Effects of B and Ti on the Toughness of HSLA Steel Weld Metals

Effects of microalloying Ti and B on the microstructures and low temperature toughness of manual metal arc (MMA) deposits were investi- gated.Weld metals containing 200-300 ppm Ti and 29-60 ppm B deposited by manual coated elec- trodes provided an optimum low temperature toughness.The addition of B in weld metals low- ered the γ→α transformation temperature which promoted the acicular ferrite (AF) transformation. Solid solutioned B suppressed grain boundary ferrite as well as side plate ferrite formation and benefited the acicular ferrite formation.Titanium protected B from oxidizing as well as nitriding and formed Ti-Mn silicate inclusions.Ultra-high volt- age electron microscope analyses showed that TiO structure in the Ti-Mn silicate inclusions was the favorable nucleation site for acicular ferrite forma- tion.

Microstructure and toughness of local brittle zone of HSLA steel multipass weld metals

By using thermo-simulation,Auger analysis and Charpy Ⅴ impact test and with the observation of the microstructures in which cleavage crack was initiated,the morphology and toughness of the local brittle zone of C-Mn and Cr-Ni-Mo multipass weld metals have been investigated.The results indicated that the local brittle zone in C-Mn weld metals with low and high Mn％ and Cr- Ni-Mo weld metals is different.With statistical analysis,it has been revealed that the more the local brittle zone and the lower their toughness,the lower the toughness of the entire weld metals.The alloy elements have a noticeable influ- ence on the toughness of the local brittle zone,thereby changing the toughness of weld metals.

Effects of alloying elements on the microstructures and mechanical properties of Ni-Fe weld metals

The effects of Ce, Ti, Nb and C on the microstructures and mechanical properties of Ni Fe weld metal and the mechanism of their strengthening are discussed. Ce has the effect on graphite morphology and weld metal with spheroidal graphite has higher mechanical properties. The proper contents of Ti and Nb obviously increase the tensile strength of Ni Fe weld metal, which is mainly attributed to the austenite grain refining and second phase (TiC and NbC) strengthening. The excess C in weld metal results in increasing the quantity of carbide and graphite precipitating along the austenite grain boundary and decreasing the mechanical properties of Ni Fe weld metal.

Microstructure and mechanical properties of ultralow carbon high-strength steel weld metals with or without Cu-Nb addition

Two types of ultralow carbon steel weld metals(with and without added Cu-Nb) were prepared using gas metal arc welding(GMAW) to investigate the correlation between the microstructure and mechanical properties of weld metals.The results of microstructure characterization showed that the weld metal without Cu-Nb was mainly composed of acicular ferrite(AF), lath bainite(LB), and granular bainite(GB).In contrast, adding Cu-Nb to the weld metal caused an evident transformation of martensite and grain coarsening.Both weld metals had a high tensile strength(more than 950 MPa) and more than 17% elongation;however, their values of toughness deviated greatly,with a difference of approximately 40 J at-50℃.Analysis of the morphologies of the fracture surfaces and secondary cracks further revealed the correlation between the microstructure and mechanical properties.The effects of adding Cu and Nb on the microstructure and mechanical properties of the weld metal are discussed;the indication is that adding Cu-Nb increases the hardenability and grain size of the weld metal and thus deteriorates the toughness.

INFLUENCE OF LOCAL BRITTLE ZONE ON THE FRACTURETOUGHNESS OF HIGH-STRENGTH LOW-ALLOYEDMULTIPASS WELD METALS

In this paper, toughness properties and microstructurc of low-alloyed multipass welds with yield strength above 700MPa have 6een studied using the weld thermal simulation and throughout thickness CTOD fracture mechanics tests. Impact testing of thermal simulated specimens showed that the primary weld metal and the fine gmmed weld metal had good toughness, while the coarse grained weld metal had the lowest toughness value as the local brittle zone (LBZ) in multipass weld metals. Cleavage fracture in CTOD testing of thick multipass weld metals was initiated from martensite-austenite (MA) phases in the LBZ. MA phases were distributed at the prior austenite grain boundaries and around ferrite grains. As the size of the local brittle zone along the fatigue crack front increases, CTOD frncture toughness of multipass weld metals decreases. The weakest link theory was used to evaluate effect of the local brittle zone on fracture toughness of thick multipass weld metals. The estimated curves agree well with the eaperimental data.

