To solve the problems of high moisture content,high viscosity,and poor engineering mechanical properties of soil,this paper using with steel slag(SS)and desulfurization ash(DS)as initial raw materials,realizing the co...To solve the problems of high moisture content,high viscosity,and poor engineering mechanical properties of soil,this paper using with steel slag(SS)and desulfurization ash(DS)as initial raw materials,realizing the coop-erative treatment of solid waste and solidification of silt soil.The synergistic utilization of SS and DS can reduce the production cost of curing agent and promote its own consumption.According to blended cement of various SS contents and inspected compressive strength performances,the most suitable raw materials ratio was selected.The best formula for this curing agent is cement:steel slag=3:7 with 5%DS,and its 28-day compressive strength can reach 30 MPa.The experiment shows that the effect of DS and Na_(2)SO_(4) reagent with the same quality on early compressive strength improvement of cement and SS system is not much different.In this study,the mineral composition and microstructure of different gel system blocks were characterized by XRD,SEM and EDX,and a large number of webbed structures were found in the SEM test,which was not seen in previous studies.Besides,unconfined compressive strength(UCS),water resistance,and toxic characteristic leaching procedure(TCLP)were used to evaluate silt solidified soil properties.The results demonstrated that the solidified silt could meet not only the standard of general subgrade;but also has a partial stabilization effect of heavy metal ions.展开更多
基金Funding from the Jiangsu Provincial Department of Science and Technology Key Research and Development Program(Social Development)(Grant No.BE2018697)the Demonstration Engineering Technology Research Center of Suqian Science and Technology Bureau(Grant No.M201912)+1 种基金the Jiangsu Provincial Science and Technology Department Social Development Project(Grant No.BE2017704)a Project Funded by the Priority Academic Program Development of Jiangsu Higher Education Institutions.
文摘To solve the problems of high moisture content,high viscosity,and poor engineering mechanical properties of soil,this paper using with steel slag(SS)and desulfurization ash(DS)as initial raw materials,realizing the coop-erative treatment of solid waste and solidification of silt soil.The synergistic utilization of SS and DS can reduce the production cost of curing agent and promote its own consumption.According to blended cement of various SS contents and inspected compressive strength performances,the most suitable raw materials ratio was selected.The best formula for this curing agent is cement:steel slag=3:7 with 5%DS,and its 28-day compressive strength can reach 30 MPa.The experiment shows that the effect of DS and Na_(2)SO_(4) reagent with the same quality on early compressive strength improvement of cement and SS system is not much different.In this study,the mineral composition and microstructure of different gel system blocks were characterized by XRD,SEM and EDX,and a large number of webbed structures were found in the SEM test,which was not seen in previous studies.Besides,unconfined compressive strength(UCS),water resistance,and toxic characteristic leaching procedure(TCLP)were used to evaluate silt solidified soil properties.The results demonstrated that the solidified silt could meet not only the standard of general subgrade;but also has a partial stabilization effect of heavy metal ions.
文摘针对南水北调东线工程中产生的大量高含水量疏浚淤泥处理难的实际工程问题,通过外加生石灰的方法对高含水量疏浚淤泥进行了改性处理,将高含水量疏浚淤泥处理成了一种可以作为淤泥堆场围堰、河堤培土加固等实际工程填土材料的松散良质土.室内试验结果表明:添加生石灰处理高含水量疏浚淤泥时,改良土塑性指数随着掺灰比的增加而降低;在同一掺灰比下,原泥初始含水量低的生石灰处理土的塑性指数比原泥初始含水量高的生石灰处理土低;处理土塑性指数的改变主要发生在龄期的前3 d.