Evaluation of diffusion and phase transformation at Ag/Al bimetal produced by cold roll welding

Aluminum and silver strips were cold welded by rolling and a bimetallic strip was produced. To create cold weld between A1 and Ag, mating surfaces were specially prepared and various rolling thickness reductions were applied. The minimum critical thickness reduction to begin cold weld was specified as 70% which equals 0.1630 critical rolling shape factors. The bimetallic strips were treated by diffusion annealing at 400 ~C and various annealing time. The A1/Ag interface of strips was observed by scanning electron microscope to investigate the formation of hard and brittle probable phases. The effect of anneal time on diffusion distance and phase transformation was also analysed by EDS analysis and line scan. A diffusion region along the interface in the Ag side was observed and its width increased with prolonging annealing time. Some 8 phases were detected close to the interface after anneal treating for 3 h and 8 phase was thicker and more continuous by increasing annealing time. The microhardness measurement showed that in spite of formation of 8 phase due to diffusion annealing, the interface hardness was reduced.

Influence of aging on damping behavior of TiNi/TiNi alloys synthesized by explosive welding

The influence of aging time,measuring frequency and strain amplitude on the internal friction of TiNi51/TiNi50.2 sandwich composite was investigated.The DSC and internal friction measurements were employed to characterize the sample.The two internal friction peaks of the specimen were confirmed corresponding to the reverse transformation of TiNi51 and TiNi50.2 component, respectively.The internal friction as a function of the temperature at different measuring frequencies was presented and it was found that the height of both internal friction peaks increased with decreasing frequency;however,the increase corresponding to TiNi50.2 component was larger than that of TiNi51 component.Furthermore,the internal friction of the TiNi/TiNi composite alloy decreased with increasing the measuring strain amplitude.The height of internal friction peak of TiNi51 component increased with increasing the aging time,whereas that of the TiNi50.2 component did not change significantly.The increase in internal friction of TiNi51 appeared to be associated with the formation and growth of precipitate during the aging process.

Effect of arc distance on temperature field and weld shape during double-sided arc welding

A new high efficiency welding method, double-sided double arc welding with double powers （DSAW-D）, is developed for thick plate of low alloy high strength steel in this study. It is well known that the thermal cycles have an important influence on the microstructure, shape, stress, distortion and mechanical property. The DSA W-D method can control the temperature field on a wide range by regulating the distance between two arcs, improve the microstructure and prevent hot and cold cracking of high strength steel. But at present, the effect of arc distance on the temperature field and shape is not clear. Therefore, the paper researches the effect of arc distance on the temperature field and weld pool during DSAW-D using finite element method. The transient temperature field of different arc distance in DSAW-D is calculated. To verify the numerical results, the temperature is measured by the thermo-couple and the calculated results agree approximately with experimental data. Farther, the thermal property and mutual effect of double-sided arcs are investigated. The temperature distributions and weld pool profile at different arc distances are obtained. The results show that arc distance is a very important factor to affect the heat process.

Welding of shape memory alloy to stainless steel for medical occluder

Dissimilar metal joining between NiTi shape memory alloy（SMA） and stainless steel was conducted.A cluster of NiTi SMA wires were first joined with tungsten inert gas（TIG） welding process,then the NiTi SMA TIG weld was welded to a stainless steel pipe with laser spot welding process.The microstructure of the welds was examined with an optical microscope and the elemental distribution in the welds was measured by electron probe microanalysis（EPMA）.The results show that TiC compounds dispersively distribute in the NiTi SMA TIG weld.However,the amount of TiC compounds greatly decreases around the fusion boundary of the laser spot weld between the NiTi SMA and stainless steel.Mutual diffusion between NiTi shape memory alloy and stainless steel happen within a short distance near the fusion boundary,and intermetallic compounds such as Ni3Ti＋（Fe,Ni）Ti appear around the fusion boundary.

Time Dependant Weld Shape in Ar-O_2 Shielded Stationary GTA Welding

The stationary gas tungsten arc welding （GTA） is carried out on SUS304 stainless steel under Ar-0.1%O2 and Ar-0.3%O2 mixed shielding to observe the evolution of the molten pool and investigate the role of Marangoni convection on the weld shape. After welding, the oxygen content in the weld metal was measured by using an oxygen/nitrogen analyzer. Small addition of oxygen to the argon based shielding gas can effectively adjust the weld pool oxygen content. Oxygen plays an important role as an surface active element in determining the pattern of Marangoni convection in the stainless steel weld pool. When the weld metal oxygen content is over the critical value, 0.01 wt pct, corresponding to the Ar-0.3%O2 mixed shielding gas, the Marangoni convection changes from outward to inward direction and the weld shape dramatically changes from wide shallow shape to narrow deep shape.

