IN the past five years the process combination of vacuum hardening, respectively vacuum carburizing with high-pressure gas quenching was successfully introduced to the market, especially in the manufacture of gears. I...IN the past five years the process combination of vacuum hardening, respectively vacuum carburizing with high-pressure gas quenching was successfully introduced to the market, especially in the manufacture of gears. In the meantime furnace concepts for various applications are available to the industry. In the following report three plant varieties are introduced, which differ in process flexibility and throughput. This report also explains criteria for the selection of a furnace in view of the existing application requirements. Besides this a short introduction is given into the vacuum carburizing process and the high-pressure gas quenching technology.展开更多
Heat-treated wood has good dimensional stability,corrosion resistance and visual quality,but it is prone to mold,which limits its application.Based on the pH value of heat-treated wood,this study examines the factors ...Heat-treated wood has good dimensional stability,corrosion resistance and visual quality,but it is prone to mold,which limits its application.Based on the pH value of heat-treated wood,this study examines the factors affecting the pathogenesis causing heat-treated wood mold.Normally,the pH value of the heat-treated wood is between 4.38 and 5.10,which is suitable for the growth of mold.However,the pH of the heat-treated copper-containing material is between 6.63 and 7.12,which deviates the treated wood from the comfortable growth conditions for the mold,thereby reducing the occurrence of mold.展开更多
Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composite...Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composites were investigated at different temperatures (773-1173K), and the microstructures of carbon/carbon composites were studied by SEM and X-ray diffraction. The experimental results showed that the inter-laminar distance of (002) plane (d002) deceased while the microcrystalline stack height (Lc) increased. The oxidation rate of felt base carbon/carbon composites was invari-able at certain temperatures. The oxidation mechanism of carbon/carbon composites changed remarkably at the oxidation temperature 973K. At the initial oxidation stage of carbon/carbon composites, carbon matrix was oxidized much more rapidly than carbon felt.展开更多
Seeds of Dodonaea viscosa （L.） Jacq, a representative species in dry and hot valleys in Southwest China, were chosen as experimental materials. In this experiment, the D. viscosa seeds were treated at 40, 60, 80 and...Seeds of Dodonaea viscosa （L.） Jacq, a representative species in dry and hot valleys in Southwest China, were chosen as experimental materials. In this experiment, the D. viscosa seeds were treated at 40, 60, 80 and 100℃ respectively before germination to study impacts of high temperature treatment on their generation rate and to further discuss the roles of fire during the process of vegetation formation in dry and hot valley areas of China. The results show that when the temperature was higher than 40 ℃, the germination rate of D. viscosa seeds was significantly higher than that of the control group, and the heat shock effect was apparent. The germination rate was the highest when the seeds were treated at 80 ℃ for 10 min, reaching 63.00%±2.55%. There was still a significant heat shock effect on the D. viscosa seeds which were stored for one year. In comparison with the conventional method of soaking seeds in hot water, the germination rate of D. viscose seeds which were treated at high temperature before germination increased significantly.展开更多
GW63K （Mg-6Gd-3Y-0.5Zr） magnesium alloys were prepared successfully by high-vacuum die-casting. Effects of fast shot speed and vacuum level on the grain size and mechanical properties of this alloy were studied. Mic...GW63K （Mg-6Gd-3Y-0.5Zr） magnesium alloys were prepared successfully by high-vacuum die-casting. Effects of fast shot speed and vacuum level on the grain size and mechanical properties of this alloy were studied. Microstructure of the alloys was analyzed by SEM, EDX and optical microscope （OM）. The effect of heat treatment on high vacuum die-casting （HVDC） GW63K alloy was also studied. The results indicate that with the increase of fast velocity, the tensile yield strength hardly changes, but the elongation first increases, then decreases. The optimum heat treatment process is solution treatment at 748 K for 2 h and aging at 473 K for 80 h. Under this condition, GW63K magnesium alloy exhibits a maximum tensile strength and elongation of 308 MPa and 9.45%. There is significant correlation between ductility and the presence of external solidified cells （ESCs）. The as-cast GW63K alloy consists ofα-Mg and Mg24（Gd,Y）5 particles. After heat treatment, Gd and Y atoms dissolve intoα-Mg matrix.展开更多
The effects of vacuum assistance on the microstructure and mechanical properties of high pressure die cast A390alloy at different slow shot speeds were evaluated.Plate-shaped specimens of hypereutectic A390aluminum al...The effects of vacuum assistance on the microstructure and mechanical properties of high pressure die cast A390alloy at different slow shot speeds were evaluated.Plate-shaped specimens of hypereutectic A390aluminum alloy were produced on a TOYO BD?350V5cold chamber die casting machine incorporated with a self-improved TOYO vacuum system.According to the results,the vacuum pressure inside the die cavity increased linearly with the increasing slow shot speed at the beginning of mold filling.Meanwhile,tensile properties of vacuum die castings were deteriorated by the porosity content.In addition,the average primary silicon size decreased from23to14μm when the slow shot speed increased from0.05to0.2m/s,which has a binary functional relationship with the slow shot speed.After heat treatment,microstructural morphologies revealed that needle-shaped and thin-flaked eutectic silicon particles became rounded while Al2Cu dissolved intoα(Al)matrix.Furthermore,the fractography revealed that the fracture mechanism has evolved from brittle transgranular fracture to a fracture mode with many dimples after heat treatment.展开更多
