Zinc metal is a promising anode material for next-generation aqueous batteries,but its practical application is limited by the formation of zinc dendrite.To prevent zinc dendrite growth,various Zn^(2+)-conducting but ...Zinc metal is a promising anode material for next-generation aqueous batteries,but its practical application is limited by the formation of zinc dendrite.To prevent zinc dendrite growth,various Zn^(2+)-conducting but water-isolating solid-electrolyte interphase(SEI)films have been developed,however,the required high-purity chemical materials are extremely expensive.In this work,phosphogypsum(PG),an industrial byproduct produced from the phosphoric acid industry,is employed as a multifunctional protective layer to navigate uniform zinc deposition.Theoretical and experimental results demonstrate that PG-derived CaSO_(4)2H_(2)O can act as an artificial SEI layer to provide fast channels for Zn^(2+)transport.Moreover,CaSO_(4)2H_(2)O could release calcium ions(Ca^(2+))due to its relatively high Kspvalue,which have a higher binding energy than that of Zn^(2+)on the Zn surface,thus preferentially adsorbing to the tips of the protuberances to force zinc ions to nucleate at inert region.As a result,the Zn@PG anode achieves a high Coulombic efficiency of 99.5%during 500 cycles and long-time stability over 1000 hours at 1 m A cm^(-2).Our findings will not only construct a low-cost artificial SEI film for practical metal batteries,but also achieve a high-value utilization of phosphogypsum waste.展开更多
基金financially supported by the National Natural Science Foundation of China (22279122,52042403)the Zhejiang Provincial Natural Science Foundation of China (LZ22B030004)+2 种基金the Ministry of Education,Singapore,under its Academic Research Fund Tier 1 (RG10/22)the National Institute of Education,Singapore,under its Academic Research Fund (RI 1/21 EAH)National Institute of Education,Singapore,under its Start-Up Grant (NIE-SUG4/20AHX)。
文摘Zinc metal is a promising anode material for next-generation aqueous batteries,but its practical application is limited by the formation of zinc dendrite.To prevent zinc dendrite growth,various Zn^(2+)-conducting but water-isolating solid-electrolyte interphase(SEI)films have been developed,however,the required high-purity chemical materials are extremely expensive.In this work,phosphogypsum(PG),an industrial byproduct produced from the phosphoric acid industry,is employed as a multifunctional protective layer to navigate uniform zinc deposition.Theoretical and experimental results demonstrate that PG-derived CaSO_(4)2H_(2)O can act as an artificial SEI layer to provide fast channels for Zn^(2+)transport.Moreover,CaSO_(4)2H_(2)O could release calcium ions(Ca^(2+))due to its relatively high Kspvalue,which have a higher binding energy than that of Zn^(2+)on the Zn surface,thus preferentially adsorbing to the tips of the protuberances to force zinc ions to nucleate at inert region.As a result,the Zn@PG anode achieves a high Coulombic efficiency of 99.5%during 500 cycles and long-time stability over 1000 hours at 1 m A cm^(-2).Our findings will not only construct a low-cost artificial SEI film for practical metal batteries,but also achieve a high-value utilization of phosphogypsum waste.