The Sm–Zr–Fe–Co–Ti quinary-alloys with ThMn12 structure has attracted wide attention for ultra-high intrinsic magnetic properties,showing potentiality to be developed into rare-earth permanent magnets.The Ti eleme...The Sm–Zr–Fe–Co–Ti quinary-alloys with ThMn12 structure has attracted wide attention for ultra-high intrinsic magnetic properties,showing potentiality to be developed into rare-earth permanent magnets.The Ti element in alloys is crucial for phase stability and magnetic properties,and lower Ti content can increase intrinsic magnetic properties but reduce phase stability.In this study,the 1:12 single-phase melt-spun ribbons with low Ti content was successfully prepared using a rapid solidification non-equilibrium method for the Sm1.1Zr_(0.2)Fe_(9.2)Co_(2.3)Ti_(0.5) quinary-alloy.However,this non-equilibrium ribbon did not achieve good magnetic hardening due to the uneven microstructure and microstrain.Then,annealing was carried out to eliminate micro-strain and homogenize microstructure,therefore,remanence and coercivity were significantly improved even the precipitation of a small amount of a-Fe phase which were not conducive to coercivity.The remanence of 86.1 emu/g and coercivity of 151 kA/m was achieved when annealing at 850℃ for 45 min.After hot pressing,under the action of high temperature and pressure,a small portion of ThMn12 phases in the magnet decompose into Sm-rich phases and a-Fe,while remanence of 4.02 kGs(1 Gs=10^(-4) T),and coercivity of 1.12 kOe(1 Oe=79.5775 A·m^(-1))were still acquired.Our findings can provide reference for exploring practical permanent magnets made of 1:12 type quinary-alloys.展开更多
实现高发光效率、高亮度和良好的热稳定性是固态照明的迫切要求。因此,用于高功率发光二极管或激光二极管(LED/LD)的高性能荧光转换材料具有重要的研究意义。在这项工作中,通过将Lu^(3+)离子引入YAG∶Ce荧光陶瓷中方法作为有效策略来改...实现高发光效率、高亮度和良好的热稳定性是固态照明的迫切要求。因此,用于高功率发光二极管或激光二极管(LED/LD)的高性能荧光转换材料具有重要的研究意义。在这项工作中,通过将Lu^(3+)离子引入YAG∶Ce荧光陶瓷中方法作为有效策略来改善YAG∶Ce荧光材料的发光性能。采用固相反应和真空烧结法制Article ID:1000-7032(2023)06-0964^(-1)1收稿日期:2022^(-1)2-31;修订日期:2023-01-30基金项目:中国科学院战略性先导科技专项(XDA22010301)Supported by The Strategic Priority Research Program of The Chinese Academy of Sciences(XDA22010301)第6 HUANG Xinyou期,et al.:LuYAG∶Ce Transparent Ceramic Phosphors for High-brightness Solid-state…备了不同Lu^(3+)含量的(Lu,Y)_(3)Al_(5)O_(12)∶Ce荧光陶瓷(LuYAG∶Ce荧光陶瓷)。随着Lu^(3+)含量的增加,LuYAG∶Ce荧光陶瓷中的Y^(3+)位点被Lu^(3+)位点取代,Ce^(3+)的发射峰呈现从573 nm到563 nm的蓝移现象。当Lu^(3+)含量为60%时,通过将LuYAG∶Ce荧光陶瓷与蓝光LED组合,其发光强度达到最大值,流明效率达到114 lm∙W^(-1)。使用450 nm激光源与LuYAG∶Ce荧光陶瓷构建了透射模式下的激光驱动照明装置。随着功率密度从2.2 W·mm^(-2)增加到39 W·mm^(-2),Lu^(3+)含量为60%的荧光陶瓷光通量从128 lm增加到1874 lm,且没有发光饱和的迹象,最佳发光效率达到128 lm·W^(-1)。因此,LuYAG∶Ce荧光陶瓷有望成为高功率LED/LD照明的潜在荧光转换材料。展开更多
基金the National Key Research and De-velopment Program of China(Grant No.2021YFB3500300)the National Natural Science Foundation of China(Grant No.51931007)the Program of Top Disciplines Construc-tion in Beijing(Grant No.PXM2019014204500031).
文摘The Sm–Zr–Fe–Co–Ti quinary-alloys with ThMn12 structure has attracted wide attention for ultra-high intrinsic magnetic properties,showing potentiality to be developed into rare-earth permanent magnets.The Ti element in alloys is crucial for phase stability and magnetic properties,and lower Ti content can increase intrinsic magnetic properties but reduce phase stability.In this study,the 1:12 single-phase melt-spun ribbons with low Ti content was successfully prepared using a rapid solidification non-equilibrium method for the Sm1.1Zr_(0.2)Fe_(9.2)Co_(2.3)Ti_(0.5) quinary-alloy.However,this non-equilibrium ribbon did not achieve good magnetic hardening due to the uneven microstructure and microstrain.Then,annealing was carried out to eliminate micro-strain and homogenize microstructure,therefore,remanence and coercivity were significantly improved even the precipitation of a small amount of a-Fe phase which were not conducive to coercivity.The remanence of 86.1 emu/g and coercivity of 151 kA/m was achieved when annealing at 850℃ for 45 min.After hot pressing,under the action of high temperature and pressure,a small portion of ThMn12 phases in the magnet decompose into Sm-rich phases and a-Fe,while remanence of 4.02 kGs(1 Gs=10^(-4) T),and coercivity of 1.12 kOe(1 Oe=79.5775 A·m^(-1))were still acquired.Our findings can provide reference for exploring practical permanent magnets made of 1:12 type quinary-alloys.
文摘实现高发光效率、高亮度和良好的热稳定性是固态照明的迫切要求。因此,用于高功率发光二极管或激光二极管(LED/LD)的高性能荧光转换材料具有重要的研究意义。在这项工作中,通过将Lu^(3+)离子引入YAG∶Ce荧光陶瓷中方法作为有效策略来改善YAG∶Ce荧光材料的发光性能。采用固相反应和真空烧结法制Article ID:1000-7032(2023)06-0964^(-1)1收稿日期:2022^(-1)2-31;修订日期:2023-01-30基金项目:中国科学院战略性先导科技专项(XDA22010301)Supported by The Strategic Priority Research Program of The Chinese Academy of Sciences(XDA22010301)第6 HUANG Xinyou期,et al.:LuYAG∶Ce Transparent Ceramic Phosphors for High-brightness Solid-state…备了不同Lu^(3+)含量的(Lu,Y)_(3)Al_(5)O_(12)∶Ce荧光陶瓷(LuYAG∶Ce荧光陶瓷)。随着Lu^(3+)含量的增加,LuYAG∶Ce荧光陶瓷中的Y^(3+)位点被Lu^(3+)位点取代,Ce^(3+)的发射峰呈现从573 nm到563 nm的蓝移现象。当Lu^(3+)含量为60%时,通过将LuYAG∶Ce荧光陶瓷与蓝光LED组合,其发光强度达到最大值,流明效率达到114 lm∙W^(-1)。使用450 nm激光源与LuYAG∶Ce荧光陶瓷构建了透射模式下的激光驱动照明装置。随着功率密度从2.2 W·mm^(-2)增加到39 W·mm^(-2),Lu^(3+)含量为60%的荧光陶瓷光通量从128 lm增加到1874 lm,且没有发光饱和的迹象,最佳发光效率达到128 lm·W^(-1)。因此,LuYAG∶Ce荧光陶瓷有望成为高功率LED/LD照明的潜在荧光转换材料。