The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature ...The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature to 300℃.It turned out that the optimum T6 heat-treatments for the tested alloy are 525℃×12 h+225℃×14 h and 525℃×12 h+250℃×12 h which integrated age-hardening and tensile properties into account,respectively.The strength of the T6-treated alloy indicates obvious anomalous temperature dependence from room temperature to 300℃,namely both ultimate tensile strength and yield strength of the tested alloy firstly increase with tensile temperature,and then decrease as temperature increases further.Elongation increased with temperature monotonously.The tensile fracture mode of the tested alloy changes from transgranular fracture to intergranular fracture with the increasing of test temperature.展开更多
To improve the corrosion resistance of coalbed methane drilling equipment,an AICoCrFeNiCu high entropy alloy coating was prepared on the AISI 4135(35CrMo)steel substrate by high velocity oxygen fuel(HVOF)technology,an...To improve the corrosion resistance of coalbed methane drilling equipment,an AICoCrFeNiCu high entropy alloy coating was prepared on the AISI 4135(35CrMo)steel substrate by high velocity oxygen fuel(HVOF)technology,and the coating was subjected to vacuum heat treatment(VHT)at different temperatures(500,700,900 and 1100℃).The corrosion test of the substrate and the coatings after VHT in coalbed methane drilling fluid was carried out.The results show that the HVOF sprayed AICoCrFeNiCu high entropy alloy(HEA)coating has a good bonding with the substrate,and the porosity of the coating is about 2.4%.There is partial segregation in the coating,and the coating mainly consists of body-centered cubic phase.The coating has good thermal stability,and the phase structure and microstructure of the coatings have changed after VHT at different temperatures.Compared with the substrate,the as-sprayed coating has better uniform corrosion resistance,and the corrosion resistance of the coating after VHT is further improved.After VHT at 500℃,the HVOF-sprayed AICoCrFeNiCu HEA coating has the best corrosion resistance.展开更多
文摘IN the past five years the process combination of vacuum hardening, respectively vacuum carburizing with high-pressure gas quenching was successfully introduced to the market, especially in the manufacture of gears. In the meantime furnace concepts for various applications are available to the industry. In the following report three plant varieties are introduced, which differ in process flexibility and throughput. This report also explains criteria for the selection of a furnace in view of the existing application requirements. Besides this a short introduction is given into the vacuum carburizing process and the high-pressure gas quenching technology.
基金Provincial Science and Technology Research Project of Guangdong(2014A040401043)
文摘Heat-treated wood has good dimensional stability,corrosion resistance and visual quality,but it is prone to mold,which limits its application.Based on the pH value of heat-treated wood,this study examines the factors affecting the pathogenesis causing heat-treated wood mold.Normally,the pH value of the heat-treated wood is between 4.38 and 5.10,which is suitable for the growth of mold.However,the pH of the heat-treated copper-containing material is between 6.63 and 7.12,which deviates the treated wood from the comfortable growth conditions for the mold,thereby reducing the occurrence of mold.
文摘Felt base carbon/carbon composites fabricated by super-high pressure impregnation carbonization process (SPIC) were heat treated at high temperature 2773K. The oxidation properties of felt base carbon/carbon composites were investigated at different temperatures (773-1173K), and the microstructures of carbon/carbon composites were studied by SEM and X-ray diffraction. The experimental results showed that the inter-laminar distance of (002) plane (d002) deceased while the microcrystalline stack height (Lc) increased. The oxidation rate of felt base carbon/carbon composites was invari-able at certain temperatures. The oxidation mechanism of carbon/carbon composites changed remarkably at the oxidation temperature 973K. At the initial oxidation stage of carbon/carbon composites, carbon matrix was oxidized much more rapidly than carbon felt.
基金Supported by the National Water Pollution Control and Treatment Science and Technology Major Project(2012ZX07101-003-04-04)~~
文摘Seeds of Dodonaea viscosa （L.） Jacq, a representative species in dry and hot valleys in Southwest China, were chosen as experimental materials. In this experiment, the D. viscosa seeds were treated at 40, 60, 80 and 100℃ respectively before germination to study impacts of high temperature treatment on their generation rate and to further discuss the roles of fire during the process of vegetation formation in dry and hot valley areas of China. The results show that when the temperature was higher than 40 ℃, the germination rate of D. viscosa seeds was significantly higher than that of the control group, and the heat shock effect was apparent. The germination rate was the highest when the seeds were treated at 80 ℃ for 10 min, reaching 63.00%±2.55%. There was still a significant heat shock effect on the D. viscosa seeds which were stored for one year. In comparison with the conventional method of soaking seeds in hot water, the germination rate of D. viscose seeds which were treated at high temperature before germination increased significantly.
