Variations in Wear Resistance of a Novel Triboalloy Pseudoelastic TiNi Alloy-with Respect to its Pseudoelasticity and Hardness

It has recently been found that TiNt shape memory alloy has another attractive property; high resistance to wear. The wear resistance of this alloy benefits from its pseudoelasticity (PE). It has, however, been noticed that other mechanical properties also affect the wear resistance, especially the hardness. Research was conducted to investigate the correlation between the wear resistance and both the PE and hardness. It has been demonstrated that when the PE is high, lower hardness leads to higher wear resistance.

Enhanced wear resistance,antibacterial performance,and biocompatibility using nanotubes containing nano-Ag and bioceramics in vitro

A good Ti-based joint implant should prevent stress shielding and achieve good bioactivity and anti-infection performance.To meet these requirements,the low-elastic-modulus alloy—Ti–35Nb–2Ta–3Zr—was used as the substrate,and functional coatings that contained bioceramics and Ag ions were prepared for coating on TiO_(2)nanotubes(diameter:(80±20)nm and(150±40)nm)using anodization,deposition,and spin-coating methods.The effects of the bioceramics(nano-β-tricalcium phosphate,microhydroxyapatite(micro-HA),and meso-CaSiO_(3))and Ag nanoparticles(size:(50±20)nm)on the antibacterial activity and the tribocorrosion,corrosion,and early in vitro osteogenic behaviors of the nanotubes were investigated.The tribocorrosion and corrosion results showed that the wear rate and corrosive rate were highly dependent on the features of the nanotube surface.Micro-HA showed great wear resistance with a wear rate of(1.26±0.06)×10^(−3)mm^(3)/(N·m)due to adhesive and abrasivewear.Meso-CaSiO_(3)showed enhanced cell adhesion,proliferation,and alkaline phosphatase activity.The coatings that contained nano-Ag exhibited good antibacterial activity with an antibacterial rate of≥89.5%against Escherichia coli.These findings indicate that hybrid coatings may have the potential to accelerate osteogenesis.

Heat Treatment Effect on Microstructure, Hardness and Wear Resistance of Cr26 White Cast Iron

High chromium cast iron（HCCI） is taken as material of coal water slurry pump impeller, but it is susceptible to produce serious abrasive wear and erosion wear because of souring of hard coal particles. The research on optimization of heat treatments to improve abrasive wear properties of HCCI is insufficient, so effect of heat treatments on the microstructure, hardness, toughness, and wear resistance of Cr26 HCCI is investigated to determine the optimal heat treatment process for HCCI. A series of heat treatments are employed. The microstructures of HCCI specimens are examined by using optical microscopy and scanning electron microscopy. The hardness and impact fracture toughness of as-cast and heat treated specimens are measured. The wear tests are assessed by a Type M200 ring-on block wear tester. The results show the following： With increase of the quenching temperature from 950 ℃ to 1050 ℃, the hardness of Cr26 HCCI increased to a certain value, kept for a time and then decreased. The optimal heat treatment process is 2 h quenching treatment at 1000 ℃, followed by a subsequent 2 h tempering at 400 ℃. The hardness of HCCI is related to the precipitation and redissolution of secondary carbides in the process of heat treatment. The subsequent tempering treatment would result in a slight decrease of hardness but increase of toughness. The wear resistance is much related to the ＂supporting＂ effect of the matrix and the ＂protective＂ effect of the hard carbide embedded in the matrix, and the wear resistance is further dependent on the hardness and the toughness of the matrix. This research can provide an important insight on developing an optimized heat treatment method to improve the wear resistance of HCCI.

