The work investigated surface and mechanical properties of untreated and treated three-layered weftknitted spacer fabrics.In order to optimize the mechanical properties of weft-knitted spacer fabrics,silica aerogels(S...The work investigated surface and mechanical properties of untreated and treated three-layered weftknitted spacer fabrics.In order to optimize the mechanical properties of weft-knitted spacer fabrics,silica aerogels(SAs)coating was employed.Scanning electron microscopy(SEM)images of untreated and treated spacer fabrics were analyzed to ensure the presence of SAs on the coated spacer fabrics.The basic properties of uncoated and coated weftknitted spacer fabrics were studied and compared.Tensile strength and initial modulus were studied according to the GB/T3923 test standard YG026 MB-250 by testing machine.Moreover,compression properties of spacer fabrics were also tested by HD026 G test instrument.In this testing,work of compression,the linearity of compression,recovery work of compression and other parameters were calculated from stress and strain curves.It was found that SAs coating has a significant influence on the mechanical properties of weftknitted spacer fabrics.The statistical analysis also verified the significant performance(P value smaller than 0.05)of treated fabric samples at the 0.05 level.展开更多
This paper introduces the construction of the multi-layered biaxial weft knitted fabric （MBWK fabric） and studies the locking angle of this kind of fabric. Moreover, a locking angle model of the MBWK fabric is estab...This paper introduces the construction of the multi-layered biaxial weft knitted fabric （MBWK fabric） and studies the locking angle of this kind of fabric. Moreover, a locking angle model of the MBWK fabric is established for the first time according to its unique construction. Two kinds of locking angles are considered under different restraint conditions: the locking angle θ1 controlled by the inserting yarns and the locking angle θ2 controlled by the stitch yarns. It is concluded that the ultimate value of the locking angle θ is the larger one of the two angles.展开更多
The effects of aramid/carbon on tensile properties of multilayered biaxial weft knitted( MBWK) fabric reinforced composites are analyzed by experiments. The tensile tests are inducted by the SHIMADZU AG-250 KNE univer...The effects of aramid/carbon on tensile properties of multilayered biaxial weft knitted( MBWK) fabric reinforced composites are analyzed by experiments. The tensile tests are inducted by the SHIMADZU AG-250 KNE universal material testing machine and Aramis V6 digital image correlation( DIC) technique.More specifically,the composite samples own four hybrid ratios(Na∶ Nc= 12∶ 0,8 ∶ 4,6 ∶ 6 and 4 ∶ 8). The results showed that the aramid/carbon hybrid MBWK fabric reinforced composites showed nearly linear response until reaching the maximum load and the inserting yarns distribution on the surface of MBWK fabrics reinforced composites had a great influence on the strain pattern distribution. Besides,the tensile strength,the tensile modulus and the elongation at breakage of 0° samples and 90° samples increased with the decreasing of aramid/carbon hybrid ratio. In a word,the changes of tensile strength, tensile modulus and elongation at breakage have a lot to do with the difference of aramid/carbon hybrid ratio.展开更多
文摘The work investigated surface and mechanical properties of untreated and treated three-layered weftknitted spacer fabrics.In order to optimize the mechanical properties of weft-knitted spacer fabrics,silica aerogels(SAs)coating was employed.Scanning electron microscopy(SEM)images of untreated and treated spacer fabrics were analyzed to ensure the presence of SAs on the coated spacer fabrics.The basic properties of uncoated and coated weftknitted spacer fabrics were studied and compared.Tensile strength and initial modulus were studied according to the GB/T3923 test standard YG026 MB-250 by testing machine.Moreover,compression properties of spacer fabrics were also tested by HD026 G test instrument.In this testing,work of compression,the linearity of compression,recovery work of compression and other parameters were calculated from stress and strain curves.It was found that SAs coating has a significant influence on the mechanical properties of weftknitted spacer fabrics.The statistical analysis also verified the significant performance(P value smaller than 0.05)of treated fabric samples at the 0.05 level.
文摘This paper introduces the construction of the multi-layered biaxial weft knitted fabric （MBWK fabric） and studies the locking angle of this kind of fabric. Moreover, a locking angle model of the MBWK fabric is established for the first time according to its unique construction. Two kinds of locking angles are considered under different restraint conditions: the locking angle θ1 controlled by the inserting yarns and the locking angle θ2 controlled by the stitch yarns. It is concluded that the ultimate value of the locking angle θ is the larger one of the two angles.
基金Tianjin Municipal Science and Technology Commission for the Financial Supports,China(No.11ZCKFSF00500)China's General Administration of Quality Supervision,Inspection and Quarantine for the Financial Supports,China(No.201210260)
文摘The effects of aramid/carbon on tensile properties of multilayered biaxial weft knitted( MBWK) fabric reinforced composites are analyzed by experiments. The tensile tests are inducted by the SHIMADZU AG-250 KNE universal material testing machine and Aramis V6 digital image correlation( DIC) technique.More specifically,the composite samples own four hybrid ratios(Na∶ Nc= 12∶ 0,8 ∶ 4,6 ∶ 6 and 4 ∶ 8). The results showed that the aramid/carbon hybrid MBWK fabric reinforced composites showed nearly linear response until reaching the maximum load and the inserting yarns distribution on the surface of MBWK fabrics reinforced composites had a great influence on the strain pattern distribution. Besides,the tensile strength,the tensile modulus and the elongation at breakage of 0° samples and 90° samples increased with the decreasing of aramid/carbon hybrid ratio. In a word,the changes of tensile strength, tensile modulus and elongation at breakage have a lot to do with the difference of aramid/carbon hybrid ratio.