Effect of Interface Form on Creep Failure and Life of Dissimilar Metal Welds Involving Nickel-Based Weld Metal and Ferritic Base Metal

For dissimilar metal welds(DMWs)involving nickel-based weld metal(WM)and ferritic heat resistant steel base metal(BM)in power plants,there must be an interface between WM and BM,and this interface suffers mechanical and microstructure mismatches and is often the rupture location of premature failure.In this study,a new form of WM/BM interface form,namely double Y-type interface was designed for the DMWs.Creep behaviors and life of DMWs containing double Y-type interface and conventional I-type interface were compared by finite element analysis and creep tests,and creep failure mechanisms were investigated by stress-strain analysis and microstructure characterization.By applying double Y-type interface instead of conventional I-type interface,failure location of DMW could be shifted from the WM/ferritic heat-affected zone(HAZ)interface into the ferritic HAZ or even the ferritic BM,and the failure mode change improved the creep life of DMW.The interface premature failure of I-type interface DMW was related to the coupling effect of microstructure degradation,stress and strain concentrations,and oxide notch on the WM/HAZ interface.The creep failure of double Y-type interface DMW was the result of Type IV fracture due to the creep voids and micro-cracks on fine-grain boundaries in HAZ,which was a result of the matrix softening of HAZ and lack of precipitate pinning at fine-grain boundaries.The double Y-type interface form separated the stress and strain concentrations in DMW from the WM/HAZ interface,preventing the trigger effect of oxide notch on interface failure and inhibiting the interfacial microstructure cracking.It is a novel scheme to prolong creep life and enhance reliability of DMW,by means of optimizing the interface form,decoupling the damage factors from WM/HAZ interface,and then changing the failure mechanism and shifting the failure location.

Failure Analysis of Dissimilar Metal Welds between Ferritic Heat Resistant Steels and Austenitic Stainless Steels in Power Plant

This study analysed the failure of dissimilar metal welds(DMWs)between ferritic heat resistant steels and austenitic stainless steels and investigated its influencing factors by means of numerical simulation,microstructure characterization and mechanical property test.Under the long-term high-temperature service condition in practical power plant,the DMW failure mode was along the interface between nickel-based weld metal(WM)and ferritic heat resistant steel,and the failure mechanism was stress/strain concentration,microstructure degradation and oxidation coupling acting on the interface.The numerical simulation results show that interface stress/strain concentration was due to the differences in coefficient of thermal expansion and creep strength,and the degree of stress/strain concentration was related to service time.The ferrite band formed at the WM/ferritic steel interface was prone to cracking,attracting the fracture along the interface.The interface crack allowed oxidation to develop along the WM/ferritic steel interface.During long-term service,the interface stress/strain concentration,microstructure and oxidation all evolved,which synergistically promoted interface failure of DMW.However,only under the long-term service of low stress conditions could trigger the interface failure of DMW.Meanwhile,long-term service would reduce the mechanical strength and plasticity of DMW.

Robust Particle Swarm Optimization Algorithm for Modeling the Effectof Oxides Thermal Properties on AMIG 304L Stainless Steel Welds

There are several advantages to the MIG(Metal Inert Gas)process,which explains its increased use in variouswelding sectors,such as automotive,marine,and construction.A variant of the MIG process,where the sameequipment is employed except for the deposition of a thin layer of flux before the welding operation,is the AMIG(Activated Metal Inert Gas)technique.This study focuses on investigating the impact of physical properties ofindividual metallic oxide fluxes for 304L stainless steel welding joint morphology and to what extent it can helpdetermine a relationship among weld depth penetration,the aspect ratio,and the input physical properties ofthe oxides.Five types of oxides,TiO_(2),SiO_(2),Fe_(2)O_(3),Cr_(2)O_(3),and Mn_(2)O_(3),are tested on butt joint design withoutpreparation of the edges.A robust algorithm based on the particle swarm optimization(PSO)technique is appliedto optimally tune the models’parameters,such as the quadratic error between the actual outputs(depth and aspectratio),and the error estimated by the models’outputs is minimized.The results showed that the proposed PSOmodel is first and foremost robust against uncertainties in measurement devices and modeling errors,and second,that it is capable of accurately representing and quantifying the weld depth penetration and the weld aspect ratioto the oxides’thermal properties.

