The effect of quenching temperature and cooling conditions on the microstructure and mechanical properties of a 0.2%Nb medium chromium wear-resistant cast steel was investigated.The microstructure,carbides and volume ...The effect of quenching temperature and cooling conditions on the microstructure and mechanical properties of a 0.2%Nb medium chromium wear-resistant cast steel was investigated.The microstructure,carbides and volume fraction of retained austenite were characterized using the optical microscope,scanning electron microscope,transmission electron microscope and X-ray diffraction.The influence of heat treatment on hardness,impact toughness and tensile properties of test steel was studied.It can be observed that lath martensite can be obtained under the condition of air cooling and oil cooling upon austenitizing in the range of 900–1020℃.Total carbide content of 0.2–1.1 wt.%under air cooling is more than that under oil cooling due to the lower cooling rate.Nb6C5,M23C6 and M7C3 were found at lower austenitizing temperature,of which niobium carbide mostly located at grain boundaries,while chromium carbides were uniformly distributed in the matrix with the size of 20–50 nm.The chromium carbides are basically dissolved into the matrix in test steel austenitized at 1020°C.Meanwhile,the negligible growth of prior austenite grain size is achieved.Specimen austenitized at 1020℃ and cooled in air+tempered at 200℃ has a best combination of hardness,plasticity and tensile strength due to fine grain size and more amount of retained austenite.Under this condition,the hardness is 58 HRC,the impact toughness is 22.92 J/cm^(2),and the tensile strength is 1136.9 MPa.展开更多
Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector...Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector plate were investigated.The results show that lath martensite can be obtained after austenitizing in the range of 860-980℃and then water cooling.With an increase in austenitizing temperature,the precipitate content gradually decreases.The precipitates are mainly composed of TiC and Ti4C2S2,and their total content is between 1.15wt.%and 1.64wt.%.The precipitate phase concentration by water-cooling is higher than that by10%NaCl cooling due to the lower cooling rate of water cooling.As the austeniting temperature increases,the hardness and tensile strength of both water cooled and 10%NaCl cooled steels firstly increase and then decrease.The experimental steel exhibits the best comprehensive mechanical properties after being austenitized at 900℃,cooled by 10%NaCl,and then tempered at 200℃.Its hardness,ultimate tensile strength,and wear rate reach551.4 HBW,1,438.2 MPa,and 0.48×10^(-2)mg·m^(-1),respectively.展开更多
The current research on the integrity of critical structures of rail vehicles mainly focuses on the design stage,which needs an effective method for assessing the service state.This paper proposes a framework for pred...The current research on the integrity of critical structures of rail vehicles mainly focuses on the design stage,which needs an effective method for assessing the service state.This paper proposes a framework for predicting the remaining useful life(RUL)of in-service structures with and without visible cracks.The hypothetical distribution and delay time models were used to apply the equivalent crack growth life data of heavy-duty railway cast steel knuckles,which revealed the evolution characteristics of the crack length and life scores of the knuckle under different fracture failure modes.The results indicate that the method effectively predicts the RUL of service knuckles in different failure modes based on the cumulative failure probability curves for different locations and surface crack lengths.This study proposes an RUL prediction framework that supports the dynamic overhaul and state maintenance of knuckle fatigue cracks.展开更多
To accurately analyze the impact of casting pores in steel,high-resolution 3D X-ray tomography technology was used to gather detailed statistical information about micropores.These micropores were classified as gas,sh...To accurately analyze the impact of casting pores in steel,high-resolution 3D X-ray tomography technology was used to gather detailed statistical information about micropores.These micropores were classified as gas,shrinkage,and gas-shrinkage pores depending on their formation origin and morphology.Clustering tendencies and affinity parameters were defined to characterize the spatial correlations among these three types of pores.The 3D data from X-ray tomography scans were then integrated into finite element analysis(FEA)software to predict how micropore shape,size,and distribution influence stress distribution within the material.The results show that certain inflection points with small local radii within the cast pores are major contributors to stress concentration.Therefore,cast pores cannot be simply modeled as ideal spherical pores.The sphericity and volume of pores have a significant impact on the stress concentration of the model.Specifically,lower sphericity and larger pore volumes result in higher stress concentrations.Moreover,the internal pores of steel castings exhibit specific global distribution characteristics.Pores located on the surface of the specimen lead to significantly higher stress concentrations compared to those located inside the specimen.展开更多