A Study on Wear Resistance, Hardness and Impact Behaviour of Carburized Fe-Based Powder Metallurgy Parts for Automotive Applications

In order to study the mechanical and triboloical properties of powder metallurgy (PM) parts under different process parameters, the specimens were used in pack carburizing processes. These specimens made from industrial test pieces were carburized in a powder pack for about two to five hours at a temperature of about 850?C - 950?C. The effects of austenitization and quenching are investigated on some specimens. Also the wear tests are performed by means of a pin-on-disc tribotester using roll bearing steel as the counterface material. The results indicate that by appropriate selection of process parameters, it is possible to obtain high wear resistance along with moderate toughness. It is concluded that surface treatments increases the wear resistance and performance of PM parts in service conditions. By increasing the role of PM in industry which resulted from their ability to produce the complex shapes, high production rate, and dimension accuracy of final products, they need to be heat treated. Carburizing method was selected as a surface hardening method for PM parts. Results of wear and hardness show considerable enhancement in mechanical properties of PM parts.

HARDNESS PROPERTY AND WEAR RESISTANCE OF Al_2O_(3P)/ Zn-Al COMPOSITE

The hardness values and the wear resistance of Al2O3P/ Zn-Al composite, prepared by means of rheological casting technology,are investigated separately in this work. The results show that the addition of Al2O3P increases the hardness values of the matrix at both room and high temperature and improves the wear resistance of the material.The hardness values and the wear resistance of the composite rise with the increase of the particle volume fraction or the decrease of the particle size.The raising of test temperature results in a rapid descending of its hardness values.However, the addition of Al2O3P improves the property of high temperature resistance of Zn-Al alloys significantly.Moreover,the effect of quenching, tempering or cycling heat treatment on the hardness values of the composite is also studied.

Design and Development of Composite Plywood that Integrates Fire Resistance,Water Resistance and Wear Resistance

In order to improve the fire resistance,water resistance and wear resistance of ordinary plywood products in the wood processing industry,three composite structures of plywood products S1,S2 and S3 were designed in this paper,and a reasonable production process was proposed.Through the physical and mechanical properties and fire resistance testing and technical and economic analysis,the applicability of composite plywood was evaluated.The results of the study showed that the physical mechanics of the three kinds of composite structure plywood met the standard requirements,and their fire resistance was far better than that of ordinary plywood.Among them,the S1 structural board had the best overall physical and mechanical properties.The S3 structural board showed the best fire resistance,which was about 1.9 times more than that of ordinary plywood,and the added cost was the lowest.The thin cork board added to the S2 structural board had poor fire performance since the air in the cork board cavities had a certain combustion-supporting effect,which inhibited the fire resistance of high-pressure laminate(HPL)layer.Moreover,the additional cost of the S2 board was the highest,and its comprehensive performance was the worst.The S3 structural plywood product composed of HPL fireproof board with a thickness of about 1 mm in the surface layer and ordinary plywood with a thickness of about 12 mm in the core layer was the most cost-effective product,which could meet the needs of various fields such as construction,home furnishing,decoration and transportation.

Microstructure,mechanical properties and dry wear resistance of β-type Ti-15Mo-xNb alloys for biomedical applications

In order to study the effect of element Nb on the microstructure and properties of the biomedical β-type Ti-Mo based alloys,Ti-15Mo-xNb（x=5,10,15 and 20 in %） alloys were investigated.The dry wear resistance of β-type Ti-15Mo-xNb alloys against Gr15 ball was investigated on CJS111A ball-disk wear instrument.Experimental results indicate that crystal structure and morphology of the Ti-15Mo-xNb alloys are sensitive to their Nb contents.Ti-15Mo-xNb alloys match those for β phase peaks and no any phases are found.The Vickers hardness values of all the Ti-15Mo-xNb alloys are higher than HV200.The compression yield strength of the Ti-15Mo-5Nb alloy is the lowest and that of the Ti-15Mo-10Nb alloy is the highest.For all the Ti-15Mo-xNb alloys,the friction coefficient is not constant but takes a higher value.In dry condition,SEM study reveals deep parallel scars on the wear surfaces of all the Ti-15Mo-xNb alloys under different loads.The friction coefficient of the Ti-15Mo-5Nb alloy under 1 N is the lowest.The wear principal mechanism for Ti-15Mo-xNb alloys is adhesive wear.