Effect of Carbon Content on the Creep Rupture Properties and Microstructure of 316H Weld Metals

Two types of 316 butt welds with carbon contents of 0.016%and 0.062%have been produced using the gas tungsten arc welding process.Theδ-ferrite content decreased from 7.2 to 2.8%in volume as the carbon content increased.The creeprupture strength and creep ductility of the two types of weld metals have been measured at 550℃over the stress range of 290-316 MPa and at 600℃over 230-265 MPa.The microstructure change and precipitation behavior of the weld metals were observed and related to the creep rupture properties.The creep rupture strength of the C2(0.062%C)weld metal was higher than that of the Cl(0.016%C)weld metal at both 550℃and 600℃.At 550℃,as the decrease in the applied stress,the difference of the creep-rupture life between the two weld metals diminished due to the higher depletion rate of carbon by precipitation of M_(23)C_(6) in the C2 weld metal,while at 600℃,the difference enlarged due to the massive precipitation ofσphase and extensive crack formation and propagation alongσ/austenite boundaries in the C1 weld metal.For both the C1 and C2 weld metal,the decrease in ductility was adverse with the transformation percentage and related to products of theδ-ferrite transformation.

Ultrasonic vibration assisted tungsten inert gas welding of dissimilar metals 316L and L415

Ultrasonic vibration assisted tungsten inert gas welding was applied to joining stainless steel 316 L and low alloy high strength steel L415.The effect of ultrasonic vibration on the microstructure and mechanical properties of a dissimilar metal welded joint of 316 L and L415 was systematically investigated.The microstructures of both heat affected zones of L415 and weld metal were substantially refined,and the clusters ofδferrite in traditional tungsten inert gas(TIG)weld were changed to a dispersive distribution via the ultrasonic vibration.The ultrasonic vibration promoted the uniform distribution of elements and decreased the micro-segregation tendency in the weld.With the application of ultrasonic vibration,the average tensile strength and elongation of the joint was improved from 613 to 650 MPa and from 16.15%to31.54%,respectively.The content ofΣ3 grain boundaries around the fusion line zone is higher and the distribution is more uniform in the ultrasonic vibration assisted welded joint compared with the traditional one,indicating an excellent weld metal crack resistance.

In-situ observation of microstructural evolution in reheated low carbon bainite weld metals with various Ni contents

Microstructural evolution in weld metals was in-situ observed through utilizing a laser scanning confocal microscope at two cooling rates.The specimens with various nickel contents were adopted for the observation.In the specimen with low fraction of Ni（≤2 wt.%）,granular bainite microstructure（i.e.broad surface relief）transformation from intragranular nucleation site was in-situ observed,while,lath bainite microstructure originating from grain boundary of austenite was in-situ observed for specimens with high mass percentage of Ni（≥4 wt.%）.With increasing nickel content,the transformation temperature dropped.The prior austenite grain size was initially depressed and subsequently coarsened dramatically with the addition of Ni.The microstructure difference was ascribed to various nucleation sites and growth direction in the matrix.On account of those observations,not only the chemical component,cooling rate and microstructure were systematically correlated,but also the microstructural evolution was definite.

Research on microstructure and properties of boron/Q235 steel laser welded dissimilar joints under synchronous thermal field

The mechanical mismatch effect frequently occurs in the dissimilar materials welded joints, thus leading to plastic gradient at the interface between the weld and heat-affected zone(HAZ). In this work, the boron steel and Q235 steel were selected for laser tailor welding,which obtained boron/Q235 steel tailor-welded blanks(TWBs). The method of welding with synchronous thermal field(WSTF) was utilized to eliminate the mismatch effects in TWBs. The WSTF was employed to adjust cooling rates of welded joints, thereby intervening in the solidification behaviors and phase transition of the molten pool. Boron/Q235 steel was welded by laser under conventional and WSTF(300-600 ℃) conditions, respectively. The results show that the microstructure of weld and HAZ(boron) was adequately transitioned to ferrites and pearlites instead of abundant martensite by WSTF. Meanwhile, the discrepancy of microhardness and yield strength between various regions of welded joints was greatly reduced, and the overall plasticity of welded joints was enhanced by WSTF. It is indicated that WSTF can effectively contribute to reducing plastic gradient and achieving mechanical congruity in welded joints by restraining the generation of hardbrittle phase, which could significantly improve the formability of TWBs in subsequent hot stamping.

