Ultrafine alumina power was obtained by calcining the precursor at 1 200 ℃ for 2 h, which was prepared by homogeneous precipitation method using aluminium salts and urea as raw materials. The effects of anions on the...Ultrafine alumina power was obtained by calcining the precursor at 1 200 ℃ for 2 h, which was prepared by homogeneous precipitation method using aluminium salts and urea as raw materials. The effects of anions on the morphology, particle size, surface area and configuration of the precursors were studied. The results show that the reactions of urea with aluminium nitrate and aluminium chloride result in agglomerates gels with bad filtering performance, the morphology is fibrillar. Aluminium sulphate-urea reactions result in the direct formation of amorphous powders with good filtering performance, of which morphology are regular spherical particles with larger granularity and smaller surface area. The reaction of mutual compound of aluminium sulphate and aluminium nitrate with molar ratio of 40:60 with urea can produce precursor with good filtering performance, spherical morphology, and uniform granularity distribution in the particle size range of 2-3 μm.展开更多
The precursor of ultrafine In 2O 3 powder was prepared by the hydrolysis, peptization and gelation of InCl 3·4H 2O used as raw material. After calcination, ultrafine In 2O 3 powder was obtained. The particl...The precursor of ultrafine In 2O 3 powder was prepared by the hydrolysis, peptization and gelation of InCl 3·4H 2O used as raw material. After calcination, ultrafine In 2O 3 powder was obtained. The particles were characterized by the methods of thermo gravimetric and differential thermal analysis (TG DTA), X ray diffractometry (XRD) and transmission electron microscopy (TEM), respectively.展开更多
The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymeri...The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.展开更多
In this work,W-Y2 O3 alloys are prepared by freeze-drying and subsequent low temperature sintering.The average size of reduced W-Y2 O3 composite powders prepared by freeze-drying method is only 18.1 nm.After low tempe...In this work,W-Y2 O3 alloys are prepared by freeze-drying and subsequent low temperature sintering.The average size of reduced W-Y2 O3 composite powders prepared by freeze-drying method is only 18.1 nm.After low temperature sintering of these composite nanopowders,the formed W-Y2 O3 alloys possess a smaller grain size of 510 nm while maintaining a comparatively higher density of 97.8%.Besides a few submicron Y2 O3 particles(about 100-300 nm)with a W-Y-O phase diffusion layer on their surface distribute at W grain boundaries,lots of nano Y2 WO6 particles(<20 nm)exist in W matrix.Moreover,many Y6 WO12(<10 nm)particles exist within submicron Y2 O3 particles.The formation of these ternary phases indicates that some oxygen impurities in the W matrix can be adsorbed by ternary phases,resulting in the purification of W matrix and the strengthening of phase boundaries.The combined action of the above factors makes the hardness of the sintered W-Y2 O3 alloys in our work as high as 656.6±39.0 HV0.2.Our work indicates that freeze-drying and subsequent low temperature sintering is a promising method for preparing high performance W-Y2 O3 alloys.展开更多
BaO-La2O3-B2O3 （BLB） glass, suitable to be used as a sealing between metals, was chosen to be the binder in preparing glass coats on the Ti-alloy substrate. The SiCN nano-powder was introduced as the filler for the ...BaO-La2O3-B2O3 （BLB） glass, suitable to be used as a sealing between metals, was chosen to be the binder in preparing glass coats on the Ti-alloy substrate. The SiCN nano-powder was introduced as the filler for the absorbing coat because it is considered to be a good high temperature absorber. The effect of the coating temperature and coating time on the tensile strength of the glass coat was investigated and the proper coating parameters to get good mechanical properties were determined. In addition, the effects of the SiCN content on the tensile strength of the absorbing coat were also discussed. Results show that it is possible to prepare the glass coat using the BLB glass as a binder. That the coat formed at 730℃ for 30 min has the best tensile strength witnesses 730 ℃, 30 min to be the proper parameter to prepare the glass coat. The BLB glass coat without SiCN powder possesses good tensile strength and the introduction of the SiCN absorber into the glass coat will lower the tensile strength. As the SiCN content increases, the tensile strength of the absorbing coat decreases, which could be attributed to the aggregation of SiCN in the coats.展开更多
基金Project(5JJ3010) supported by the Natural Science Foundation of Hunan Province, China
文摘Ultrafine alumina power was obtained by calcining the precursor at 1 200 ℃ for 2 h, which was prepared by homogeneous precipitation method using aluminium salts and urea as raw materials. The effects of anions on the morphology, particle size, surface area and configuration of the precursors were studied. The results show that the reactions of urea with aluminium nitrate and aluminium chloride result in agglomerates gels with bad filtering performance, the morphology is fibrillar. Aluminium sulphate-urea reactions result in the direct formation of amorphous powders with good filtering performance, of which morphology are regular spherical particles with larger granularity and smaller surface area. The reaction of mutual compound of aluminium sulphate and aluminium nitrate with molar ratio of 40:60 with urea can produce precursor with good filtering performance, spherical morphology, and uniform granularity distribution in the particle size range of 2-3 μm.
