In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chlori...In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chloride diffusion law of coal gangue concrete specimens by crack width, curing temperature and water-cement ratio. Three groups of crack width (0 mm, 0.05 - 0.12 mm, 0.12 - 0.2 mm), three curing temperatures (high temperature 45, medium temperature 25, low temperature 10), three water cement ratios (0.3, 0.4, 0.5) were set in the experiment. The results show that when the curing temperature and water cement ratio are constant, the crack width less than 0.12 mm has little effect on the chloride content and chloride diffusion coefficient. When the crack width is larger than 0.12 mm, the chloride penetration depth increases with the crack width. The resistance to chloride ion penetration of gangue concrete is greatly influenced by the water cement ratio. The influ-ence degree of three factors on chloride ion migration coefficient of gangue concrete is as follows: water cement ratio > crack width > curing temperature.展开更多
The QDB-5 sulfur tolerant CO shift catalyst, with anti-methanation property by supported compositing alkali promoters, has been proved to effectively reduce the outlet methane content in the condition of a low water g...The QDB-5 sulfur tolerant CO shift catalyst, with anti-methanation property by supported compositing alkali promoters, has been proved to effectively reduce the outlet methane content in the condition of a low water gas ratio. Thus, a new technology based on a lower water/gas ratio than before has been developed with the new catalyst. The CO conversion at lower temperatures and catalyst stability were confirmed by long term industrial application. The high temperature catalyst performance also showed a better result than the conventional commercial catalyst, with higher CO conversion and well controlled methane outlet. Our research and the industrial application of catalyst have shown the importance of alkali metals as core promoters for such kind of catalysts.展开更多
文摘In order to investigate the chloride ion penetration resistance of coal gangue concrete under multi-factor comprehensive action, the non-steady-state accelerated chloride ion migration test was used to test the chloride diffusion law of coal gangue concrete specimens by crack width, curing temperature and water-cement ratio. Three groups of crack width (0 mm, 0.05 - 0.12 mm, 0.12 - 0.2 mm), three curing temperatures (high temperature 45, medium temperature 25, low temperature 10), three water cement ratios (0.3, 0.4, 0.5) were set in the experiment. The results show that when the curing temperature and water cement ratio are constant, the crack width less than 0.12 mm has little effect on the chloride content and chloride diffusion coefficient. When the crack width is larger than 0.12 mm, the chloride penetration depth increases with the crack width. The resistance to chloride ion penetration of gangue concrete is greatly influenced by the water cement ratio. The influ-ence degree of three factors on chloride ion migration coefficient of gangue concrete is as follows: water cement ratio > crack width > curing temperature.
文摘The QDB-5 sulfur tolerant CO shift catalyst, with anti-methanation property by supported compositing alkali promoters, has been proved to effectively reduce the outlet methane content in the condition of a low water gas ratio. Thus, a new technology based on a lower water/gas ratio than before has been developed with the new catalyst. The CO conversion at lower temperatures and catalyst stability were confirmed by long term industrial application. The high temperature catalyst performance also showed a better result than the conventional commercial catalyst, with higher CO conversion and well controlled methane outlet. Our research and the industrial application of catalyst have shown the importance of alkali metals as core promoters for such kind of catalysts.