With its high strength and hardness, wear-resistant steel has become an important material in the field of construction machinery manufacturing.Given that quenching technology is a crucial component of wear-resistant ...With its high strength and hardness, wear-resistant steel has become an important material in the field of construction machinery manufacturing.Given that quenching technology is a crucial component of wear-resistant steel production, the selection of the cooling method to be used during this process is important.In this study, the feasibility of quenching wear-resistant steel by air-atomized water spray cooling was studied, and the cooling rate, microstructure, and hardness of wear-resistant steel under various cooling device structures were analyzed.The results reveal that the air-atomized water spray cooling method is an effective technique in quenching wear-resistant steel.Furthermore, martensite and uniform hardness were obtained by the air-atomized water spray cooling technique.As the space between the nozzles in each row in the device increased, the cooling rate was reduced during quenching.Meanwhile, the martensite content decreased, and more carbides were observed in the martensitic structure.A mixture comprising self-tempered martensite and bainite was formed at a large distance over a longer period of time.All these factors resulted in lower hardness and worse property uniformity.展开更多
Using ABAQUS software and cylindrical ellipsoid and body heat sources with a peak-heat-flux- attenuation function, a finite element model of the temperature field in the laser-arc hybrid welding of 4.5-mm BW300TP wear...Using ABAQUS software and cylindrical ellipsoid and body heat sources with a peak-heat-flux- attenuation function, a finite element model of the temperature field in the laser-arc hybrid welding of 4.5-mm BW300TP wear-resistant steel is proposed. The proposed model considers convection, radiation, molten pool flow, and heat conduction effect on temperature. A comparison of the simulation and actual welding test results confirms the reliability of the model. This welding heat-process model can provide the cooling rate at any position in the heat affected zone (HAZ) and can be used as a reference for the analysis of material properties and for process optimization.展开更多
Baosteel’s first BTW1 austenitic high-manganese wear-resistant steel exhibits strong deformation-induced hardening characteristics.Compared with common low-alloy martensitic wear-resistant steels in the market, it ha...Baosteel’s first BTW1 austenitic high-manganese wear-resistant steel exhibits strong deformation-induced hardening characteristics.Compared with common low-alloy martensitic wear-resistant steels in the market, it has improved impact wear resistance, hard abrasive wear, erosion wear performance, and impact toughness.The metallurgical properties of such austenitic wear-resistant steel lead to the risk of failure because of hot cracking defects in the welded structure.In wear-resistant applications, evaluating hot cracking susceptibility is necessary to avoid the effect of welding defects.In this study, the Varestraint test is used to quantitatively analyze and evaluate the hot cracking susceptibility of BTW1 austenitic high-manganese wear-resistant steel.The test results show that by controlling the content of impurity elements and grain refinement, BTW1 austenitic high-manganese wear-resistant steel effectively reduces hot cracking tendency and has a low incidence of hot cracking under small strain conditions.The developed matching welding process can effectively avoid the influence of hot cracking susceptibility.展开更多
Renovation design of wasteland on the original Quarter A of Panzhihua Nongnongping Steelcasting Factory was taken for example in this study, natural conditions and biological landscapes in the study area were investig...Renovation design of wasteland on the original Quarter A of Panzhihua Nongnongping Steelcasting Factory was taken for example in this study, natural conditions and biological landscapes in the study area were investigated. Principles and theories of the renovation design were introduced, it was proposed that protection and landscape renovation of industrial heritage had to be insisted to make regular and unique overall spatial layouts. On this basis, design approaches for the wasteland landscape renovation of the steel-casting factory were proposed as "maintaining original images, realizing the functional substitution; optimizing spatial structure; updating seriously-damaged industrial facilities with insignificant functionality; improving and recovering landscape soil; recovering and reconstructing vegetation".展开更多
The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and networ...The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.展开更多
The influence of microalloying additions on the mechanical properties of a low-carbon cast steel containing combinations of V, Nb, and Ti in the as-cast condition was evaluated. Tensile and hardness test results indic...The influence of microalloying additions on the mechanical properties of a low-carbon cast steel containing combinations of V, Nb, and Ti in the as-cast condition was evaluated. Tensile and hardness test results indicated that good combinations of strength and ductility could be achieved by V and Nb additions. While the yield strength and UTS (ultimate tensile strength) increased up to the range of 378-435 MPa and 579- 590 MPa, respectively in the microalloyed heats, their total elongation ranged from 18% to 23%. The presence of Ti, however, led to some reduction in the strength. Microstructural studies including scanning electron microscopy (SEM) and optical microscopy revealed that coarse TiN particles were responsible for this behavior. The Charpy impact values of all compositions indicated that microalloying additions significantly decreased the impact energy and led to the dominance of cleavage facets on the fracture surfaces. It seems that the increase in the hardness of coarse ferrite grains due to the precipitation hardening is the main reason for brittle fracture.展开更多