Study on gas metal arc welding of two types of TMCP steels

Gas metal arc welding experiments were conducted on two types of steels with 0.41% carbon equivalent(Ceq) and 0.31% Cequsing WER70T wire and 20% CO_(2)and 80% Ar as shielding gas.The two types of steels show satisfactory weldability.The transition temperatures of 50% upper shelf energy(Tk0.5) for Charpy-V impact test of both the welded joints are below-40 ℃.However, the toughness of the fusion line zone and heat-affected zone(HAZ) of the two steel joints exhibits differences, with the toughness of 0.41% Ceqsteel being better than that of 0.31% Ceqsteel.The Tk0.5of the fusion line zone and the HAZ of 0.41% Ceqsteel is below-60℃,whereas that of 0.31% Ceqsteel is above-40℃.The welded joint of 0.41% Ceqsteel has low hardness fluctuation, while that of 0.31% Ceqsteel exhibits a narrow, softened zone, which has no obvious influence on the tested tensile strength.The coarse grain heat-affected zone(CGHAZ)microstructure of 0.41% Ceqsteel is bainite, while that of 0.31% Ceqsteel is bainite with ferrite and minor pearlite.

Microstructures and properties of welded joint of aluminum alloy to galvanized steel by Nd:YAG laser + MIG arc hybrid brazing-fusion welding

According to the differences in melting point between aluminum alloy and steel, 6013-T4 aluminum alloy was joined to galvanized steel by large spot Nd：YAG laser ＋ MIG arc hybrid brazing-fusion welding with ER4043（AlSi5） filler wire. The microstructures and mechanical properties of the brazed-fusion welded joint were investigated. The joint is divided into two parts of fusion weld and brazed seam. There is a zinc-rich zone at fusion weld toe, which consists of α（Al）-Zn solid solution and Al-Zn eutectic. The brazed seam is the Fe-Al intermetallic compounds （IMCs） layer of 2-4μm in thickness, and the IMCs include FeAl2, Fe2Al5 and Fe4Al13. FeAl2 and Fe2Al5 are located in the compact reaction layer near the steel side, and Fe4Al13 with tongue shape or sawtooth shape grows towards the fusion weld. The tensile strength of the joint firstly increases and then decreases as the welding current and laser power increase, the highest tensile strength can be up to 247.3 MPa, and the fracture usually occurs at fusion zone of the fusion weld. The hardness is the highest at the brazed seam because of hard Fe-Al IMCs, and gradually decreases along the fusion weld and galvanized steel, respectively.

Microstructure and mechanical properties of AZ31B magnesium alloy gas metal arc weld

Wrought magnesium alloy sheets were butt welded with gas metal arc welding process. Pores in the weld were investigated under different welding parameters, the causes of pore formation were systematically disposed, and the effects of porosity on the microstructure and mechanical properties of the joint were analyzed. The microstructure examination shows that the pores mainly appear close to the top or bottom part of the weld, and could connect to each other and lead to the formation of cracks in the welds. However, the pores can be controlled with proper welding parameters. The tensile testing results reveal that the average joint strength is close to or higher than that of the base metal. The microhardness in the weld can be even higher than that in the base metal due to the second ohase strengthening of β-Mg17（A1, Zn）12 formed in the weld.

THRESHOLD STRESS INTENSITIES FOR HYDROGEN-INDUCED DELAYED FAILURE OF WELD METAL OF AUSTENITIC STAINLESS STEEL

It was found that hydrogen induced delayed failure could occur in 308L and 347L weld metals,and the threshold stress intensities of 308L and 347L welds were lower than that of 304L austenitic stainless steel.When dynamically charged under load on a single edge notched specimen,the threshold stress intensities of 308L,347L and 304L decrease with the increase in the diffusible hydrogen content C 0 and the experimental results are as follows:K ⅠH =85.2-10.7 ln C 0 (308L),K ⅠH =76.1-9.3 ln C 0 (347L),K ⅠH =91.7-10.1 ln C 0 (304L).The morphology of the hydrogen induced delayed fracture in the three materials are correlated with the K Ⅰ and C 0 values.

