Enlarged-end tool for friction stir lap welding towards hook defect controlling

Hook defect is one of the trickiest issues for friction stir lap welding,which remains to be resolved.In this study,a designed pin with an enlarged-end was proposed to control the interfacial hook defect by optimizing its morphology orientation.The insert aduncous structure at the advancing side is dissected by multilayer metallographic observation,which is the main character to terminate the inner-ward extension of the hook.The application of this tool was verified practical with a varied plunge depth of pin into the lower plate from 0.1 mm to 1.6 mm.The angle of the hook was small and terminated at the insert-structure or oriented toward the material convergence region.No joint fractured along the hook line and the highest joint efficiency reached 86%of the parent 6082-T4 aluminum alloy.

Enhanced Fatigue Properties of 2219 Al Alloy Joints via Bobbin Tool Friction Stir Welding

In the present study,2219-T87 Al alloy plates,4 mm in thickness,were subjected to bobbin tool friction stir welding(BTFSW)under relatively high welding speeds of 200 and 400 mm/min,with the aim to analyze the effect of welding speeds on fatigue properties of the joints.The results showed that the tension–tension high-cycle fatigue performance of the BT-FSW joints at room temperature was significantly enhanced compared to that of other joints of 2xxx series Al alloys counterparts.Particularly at a high welding speed of 400 mm/min,the fatigue strength of the joint reached 78%of the base material together with a high tensile strength of 311 MPa.It was found that the joint line remnants had no effects on the fatigue properties of the BT-FSW joints due to the elimination of root flaws under the action of the lower shoulder.Most of the samples with the welding speed of 200 mm/min failed at the thermo-mechanical zone(TMAZ)during fatigue tests,attributable to the coarsened grains and precipitates,but all of the samples with high welding speed of 400 mm/min randomly failed at the nugget zone due to the improved hardness value in the TMAZ.

Improving weld formability by a novel dual-rotation bobbin tool friction stir welding

A novel dual-rotation bobbin tool friction stir welding （DBT-FSW） was developed, in which the upper shoulder （US） and lower shoulder （LS） have different rotational speeds. This process was tried to weld 3.2 mm thick alunlinum-lithium alloy sheets. The metallographic analysis and torque measurement were carried out to characterize the weld formabiliW. Experimental results show that compared to conven- tional bobbin tool friction stir welding, the DBT-FSW has an excellent process stability, and can produce the defect-free joints in a wider range of welding parameters. These can be attributed to the significant improvement of material flow caused by the formation of a staggered layer structure and the unbalanced force between the US and LS during the DBT-FSW process.

Non-keyhole Friction Stir Welding for 6061-T6 Aluminum Alloy

A novel non-keyhole friction stir welding technique was proposed to weld the butt joint of 6061-T6 aluminum alloy with the thickness of 6 mm.A sound joint was obtained by this technique,simultaneously eliminating the flash,shoulder mark and keyhole defects.The sleeve directly affected zone(SDAZ)and the sleeve indirectly affected zone(SIAZ)were divided into the joint according to the plunging position of the hollow sleeve.The lack of root penetration defect was avoided when the plunging depth of the hollow sleeve was only 4.2 mm,because the hollow part inside the sleeve improved the material flow below the sleeve.An S-shaped line was left at the SIAZ,and the height of it had the minimum value of 1.47 mm at 20 mm/min.Whether the failure location of the joint was in SIAZ/SDAZ or the heat-affected zone(HAZ)depended on the height and bonding strength of the S-shaped line.The joint fracture location changed from the SIAZ/SDAZ at 35 mm/min to the HAZ at 20 and 30 mm/min.The maximum tensile strength of 224.3 MPa was obtained at 30 mm/min which was 73.7%of that of the base material.The fracture surface morphology exhibited the typical ductile fracture.

Comparative study on local and global mechanical properties of bobbin tool and conventional friction stir welded 7085-T7452 aluminum thick plate

7085-T7452 plates with a thickness of 12 mm were welded by conventional single side and bobbin tool friction stir welding （SS-FSW and BB-FSW, respectively） at different welding parameters. The temperature distribution, microstructure evolution and mechanical properties of joints along the thickness direction were investigated, and digital image correlation （DIC） was utilized to evaluate quantitatively the deformation of different zones during tensile tests. The results indicated that heat-affected zone （HAZ）, the local softening region, was responsible for the early plastic deformation and also the fracture location for SS-FSW samples, while a rapid fracture was observed in weld nugget zone （WNZ） before yield behavior for all BB-FSW specimens. The ultimate tensile strength （UTS） of SS-FSW joints presented the highest value of 410 MPa, 82% of the base material, at a rotational speed of 300 rpm and welding speed of 60 mm/min, much higher than that of BB-FSW joints, with a joint efficiency of only 47%. This should be attributed to the Lazy S defect produced by a larger extent of heat input during the BB-FSW process, The whole joint exhibited a much higher elongation than the slices. Scanning electron microscopic （SEM） analysis of the fracture morphologies showed that joints failed through ductile fracture for SS-FSW and brittle fracture for BB-FSW.

Assessing the Bonding Interface Characteristics and Mechanical Properties of Bobbin Tool Friction Stir Welded Dissimilar Aluminum Alloy Joints

This study focuses on the bonding interface characteristics and mechanical properties of the bobbin tool friction stir welded dissimilar AA6056 and AA2219 aluminum alloy joints using diff erent welding speeds.Voids arise solely in the stir zone at the AA2219 side.A distinct boundary with limited material mixing develops at the middle section of the bonding interface,while excellent material mixing with an irregularly jagged pattern forms at the top and bottom sections of the bonding interface.Increasing the welding speed,the material mixing is rarely changed at the middle section in comparison with the bottom section.Furthermore,a small diff erence between Guinier–Preston dissolution and Q phase precipitation leads to rare change of hardness in the heat aff ected zone(HAZ)at the AA6056 side.The increased hardness of the HAZ at the AA2219 side is attributed to avoidance of the dissolution ofθ’’phase precipitates.A maximum tensile strength of 181 MPa is obtained at 300 mm min-1.Fractures occur at the AA6056 side near the top and bottom surfaces and at the bonding interface in the middle section of the joints.The regions close to the top and bottom surfaces of the joints show a better ductility.