Wear characteristics of spheroidal graphite roll WC-8Co coating produced by electro-spark deposition

Electro-spark deposition（ESD） was adopted for preparing high property coatings by depositing WC-8Co cemented carbide on an spheroidal graphite roll substrate.The microstructure and properties of the coating were investigated by X-ray diffraction（XRD）, scanning electron microscopy（SEM） with energy dispersive X-ray（EDX） and ball-disc configuration wear tester.The results show that nanosized particles and amorphous structures prevail in the coating which is metallurgically bonded to the substrate.The microstructures of the transition zone include columnar structure and equiaxed structure.The primary phases of the coating contain W2C, W6C2.54, Fe3W3C, and Co3W3C.The results of abrasive test show that the coating has low friction coefficients（μaverage = 0.18） and the wear mechanisms are mainly abrasive wear, fatigue wear, and oxidation wear.The maximum microhardness value of the coating is about 17410 N/mm2.The study reveals that the electro-spark deposition process has better coating quality and the coating has high wear resistance and hardness.

Preparation and properties of the Ni-Al/Fe-Al intermetallics composite coating produced by plasma cladding

A novel approach to produce an intermetallic composite coating was put forward.The microstructure,microhardness,and dry-sliding wear behavior of the composite coating were investigated using X-ray diffraction （XRD）,scanning electron microscopy （SEM）,energy dispersive spectrum （EDS） analysis,microhardness test,and ball-on-disc wear experiment.XRD results indicate that some new phases FeAl,Fe0.23Ni0.77Al,and Ni3Al exit in the composite coating with the Al2O3 addition.SEM results show that the coating is bonded with carbon steel metallurgically and exhibits typical rapid directional solidification structures.The Cr7C3 carbide and intermetallic compounds co-reinforced composite coating has a high average hardness and exhibits an excellent wear resistance under dry-sliding wear test compared with the Cr7C3 carbide-reinforced composite coating.The formation mechanism of the intermetallic compounds was also investigated.

Effect of Salt Spray Corrosion on Tribological Properties of HVOF Sprayed NiCr-Cr3C2 Coating with Intermediate Layer

The objective of the present work was to determine the influence of the neutral salt spray corrosion on the wear resistance of HVOF sprayed NiCr-Cr3C2 coating with intermediate layer. Ni-Zn-Al2O3 coatings as interlayers were prepared by low pressure cold spray（LPCS） between NiCr-Cr3C2 cermet coatings to form a sandwich structure to enhance the corrosion resistance properties. The tribological properties were examined using the UMT-3 fricition and wear tester by line-contact reciprocating sliding under dry and salt spray one week corrosion. The morphology, element distribution, and phase compositions of the coating and worn sufaces were analyzed by using scanning electron microscopy, energy dispersive spectrometry, and X-ray diffraction respectively. The corrosion behavior of the coating was studied by the open-circuit potential, the electrochemical impedance spectroscopy, potentiodynamic polarization, and salt spray corrosion methods. It is found that the sandwich structured coating has better corrosion resistance than the single layer coating. The results show that under dry wear conditions, the wear mechanism is abrasive and adhesive wear, whereas under salt spray corrosion conditions it becomes corrosion wear. The friction coefficient of the sandwich structured coating after salt spray corrosion is slightly lower than the dry friction coefficient, but the weight of the wear loss is lower than that under dry condition.

Effect of Attapulgite Added in Plating Bath on the Properties of Ni/TiC Nano-composite Coatings

Pure copper plates were coated by Ni-TiC dipulse current plating method. The effects of adding different concentration（ranging from 0.5 g/L to 3.0 g/L） of attapulgite nano particles to the plating bath on the surface morphology, wear resistance, and oxidation resistance of Ni/TiC/Attapulgite nano-composite coatings were investigated. The experimental results show that the composite coating is flat and compact with adding 3.0 g/L in the bath, and the coating preferred orientation is changed from the planes（111） to（200）. The coefficient of the composite coatings decreases from 0.68 to 0.18 with increasing content of attapulgite in the bath, a mixed mode of adhesive-abrasive wear occurs for all coatings, and the wear mechanism shows a transition from adhesive-abrasive to predominantly abrasive wear mechanism when the concentration of attapulgite is beyond 1.5 g/L in electrolyte. The oxidation resistance of composite coatings is the best prepared when adding attapulgite particles at 0.5 g/L in the bath, the oxide mainly consists of a NiO phase by X-ray analysis.

Microstructure and Wear Properties of Fe-based Amorphous Coatings Deposited by High-velocity Oxygen Fuel Spraying

Fe-based powder with a composition of Fe_（42.87）Cr_（15.98）Mo_（16.33）C_（15.94）B_（8.88）（at.%）was used to fabricate coatings by high-velocity oxygen fuel spraying.The effects of the spraying parameters on the microstructure and the wear properties of the Fe-based alloy coatings were systematically studied.The results showed that the obtained Fe-based coatings with a thickness of about 400μm consisted of a large-volume amorphous phase and some nanocrystals.With increasing the fuel and oxygen flow rates,the porosity of the obtained coatings decreased.The coating deposited under optimized parameters exhibited the lowest porosity of 2.8%.The excellent wear resistance of this coating was attributed to the properties of the amorphous matrix and the presence of nanocrystals homogeneously distributed within the matrix.The wear mechanism of the coatings was discussed on the basis of observations of the worn surfaces.

Distribution Characteristics and Reinforcing Behavior of(Ti,Nb)C Reinforced Particle in the Coating Fabricated by Laser Rapid Cladding

（Ti, Nb）C reinforced Fe based laser coatings were prepared with normal and high scanning velocities of the laser beam. The distribution characteristics of reinforced particles in the coatings were investigated. The mechanical properties of coatings were tested. The results showed that the morphologies of the microstructure and the reinforced particle changed dramatically at high solidification rate due to rapid laser processing compared with that prepared by normal processing. Two kinds of particles were observed in the coating. One was （Ti, Nb）C multiple carbide particle with the size of micron and sub micron scales, in which a mass of dislocations were found. Another was nano sized particle including a Fe and （Ti, Nb）C obtained by rapid solidification. The microstructure of the coatings was highly refined and a large number of twin crystals were found in matrix. The resuhs of mechanical properties test revealed that the wear resistance of the coaling was improved by rapid laser processing, compared with that of the coating prepared with normal speeds. The ahove-mentioned conclusion indicated that rapid laser cladding can promote not on ly the processing efficiency but also lhe mechanical properties of the coating.