In this study, the effect of melting temperature on the microstructural evolutions, behavior, and corrosion morphology of Hadfield steel in the casting process is investigated. The mold was prepared by the sodium sili...In this study, the effect of melting temperature on the microstructural evolutions, behavior, and corrosion morphology of Hadfield steel in the casting process is investigated. The mold was prepared by the sodium silicate/CO_2 method, using a blind riser, and then the desired molten steel was obtained using a coreless induction furnace. The casting was performed at melting temperatures of 1350, 1400, 1450, and 1500°C, and the cast blocks were immediately quenched in water. Optical microscopy was used to analyze the microstructure, and scanning electron microscopy(SEM) and X-ray diffractrometry(XRD) were used to analyze the corrosion morphology and phase formation in the microstructure, respectively. The corrosion behavior of the samples was analyzed using a potentiodynamic polarization test and electrochemical impedance spectroscopy(EIS) in 3.5 wt% NaCl. The optical microscopy observations and XRD patterns show that the increase in melting temperature led to a decrease of carbides and an increase in the austenite grain size in the Hadfield steel microstructure. The corrosion tests results show that with increasing melting temperature in the casting process, Hadfield steel shows a higher corrosion resistance. The SEM images of the corrosion morphologies show that the reduction of melting temperature in the Hadfield steel casting process induced micro-galvanic corrosion conditions.展开更多
The effect of main alloying elements on thermal wear of cast hot-forging die steels was studied. The wear mechanism was discussed. The results show that alloying elements have significant influences on the thermal wea...The effect of main alloying elements on thermal wear of cast hot-forging die steels was studied. The wear mechanism was discussed. The results show that alloying elements have significant influences on the thermal wear of cast hot-forging die steels. The wear rates decrease with an increase in chromium content from 3% to 4% and molybdenum content from 2% to 3%, respectively. With further increase of chromium and molybdenum contents, chromium slightly reduces the wear resistance and molybdenum severely deteriorates the wear resistance with high wear rate. Lower vanadium/carbon ratio (1.5-2.5) leads to a lower wear resistance with higher wear rate. With an increase in vanadium/carbon ratio, the wear resistance of the cast steel substantially increases. When vanadium/carbon ratio is 3, the wear rate reaches the lowest value. The predominant mechanism of thermal wear of cast hot-forging die steels are oxidation wear and fatigue delamination. The Fe2O3 and Fe3O4 or lumps of brittle wear debris are formed on the wear surface.展开更多
In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail...In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail. It was found that the strips possessed a fine microstructure compared with the mould cast steels. With increasing phosphorus content more ferrite has been formed with finer grains.展开更多
Solidification cracking that occurs during continuous casting of 1Cr13 stainless steel was investigated with and without final elec- tromagnetic stirring (F-EMS). The results show that cracks initiates and propagate...Solidification cracking that occurs during continuous casting of 1Cr13 stainless steel was investigated with and without final elec- tromagnetic stirring (F-EMS). The results show that cracks initiates and propagates along the grain boundaries where the elements of carbon and sulfur are enriched. The final stirrer should be appropriately placed at a location that is 7.5 m away from the meniscus, and the appropri- ate thickness of the liquid core in the stirring zone is 50 ram. As a stirring current of 250 A is imposed, it can promote colurnnar-equiaxed transition, decrease the secondary dendrite arm spacing, and reduce the segregation of both carbon and sulfur. F-EMS can effectively de- crease the amount of cracks in 1Cr13 stainless steel.展开更多
A new method called mixed Lagrangian and Eulerian (MiLE) method was used to simulate the continuous casting process in a mold of free-cutting steel 38MnVS.The simulation results are basically in agreement with exper...A new method called mixed Lagrangian and Eulerian (MiLE) method was used to simulate the continuous casting process in a mold of free-cutting steel 38MnVS.The simulation results are basically in agreement with experimental data in the literature,achieving the three-dimensional visualization of temperature distribution,melt flow,shell thickness,and stress distribution of blooms in a mold.It is shown that the flow velocity of steel melt becomes smaller gradually as the casting proceeds.When the flow reaches a certain depth,two types of flow patterns can be observed in the upper zone of the mold.The first flow pattern is to flow downwards,and the second one is to flow upwards to the meniscus.The corner temperature is higher,and the thickness is thinner than those in the mid-face.The effective stress in the corner area is much bigger than that in the mid-face,indicating that the corner area is the dangerous zone of cracking.展开更多
Thermal wear of cast hot-forging die steel modified by rare earths(RE) was studied and compared with commercially used die steels. The function of RE and the mechanism of thermal wear of cast steel modified by RE we...Thermal wear of cast hot-forging die steel modified by rare earths(RE) was studied and compared with commercially used die steels. The function of RE and the mechanism of thermal wear of cast steel modified by RE were discussed. The results showed that with increasing content of RE, the wear rate of cast steel reduced at first and then increased. By adding 0.05% (mass fraction) RE, the cast hot-forging die steel with optimum thermal wear resistance was obtained, which was better than that of H13 and 3Cr2WSV. The large amount of coarse inclusions, (RE)2O2S, resulted from excessive RE, which obviously deteriorated thermal wear resistance. The mechanism of thermal wear of the modified cast die steel is oxidation wear and oxide fatigue delamination. The wear debris are lumps of Fe2O3 and Fe3O4.展开更多
