AA2219 aluminium alloy joints were fabricated by variable polarity tungsten inert gas （VPTIG） welding process and the effects of post weld heat treatment （PWHT） on the tensile properties, microstructure and fatigu...AA2219 aluminium alloy joints were fabricated by variable polarity tungsten inert gas （VPTIG） welding process and the effects of post weld heat treatment （PWHT） on the tensile properties, microstructure and fatigue behaviour of the welded joints were investigated. The VPTIG welding process was adopted because it could meet the need of cathode cleaning and meanwhile it could reduce the deterioration of tungsten electrode furthest. The welded samples were divided into as-welded （AW） sample and PWHT sample. The PWHT method used on the samples was solution treatment （535 ℃, 30 rain）, water quenching and artificial aging （175 ℃, 12 h）. The experimental results show that, compared with the AW samples, the microstructure characteristics and mechanical properties of the AA2219 joints after PWHT were significantly improved. The improvement of yield strength, ultimate tensile strength, and fatigue strength are 42.6%, 43.1% and 18.4%, respectively.展开更多
基金Project(51275343)supported by the National Natural Science Foundation of China
文摘AA2219 aluminium alloy joints were fabricated by variable polarity tungsten inert gas （VPTIG） welding process and the effects of post weld heat treatment （PWHT） on the tensile properties, microstructure and fatigue behaviour of the welded joints were investigated. The VPTIG welding process was adopted because it could meet the need of cathode cleaning and meanwhile it could reduce the deterioration of tungsten electrode furthest. The welded samples were divided into as-welded （AW） sample and PWHT sample. The PWHT method used on the samples was solution treatment （535 ℃, 30 rain）, water quenching and artificial aging （175 ℃, 12 h）. The experimental results show that, compared with the AW samples, the microstructure characteristics and mechanical properties of the AA2219 joints after PWHT were significantly improved. The improvement of yield strength, ultimate tensile strength, and fatigue strength are 42.6%, 43.1% and 18.4%, respectively.