Effect of residual structural strain caused by the addition of Co3O4 nanoparticles on the structural, hardness and magnetic properties of an Al/Co3O4 nanocomposite produced by powder metallurgy

Al composites are of interest due to their appropriate ratio of strength to weight.In our research,an Al/Co3O4 nanocomposite was generated using a sintering technique.The powders of Al with various Co3O4 nanoparticle contents(0 wt%,0.5 wt%,1.0 wt%,1.5 wt%,2.0 wt%,and2.5 wt%)were first blended using planetary milling for 30 min,and compressed in a cylindrical steel mold with a diameter of 1 cm and a height of5 cm at a pressure of 80 MPa.The samples were evaluated with X-ray diffractometry(XRD),scanning electron microscopy(SEM),Vickers hardness,and a vibrating sample magnetometer(VSM).Although the crystallite size of the Al particles remained constant at 7–10 nm,the accumulation of nanoparticles in the Al particle interspace increased the structural tensile strain from 0.0045 to 0.0063,the hardness from HV 28 to HV 52 and the magnetic saturation from 0.044 to 0.404 emu/g with an increase in Co3O4 nanoparticle content from 0 wt%to 2.5 wt%.

Structural,electrical and magnetic studies on Y-Fe-O system

The compounds of iron substituted yttrium oxide systems have been prepared for the importance in the field of magneto electric materials.The polycrystalline samples of Y2–xFexO3–y(x=0.1,0.2) were prepared by solid-state reaction method.The single-phase formation of these compounds was confirmed by X-ray diffraction studies.It was found that the samples crystallized in tetragonal phase and the lattice parameters were calculated as a=1.0559(7) nm,c=1.0832(9) nm for Y1.9Fe0.1O3–y and a=1.0545(6) nm,c=1.0841(8)...

Organometallic L-Alanine Cadmium Iodide Crystals for Optical Device Fabrication

Single crystals of L-alanine cadmium iodide(LACI)were grown by the slow evaporation technique at room temperature.A single-crystal X-ray diffraction(SXRD)model was used to evaluate the crystal structure of the as-grown LACI crystal.The energy dispersive X-ray(EDX)analysis and ultraviolet-visible-near infrared(UV-vis-NIR)transmittance studies were carried out,and the results reveal the presence of elements in the title compound.From the transmittance data,the optical bandgap as a function of photon energy was estimated,and the different optical constants were calculated.A fluorescence study was performed for the LACI crystal.Thermogravimetric and differential thermal analyses have also been studied to investigate the thermal property of the LACI crystal.The efficiency of the second harmonic generation(SHG)of the title crystal was investigated.The magnetic and electrical properties were estimated by the vibrating sample magnetometer(VSM)analysis and impedance study,respectively.

Magnetic Cotton Fabric Coated with Poly (vinyl alcohol ) (PVA)/ Magnetic Attapulgite (MAT) Composite Solution

Magnetic fiber or fabric incorporating magnetic particles was widely used in the field of magnetic health-care.The cotton fabric was modified with poly(vinyl alcohol)(PVA)/magnetic attapulgite(MAT)composite solution by coating,which was the PVA solution blended with MAT.The mechanical and magnetic properties were characterized by scanning electronic microscopy(SEM),vibrating sample magnetometer(VSM)and tensile strength test.The results of SEM show that MAT can scatter uniformly in the PVA film and the PVA/MAT polymer film has good combination with cotton fabric.The results of other tests show that the addition of PVA/MAT polymer film not only brings uniform magnetism to cotton fabric,but also increases the mechanical strength of the material.Besides,the proportion of PVA/MAT and dipping time are studied in order to determine the best parameters for further study on magnetic cotton fabric.

Comparison of rare earths doping(neodymium and samarium) on structural and magnetic properties of Ni-Zn-Bi nanoferrites