A three-dimensional heat transfer model for continuous steel slab casting has been developed with realistic spray cooling patterns and a coupled microsegregation solidification model that calculates the solidification...A three-dimensional heat transfer model for continuous steel slab casting has been developed with realistic spray cooling patterns and a coupled microsegregation solidification model that calculates the solidification path for multi-component steels. Temperature and composition dependent properties are implemented in a database for 15 chemical species. Considerable effort is made to accurately model the spray cooling heat transfer. Each spray nozzle position and distribution is considered, including variations of the spray patterns with flow rate, and spray overlap. Nozzle type, layout, nozzle-to-slab distance, and spray span and flux are variable. Natural convection, thermal radiation and contact cooling of individual rolls are computed. The present model provides more comprehensive information and realistic slab surface temperatures than results from a model using the 'averaged' treatment of boundary conditions. Cooling operating conditions and parameters of individual spray nozzles can be analyzed to optimize nozzle spray distribution, improve product quality, and troubleshoot issues such as nozzle clogging that may arise during production. One spray cooling correlation is used for the entire machine, achieving as good or better agreement with surface temperature measurements than was found previously for the model using an 'averaged' treatment of boundary conditions and using three machine-segment-dependent correlations.展开更多
In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing ...In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.展开更多
The present work investigated the solidification microstructure of AISI M2 high speed steel manufactured by different casting technologies, namely iron mould casting and continuous casting. The results revealed that t...The present work investigated the solidification microstructure of AISI M2 high speed steel manufactured by different casting technologies, namely iron mould casting and continuous casting. The results revealed that the as-cast structure of the steel was composed of the iron matrix and the M2C eutectic carbide networks, which were greatly refined in the ingot made by continuous casting process, compared with that by the iron mould casting process. M2C eutectic carbides presented variation in their morphologies and growth characteristics in the ingots by both casting methods. In the ingot by iron mould casting, they have a plate-like morphology and grow anisotropically. However, in the ingot made by continuous casting, the carbides evolved into the fiber-like shape that exhibited little characteristics of anisotropic growth. It was noticed that the fiber-like M2C was much easier to decompose and spheroidize after heated, as a result, the carbides refined remarkably, compared with the case of plate-like carbides in the iron mould casting ingot.展开更多
This study first investigated cracks on the surface of an actual steel strip. Formulating the Anand model in ANSYS software, we then simulated the stress field in the molten pool of type 304 stainless steel during the...This study first investigated cracks on the surface of an actual steel strip. Formulating the Anand model in ANSYS software, we then simulated the stress field in the molten pool of type 304 stainless steel during the twin-roll casting process. Parameters affecting the stress distribution in the molten pool were analyzed in detail and optimized. After twin-roll casting, a large number of transgranular and intergranular cracks resided on the surface of the thin steel strip, and followed a tortuous path. In the molten pool, stress was enhanced at the exit and at the roller contact positions. The stress at the exit decreased with increasing casting speed and pouring temperature. To ensure high quality of the fabricated strips, the casting speed and pouring temperature should be controlled above 0.7 m/s and 1520℃, respectively.展开更多
文摘The effect of quenching temperature and cooling conditions on the microstructure and mechanical properties of a 0.2%Nb medium chromium wear-resistant cast steel was investigated.The microstructure,carbides and volume fraction of retained austenite were characterized using the optical microscope,scanning electron microscope,transmission electron microscope and X-ray diffraction.The influence of heat treatment on hardness,impact toughness and tensile properties of test steel was studied.It can be observed that lath martensite can be obtained under the condition of air cooling and oil cooling upon austenitizing in the range of 900–1020℃.Total carbide content of 0.2–1.1 wt.%under air cooling is more than that under oil cooling due to the lower cooling rate.Nb6C5,M23C6 and M7C3 were found at lower austenitizing temperature,of which niobium carbide mostly located at grain boundaries,while chromium carbides were uniformly distributed in the matrix with the size of 20–50 nm.The chromium carbides are basically dissolved into the matrix in test steel austenitized at 1020°C.Meanwhile,the negligible growth of prior austenite grain size is achieved.Specimen austenitized at 1020℃ and cooled in air+tempered at 200℃ has a best combination of hardness,plasticity and tensile strength due to fine grain size and more amount of retained austenite.Under this condition,the hardness is 58 HRC,the impact toughness is 22.92 J/cm^(2),and the tensile strength is 1136.9 MPa.