基金Projects(51171113,51301107)supported by the National Natural Science Foundation of ChinaProjects(2012M511089,2013T60444)supported by China Postdoctoral Science Foundation
文摘GW63K （Mg-6Gd-3Y-0.5Zr） magnesium alloys were prepared successfully by high-vacuum die-casting. Effects of fast shot speed and vacuum level on the grain size and mechanical properties of this alloy were studied. Microstructure of the alloys was analyzed by SEM, EDX and optical microscope （OM）. The effect of heat treatment on high vacuum die-casting （HVDC） GW63K alloy was also studied. The results indicate that with the increase of fast velocity, the tensile yield strength hardly changes, but the elongation first increases, then decreases. The optimum heat treatment process is solution treatment at 748 K for 2 h and aging at 473 K for 80 h. Under this condition, GW63K magnesium alloy exhibits a maximum tensile strength and elongation of 308 MPa and 9.45%. There is significant correlation between ductility and the presence of external solidified cells （ESCs）. The as-cast GW63K alloy consists ofα-Mg and Mg24（Gd,Y）5 particles. After heat treatment, Gd and Y atoms dissolve intoα-Mg matrix.
基金Project(51775297)supported by the National Natural Science Foundation of ChinaProject(2015M580093)supported by the China Postdoctoral Science Foundation
文摘The effects of vacuum assistance on the microstructure and mechanical properties of high pressure die cast A390alloy at different slow shot speeds were evaluated.Plate-shaped specimens of hypereutectic A390aluminum alloy were produced on a TOYO BD?350V5cold chamber die casting machine incorporated with a self-improved TOYO vacuum system.According to the results,the vacuum pressure inside the die cavity increased linearly with the increasing slow shot speed at the beginning of mold filling.Meanwhile,tensile properties of vacuum die castings were deteriorated by the porosity content.In addition,the average primary silicon size decreased from23to14μm when the slow shot speed increased from0.05to0.2m/s,which has a binary functional relationship with the slow shot speed.After heat treatment,microstructural morphologies revealed that needle-shaped and thin-flaked eutectic silicon particles became rounded while Al2Cu dissolved intoα(Al)matrix.Furthermore,the fractography revealed that the fracture mechanism has evolved from brittle transgranular fracture to a fracture mode with many dimples after heat treatment.
基金This work is supported by National Natural Science Foundation of China(Nos.51771115 and 51775334)National Science and Technology Major Project(2017ZX04006001)+1 种基金Joint Fund for Space Science and Technology(6141B06300401 and 6141B06310106)Science Innovation Foundation of Shanghai Academy of Spaceflight Technology(No.SAST2016048).
文摘The aim of this work is firstly to optimize T6 heat-treatment of low-pressure sand-cast Mg-10Gd-3Y-0.5Zr alloy,and then systematically investigate the mechanical behavior of the T6-treated alloy from room temperature to 300℃.It turned out that the optimum T6 heat-treatments for the tested alloy are 525℃×12 h+225℃×14 h and 525℃×12 h+250℃×12 h which integrated age-hardening and tensile properties into account,respectively.The strength of the T6-treated alloy indicates obvious anomalous temperature dependence from room temperature to 300℃,namely both ultimate tensile strength and yield strength of the tested alloy firstly increase with tensile temperature,and then decrease as temperature increases further.Elongation increased with temperature monotonously.The tensile fracture mode of the tested alloy changes from transgranular fracture to intergranular fracture with the increasing of test temperature.
基金supported by the National Key R&D Program of China(Grant No.2022YFB3706600)the National Natural Science Foundation of China(Grant Nos.52175196 and 52275218)the Fundamental Research Funds for Central Universities(Grant No.265QZ2021008).
文摘To improve the corrosion resistance of coalbed methane drilling equipment,an AICoCrFeNiCu high entropy alloy coating was prepared on the AISI 4135(35CrMo)steel substrate by high velocity oxygen fuel(HVOF)technology,and the coating was subjected to vacuum heat treatment(VHT)at different temperatures(500,700,900 and 1100℃).The corrosion test of the substrate and the coatings after VHT in coalbed methane drilling fluid was carried out.The results show that the HVOF sprayed AICoCrFeNiCu high entropy alloy(HEA)coating has a good bonding with the substrate,and the porosity of the coating is about 2.4%.There is partial segregation in the coating,and the coating mainly consists of body-centered cubic phase.The coating has good thermal stability,and the phase structure and microstructure of the coatings have changed after VHT at different temperatures.Compared with the substrate,the as-sprayed coating has better uniform corrosion resistance,and the corrosion resistance of the coating after VHT is further improved.After VHT at 500℃,the HVOF-sprayed AICoCrFeNiCu HEA coating has the best corrosion resistance.