Effect of Mitigating Strength Retrogradation of Alkali Accelerator by the Synergism of Sodium Sulfate and Waste Glass Powder

This work aims to utilize waste glass powder(WGP)as a plementary material to mitigate the strength shrinkage caused by the alkaline accelerator.Waste glass power was used to replace cement by 0%,10%,and 20%to evaluate waste glass powder on the alkaline accelerator’s strength retrogradation.The results show that the strength improvement effect of unitary glass powder is inconspicuous.Innovative methods have been proposed to use sodium sulfate and waste glass powder synergism,using the activity of amorphous silica in glass powder.Compared with the reference group,the compressive strength of 28d mortar increases by 67%when the sodium sulfate content is 2.5%,and the replacement amount of waste glass powder is 10%.Besides,XRD and SEM analysis of hydration products also confirmed that the synergistic effect of sodium sulfate and waste glass powder could reduce strength inversion.The findings presented in this paper are pivotal for using waste glass to solve the problem of strength inversion caused by the alkaline accelerator.

Influence of Ultra Fine Glass Powder on the Properties and Microstructure of Mortars

This study focuses on the effect of ultrafine waste glass powder on cement strength,gas permeability and pore structure.Varying contents were considered,with particle sizes ranging from 2 to 20μm.Moreover,alkali activation was considered to ameliorate the reactivity and cementitious properties,which were assessed by using scanning electron microscopy(SEM),energy-dispersive X-ray spectroscopy(EDS),and specific surface area pore size distribution analysis.According to the results,without the addition of alkali activators,the performance of glass powder mortar decreases as the amount of glass powder increases,affecting various aspects such as strength and resistance to gas permeability.Only 5%glass powder mortar demonstrated a compressive strength at 60 days higher than that of the control group.However,adding alkali activator(CaO)during hydration ameliorated the hydration environment,increased the alkalinity of the composite system,activated the reactivity of glass powder,and enhanced the interaction of glass powder and pozzolanic reaction.In general,compared to ordinary cement mortar,alkali-activated glass powder mortar produces more hydration products,showcases elevated density,and exhibits improved gas resistance.Furthermore,alkali-activated glass powder mortar demonstrates an improvement in performance across various aspects as the content increases.At a substitution rate of 15%,the glass powder mortar reaches its optimal levels of strength and resistance to gas permeability,with a compressive strength increase ranging from 28.4%to 34%,and a gas permeation rate reduction between 51.8%and 66.7%.

Effect of Glass Powder on Chloride Ion Transport and Alkali-aggregate Reaction Expansion of Lightweight Aggregate Concrete

The effects of glass powder on the strength development, chloride permeability and potential alkali-aggregate reaction expansion of lightweight aggregate concrete were investigated. Ground blast furnace slag, coal fly ash and silica fume were used as reference materials. The re- placement of cement with 25% glass powder slightly decreases the strengthes at ？ and 28 d, but shows no effect on 90 d＇s. Silica fume is very effective in improving both the strength and chloride penetration resistance, while ground glass powder is much more effective than blast furnace slag and fly ash in improving chloride penetration resistance of the concrete. When expanded shale or clay is used as coarse aggregate, the concrete containing glass powder does not exhibit deleterious expansion even if alkali-reactive sand is used as fine aggregate of the concrete.

Experimental Evaluation of Compressive Strength and Gas Permeability of Glass- Powder-Containing Mortar

Glass powder of various particle sizes(2,5,10 and 15μm)has been assessed as a possible cement substitute for mortars.Different replacement rates of cement(5%,10%,15%,and 20%)have been considered for all particle sizes.The accessible porosity,compressive strength,gas permeability and microstructure have been investigated accordingly.The results have shown that adding glass powder up to 20%has a significantly negative effect on the porosity and compressive strength of mortar.The compressive strength initially rises with a 5%replacement and then decreases.Similarly,the gas permeability of the mortar displays a non-monotonic behavior;first,it decreases and then it grows with an increase in the glass powder content and particle size.The porosity and gas permeability attain a minimum for a 5%content and 10μm particle size.Application of a Nuclear magnetic resonance(NMR)technique has revealed that incorporating waste glass powder with a certainfineness can reduce the pore size and the number of pores of the mortar.Compared with the control mortar,the pore volume of the waste glass mortar with 5%and 10μm particle size is significantly reduced.When cement is partially replaced by glass powder with a particle size of 10μm and a 5%percentage,the penetration resistance and compressive strength of the mortar are significantly improved.

Early-Age Properties Development of Recycled Glass Powder Blended Cement Paste:Strengths,Shrinkage,Nanoscale Characteristics,and Environmental Analysis

Recycling solid waste in cement-based materials cannot only ease its load on the natural environment but also reduce the carbon emissions of building materials.This study aims to investigate the effect of recycled glass powder(RGP)on the early-age mechanical properties and autogenous shrinkage of cement pastes,where cement is replaced by 10%,20%and 30%of RGP.In addition,the microstructure and nano-mechanical properties of cement paste with different RGP content and water to binder(W/B)ratio were also evaluated using SEM,MIP and nanoindentation techniques.The results indicate that the early-age autogenous shrinkage decreases with the increase of RGP content and W/B ratio.While the mechanical strength deteriorates due to the addition of RGP,it can be compensated by reducing the W/B ratio.Although the addition of RGP increases the total porosity of the hardened paste,it reduces the small size porosity(<50 nm).In addition,the proportions of different types of C-S-H are changed,and the volume fraction of porosity is increased,but that of hydration products of cement paste is reduced due to the incorporation of RGP.Besides its pozzolanic activity,the mitigated shrinkage deformation that RGP is generating in cement pastes is encouraging for its use as a novel supplementary cementitious material that reduces the early-age cracking risk of cement-based materials.Meanwhile,the life cycle assessments indicate that the RGP-cement component is an economical and eco-friendly novel engineering material.