Hardness, Wear Resistance and Fracture Toughness of Cast Hiduminium/Corundum Particulate Composites

This paper reports some results obtained in an investigation to see how increasing the corundum dispersoid content from 0% to 7% in a matrix of as-cast and wrought hiduminium alloy affects the hardness. wear resistance and fracture toughness of the composite. The results show that as the corundum content is increased, the hardness and the wear resistance increase remarkably,whereas the fracture toughness drops significantly. It was found that Just a minute amount of corundum is sufficient to cause a fairly large change in these mechanical properties. The hardness of the material is also affected signifIcantly by the aging time. Moreover, if other factors are kept constant, hot extrusion improves both its hardness and its wear resistance. whereas the fracture toughness is decreased

Reactive HVOF sprayed TiN-matrix composite coating and its corrosion and wear resistance properties

TiN-matrix composite coating was prepared on 45# steel by reactive high-velocity oxy-fuel （HVOF） spraying. Its microstructure, phase composition, micro-hardness, corrosion resistance in 3.5% NaC1 solution and wear resistance were analyzed. The results suggest that the TiN-matrix composite coating is well bonded with the substrate. The micro-hardness measured decreases with the increase of applied test loads. And the micro-hardness of the coating under heavy loads is relatively high. The TiN-matrix composite coating exhibits an excellent corrosion resistance in 3.5% NaC1 solution. The corrosion potential of coating is positive and the passivation zone is broad, which indicates that the TiN-matrix composite coating is stable in the electrolyte and provides excellent protection to the substrate. The wear coefficient of the coating under all loads maintains at 0.49-0.50. The wear mechanism of the coating is revealed to be three-body abrasive wear. Yet the failure forms of TiN-matrix composite coating under different loads have an obvious difference. The failure form of coating under light loads is particle spallation due to the stress concentration while that of coating under heavy loads is crackin~ between inter-lamellae.

Effects of slurry pack cementation temperature on microstructure and wear resistance of Ti-Al co-deposited coating on copper plated nickel layer

In order to improve the wear resistance properties of copper substrate, a layer of electroplated nickel was firstly deposited on copper substrate, subsequently these electroplated specimens were treated by slurry pack cementation process with a slurry pack cementation mixture composed of TiO2 as titanizing source, pure Al powder as aluminzing source and also a reducer for titanizing, an activator of NH4Cl and albumen （egg white） as cohesive agent. The Ti-Al coating was fabricated on the surface of electro-deposited nickel layer on copper matrix followed by the slurry pack cementation process. The effects of slurry pack cementation temperature on the microstructures and wear resistance of Ti-Al coating were studied. The results show that the microstructure of the coating changed from NiAl＋Ni3（Ti,Al） to NiAl ＋Ni3（Ti,Al）＋Ni4Ti3 to Ni4Ti3＋NiAl, and to NiAl＋Ni3（Ti,Al）＋NiTi with slurry pack cementation temperature ranging from 800 ℃ to 950 ℃ in 12 h. The friction coefficient of Ti-Al coating decreased and the hardness increased with increasing the slurry pack cementation temperature. The minimum friction coefficient was 1/3 and the minimum hardness was 5 times larger than that of pure copper.

Greatly enhanced corrosion/wear resistances of epoxy coating for Mg alloy through a synergistic effect between functionalized graphene and insulated blocking layer

The poor corrosion and wear resistances of Mg alloys seriously limit their potential applications in various industries.The conventional epoxy coating easily forms many intrinsic defects during the solidification process,which cannot provide sufficient protection.In the current study,we design a double-layer epoxy composite coating on Mg alloy with enhanced anti-corrosion/wear properties,via the spin-assisted assembly technique.The outer layer is functionalized graphene(FG)in waterborne epoxy resin(WEP)and the inner layer is Ce-based conversion(Ce)film.The FG sheets can be homogeneously dispersed within the epoxy matrix to fill the intrinsic defects and improve the barrier capability.The Ce film connects the outer layer with the substrate,showing the transition effect.The corrosion rate of Ce/WEP/FG composite coating is 2131 times lower than that of bare Mg alloy,and the wear rate is decreased by~90%.The improved corrosion resistance is attributed to the labyrinth effect(hindering the penetration of corrosive medium)and the obstruction of galvanic coupling behavior.The synergistic effect derived from the FG sheet and blocking layer exhibits great potential in realizing the improvement of multi-functional integration,which will open up a new avenue for the development of novel composite protection coatings of Mg alloys.

