IN SITU TEM OBSERVATION OF MICROSTRUCTURES OF AUSTENITIC-0.45%C STEELS WELD JOINT

The successive alteration o the microstructure from the weld metal zone through weld bond to the heat affected zone of a Cr18Ni13 austenitic-0.45%C steels weld joint was observed in situ using transmission electron microscopy.It was found a new type of microstructure called pearlite-like structure and observed the characteristics of the boundary of dissimilar phases. Based on the definition of various zones of the dissimilar steels weld joint under the optical mi- croscope,the transmission electron microscopic characteristics,including microstructures and compositions,of each zone are described and discussed.

Effect of Post-weld Heat Treatment on Mechanical Characteristics of AZ31 Magnesium Alloy Welded Joints

Tungsten inert gas（TIG） welding was performed on 2.7 mm thick commercial extruded AZ31 B magnesium alloy plates. We investigated the effect of post-weld heat treatment（PWHT） on the microstructure, mechanical properties and precipitated phase of the weld joints. The results showed that during the annealing treatment（200 ℃-1 h, 250 ℃-1 h, 300 ℃-1 h, 350 ℃-1 h, 400 ℃-1 h, and 450 ℃-1 h）, the average grain size in the weld seam was the minimum after annealing at 400 ℃ for 1 hour, and then abnormally grew up after annealing at 450 ℃ for 1 hour. The mechanical properties enhanced when the joints were processed from 200 ℃-1 h to 400 ℃-1 h but sharply decreased with increasing annealing temperature. In contrast to the annealing treatment, solution treatment（250 ℃-10 h, 300 ℃-10 h, 350 ℃-10 h, 400 ℃-10 h, and 450 ℃-10 h） exhibited a better ductility but a slight deterioration in tensile strength. Especially speaking, no eutectic compounds（such as Mg17 Al12） were observed in the weld seam. The supersaturated Al atoms were precipitated in a coarse spherical shape dispersed in the weld seam. The precipitated Al atoms dissolved in the matrix substances at the condition（400 ℃-1 h） or（250 ℃-10 h）. The solution treatment caused grain coarsening and precipitated Al atoms dissolved in the weld seam substantially, which resulted in a drop in micro-hardness at the weld seam compared to the area of the annealed joints.

Microstructure and Corrosion Resistance of Dissimilar Weld-Joints between Duplex Stainless Steel 2205 and Austenitic Stainless Steel 316L

The microstructure and corrosion resistance of dissimilar weld-joints between stainless steel SAF 2205 and stainless steel AISI 316L were investigated. Welding was accomplished by different types of welding wires AWS ER 347, AWS ER 316L and AWS ER 309L. To verify soundness of welded samples, nondestructive tests were performed. Metallographic samples were prepared from cross-section areas of weld- joints to investigate microstructure of different regions of weld-joints by optical microscopy and scanning electron microscopy. Corrosion resistance of weld-joints was evaluated in NaCI solution by potentiodynamic polarization and electrochemical impedance techniques. In the weld metal AWS ER 347, the brittle sigma phase was created, resulting in the decrease of weld-joint corrosion resistance. According to the results of metallurgical investigations and corrosion tests, welding wire AWS ER 309L was suitable for welding duplex stainless steel （SAF 2205） to austenitic stainless steel （AIS1316L） by gas tungsten arc welding （GTAW） process.

Microstructure and properties in dissimilar/similar weld joints between DP780 and DP980 steels processed by fiber laser welding

The microstructure and mechanical properties（strength, fatigue and formability） of dissimilar/similar weld joints between DP780 and DP980 steels were studied. The microstructure in fusion zone（FZ） was lath martensite（LM）, and alloying elements in the FZ were uniformly distributed. The hardness in the FZ of dissimilar weld joint was similar to the average value（375 HV） of the two similar weld joints. The microstructural evolution in heat affected zone（HAZ） of dissimilar/similar weld joints was as follows：LM（coarse-grained HAZ） →finer LM（fine-grained HAZ） →M-A constituent and ferrite（intercritically HAZ） →tempered martensite（TM） and ferrite（sub-critical HAZ）. Lower hardness in intercritically HAZ and sub-critical HAZ（softening zones） was observed compared to base metal（BM） in dissimilar/similar weld joints. The size of softening zone was 0.2-0.3 mm and reduction in hardness was ~7.6%-12.7% of BM in all the weld joints, which did not influence the tensile properties of weld joints such that fracture location was in BM. Formability of dissimilar weld joints was inferior compared to similar weld joints because of the softening zone, non-uniform microstructure and hardness on the two sides of FZ. The effect of microstructure on fatigue life was not influenced due to the presence of welding concavity.

Microstructure Characterization of the Fusion Zone of an Alloy 600-82 Weld Joint

Characterization of the microstructure of the fusion zone of an Alloy 600-82 weld joint was conducted, with focus on the weld residual strain distribution and the comparison of the microstructure of heat affected zone （HAZ） with that of cold worked alloy. Peak of the residual strain was observed to approach to the fusion boundary in HAZ while the strain increased from the top of the weld to the root. Strain distribution in the HAZ was found to be concentrated adjacent to grain boundaries （GBs）, with a peak of approximately three times of that in grain. Further, triple junctions of the GB appear to cause a higher strain concentration than single GBs. The microstructure of HAZ consists of partially tangled dislocations, which is different from slip bands of high density dislocations in cold worked alloy. This may cause a relatively higher intergranular cracking resistance of HAZ due to the difficulty in transferring tangled dislocations to GB in HAZ under deformation.

Influence of a non-rotating shoulder on heat generation,microstructure and mechanical properties of dissimilar AA2024/AA7050 FSW joints

Friction stir welding （FSW） and stationary shoulder friction stir welding （SSFSW） were carried out for the butt joining of dissimilar AA2024-T3 and AA7050-T7651 aluminium alloys with thicknesses of 2 mm. A comparison between the two processes was performed by varying the welding speed while keeping the rotational speed constant, Through the analysis of the force and torque produced during welding and a simple analytical model, it was possible to show that in SSFSW there is more effective coupling with the tool and the heat produced is more efficiently distributed. This process decreases both the welding area and the diffusion at the interface of the two alloys compared with FSW. The minimum microhardness occurred at the advancing side （AS） at the interface between the thermo-mechanically affected zone （TMAZ） and the stir zone （SZ） in both processes, although the decrease was more gradual in SSFSW. This interface is also where all specimens failed for both welding technologies. An increase in tensile strength was measured in SSFSW compared with standard FSW. Furthermore, it was possible to establish the mechanical performance of the material in the fracture zone using digital image correlation.