Hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） for 2A14-T6 high strength aluminum alloy was carried out and the effects of variable polarity frequency with constant pulse cur...Hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） for 2A14-T6 high strength aluminum alloy was carried out and the effects of variable polarity frequency with constant pulse current frequency 40 kHz on weld bead geometry, microstrueture and microhardness were analyzed. Experimental results indicate that, compared to that of the conventional VP-GTAW process, the weld depth and ratio of weld depth to width are improved significantly by the variable polarity frequency in the HPVP-GTAW process, which the ratio of weld depth to width is improved by 36% at equal variable polarity frequency of 100 Hz, and improved by 55% with that of 200 Hz. Weld microstructure and microhardness distribution are changed obviously with the increase of variable polarity frequency. In the conventional VP-GTA W process, the grains in weld central zone are coarser, and the microhardness in weld central zone and fusion zone is about 95 HV and the lowest 82 HV, respectively. The microhardness is enhanced to a certain extent both in the weld central zone and fusion zone with the variation of variable polarity frequency in the HPVP-GTAW process due to the refinement and uniformity of weld microstructure. With the variable polarity frequency of 600 Hz, the microhardness in weld central zone and fusion zone reaches nearly 110 HV and 97 HV, respectively.展开更多
A novel ultrafast-convert hybrid pulse variable polarity gas tungsten arc welding process （HPVP-GTAW） is developed. High frequency pulse square-wave current which has a frequency of more than 20 kHz is exactly integ...A novel ultrafast-convert hybrid pulse variable polarity gas tungsten arc welding process （HPVP-GTAW） is developed. High frequency pulse square-wave current which has a frequency of more than 20 kHz is exactly integrated in the positive polarity current duration. The effects of pulse current parameters on arc characteristics and weld penetration have been studied during the HPVP-GTAW process using Al-5. 8 Mg alloy plates. The arc characteristics studied by arc voltage and its profile, weld penetration noted by the ratio of weld depth to width have been found to be influenced significantly by the pulse current. The experimental results show that the HPVP-GTA W process can improve the arc profile predominantly and obtain the higher weld penetration with lower heat input. The observation may help in understanding the weld characteristics with respect to variation in the pulse current parameters which may be beneficial in using the novel HPVP-GTAW process to produce the better weld quality of aluminum alloy plates.展开更多
Optimization of hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process was carried out to obtain the optimum weld characteristics of 5AO6-HX4 aluminum-magnesium alloy sheets ...Optimization of hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process was carried out to obtain the optimum weld characteristics of 5AO6-HX4 aluminum-magnesium alloy sheets of 3 mm thickness. The square butt joints were produced by HPVP-GTA W process, the microstructure and mechanical properties were systematically investigated. It is observed that the process parameters influence the weld microstructure and mechanical properties significantly. Weld microstructure is mainly composed of grid a （A1） solid solution, with a large number of intermetallic （ Mg2Al3 ） precipitates distributed in the matrix. The amount of ~ （ Mg2Al3 ） precipitates has an obvious difference with different parameters. Compared with that of the base material, tensile strength of 5AO6-HX4 alloy welded joints has a certain reduction, as well as the elongation and reduction of area. The optimized welding process parameters for 5A06-HX4 alloy sheets are presented.展开更多