文摘Effects of quenching temperature and cooling conditions(water cooling and 10%NaCl cooling)on microstructure and mechanical properties of a 0.2%Ti low alloy martensitic wear-resistant steel used for die casting ejector plate were investigated.The results show that lath martensite can be obtained after austenitizing in the range of 860-980℃and then water cooling.With an increase in austenitizing temperature,the precipitate content gradually decreases.The precipitates are mainly composed of TiC and Ti4C2S2,and their total content is between 1.15wt.%and 1.64wt.%.The precipitate phase concentration by water-cooling is higher than that by10%NaCl cooling due to the lower cooling rate of water cooling.As the austeniting temperature increases,the hardness and tensile strength of both water cooled and 10%NaCl cooled steels firstly increase and then decrease.The experimental steel exhibits the best comprehensive mechanical properties after being austenitized at 900℃,cooled by 10%NaCl,and then tempered at 200℃.Its hardness,ultimate tensile strength,and wear rate reach551.4 HBW,1,438.2 MPa,and 0.48×10^(-2)mg·m^(-1),respectively.
基金Supported by National Natural Science Foundation of China (Grant No.52175123)Sichuan Provincial Outstanding Youth Fund (Grant No.22JDJQ0025)Independent Exploration Project of State Key Laboratory of Railway Transit Vehicle System (Grant No.2024RVL-T03)。
文摘The current research on the integrity of critical structures of rail vehicles mainly focuses on the design stage,which needs an effective method for assessing the service state.This paper proposes a framework for predicting the remaining useful life(RUL)of in-service structures with and without visible cracks.The hypothetical distribution and delay time models were used to apply the equivalent crack growth life data of heavy-duty railway cast steel knuckles,which revealed the evolution characteristics of the crack length and life scores of the knuckle under different fracture failure modes.The results indicate that the method effectively predicts the RUL of service knuckles in different failure modes based on the cumulative failure probability curves for different locations and surface crack lengths.This study proposes an RUL prediction framework that supports the dynamic overhaul and state maintenance of knuckle fatigue cracks.
基金The National Natural Science Foundation of China(No.51578137).
文摘To accurately analyze the impact of casting pores in steel,high-resolution 3D X-ray tomography technology was used to gather detailed statistical information about micropores.These micropores were classified as gas,shrinkage,and gas-shrinkage pores depending on their formation origin and morphology.Clustering tendencies and affinity parameters were defined to characterize the spatial correlations among these three types of pores.The 3D data from X-ray tomography scans were then integrated into finite element analysis(FEA)software to predict how micropore shape,size,and distribution influence stress distribution within the material.The results show that certain inflection points with small local radii within the cast pores are major contributors to stress concentration.Therefore,cast pores cannot be simply modeled as ideal spherical pores.The sphericity and volume of pores have a significant impact on the stress concentration of the model.Specifically,lower sphericity and larger pore volumes result in higher stress concentrations.Moreover,the internal pores of steel castings exhibit specific global distribution characteristics.Pores located on the surface of the specimen lead to significantly higher stress concentrations compared to those located inside the specimen.