CONTRACTED EFFECT OF BELL-SHADE SHAPE WELDING ARC AND ACCOMPANIED MAGNETIC FIELD WITH SPIRAL PIPE SHAPE

ＣＯＮＴＲＡＣＴＥＤＥＦＦＥＣＴＯＦＢＥＬＬＳＨＡＤＥＳＨＡＰＥＷＥＬＤＩＮＧＡＲＣＡＮＤＡＣＣＯＭＰＡＮＩＥＤＭＡＧＮＥＴＩＣＦＩＥＬＤＷＩＴＨＳＰＩＲＡＬＰＩＰＥＳＨＡＰＥ①ＹｕＪｉａｎｒｏｎｇ，ＺｈａｎｇＪｉａｙｉｎｇ，ＪｉａｎｇＬｉｐｅｉ，...

Surface grain refinement mechanism of SMA490BW steel cross joints by ultrasonic impact treatment

Ultrasonic impact treatment (UIT) is a postweld technique for improving the fatigue strength of welded joints. This technique makes use of ultrasonic vibration to impact and plastically deform a weld toe and can achieve surface grain refinement of the weld toe, which is considered as the main reason for the improvement of fatigue strength. In this paper, the microstructure of the surface of a treated weld toe was observed by metallographic microscopy and transmission electron microscopy (TEM). The results show that UIT could produce severe plastic deformation on the surface layer of the weld toe and the maximum depth of plastic deformation extended to approximately 260 μm beneath the treated surface. Repeated processing could exacerbate the plastic deformation on the surface layer, resulting in finer grains. We can conclude that the surface grain refinement mechanism of SMA490BW welded joints is related to the high density of dislocation tangles and dislocation walls. © 2017, University of Science and Technology Beijing and Springer-Verlag Berlin Heidelberg.

Modeling the keyhole shape and dimension in plasma arc welding

It is of great significance to model the keyhole shape and dimensions to optimize the plasma arc welding process parameters. In this study, through employing a combined volumetric heat source mode, the weld pool in keyhole plasma arc welding is determined firstly, and then the dynamic force-balance condition on the interface between the plasma jet and the molten metal is dealt with in describing the keyhole formation inside the weld pool. The effects of welding current on the shape and size of keyhole are numerically analyzed. The sharp transformation from a partial keyhole to a full-penetration keyhole is quantitatively demonstrated.

Analysis on the joint tensile strength and fractography of TiNi shape memory alloy precise pulse resistance butt welding

This paper studies mechanical property and fractography of the welded joints obtained in different welding parameters such as welding heat and welding press with/without gas shield in TiNi shape memory alloy precise pulse resistance butt welding using tensile strength test, XRD, SEM and TEM measures. The optimum welding parameters obtaining high tensile strength welded joint are got. On the condition of welding press magneting current 2 A and welding heat 75%, the joint strength is the highest. This is important for to study other properties of TiNi shape memory alloy further. The experimental results state that argon gas shield have different effects on different welding parameters, less on welding press, but great on welding heat. But excessive welding press and welding heat have great effects on joint tensile strength. Too high welding heat can produce the new intermetallic compound, this intermetallic compound lead to dislocation density to increase and form the potential crack initiation, which can easily make the joint fracture under stress effect and decrease the shape memory ratio of joint for high density dislocation groups existing in the twinned martensite.

Numerical simulation of dynamic thermal process during doublesided asymmetrical TIG backing welding of large thick plates

The dynamic thermal process during double-sided asymmetrical TIG backing welding of large thick plates （ 1 000 mm×700 mm×50 mm） is numerically simulated using MSC. MARC. The effect of arc distance on the thermal cycle in weld zone during double-sided asymmetrical T1G backing welding is investigated. The results show that the workpiece experiences double-peak thermal cycle in double-sided asymmetrical TIG backing welding. On the one hand, the fore arc has the pre- heating effect on the rear pass, and the pre-heating temperature depends on the distance between the double arcs, the heat input of fore arc, and the initial temperature of workpiece. On the other hand, the rear arc has the post-heating effect on the fore pass. The mutual effects of two heat sources decrease with the increase of arc distance.