Microstructures and mechanical properties of metal inert-gas arc welded Mg-steel dissimilar joints

The joining of Mg alloy to steel was realized by metal inert-gas arc welding, and the weld thermal cycle characteristics and Mg-steel joints were investigated. The results show that the temperature distribution in the joints is uneven. Mg alloy welds present a fine equiaxed grain structure. There exists a transition layer consisting mainly of AlFe, AlFe3 and Mg（Fe, Al）2O4 phases at Mg/steel interface, and it is the weakest link in Mg？steel joints. The welding heat input and weld Al content have the significant effect on the joint strength. The joint strength increases with increasing the heat input from 1680 J/cm to 2093 J/cm, due to promoting Mg/steel interface reaction. When weld Al content is increased to 6.20%, the joint strength reaches 192 MPa, 80% of Mg alloy base metal strength. It is favorable to select the suitable welding heat input and weld Al content for improving joint strength.

Effect of Al-foil addition on microstructure and temperature field of laser fusion welded joints of DP590 dual-phase steel and AZ31B magnesium alloy

The experiments of laser fusion welding with Al-foil addition was carried out for DP590 dual-phase steel and AZ31B magnesium alloy in an overlap steel-on-magnesium configuration.Temperature field was simulated by COMSOL finite element software for steel/magnesium laser fusion welding.The results show that when Al-foil is added,some defects,such as pores,cracks and softening in heat affected zone(HAZ),can be avoided in welding joint,the bonding strength of steel/magnesium joints is increased,heat transfer between steel and magnesium is regulated.In the case of adding Al-foil,welding pool is divided into two parts,the upper and lower pools contact each other but do not mix,the transition layer at the interface between the upper and lower molten pools mainly contains Al−Fe phases,such as AlFe,Al2Fe and AlFe3,and these new phases are helpful for promoting the metallurgical connection between the upper and lower molten pools.Hence,adding Al-foil laser fusion welding is an effective way in joining steel to magnesium alloy.

Development of ultra-narrow gap welding with constrained arc by flux band

Narrow gap welding has merits of lower residual stress and distortion, and superior mechanical properties of joints. A major problem of this process is the lack of fusion in sidewalls, hence many methods of weaving arc have been developed to increase heating effect of arc to the sidewalls. In this work, a new approach Without weaving arc is attempted to ensure the penetration of sidewall, and ultra-narrow gap welding with the gap of less than 5 mm was executed successfully. In this approach, the width of gap is decreased further, so that the sidewalls are made within range of arc heating to obtain the enough heat. In order to prevent the arc from being attracted by sidewall and going up along the sidewalls, two pieces of flux bands consisting of the specified aggregates are adhered to the sidewalls to constrain the arc. In addition, when flux band being heated by the arc, slag and gases are formed to shield the arc and the weld pool. This technique was tested on the welding experiment of pipeline steel with thickness of 20 mm. The involved welding parameters were obtained, that is, the width of gap is 4 mm, the welding current 250 A, and the heat input 0. 5 kJ/mm, the width of heat-affected zone is 1 -2 mm.

Prediction of Ac1 temperature in P92 steel weld metal

The effects of major alloying elements on the Ac, temperature in P92 steel weld metal were evaluated by Thermo- Calc, and a formula relating Ac1 to the content of major alloying elements was developed using multiple regression method. Results show that both C and N reduce Ac, temperature in weld metal, the effect of N on Ac, is greater than that of C, but their influence on Act is not so significant when they individually vary in the specified chemical composition ranges. Si, Cr, Mo and W increase the Acl temperature, and the descending order of their effects is determined as Si, Mo, W, Cr. Mn and Ni decrease the AcI in weld metal, the decreasing effect is especially remarkable when the （ Mn ＋ Ni） ≥ 1%. The effect of Co is moderate and is much smaller compared to Ni. The variations of Acl for the ranges of micro-alloying elements Nb and V are also evaluated, the effect of V is greater compared to Nb and the effect of Nb could be ignored in the specified chemical composition range. A prediction formula for Ac, temperature in P92 steel weld metal within the specified chemical composition ranges was developed based on the comprehensive consideration of the calculated Ac, temperatures and the experimentally measured results.