采用复合超高频脉冲方波变极性钨极氩弧焊技术(HPVP-GTAW,Hybrid ultrahigh frequency Pulse Variable Polarity Gas Tungsten Arc Welding)完成了2219-T87高强铝合金平板堆焊试验,研究了HPVP-GTAW工艺脉冲电流参数对焊缝成形参数的影...采用复合超高频脉冲方波变极性钨极氩弧焊技术(HPVP-GTAW,Hybrid ultrahigh frequency Pulse Variable Polarity Gas Tungsten Arc Welding)完成了2219-T87高强铝合金平板堆焊试验,研究了HPVP-GTAW工艺脉冲电流参数对焊缝成形参数的影响规律.结果表明,与常规变极性钨极氩弧焊(VP-GTAW)工艺相比,HPVP-GTAW工艺有利于增加焊缝熔深,提高焊缝深宽比;调节脉冲电流参数,将对焊缝成形行为产生显著影响.在正极性期间平均电流恒定的条件下,随着脉冲电流频率的增加,焊缝熔深、深宽比整体提高,60 kHz条件下深宽比增加了60%;适当增大脉冲峰值电流与基值电流的比值,焊缝深宽比有所增大;与占空比50%和80%条件相比,20%条件下焊缝深宽比最高,且随着峰值电流与基值电流比值的提高,其焊缝深宽比增幅最为明显.展开更多
采用裂纹尖端张开位移(crack tip opening displacement,CTOD)试验研究了高强2219铝合金变极性钨极氩弧焊(variable polarity tungsten inert gas welding,VPTIG)接头各部位的低温断裂韧性,利用扫描电镜对各部位的CTOD试验断口特征进行...采用裂纹尖端张开位移(crack tip opening displacement,CTOD)试验研究了高强2219铝合金变极性钨极氩弧焊(variable polarity tungsten inert gas welding,VPTIG)接头各部位的低温断裂韧性,利用扫描电镜对各部位的CTOD试验断口特征进行分析,并结合金相组织进一步阐明组织与断裂韧性的关联.研究结果表明,2219铝合金VPTIG焊接头各部位表现出不同的低温断裂韧性,熔合线最低,热影响区高于焊缝,但均低于母材.扫描电镜断口观察结果表明,母材、焊缝及热影响区的断裂机制为剪切断裂,熔合线的断裂机制为准解理断裂.金相组织分析较好地解释了焊接接头不同部位断裂韧性的差异.展开更多
AA 2219-0 Al-Cu alloy single bead welds were obtained by hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process with pulse frequency varying from 25 kHz to 70 kHz. Weld hardn...AA 2219-0 Al-Cu alloy single bead welds were obtained by hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process with pulse frequency varying from 25 kHz to 70 kHz. Weld hardness characteristics which mainly depicted by microhardness and its gradient were investigated systematically. The results show that pulse frequency has a great effect on the hardness characteristics. The weld zone microhardness and its gradient with different pulse frequency present an evident fluctuant trend. The fluctuation of gradient is slight, illustrating that the mierostructure is uniform with pulse frequcncy varied from 35 kHz to 60 kHz. The fusion zone microhardness and its gradient foUow the similar trends but fluetuate greatly. Maximum value of gradient appears around the fusion boundary due to the coarse and non- uniform microstrueture. The maximum gradient at 60 kHz is only 25.5 % of that at 45 kHz. According to the study, the best hardness characteristics are achieved at 60 kHz frequency.展开更多
基金This work is supported by the National Natural Science Foundation of China （Grant No. 51005011 ） and the Fundamental Research Funds for the Central Universities （ YWF-12-LGJC-001 ）.
文摘Hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） for 2A14-T6 high strength aluminum alloy was carried out and the effects of variable polarity frequency with constant pulse current frequency 40 kHz on weld bead geometry, microstrueture and microhardness were analyzed. Experimental results indicate that, compared to that of the conventional VP-GTAW process, the weld depth and ratio of weld depth to width are improved significantly by the variable polarity frequency in the HPVP-GTAW process, which the ratio of weld depth to width is improved by 36% at equal variable polarity frequency of 100 Hz, and improved by 55% with that of 200 Hz. Weld microstructure and microhardness distribution are changed obviously with the increase of variable polarity frequency. In the conventional VP-GTA W process, the grains in weld central zone are coarser, and the microhardness in weld central zone and fusion zone is about 95 HV and the lowest 82 HV, respectively. The microhardness is enhanced to a certain extent both in the weld central zone and fusion zone with the variation of variable polarity frequency in the HPVP-GTAW process due to the refinement and uniformity of weld microstructure. With the variable polarity frequency of 600 Hz, the microhardness in weld central zone and fusion zone reaches nearly 110 HV and 97 HV, respectively.