Excellent magnetic properties in ferrites are required for high-frequency applications and for wastewater treatment. Thus, the present study shows the comparison of magnetic and structural properties of Nd and Sm substituted Ni-Zn-Bi ferrites with the series Ni_(0.5)Zn_(0.5)Bi_(0.04)Nd_(x)Fe_(1.96-x)O_4(with step size 0.002)and Ni_(0.5)Zn_(0.5)Bi_(0.04)Sm_(x)Fe_(1.96-x)O_4(with step size 0.02) prepared using citrate precursor method. The impact of the substitution of rare earth ions(Nd and Sm) on magnetic properties of the synthesized samples is observed using a vibrating sample magnetometer(VSM). The saturation magnetization values enhance considerably from 52 to 58 emu/g for Nd^(3+)ions and 39 to 57 emu/g for Sm^(3+) ions, thus, making these materials magnetically hard. Further, the higher value of coercivity is also observed ranging from133 to 167 Oe for Nd^(3+)ions and 81 to 155 Oe for Sm^(3+) ions. The shape of hysteresis loops indicates a super paramagnetic and ferromagnetic behavior in the obtained samples. The squareness ratio value is<0.5, suggesting the uniaxial anisotropy of particles and hence, these ferrites are suitable for microwaveabsorbing and in permanent magnetic materials. The X-ray diffraction(XRD) pattern shows the formation of pure cubic crystallites, where, lattice parameters range from 0.840 to 0.839 nm and from 0.838to 0.839 nm for Nd^(3+)and Sm^(3+) ions substitution, respectively. The crystallite size ranges between 28.63to 29.89 nm and 18.33 to 26.23 nm, for substitution of Nd^(3+)and Sm^(3+) ions, respectively. Field emission scanning electron microscopy(FESEM) shows the formation of homogeneous grains, whereas, energy dispersive spectrometer(EDS) counts describe the purity of the samples. The Sm concentration x = 0.10has the maximum surface area with value of 42.6 m^(2)/g which proves to be having good data storage application due to high surface area. The zero-field cooled(ZFC) and field cooled(FC) data show that Nddoped Ni-Zn-Bi nanoferrites show superparamagnetic behaviour in the room temperature range which makes them suitable for practical applications.

Systematic study of Ce^(3+) on the structural and magnetic properties of Cu nanosized ferrites for potential applications

Ce^（3＋） substituted Cu-spinel nanoferrites CuCe_xFe_（2-x）O_4（x=0.00, 0.02, 0.04, 0.06, 0.08 and 0.10） were synthesized via sol-gel self-combustion hybrid route. Single phase spinel ferrite of Cu nanoferrites were examined using X-ray diffraction（XRD） analysis whereas the multiphase structure was observed as Ce contents increased from x=0.06. Field emission scanning electron microscopy（FESEM）, Thermogravimetric and differential thermal analysis（TGA and DTA） and Fourier transform infrared spectroscopy（FTIR） were used to find out the morphology phase and metal stretching vibrations of Ce^（3＋） substituted nanocrystalline ferrites. The crystallite size was increased and found in the range of 25-91 nm. The agglomerations in Cu ferrite samples increase as the Ce^（3＋） concentration increases. The magnetic properties such as remanence, saturation magnetization, coercivity, Bohr magneton and magnetocrystalline anisotropy constant（K） were determined using M-H loops recorded from a vibrating sample magnetometer（VSM）. Saturation magnetization, remanence and coercivity are increased as the Ce^（3＋）contents increase in Cu nanocrystalline samples. Moreover, law of approach to saturation（LoA） was used to calculate the maximum value of saturation for Ce-doped Cu nanoferrites. The soft magnetic behaviour of the Cu nanoferrite is observed as compared to the samples substituted with the increased Ce contents in Cu nanocrystalline ferrite. Bohr magneton and magnetocrystalline anisotropy are found to increase with the substitution of rare earth Ce^（3＋） contents in Cu spinel nanocrystalline ferrite. Cedoped Cu nanocrystalline ferrites with excellent properties may be suitable for potential applications in sensing, security, switching, core, multilayer chip inductor, biomedical and microwave absorption applications.

A facile and green synthetic approach toward fabrication of starch-stabilized magnetite nanoparticles

A facile and green synthetic approach for fabrication of starch-stabilized magnetite nanoparticles was implemented at moderate temperature. This synthesis involved the use of iron salts, potato starch,sodium hydroxide and deionized water as iron precursors, stabilizer, reducing agent and solvent respectively. The nanoparticles（NPs） were characterized by UV-vis, PXRD, HR-TEM, FESEM, EDX, VSM and FT-IR spectroscopy. The ultrasonic assisted co-precipitation technique provides well formation of highly distributed starch/Fe3O4-NPs. Based on UV–vis analysis, the sample showed the characteristic of surface plasmon resonance in the presence of Fe3O4-NPs. The PXRD pattern depicted the characteristic of the cubic lattice structure of Fe3O4-NPs. HR-TEM analysis showed the good dispersion of NPs with a mean diameter and standard deviation of 10.68 4.207 nm. The d spacing measured from the lattice images were found to be around 0.30 nm and 0.52 nm attributed to the Fe3O4 and starch, respectively. FESEM analysis confirmed the formation of spherical starch/Fe3O4-NPs with the emission of elements of C, O and Fe by EDX analysis. The magnetic properties illustrated by VSM analysis indicated that the as synthesized sample has a saturation magnetization and coercivity of 5.30 emu/g and 22.898 G respectively.Additionally, the FTIR analysis confirmed the binding of starch with Fe3O4-NPs. This method was cost effective, facile and eco-friendly alternative for preparation of NPs.