Polystyrene(PS)is rich in plastic materials,but it produces a large amount of waste every year,causing a huge burden on the environment.Although PS plastic is the source of a common"white pollution"in daily ...Polystyrene(PS)is rich in plastic materials,but it produces a large amount of waste every year,causing a huge burden on the environment.Although PS plastic is the source of a common"white pollution"in daily life,it still has a high utilization value.At the same time,the flammability of PS material determines that it cannot be applicated in places where fire accidents occur frequently.As a result,its application has been greatly limited.In order to realize the efficient utilization of waste PS and broaden its scope of application,PS was modified by hyper-crosslinking in order to improve its fire-retardant performance.In this method,the PS solution with high purity was obtained by dissolving waste PS foam with 1,2-dichloroethane(DCE),and then the hyper-crosslinked polymer with high specific surface area was prepared by adding cross-linking agent formaldehyde dimethyl acetal(FDA)and a Lewis-acid catalyst ferric chloride(FeCl_(3)).Further studies showed that the effects of the amount of cross-linking agent FDA,catalyst FeCl_(3) and PS on the reaction products were different.In addition,compared the as-prepared fire-retardant materials with PS foam from the aspects of flame retardancy and thermal insulation,it can be concluded that the fire-retardant performance of the materials prepared by this method has been significantly enhanced.And it is proved that this method is feasible towards the preparation of a large number of fire-retardant composite materials by using a scale-up experiment.展开更多
基金Thanks for financial support from the National Natural Science Foun-dation of China(No.51906252)the Natural Science Foundation of Jiangsu Province(NO.BK20190632)China Postdoctoral Science Foun-dation(2019M661980).
文摘Polystyrene(PS)is rich in plastic materials,but it produces a large amount of waste every year,causing a huge burden on the environment.Although PS plastic is the source of a common"white pollution"in daily life,it still has a high utilization value.At the same time,the flammability of PS material determines that it cannot be applicated in places where fire accidents occur frequently.As a result,its application has been greatly limited.In order to realize the efficient utilization of waste PS and broaden its scope of application,PS was modified by hyper-crosslinking in order to improve its fire-retardant performance.In this method,the PS solution with high purity was obtained by dissolving waste PS foam with 1,2-dichloroethane(DCE),and then the hyper-crosslinked polymer with high specific surface area was prepared by adding cross-linking agent formaldehyde dimethyl acetal(FDA)and a Lewis-acid catalyst ferric chloride(FeCl_(3)).Further studies showed that the effects of the amount of cross-linking agent FDA,catalyst FeCl_(3) and PS on the reaction products were different.In addition,compared the as-prepared fire-retardant materials with PS foam from the aspects of flame retardancy and thermal insulation,it can be concluded that the fire-retardant performance of the materials prepared by this method has been significantly enhanced.And it is proved that this method is feasible towards the preparation of a large number of fire-retardant composite materials by using a scale-up experiment.