基金The research is supported by the National Natural Science Foundation of China （ No. 50975015 and No. 51005011 ） the China Postdoctoral Science Foundation （No. 20090460186）.
文摘A novel ultrafast-convert hybrid pulse variable polarity gas tungsten arc welding process （HPVP-GTAW） is developed. High frequency pulse square-wave current which has a frequency of more than 20 kHz is exactly integrated in the positive polarity current duration. The effects of pulse current parameters on arc characteristics and weld penetration have been studied during the HPVP-GTAW process using Al-5. 8 Mg alloy plates. The arc characteristics studied by arc voltage and its profile, weld penetration noted by the ratio of weld depth to width have been found to be influenced significantly by the pulse current. The experimental results show that the HPVP-GTA W process can improve the arc profile predominantly and obtain the higher weld penetration with lower heat input. The observation may help in understanding the weld characteristics with respect to variation in the pulse current parameters which may be beneficial in using the novel HPVP-GTAW process to produce the better weld quality of aluminum alloy plates.
基金This work was supported by the National Natural Science Foundation of China under grant No. 51005011 and the Fundamental Research Funds for the Central Universities.
文摘Optimization of hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process was carried out to obtain the optimum weld characteristics of 5AO6-HX4 aluminum-magnesium alloy sheets of 3 mm thickness. The square butt joints were produced by HPVP-GTA W process, the microstructure and mechanical properties were systematically investigated. It is observed that the process parameters influence the weld microstructure and mechanical properties significantly. Weld microstructure is mainly composed of grid a （A1） solid solution, with a large number of intermetallic （ Mg2Al3 ） precipitates distributed in the matrix. The amount of ~ （ Mg2Al3 ） precipitates has an obvious difference with different parameters. Compared with that of the base material, tensile strength of 5AO6-HX4 alloy welded joints has a certain reduction, as well as the elongation and reduction of area. The optimized welding process parameters for 5A06-HX4 alloy sheets are presented.
文摘采用裂纹尖端张开位移(crack tip opening displacement,CTOD)试验研究了高强2219铝合金变极性钨极氩弧焊(variable polarity tungsten inert gas welding,VPTIG)接头各部位的低温断裂韧性,利用扫描电镜对各部位的CTOD试验断口特征进行分析,并结合金相组织进一步阐明组织与断裂韧性的关联.研究结果表明,2219铝合金VPTIG焊接头各部位表现出不同的低温断裂韧性,熔合线最低,热影响区高于焊缝,但均低于母材.扫描电镜断口观察结果表明,母材、焊缝及热影响区的断裂机制为剪切断裂,熔合线的断裂机制为准解理断裂.金相组织分析较好地解释了焊接接头不同部位断裂韧性的差异.
基金The research is supported by the National Natural Science Foundation of China （No. 51005011 ） the Fundamental Research Funds for the Central Universities.
文摘AA 2219-0 Al-Cu alloy single bead welds were obtained by hybrid ultrahigh frequency pulse variable polarity gas tungsten arc welding （HPVP-GTAW） process with pulse frequency varying from 25 kHz to 70 kHz. Weld hardness characteristics which mainly depicted by microhardness and its gradient were investigated systematically. The results show that pulse frequency has a great effect on the hardness characteristics. The weld zone microhardness and its gradient with different pulse frequency present an evident fluctuant trend. The fluctuation of gradient is slight, illustrating that the mierostructure is uniform with pulse frequcncy varied from 35 kHz to 60 kHz. The fusion zone microhardness and its gradient foUow the similar trends but fluetuate greatly. Maximum value of gradient appears around the fusion boundary due to the coarse and non- uniform microstrueture. The maximum gradient at 60 kHz is only 25.5 % of that at 45 kHz. According to the study, the best hardness characteristics are achieved at 60 kHz frequency.