文摘With its high strength and hardness, wear-resistant steel has become an important material in the field of construction machinery manufacturing.Given that quenching technology is a crucial component of wear-resistant steel production, the selection of the cooling method to be used during this process is important.In this study, the feasibility of quenching wear-resistant steel by air-atomized water spray cooling was studied, and the cooling rate, microstructure, and hardness of wear-resistant steel under various cooling device structures were analyzed.The results reveal that the air-atomized water spray cooling method is an effective technique in quenching wear-resistant steel.Furthermore, martensite and uniform hardness were obtained by the air-atomized water spray cooling technique.As the space between the nozzles in each row in the device increased, the cooling rate was reduced during quenching.Meanwhile, the martensite content decreased, and more carbides were observed in the martensitic structure.A mixture comprising self-tempered martensite and bainite was formed at a large distance over a longer period of time.All these factors resulted in lower hardness and worse property uniformity.
文摘Using ABAQUS software and cylindrical ellipsoid and body heat sources with a peak-heat-flux- attenuation function, a finite element model of the temperature field in the laser-arc hybrid welding of 4.5-mm BW300TP wear-resistant steel is proposed. The proposed model considers convection, radiation, molten pool flow, and heat conduction effect on temperature. A comparison of the simulation and actual welding test results confirms the reliability of the model. This welding heat-process model can provide the cooling rate at any position in the heat affected zone (HAZ) and can be used as a reference for the analysis of material properties and for process optimization.
文摘Baosteel’s first BTW1 austenitic high-manganese wear-resistant steel exhibits strong deformation-induced hardening characteristics.Compared with common low-alloy martensitic wear-resistant steels in the market, it has improved impact wear resistance, hard abrasive wear, erosion wear performance, and impact toughness.The metallurgical properties of such austenitic wear-resistant steel lead to the risk of failure because of hot cracking defects in the welded structure.In wear-resistant applications, evaluating hot cracking susceptibility is necessary to avoid the effect of welding defects.In this study, the Varestraint test is used to quantitatively analyze and evaluate the hot cracking susceptibility of BTW1 austenitic high-manganese wear-resistant steel.The test results show that by controlling the content of impurity elements and grain refinement, BTW1 austenitic high-manganese wear-resistant steel effectively reduces hot cracking tendency and has a low incidence of hot cracking under small strain conditions.The developed matching welding process can effectively avoid the influence of hot cracking susceptibility.
文摘Renovation design of wasteland on the original Quarter A of Panzhihua Nongnongping Steelcasting Factory was taken for example in this study, natural conditions and biological landscapes in the study area were investigated. Principles and theories of the renovation design were introduced, it was proposed that protection and landscape renovation of industrial heritage had to be insisted to make regular and unique overall spatial layouts. On this basis, design approaches for the wasteland landscape renovation of the steel-casting factory were proposed as "maintaining original images, realizing the functional substitution; optimizing spatial structure; updating seriously-damaged industrial facilities with insignificant functionality; improving and recovering landscape soil; recovering and reconstructing vegetation".
基金Project supported by the Innovation Fund for Outstanding Scholar of Henan Province (0621000600)
文摘The toughness of 31Mn2SiRE wear-resistance cast steel were increased by means of RE compound modification and high temperature austenitizing. The results show that the microstructures can be refined, needle and network ferrite are eliminated, the dislocation density and the quantity of dislocated martensite are increased remarkably, and the shape and distribution of inclusions are improved by the addition of RE. Therefore, the mechanical properties of the modified steel can be greatly increased, especially the toughness (αK) by 44%, yield strength (σs) by 10%, and elongation (δ5) by 42%.
文摘The influence of microalloying additions on the mechanical properties of a low-carbon cast steel containing combinations of V, Nb, and Ti in the as-cast condition was evaluated. Tensile and hardness test results indicated that good combinations of strength and ductility could be achieved by V and Nb additions. While the yield strength and UTS (ultimate tensile strength) increased up to the range of 378-435 MPa and 579- 590 MPa, respectively in the microalloyed heats, their total elongation ranged from 18% to 23%. The presence of Ti, however, led to some reduction in the strength. Microstructural studies including scanning electron microscopy (SEM) and optical microscopy revealed that coarse TiN particles were responsible for this behavior. The Charpy impact values of all compositions indicated that microalloying additions significantly decreased the impact energy and led to the dominance of cleavage facets on the fracture surfaces. It seems that the increase in the hardness of coarse ferrite grains due to the precipitation hardening is the main reason for brittle fracture.