文摘The precursor of ultrafine In 2O 3 powder was prepared by the hydrolysis, peptization and gelation of InCl 3·4H 2O used as raw material. After calcination, ultrafine In 2O 3 powder was obtained. The particles were characterized by the methods of thermo gravimetric and differential thermal analysis (TG DTA), X ray diffractometry (XRD) and transmission electron microscopy (TEM), respectively.
文摘The ultrafine powders of YBa2Cu3O7-x with the size of 100nm were synthesized by Sol-Gel process using cit-rate as complex and ammonium hydroxide to adjust pH of solu-tion. The process of Sol formation and Gel polymerization of YBa2Cu3O7-x in the Sol-Gel synthetic reaction has bee studied. The particle size ,pruity, sintering activity and superconducting properties of YBa2Cu3O7-x prepared by Sol-Gel method are better than by solid state reaction.
基金supported by the National Natural Science Foundation of China(Nos.51822404 and 51574178)the Science and Technology Program of Tianjin(No.18YFZCGX00070)+1 种基金the Natural Science Foundation of Tianjin(No.18JCYBJC17900)the Seed Foundation of Tianjin University(Nos.2018XRX-0005 and 2019XYF-0066)。
文摘In this work,W-Y2 O3 alloys are prepared by freeze-drying and subsequent low temperature sintering.The average size of reduced W-Y2 O3 composite powders prepared by freeze-drying method is only 18.1 nm.After low temperature sintering of these composite nanopowders,the formed W-Y2 O3 alloys possess a smaller grain size of 510 nm while maintaining a comparatively higher density of 97.8%.Besides a few submicron Y2 O3 particles(about 100-300 nm)with a W-Y-O phase diffusion layer on their surface distribute at W grain boundaries,lots of nano Y2 WO6 particles(<20 nm)exist in W matrix.Moreover,many Y6 WO12(<10 nm)particles exist within submicron Y2 O3 particles.The formation of these ternary phases indicates that some oxygen impurities in the W matrix can be adsorbed by ternary phases,resulting in the purification of W matrix and the strengthening of phase boundaries.The combined action of the above factors makes the hardness of the sintered W-Y2 O3 alloys in our work as high as 656.6±39.0 HV0.2.Our work indicates that freeze-drying and subsequent low temperature sintering is a promising method for preparing high performance W-Y2 O3 alloys.
文摘BaO-La2O3-B2O3 （BLB） glass, suitable to be used as a sealing between metals, was chosen to be the binder in preparing glass coats on the Ti-alloy substrate. The SiCN nano-powder was introduced as the filler for the absorbing coat because it is considered to be a good high temperature absorber. The effect of the coating temperature and coating time on the tensile strength of the glass coat was investigated and the proper coating parameters to get good mechanical properties were determined. In addition, the effects of the SiCN content on the tensile strength of the absorbing coat were also discussed. Results show that it is possible to prepare the glass coat using the BLB glass as a binder. That the coat formed at 730℃ for 30 min has the best tensile strength witnesses 730 ℃, 30 min to be the proper parameter to prepare the glass coat. The BLB glass coat without SiCN powder possesses good tensile strength and the introduction of the SiCN absorber into the glass coat will lower the tensile strength. As the SiCN content increases, the tensile strength of the absorbing coat decreases, which could be attributed to the aggregation of SiCN in the coats.