The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.O...The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.展开更多
Coarse grained WC-9Co cemented carbides with 0-1.0% TaC(mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using sc...Coarse grained WC-9Co cemented carbides with 0-1.0% TaC(mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using scanning electron microscopy(SEM), energy dispersive X-ray analysis(EDS), X-ray diffractometry(XRD) and mechanical properties tests. The results show that the maximum values of hardness and strength are HV 1124 and 2466 MPa respectively when 0.4% TaC is added. When the content of TaC is more than 0.6%, the grain size of WC is no longer affected by the amount of TaC, and(W,Ta)C occurs as well. Moreover, the strength and fracture toughness increase and the(Ta+W) content decreases with the increase of TaC content. The dependence of(Ta+W) content on the mechanical properties indicates that(Ta+W) content in Co should be decreased as low as possible to improve the mechanical properties of coarse grained WC-TaC-9Co cemented carbides with the microstructure of WC+γ two phase regions.展开更多
A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of...A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.展开更多
基金Funded by the Technology Innovation Leading Program of Shaanxi(No.2022QFY08-02)。
文摘The effects of ultrafine WC(WC_(UF),0.5μm) or W(1μm) and C(0.3μm)(W+C)_(UF) additives on the densification,microstructure and mechanical properties of coarse-grained cemented carbides were compared systematically.Overall,the cemented carbides with WC_(UF)/(W+C)_(UF) additives are almost fully densification to be higher than 99%,and the average grain size is kept above 2.8μm.The WC_(UF) additive assists grains to(truncated)trigonal prism shape by two dimensional(2D) growth,whereas the(W+C)_(UF) additive assists grains to rounded shape by three dimensional(3D) growth,lowers WC contiguity and increases face-centered-cubic Co.The hardness and bending strength of(75WC_(C)-15WC_(UF))-10Co are 86.6 HRA and 2 272 MPa,respectively,both higher than those of(75WC_(C)-15(W+C)_(UF))-10Co,which could be ascribed to the enhanced densification and unblemished grains.However,the fracture toughness of the(75WC_(C)-15(W+C)_(UF))-10Co is 23.5 MPa·m^(1/2),higher than that of the(75WC_(C)-15WC_(UF))-10Co due to the uniform WC-Co structure and flexible binder phase.
基金Project(2013zzts025)supported by the Fundamental Research Funds for the Central Universities of China
文摘Coarse grained WC-9Co cemented carbides with 0-1.0% TaC(mass fraction) were fabricated by HIP-sintering and gas quenching. The effects of TaC on the microstructures and mechanical properties were investigated using scanning electron microscopy(SEM), energy dispersive X-ray analysis(EDS), X-ray diffractometry(XRD) and mechanical properties tests. The results show that the maximum values of hardness and strength are HV 1124 and 2466 MPa respectively when 0.4% TaC is added. When the content of TaC is more than 0.6%, the grain size of WC is no longer affected by the amount of TaC, and(W,Ta)C occurs as well. Moreover, the strength and fracture toughness increase and the(Ta+W) content decreases with the increase of TaC content. The dependence of(Ta+W) content on the mechanical properties indicates that(Ta+W) content in Co should be decreased as low as possible to improve the mechanical properties of coarse grained WC-TaC-9Co cemented carbides with the microstructure of WC+γ two phase regions.
文摘A kind of W/DLC/W-S-C composite film was fabricated by magnetron sputtering method.Effects of WSx content on the structure and the adhesion of the composite films were investigated.In addition,tribological behavior of the composite films was studied in the conditions of the ambient air and N2 gas atmosphere by ball-on-disk tester.The results indicate that the composite films show dense and amorphous microstructure.The WCx and WSx compounds are found in amorphous diamond like carbon matrix in the top layers of W-S-C.A proper WSx content is beneficial for improving the adhesion of the composite films.In air atmosphere,the composite films with high C content have better wear resistance and the friction coefficients range from 0.15 to 0.25.In N2 condition,high WSx content is benefit for the wear resistance and the friction coefficients of the composite films range from 0.03 to 0.1.