CATHODIC PROCESS AND WEAR RESISTANCE OF ELECTRO-DEPOSITED RE-Ni-W-P-SiC COMPOSITE COATING

Cathodic deposition current density of the composite coatings increases when SiC par-ticles and rare earth (RE) were added in the bath, which is profitable for Ni- W-P alloy to deposit in the cathod, forming Ni-W-P-SiC and RE-Ni-W-P-SiC composite coatings. On the contrary, the addition of PTFE in the bath decreases cathodic deposition current density of the coatings. The current density increases a little when the amount of RE is 7-9g/l; however, the current density increases greatly when the amount of RE is increased to 11-13g/l. Bui ij the amount of RE is raised further, the current density decreases. Hardness and wear resistance of RE-Ni-W-P-SiC composite coating have been studied, and the results show that the hardness and wear resistance of RE-Ni-W-P-SiC composite coating increase with increasing heat treatment tempera-ture, which reach peak values at 400℃; while the hardness and wear resistance of the coating decrease with the rise of heat treated temperature continuously.

Nitriding of Hard Fe Electrodepositionand Its Effects on Wear Resistance

Nitriding is employed for the hard Fe electrodeposition to produce a hard-facing and antiwear coating. It only takes 1 h for the hard Fe coating, which is much shorter than nitriding the Fe and steel. The results showed that the nitriding can increase the microhardness, wear resistance of the coating, as well as the bonding strength of the coating with the substrate. Additionally it can eliminate the brittleness, turn the internal stress of the coating from tension to compression. The wear resistance of the nitrided Fe coating is 4.6 times as high as that of Cr coating. It is simple and economic to combine hard Fe electroplating and nitriding, which is a good technology of the tribological surface modification.

Microstructure and wear resistance of Fe-based and Co-based coating of AISI H13

Fe-based and Co-based cladding layers were prepared on the surface of AISI H13 hot die steel by laser cladding technology.The microstructure,hardness and abrasion resistance of the two cladding layers were studied by means of optical microscope,scanning electron microscope,rockwell hardness tester,and high temperature friction and wear tester.Also,the red hardness of the cladding layers was measured,after holding the layers at 600℃ for 1 hour by muffle furnace and repeated 4 times.The rockwell hardness values of the substrate,the Fe-based and the Co-based alloy coating measured were HRC 47,HRC 52 and HRC 48,respectively.The red hardness values of the substrate and the Fe-based cladding layer were decreased,while that of the Co-based cladding layer was increased.The Co-based cladding layer has the minimal wear loss weight and friction coefficient among them.The wear mechanisms of the substrate,the Fe-based layer and the Cobased layer attribute mainly to abrasive wear,adhesion wear,and both of them,respectively.

Effect of Titanium Content on Microstructure and Wear Resistance of Hardfacing Alloy

The hardfacing alloys with different concentrations of titanium were deposited on carbon steel substrates by shielded metal arc welding, and the effect of titanium content on the microstructure characteristics of the hardfacing alloys was investigated. The wear resistance test of the hardfacing alloys was carried out by using a slurry rubber wheel abrasion test machine, and the wear behaviour was also studied. The results indicate that the addition of titanium can effectively promote the precipitation of the complex carbides of Nb and Ti due to the prior precipitation of titanium carbide which acts as nucleation sites for complex carbides. With the increase of titanium content, the wear resistance of the hardfacing alloys is increased gradually resulting from the refinement of microstructure and dispersive distribution of fine carbide precipitates. And the wear mechanism is mainly minimum plastic deformation with interrupted grooves due to the strengthening and protecting effects of carbide precipitates.