文摘In this study, the effect of melting temperature on the microstructural evolutions, behavior, and corrosion morphology of Hadfield steel in the casting process is investigated. The mold was prepared by the sodium silicate/CO_2 method, using a blind riser, and then the desired molten steel was obtained using a coreless induction furnace. The casting was performed at melting temperatures of 1350, 1400, 1450, and 1500°C, and the cast blocks were immediately quenched in water. Optical microscopy was used to analyze the microstructure, and scanning electron microscopy(SEM) and X-ray diffractrometry(XRD) were used to analyze the corrosion morphology and phase formation in the microstructure, respectively. The corrosion behavior of the samples was analyzed using a potentiodynamic polarization test and electrochemical impedance spectroscopy(EIS) in 3.5 wt% NaCl. The optical microscopy observations and XRD patterns show that the increase in melting temperature led to a decrease of carbides and an increase in the austenite grain size in the Hadfield steel microstructure. The corrosion tests results show that with increasing melting temperature in the casting process, Hadfield steel shows a higher corrosion resistance. The SEM images of the corrosion morphologies show that the reduction of melting temperature in the Hadfield steel casting process induced micro-galvanic corrosion conditions.
基金Item Sponsored by Early-Term Key Technology of Industrialization and Whole Set Equipment From Plan Committee of China(1999317) ,863 Project of China (2002AA331180) ,and Project of Key Lab of Universities in Jiangsu Province of China(Kjsmcx04004)
文摘The effect of main alloying elements on thermal wear of cast hot-forging die steels was studied. The wear mechanism was discussed. The results show that alloying elements have significant influences on the thermal wear of cast hot-forging die steels. The wear rates decrease with an increase in chromium content from 3% to 4% and molybdenum content from 2% to 3%, respectively. With further increase of chromium and molybdenum contents, chromium slightly reduces the wear resistance and molybdenum severely deteriorates the wear resistance with high wear rate. Lower vanadium/carbon ratio (1.5-2.5) leads to a lower wear resistance with higher wear rate. With an increase in vanadium/carbon ratio, the wear resistance of the cast steel substantially increases. When vanadium/carbon ratio is 3, the wear rate reaches the lowest value. The predominant mechanism of thermal wear of cast hot-forging die steels are oxidation wear and fatigue delamination. The Fe2O3 and Fe3O4 or lumps of brittle wear debris are formed on the wear surface.
基金This work was supported by the Major State Basic Research Development Program of China(973 Program)under the contract number of 2004CB619108the National Natural Science Foundation of China(No.50574018)the NECT-04-0278 Project of the Ministry of Education of China.
文摘In the present paper, low carbon steel strips with different phosphorus contents were produced using a twin roll strip casting process. The solidification structure was studied and its features were analyzed in detail. It was found that the strips possessed a fine microstructure compared with the mould cast steels. With increasing phosphorus content more ferrite has been formed with finer grains.
基金financially supported by the National Natural Science Foundation of China (No. 50834009)the Key Project of the Ministry of Education of China (No. 311014)the 111 Project of China (No. B07015)
文摘Solidification cracking that occurs during continuous casting of 1Cr13 stainless steel was investigated with and without final elec- tromagnetic stirring (F-EMS). The results show that cracks initiates and propagates along the grain boundaries where the elements of carbon and sulfur are enriched. The final stirrer should be appropriately placed at a location that is 7.5 m away from the meniscus, and the appropri- ate thickness of the liquid core in the stirring zone is 50 ram. As a stirring current of 250 A is imposed, it can promote colurnnar-equiaxed transition, decrease the secondary dendrite arm spacing, and reduce the segregation of both carbon and sulfur. F-EMS can effectively de- crease the amount of cracks in 1Cr13 stainless steel.
基金supported by the National Natural Science Foundation of China (No.50874007)
文摘A new method called mixed Lagrangian and Eulerian (MiLE) method was used to simulate the continuous casting process in a mold of free-cutting steel 38MnVS.The simulation results are basically in agreement with experimental data in the literature,achieving the three-dimensional visualization of temperature distribution,melt flow,shell thickness,and stress distribution of blooms in a mold.It is shown that the flow velocity of steel melt becomes smaller gradually as the casting proceeds.When the flow reaches a certain depth,two types of flow patterns can be observed in the upper zone of the mold.The first flow pattern is to flow downwards,and the second one is to flow upwards to the meniscus.The corner temperature is higher,and the thickness is thinner than those in the mid-face.The effective stress in the corner area is much bigger than that in the mid-face,indicating that the corner area is the dangerous zone of cracking.
