Based on the measured thermal cycle of double-wire submerged arc welding （SAW）, the gleeble thermal test was performed. Meanwhile, the Charpy V-notch impact test at -50 ℃ and hardness test at room temperature were ...Based on the measured thermal cycle of double-wire submerged arc welding （SAW）, the gleeble thermal test was performed. Meanwhile, the Charpy V-notch impact test at -50 ℃ and hardness test at room temperature were carried out after the thermal test. Thermally cycled microstructure and fracture surfaces were observed too. The results indicate that impact toughness of heat-affected zone （HAZ） at -50 ℃ is lower than that of parent metal with different wire spacing and welding speed. The microstracture of coarse-grains heat-affected zone （ CGHAZ ） is mainly made up of lath bainite with serious brittleness. The study also shows that a smaller energy input could be adopted to ensure the toughness of welded joints at the welding process in a common molten pool, while a higher energy input could be exerted to enhance welding efficieney at the welding process in two separate molten pools.展开更多
文摘Based on the measured thermal cycle of double-wire submerged arc welding （SAW）, the gleeble thermal test was performed. Meanwhile, the Charpy V-notch impact test at -50 ℃ and hardness test at room temperature were carried out after the thermal test. Thermally cycled microstructure and fracture surfaces were observed too. The results indicate that impact toughness of heat-affected zone （HAZ） at -50 ℃ is lower than that of parent metal with different wire spacing and welding speed. The microstracture of coarse-grains heat-affected zone （ CGHAZ ） is mainly made up of lath bainite with serious brittleness. The study also shows that a smaller energy input could be adopted to ensure the toughness of welded joints at the welding process in a common molten pool, while a higher energy input could be exerted to enhance welding efficieney at the welding process in two separate molten pools.