Influence of pin size on welding shape and mechanical properties of friction stir welded 2014 Al alloy

The influence of pin size on microstructure and mechanical properties of friction stir welded 2014 Al alloy was investigated. Three different size stir pins were used to carry out the welding process. The results show that the size of the pin has a significant effects on the joint structure and mechanical properties. For one given thickness material, excellent weld can be achieved by using a appropriate size friction stir tool. The appearance of the weld is good and no obvious defect is found using this tool. The grain of the weld nugget is very fine and the precipitation distributes equably. The weld structure can change smoothly from the weld nugget to the thermo-mechanic affected zone. The tensile strength is high enough and the synthesis mechanical properties of the weld are very good. When welded by an improper size pin, some defects such as voids and crack often occur in the weld, and which strongly affect the mechanical properties of the weld.

Weld shape and microstructure of TC4 laser welding with activating flux of Na_(2)SiF_(6)

Na_(2)SiF_(6) was used as surface activating flux for laser welding of TC4 titanium alloy. The effect of Na_(2)SiF_(6) on TC4 titanium alloy laser welding was determined by observing the weld surface. The morphological characteristics of the high temperature plasma above the workpiece was observed and analyzed by using high-speed digital camera system. The variation of weld depth,width and microstructure were analyzed by optical microscope. The experimental results show that laser weld of TC4 titanium alloy has good appearance with activating flux of Na_(2)SiF_(6), weld penetration increases by about 0.8%–12%, while weld surface width decrease by about 10%–29%, the depth to width ratio is effectively improved. The inhomogeneity of weld microstructure was improved, and the crystallization direction of β columnar crystals on the upper part of the weld was changed, the grain size and microstructure of the weld were refined by Na_(2)SiF_(6).

ANN Based Predictive Modelling of Weld Shape and Dimensions in Laser Welding of Galvanized Steel in Butt Joint Configurations

The quality assessment and prediction becomes one of the most critical requirements for improving reliability, efficiency and safety of laser welding. Accurate and efficient model to perform non-destructive quality estimation is an essential part of this assessment. This paper presents a structured and comprehensive approach developed to design an effective artificial neural network based model for weld bead geometry prediction and control in laser welding of galvanized steel in butt joint configurations. The proposed approach examines laser welding parameters and conditions known to have an influence on geometric characteristics of the welds and builds a weld quality prediction model step by step. The modelling procedure begins by examining, through structured experimental investigations and exhaustive 3D modelling and simulation efforts, the direct and the interaction effects of laser welding parameters such as laser power, welding speed, fibre diameter and gap, on the weld bead geometry (i.e. depth of penetration and bead width). Using these results and various statistical tools, various neural network based prediction models are developed and evaluated. The results demonstrate that the proposed approach can effectively lead to a consistent model able to accurately and reliably provide an appropriate prediction of weld bead geometry under variable welding conditions.

Prediction of Weld Joint Shape and Dimensions in Laser Welding Using a 3D Modeling and Experimental Validation

This paper presents an experimentally validated weld joint shape and dimensions predictive 3D modeling for low carbon galvanized steel in butt-joint configurations. The proposed modelling approach is based on metallurgical transformations using temperature dependent material properties and the enthalpy method. Conduction and keyhole modes welding are investigated using surface and volumetric heat sources, respectively. Transition between the heat sources is carried out according to the power density and interaction time. Simulations are carried out using 3D finite element model on commercial software. The simulation results of the weld shape and dimensions are validated using a structured experimental investigation based on Taguchi method. Experimental validation conducted on a 3 kW Nd: YAG laser source reveals that the modelling approach can provide not only a consistent and accurate prediction of the weld characteristics under variable welding parameters and conditions but also a comprehensive and quantitative analysis of process parameters effects. The results show great concordance between predicted and measured values for the weld joint shape and dimensions.