基金Project supported by the Itemof Early-TermKey Technology of Industrialization ,Plan Committee of China (1999317) 863project of China (2002AA331180)
文摘Thermal wear of cast hot-forging die steel modified by rare earths(RE) was studied and compared with commercially used die steels. The function of RE and the mechanism of thermal wear of cast steel modified by RE were discussed. The results showed that with increasing content of RE, the wear rate of cast steel reduced at first and then increased. By adding 0.05% (mass fraction) RE, the cast hot-forging die steel with optimum thermal wear resistance was obtained, which was better than that of H13 and 3Cr2WSV. The large amount of coarse inclusions, (RE)2O2S, resulted from excessive RE, which obviously deteriorated thermal wear resistance. The mechanism of thermal wear of the modified cast die steel is oxidation wear and oxide fatigue delamination. The wear debris are lumps of Fe2O3 and Fe3O4.
基金The authors are grateful to IPSCO Inc. for supporting this research program and for providing surface temperature measure-ments, and measurements of the spray nozzle flow characteris-tics. Without the nozzle flow pattern measurements made by Dr. L.K.Chia
文摘A three-dimensional heat transfer model for continuous steel slab casting has been developed with realistic spray cooling patterns and a coupled microsegregation solidification model that calculates the solidification path for multi-component steels. Temperature and composition dependent properties are implemented in a database for 15 chemical species. Considerable effort is made to accurately model the spray cooling heat transfer. Each spray nozzle position and distribution is considered, including variations of the spray patterns with flow rate, and spray overlap. Nozzle type, layout, nozzle-to-slab distance, and spray span and flux are variable. Natural convection, thermal radiation and contact cooling of individual rolls are computed. The present model provides more comprehensive information and realistic slab surface temperatures than results from a model using the 'averaged' treatment of boundary conditions. Cooling operating conditions and parameters of individual spray nozzles can be analyzed to optimize nozzle spray distribution, improve product quality, and troubleshoot issues such as nozzle clogging that may arise during production. One spray cooling correlation is used for the entire machine, achieving as good or better agreement with surface temperature measurements than was found previously for the model using an 'averaged' treatment of boundary conditions and using three machine-segment-dependent correlations.
基金Item Sponsored by Guiding Programme of Science and Technology Research of Hebei of China(94122123)
文摘In isothermal spheroidizing process,the spheroidization and growth of the carbide formed in hot-deformed high-carbon chromium cast steel at high temperature were investigated.The results showed that the spheroidizing growth of carbide proceeds in such a way that the bigger carbide particles swallow the smaller ones,and the short rhabdoid carbides dissolve and are spheroidized by itself.When the samples were held at 720℃ for more than 3 h,the spheroidization is not obvious.The feature of the process is the size increment and the amount decrement of carbide particles.The empirical equation for growth rate of carbides was obtained.The volume fraction of carbides keeps constant.The growth process agrees well with Ostwald Ripening Law.
基金supported by the Fund Project for Transformation of Scientific and Technological Achievements of Jiangsu Province,China(No.BA2010139)
文摘The present work investigated the solidification microstructure of AISI M2 high speed steel manufactured by different casting technologies, namely iron mould casting and continuous casting. The results revealed that the as-cast structure of the steel was composed of the iron matrix and the M2C eutectic carbide networks, which were greatly refined in the ingot made by continuous casting process, compared with that by the iron mould casting process. M2C eutectic carbides presented variation in their morphologies and growth characteristics in the ingots by both casting methods. In the ingot by iron mould casting, they have a plate-like morphology and grow anisotropically. However, in the ingot made by continuous casting, the carbides evolved into the fiber-like shape that exhibited little characteristics of anisotropic growth. It was noticed that the fiber-like M2C was much easier to decompose and spheroidize after heated, as a result, the carbides refined remarkably, compared with the case of plate-like carbides in the iron mould casting ingot.
基金projects supported by Natural Science Foundation of Hebei Province,China(E2012203019)
文摘This study first investigated cracks on the surface of an actual steel strip. Formulating the Anand model in ANSYS software, we then simulated the stress field in the molten pool of type 304 stainless steel during the twin-roll casting process. Parameters affecting the stress distribution in the molten pool were analyzed in detail and optimized. After twin-roll casting, a large number of transgranular and intergranular cracks resided on the surface of the thin steel strip, and followed a tortuous path. In the molten pool, stress was enhanced at the exit and at the roller contact positions. The stress at the exit decreased with increasing casting speed and pouring temperature. To ensure high quality of the fabricated strips, the casting speed and pouring temperature should be controlled above 0.7 m/s and 1520℃, respectively.