Durable superomniphobic surfaces are desirable for their practical applications,including selfcleaning,non-fouling,protective clothing and the separation of liquids.The plasma-induced polymerization of environmentally...Durable superomniphobic surfaces are desirable for their practical applications,including selfcleaning,non-fouling,protective clothing and the separation of liquids.The plasma-induced polymerization of environmentally friendly C6 from a perfluoralkyl methlacrylate copolymer emulsion,AG-E081,was performed and a durable omniphobic fabric was achieved.C6 is an ecological alternative to C8(eight CF2 groups)fluorinated compounds,and it was thereafter successfully incorporated into aramid fabric to achieve a durable superomniphobic surface.The fabric became water and oil repellent with an extremely high water contact angle of 180°.As tested by the water spray AATCC test and hydrocarbon resistance test,the as-prepared fabric gained 100°(ISO 5)and grade number 4 respectively.Furthermore,the fabrics also showed significantly improved washing durability after ten washing cycles.By scanning electron microscopy(SEM),Fourier-transform infrared spectroscopy(FTIR)and x-ray photoelectron spectroscopy(XPS)tests,it is indicated that the durable superomniphobicity can be attributed to the roughness and activation of the aramid surface by the plasma pre-treatment,which induces more adsorption and chemical graft of the C6 copolymer.展开更多
In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with commo...In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with common ZnO/cotton composite. Firstly, the cotton fibers were pre-treated by hydrogen peroxide solution（H;O;） and sodium hydroxide（NaOH）, urea（CON;H;）. Secondly, the fabric was fabricated via in situ deposition. The effects of concentration of treatment liquid, ammonia-smoking time and curing temperature on the tensile property of the fabric, UV blocking property and water-washing durability test of as-obtained cotton fabrics were investigated. Thirdly, the as-obtained cotton sample was characterized by X-ray diffraction（XRD） and field emission scanning electron microscopy（FESEM）. It was shown that ZnO nanoparticles were assembled between cotton fibers, the surface and inside of the lumen and the mesopores of cotton fibers, while the content of nano-ZnO assembled in fabric can reach 15.63 wt%. It is proved that the finished fabric can obtain a very excellent UV blocking property, under the condition of zinc ion in concentration of 15 wt%, ammonia-smoking time for 10 min, curing temperature at 150 ℃ for 2 min.展开更多
基金supported by the Fundamental Research Funds for the Central Universities 2232019A3-12National Natural Science Foundation of China(No.11375042)。
文摘Durable superomniphobic surfaces are desirable for their practical applications,including selfcleaning,non-fouling,protective clothing and the separation of liquids.The plasma-induced polymerization of environmentally friendly C6 from a perfluoralkyl methlacrylate copolymer emulsion,AG-E081,was performed and a durable omniphobic fabric was achieved.C6 is an ecological alternative to C8(eight CF2 groups)fluorinated compounds,and it was thereafter successfully incorporated into aramid fabric to achieve a durable superomniphobic surface.The fabric became water and oil repellent with an extremely high water contact angle of 180°.As tested by the water spray AATCC test and hydrocarbon resistance test,the as-prepared fabric gained 100°(ISO 5)and grade number 4 respectively.Furthermore,the fabrics also showed significantly improved washing durability after ten washing cycles.By scanning electron microscopy(SEM),Fourier-transform infrared spectroscopy(FTIR)and x-ray photoelectron spectroscopy(XPS)tests,it is indicated that the durable superomniphobicity can be attributed to the roughness and activation of the aramid surface by the plasma pre-treatment,which induces more adsorption and chemical graft of the C6 copolymer.
基金Funded by the National Key R&D Program of China(2017YFB0309100)
文摘In order to fabricate a novel ZnO/cotton composite, a high proportion of ZnO nanoparticles were assembled in cotton fibers, and the as-obtained cotton fabric can possess better UV blocking property compared with common ZnO/cotton composite. Firstly, the cotton fibers were pre-treated by hydrogen peroxide solution（H;O;） and sodium hydroxide（NaOH）, urea（CON;H;）. Secondly, the fabric was fabricated via in situ deposition. The effects of concentration of treatment liquid, ammonia-smoking time and curing temperature on the tensile property of the fabric, UV blocking property and water-washing durability test of as-obtained cotton fabrics were investigated. Thirdly, the as-obtained cotton sample was characterized by X-ray diffraction（XRD） and field emission scanning electron microscopy（FESEM）. It was shown that ZnO nanoparticles were assembled between cotton fibers, the surface and inside of the lumen and the mesopores of cotton fibers, while the content of nano-ZnO assembled in fabric can reach 15.63 wt%. It is proved that the finished fabric can obtain a very excellent UV blocking property, under the condition of zinc ion in concentration of 15 wt%, ammonia-smoking time for 10 min, curing temperature at 150 ℃ for 2 min.