallized Y2 O3 pow ders ,w ith particle sizes of 50 ～3000 n m and 20 n m , respectively .展开更多
Ultrafine γ-A12O3 particles are synthesized in Triton X- 10 0/n - hexanol/cycloh exan e/wat er water in o if(w/o )Inicroemulsion by mixing two separately prepared microemulsions containing Al(NO)3 and (Wb)ZCO, respec...Ultrafine γ-A12O3 particles are synthesized in Triton X- 10 0/n - hexanol/cycloh exan e/wat er water in o if(w/o )Inicroemulsion by mixing two separately prepared microemulsions containing Al(NO)3 and (Wb)ZCO, respectively.The ultrafine Al2O3 particles are characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD)and their size and distribution are measured. The effects of water, surfactallt and reactant concentrations on the particlesize and distribution are studied. The results show that the particle size and distribution can be changed by varying thepreparation conditions, and the size of the microemulsion droplets has a controlling effect on the size of the pafticles. A. possible mechanism of ultrafine particles (UFPs) prepared by microemulsions is proposed.展开更多
The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying & calcining-continuous reduc...The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying & calcining-continuous reduction technology were investigated.In comparison to the conventional H2 sintering processing,microwave sintering to W-15Cu can be achieved at lower sintering temperature and shorter sintering time.Furthermore,higher performances in microwave sintered compacts were obtained,but high microwave sintering temperature or long microwave sintering time could result in coarser microstructures.展开更多
The availability using oxygen-rich powders to prepare ultrafine Ti(C,N)-based cermets was investigated. The deoxidation process, denitrification phenomenon and the effect of deoxidation on microstructure and mechanica...The availability using oxygen-rich powders to prepare ultrafine Ti(C,N)-based cermets was investigated. The deoxidation process, denitrification phenomenon and the effect of deoxidation on microstructure and mechanical properties of sintered samples were discussed, respectively. The results show that oxygen in the samples prepared even with high oxygen contained in starting powders can be almost completely cleaned away through suitable sintering process. The ultrafine oxygen-rich powders have a significant effect on microstructure, which promotes the formation of white core phase. A ultrafine Ti(C,N)-based cermet with mean particle size of 0. 30 μm, uniform microstructure and excellent mechanical properties is successfully prepared. It is also found that there exists severe denitrification phenomenon in the preparation process of ultrafine Ti(C,N)-based cermet.展开更多
基金Funded by the Technology Innovation Leading Program of Shaanxi(No.2022QFY08-02)。
文摘The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.
文摘Using yttriu m nitrate as the m other salt , synthesis of ultrafine yttria po w der through w et che mical route w as investigated . Choice of precipitant has dra m atic effects on co m position ,particle size distribution and particle m orphology of the precipitates . When a m m onia solutionw as used as the precipitant , the precursor precipitate w as m ainly Y2( O H) 5 14( N O3) 0 86· H2 O with co m paratively large particle size , broad size distribution and co m plex particleshapes . When sodiu m hydroxide solution w as used , roughly spherical α Y( O H)3·3 H2 Opre cipitate w ith sm all particle size and narro w size distribution w as obtained . The transfor m a tion sequence of dry α Y( O H)3 ·3 H2 O gel during calcination w as determ ined to be α Y( O H) 3·3 H2 O→ Y O O H→ Y2 O3 . After calcining at 600 ℃ for 1 hour , both Y2( O H) 5 14( N O3) 0 86· H2 O and α Y( O H) 3·3 H2 O transfor m to well crystallized Y2 O3 pow ders ,w ith particle sizes of 50 ～3000 n m and 20 n m , respectively .
文摘Ultrafine γ-A12O3 particles are synthesized in Triton X- 10 0/n - hexanol/cycloh exan e/wat er water in o if(w/o )Inicroemulsion by mixing two separately prepared microemulsions containing Al(NO)3 and (Wb)ZCO, respectively.The ultrafine Al2O3 particles are characterized by transmission electron microscopy (TEM) and X-ray diffraction (XRD)and their size and distribution are measured. The effects of water, surfactallt and reactant concentrations on the particlesize and distribution are studied. The results show that the particle size and distribution can be changed by varying thepreparation conditions, and the size of the microemulsion droplets has a controlling effect on the size of the pafticles. A. possible mechanism of ultrafine particles (UFPs) prepared by microemulsions is proposed.
基金Funded by the Project for Science and Technology Plan of Wuhan City(200910321092)the Youth Science Plan for Light of the Morning Sun of Wuhan City (200750731270)
文摘The effects of microwave sintering and conventional H2 sintering on the microstructure and properties of W-15Cu alloy using ultrafine W-15Cu composite powder fabricated by spray drying & calcining-continuous reduction technology were investigated.In comparison to the conventional H2 sintering processing,microwave sintering to W-15Cu can be achieved at lower sintering temperature and shorter sintering time.Furthermore,higher performances in microwave sintered compacts were obtained,but high microwave sintering temperature or long microwave sintering time could result in coarser microstructures.
基金Project(50323008) supported by the National Natural Science Foundation of China
文摘The availability using oxygen-rich powders to prepare ultrafine Ti(C,N)-based cermets was investigated. The deoxidation process, denitrification phenomenon and the effect of deoxidation on microstructure and mechanical properties of sintered samples were discussed, respectively. The results show that oxygen in the samples prepared even with high oxygen contained in starting powders can be almost completely cleaned away through suitable sintering process. The ultrafine oxygen-rich powders have a significant effect on microstructure, which promotes the formation of white core phase. A ultrafine Ti(C,N)-based cermet with mean particle size of 0. 30 μm, uniform microstructure and excellent mechanical properties is successfully prepared. It is also found that there exists severe denitrification phenomenon in the preparation process of ultrafine Ti(C,N)-based cermet.