Air plasma spraying process was employed to fabricate various hydroxyapatite(HA)coatings on titanium substrates.The influence of processing parameters on the phase composition and the microstructure of the obtained co...Air plasma spraying process was employed to fabricate various hydroxyapatite(HA)coatings on titanium substrates.The influence of processing parameters on the phase composition and the microstructure of the obtained coatings was investigated.The effect of heat treatment on as-sprayed coating in terms of the crystallinity and microstructure was also studied.The phase composition of coatings was analyzed by X-ray diffraction(XRD)and FTIR.The surface and cross-section morphologies and microstructure of coatings as well as the morphology of feedstock were evaluated using scanning electron microscope(SEM).The crystallization temperature of amorphous HA phase in as-sprayed coating was examined by using differential thermal analysis(DTA). The results suggest that phase composition and microstructure of as-sprayed HA coatings strongly depend on the spraying parameters,and heat treatment at 760 ℃for 2 h is one of effective means for increasing the crystallinity and improvement in microstructure of as-sprayed HA coatings.展开更多
The normal temperature corrosion of VC coating on the substrate of Cr12MoV prepared by TD process was tested in 5% NaCl aqueous solution, its surface morphologies and corrosion components after salt spray were observe...The normal temperature corrosion of VC coating on the substrate of Cr12MoV prepared by TD process was tested in 5% NaCl aqueous solution, its surface morphologies and corrosion components after salt spray were observed with SEM and EDS, respectively, and the effects of salt spray on micro-structures of VC coating were analyzed. Moreover, the invalidation mechanism of VC coating after salt spray and its effect on substrate material were discussed. The experimental results shown that the uniformity and integrity of VC coating surface are destroyed by salt spray for 120 h, a large number of the pits are produced on the coating surface, and the coating falls off, which speeds corrosion breakage of its substrate; the oxidated film on its surface becomes rougher, broken and discontinuous, and falls off easily, which reduce the ability of resistance salt spray; the failure modes of VC coating after salt spray are expressed with falling off of oxidated film, stress concentration and pore effect and so on, the corrosion breakage of oxidated film is the corrosion result of deoxidization corrosion from oxygen and HCl produced by NaCl and vapor.展开更多
On-line temperature monitoring of plasma sprayed coating is presented, which is based on IR pyrometery combined to robot trajectories. Temperature fields of the substrate before spraying and the deposited coating when...On-line temperature monitoring of plasma sprayed coating is presented, which is based on IR pyrometery combined to robot trajectories. Temperature fields of the substrate before spraying and the deposited coating when the damage happens are taken to investigate the temperature fluctuation information. Experimental results demonstrate that coating damage always occurs in the temperature transition area of the substrate from the higher to the lower, as well as the higher temperature area. The temperature difference between the peak and the mean of the relevant regions is beyond 30 - 50℃ or even higher. This case provides the omen of coating damage and the focusing scopes for the process control of coating temperature in plasma spraying展开更多
Aiming at the plasma spraying process control, the control system model is developed on the basis of analyzing control parameters and coating properties and their correlation, and the corresponding control method and ...Aiming at the plasma spraying process control, the control system model is developed on the basis of analyzing control parameters and coating properties and their correlation, and the corresponding control method and regulations are also given. With the developed expert controller for plasma spraying process, stable spraying can be realized using ordinary spraying powder and the coating of compaction, homogeneity and high bonding strength can be obtained.展开更多
文摘Air plasma spraying process was employed to fabricate various hydroxyapatite(HA)coatings on titanium substrates.The influence of processing parameters on the phase composition and the microstructure of the obtained coatings was investigated.The effect of heat treatment on as-sprayed coating in terms of the crystallinity and microstructure was also studied.The phase composition of coatings was analyzed by X-ray diffraction(XRD)and FTIR.The surface and cross-section morphologies and microstructure of coatings as well as the morphology of feedstock were evaluated using scanning electron microscope(SEM).The crystallization temperature of amorphous HA phase in as-sprayed coating was examined by using differential thermal analysis(DTA). The results suggest that phase composition and microstructure of as-sprayed HA coatings strongly depend on the spraying parameters,and heat treatment at 760 ℃for 2 h is one of effective means for increasing the crystallinity and improvement in microstructure of as-sprayed HA coatings.
基金Funded by the Foundation for Applied Basic Research of Changzhou City, China (CJ20110019)the Innovation Program of Graduated Student of Jiangsu Province(XM10-243)
文摘The normal temperature corrosion of VC coating on the substrate of Cr12MoV prepared by TD process was tested in 5% NaCl aqueous solution, its surface morphologies and corrosion components after salt spray were observed with SEM and EDS, respectively, and the effects of salt spray on micro-structures of VC coating were analyzed. Moreover, the invalidation mechanism of VC coating after salt spray and its effect on substrate material were discussed. The experimental results shown that the uniformity and integrity of VC coating surface are destroyed by salt spray for 120 h, a large number of the pits are produced on the coating surface, and the coating falls off, which speeds corrosion breakage of its substrate; the oxidated film on its surface becomes rougher, broken and discontinuous, and falls off easily, which reduce the ability of resistance salt spray; the failure modes of VC coating after salt spray are expressed with falling off of oxidated film, stress concentration and pore effect and so on, the corrosion breakage of oxidated film is the corrosion result of deoxidization corrosion from oxygen and HCl produced by NaCl and vapor.
基金The work is supported by the National Natural Science Foundation of China （No. 51005085）.
文摘On-line temperature monitoring of plasma sprayed coating is presented, which is based on IR pyrometery combined to robot trajectories. Temperature fields of the substrate before spraying and the deposited coating when the damage happens are taken to investigate the temperature fluctuation information. Experimental results demonstrate that coating damage always occurs in the temperature transition area of the substrate from the higher to the lower, as well as the higher temperature area. The temperature difference between the peak and the mean of the relevant regions is beyond 30 - 50℃ or even higher. This case provides the omen of coating damage and the focusing scopes for the process control of coating temperature in plasma spraying
文摘Aiming at the plasma spraying process control, the control system model is developed on the basis of analyzing control parameters and coating properties and their correlation, and the corresponding control method and regulations are also given. With the developed expert controller for plasma spraying process, stable spraying can be realized using ordinary spraying powder and the coating of compaction, homogeneity and high bonding strength can be obtained.