Influence of carbon content on wear resistance and wear mechanism of Mn13Cr2 and Mn18Cr2 cast steels

By means of impact abrasion tests, micro-hardness tests, and worn surface morphology observation via SEM, a comparison research based upon different impact abrasive wear conditions was conducted in this research to study the influence of different carbon contents(1.25 wt.%, 1.35 wt.%, and 1.45 wt.%) on the wear resistance and wear mechanism of water-quenched Mn13Cr2 and Mn18Cr2 cast steels. The research results show that the wear resistance of the Mn18Cr2 cast steel is superior to that of the Mn13Cr2 cast steel under the condition of the same carbon content and different impact abrasive wear conditions because the Mn18Cr2 cast steel possesses higher worn work hardening capacity as well as a more desirable combination of high hardness and impact toughness than that of the Mn13Cr2 cast steel. When a 4.5 J impact abrasive load is applied, the wear mechanism of both steels is that plastic deformation fatigue spalling and micro-cutting coexist, and the former dominates. When the carbon content is increased, the worn work hardening effect becomes increasingly dramatic, while the wear resistance of both steels decreases, which implies that an increase in impact toughness is beneficial to improving the wear resistance under severe impact abrasive wear conditions. Under the condition of a 1.0 J impact abrasive load, the wear mechanism of both steels is that plastic deformation fatigue spalling and micro-cutting coexist, and the latter plays a leading role. The worn work hardening effect and wear resistance intensify when the carbon content is increased, which implies that a higher hardness can be conducive to better wear resistance under low impact abrasive condition.

Influence of Rare Earth on Wear Resistance of Wear Resistant Cast Iron Containing Low Alloy

The Influence of RE on wear resistance of wear resistant cast iron containing low alloy was studied by means of slide wear and impact wear test. Moreover, its microstructure and characteristics of wearing surface was analyzed. The experimental results show that RE can improve the wear resistance of wear resistant cast iron containing low alloy, especially for impact wear resistance. The optimum wear resistance of wear resistant cast iron containing low alloy modified by RE of 0.046% can be obtained by normalization at 950 ℃ for 3 h. Moreover, the coordinated effect of rare earths and heat treatment was also revealed in this paper.

Effect of Rare Earth Elements on the Impact Wear Resistance of Nitrocarburizing Layers

In this paper the effect of rare earth elements on the toughness and impact wear resistance of nitrocarburiz- ing layers is studied.The experimental results show that the toughness and impact wear resistance of RE-nitrocarburizing layers are increased significantly compared with that of conventional nitrocarburizing lay- ers.The service life of hot die for manufacturing bicycle bolts increased more than 100%.The impact wear mechanism of RE-nitrocarburizing layers is investigated by SEM as well.

Study on the Thermal Fatigue Behavior of Hot Deformed Wear Resistance Cast Iron and Effect of Carbide

The thermal fatigue behavior of wear resistance cast iron with different quantity of deformation has been investigated. The results show that eutectic carbide is the main location and passage for initiation and extension of thermal fatigue cracks, approving that the more serious, the carbide breaks. The higher thermal fatigue resistance of wear resistance cast iron will be and thermal fatigue fracture belongs mainly to brittleness.

Effect of Cooling Rate after hot Deformation on Structure and Mechanical Properties of Low Alloy Wear Resistance Cast iron

The effect of cooling rate after 40% hot deformation on structure and mechanical properties of low alloy wear resistance cast iron was investigated by metallographic, scanning electron microscopes and detection of properties. The results show that for the cast steel after deformed, the amount of granular carbides of precipitation during the cooling decreased with the increase of the cooling rate, but the hardness was obviously enhanced, as a result, better mechanical properties will be obtained by force air cooling(cooling rate is about 7 ℃·s-1). And the reason of the change for structure and mechanical properties of the cast steel were analyzed.