We reported a rapid synthesis of Sm^(3+)/Zr^(4+)co-doped Gd2Ti2O7 pyrochlore simulated nuclear wastes solidification by self-propagation plus quick pressing technique.With increment excess contents of Sm2O3 and ZrO2 f...We reported a rapid synthesis of Sm^(3+)/Zr^(4+)co-doped Gd2Ti2O7 pyrochlore simulated nuclear wastes solidification by self-propagation plus quick pressing technique.With increment excess contents of Sm2O3 and ZrO2 from 0 to 10wt%,the phase composition of the products is a mixed phase of pyrochlore structure and defective fluorite structure by X-ray diffraction(XRD)analysis and Raman spectrum.In addition,the SEM results demonstrate the fracture surface and microstructure of Gd2Ti2O7-based pyrochlore.The densified pyrochlore waste form exhibits high bulk density of 5.56 g·cm^(-3) and vickers hardness of 11.20±0.2 GPa.The leaching tests show that the elemental leaching rates of Gd,Sm,and Cu after 42 days are 1.92×10^(-4),1.51×10^(-4),and 3.90×10^(-3) g·m^(-2)·d^(-1),respectively.展开更多
基金Funded by the National Natural Science Foundation of China(No.51672228)the Project of State Key Laboratory of Environmentfriendly Energy Materials(Southwest University of Science and Technology,Nos.18fksy0214 and 20fksy11)+1 种基金the Postgraduate Innovation Fund Project by Southwest University of Science and Technology(No.19ycx0016)the Science Development Foundation of China Academy of Engineering Physics。
文摘We reported a rapid synthesis of Sm^(3+)/Zr^(4+)co-doped Gd2Ti2O7 pyrochlore simulated nuclear wastes solidification by self-propagation plus quick pressing technique.With increment excess contents of Sm2O3 and ZrO2 from 0 to 10wt%,the phase composition of the products is a mixed phase of pyrochlore structure and defective fluorite structure by X-ray diffraction(XRD)analysis and Raman spectrum.In addition,the SEM results demonstrate the fracture surface and microstructure of Gd2Ti2O7-based pyrochlore.The densified pyrochlore waste form exhibits high bulk density of 5.56 g·cm^(-3) and vickers hardness of 11.20±0.2 GPa.The leaching tests show that the elemental leaching rates of Gd,Sm,and Cu after 42 days are 1.92×10^(-4),1.51×10^(-4),and 3.90×10^(-3) g·m^(-2)·d^(-1),respectively.