Double-sided gas tungsten arc welding process on TC4 titanium alloy

TC4 titanium alloy was welded by double-sided gas tungsten arc welding(GTAW) process in comparison with conventional GTAW process, the microstructure and mechanical performance of weld were also studied. The results indicate that double-sided GTAW is superior over regular single-sided GTAW on the aspects of increasing penetration, reducing welding deformation and improving welding efficiency. Good weld joint was obtained, which can reach 96.14% tensile strength and 70.85% elongation percentage of the base metal. The grains in heat-affected zone(HAZ) are thin and equiaxed and the degree of grain coarsening increases as one moves to the weld center line, and the interior of grains are α and α′ structures. The coarse columned and equiaxed grains, which interlace martensitic structures α′ and acicular α structures, are observed in weld zone. The fracture mode is ductile fracture.

Study on welding deformation of the side beam based on numerical simulation method

The welding deformation is a key factor affecting the production quality of the side beam of the subway bogie frame. A major issue is how to control the welding deformation during the manufacturing processes. Based on the ＂Local- Global＂ method, the thermal cycle and the stress of a local model extracted from the global side beam model were simulated. The simulated strain result was mapped into the global model as an initial load to simulate the welding assembly deformation. Then the deformation distribution of the side beam was obtained by elastic finite element method, and compared with the measurement results. Furthermore, the welding deformation under different welding sequences and constraints was simulated. The influence of the welding sequences and constraints on the side beam deformation was analyzed. The results indicate that the deformation is the smallest when the sequence is symmetrical and decreases with the increase in constraints.

Numerical Simulation of Current Density Distribution in Keyhole Double-Sided Arc Welding

In the double-sided arc welding system (DSAW) composing of PAW+TIG arcs, the PAW arc is guided by the TIG arc so that the current mostly flows through the direction of the workpiece thickness and the penetration is greatly improved. To analyze the current density distribution in DSAW is beneficial to understanding of this process. Considering all kinds of dynamic factors acting on the weldpool, this paper discusses firstly the surface deformation of the weldpool and the keyhole formation in PAW+TIG DSAW process on the basis of the magnetohydrodynamic theory and variation principles. Hence, a model of the current density distribution is developed. Through numerical simulation, the current density distribution in PAW+TIG DSAW process is quantitatively analyzed. It shows that the minimal radius of keyhole formed in PAW+TIG DSAW process is 0.5 mm and 89.5 percent of current flows through the keyhole.

Effect of activating flux on arc shape and arc voltage in tungsten inert gas welding

The effects of activating fluxes on welding arc were investigated. A special set of water-cooling system and stainless steel were used as parent material. During welding process, high-speed camera system and oscillograph were used for capturing instantaneous arc shape and arc voltage respectively. The experimental results indicate that the SiO2 flux can increase the arc voltage, while TiO2 has no this effect on arc voltage. Compared with conventional tungsten inert gas welding (C-TIG), it is found that the arc shape of A-TIG welding used with the SiO2 flux has changed obviously.

Effect of Welding Parameters on GTA Weld Shape for Pure Iron Plate under Ar-O_2 Mixed Shielding

Weld shape variation for different welding parameters is investigated on pure iron plate under gas tungsten arc （GTA） welding with argon-oxygen mixed shielding. Results showed that small addition of oxygen to the argon base shielding gas can effectively adjust the oxygen adsorption to the molten pool. An inward Marangoni convection occurs on the pool surface when the oxygen content in the weld pool is over the critical value, 80×10^-6, for pure iron plate under Ar-0.3%O2 mixed shielding. Low oxygen content in the weld pool changes the inward Marangoni to an outward direction under the Ar-0.1%O2 shielding. The GTA weld shape depends to a large extent on the pattern and strength of the Marangoni convection on the pool surface, which is determined by the content of surface active element, oxygen, in the weld pool and the welding parameters. The strength of the Marangoni convection on the liquid pool is a product of the temperature coefficient of the surface tension （dσ/dT） and the temperature gradient （dT/dr） on the pool surface. Different welding parameters will change the temperature distribution and gradient on the pool surface, and therefore, affect the strength of Marangoni convection and the weld shape.

Effect of arc force on shape of the welding pool

Based on the three-dimensional model of TIG weld pool established,the effect of the arc force on liquid surface was investigated.The simulation was carried out with finite elements software Surface Evolver.The influence of the arc force on the weld pool shape was also studied.According to the results,the variation of the weld shape and the parameters with different arc force strength was obtained.Compared with the back weld pool,the top weld pool was influenced more strongly by the arc force.These results provide an effective basis for further study of the TIG weld pool.