Effect of heat treatment on stress corrosion cracking, fracture toughness and strength of 7085 aluminum alloy

The influences of heat treatment on stress corrosion cracking （SCC）, fracture toughness and strength of 7085 aluminum alloy were investigated by slow strain rate testing, Kahn tear testing combined with scanning electron microscopy （SEM） and transmission electron microscopy （TEM）. The results show that the fracture toughness of T74 overaging is increased by 22.9% at the expense of 13.6% strength, and retrogression and reaging （RRA） enhances fracture toughness 14.2% without reducing the strength compared with T6 temper. The fracture toughness of dual-retrogression and reaging （DRRA） is equivalent to that of T74 with an increased strength of 14.6%. The SCC resistance increases in the order： T6〈RRA〈DRRA≈T74. The differences of fracture toughness and SCC were explained on the basis of the role of matrix precipitates and grain boundary orecioitates.

Effect of welding heat input and post-welded heat treatment on hardness of stir zone for friction stir-welded 2024-T3 aluminum alloy

The microstructure and hardness of the stir zone （SZ） with different welding heat inputs were investigated for friction stir-welded 2024-T3 aluminum by transmission electron microscopy, differential scanning calorimeter and Vickers micro-hardness test. The results show that welding heat input has a significant effect on the hardness of the SZ. Under high welding heat input condition, a higher welding speed is beneficial for improving the hardness of the SZ. However, when the welding heat input is low, the hardness of the SZ elevates with increasing the rotation speed. The hardness of the SZ decreases after post-welded heat treatment due to overaging. The joints welded at 500 r/min and 100 mm/min show a high resistance to overaging. The reduction of hardness in the SZ is only 3.8%, while in other joints, the reduction is more than 10%. The morphology of strengthening precipitates plays important roles for the improvement of hardness.

Effect of post-weld heat treatment on microstructure and properties of Ti-23Al-17Nb alloy laser beam welding joints

The mechanical properties of Ti-23Al-17Nb (mole fraction,%) laser beam welding alloy joint at room temperature are comparable to that of the base materials.However,the strength and ductility of the as-welded joint deteriorate seriously after high temperature circulation.The effect of post-welded heat treatment on the microstructure and mechanical properties of the joint was investigated.The heat treatment was taken at 980 ℃ for 1.5 h,then furnace cooling and air cooling were performed separately.The results indicate that proper post-welded heat treatment improves the ductility of the joint at high temperature.

Effects of laser heat treatment on salt spray corrosion of 1Cr5Mo heat resistant steel welding joints

The surface of 1Cr5 Mo heat-resistant steel welding joint was processed with CO2 laser, and the corrosion behaviors before and after laser heat treatment(LHT) were investigated in the salt spray corrosion environments. The microstructures, phases, residual stresses and retained austenite content of 1Cr5 Mo steel welding joint before and after LHT were analyzed with optical microscope and X-ray diffraction, respectively. The cracking morphologies and chemical compositions of corrosion products after salt spray corrosion were analyzed with field emission scanning electron microscopy(FESEM) and energy disperse spectroscopy(EDS), respectively, the polarization curves were measured on a PS-268 A type electrochemical workstation, and the mechanism of corrosion resistance by LHT was investigated as well. The results show that the passive film of original sample is destroyed owing to the corrosive media penetrating into the subsurface, resulting in the redox reaction. The content of residual austenite in the surface and the self-corrosion potential are increased by LHT, which is contributed to improving the capability of salt spray corrosion resistance.

Effects of heat treatment on the intermetallic compounds and mechanical properties of the stainless steel 321–aluminum 1230 explosive-welding interface

The effects of heat treatment on the microstructure and mechanical properties of intermetallic compounds in the interface of stainless steel 321 explosively bonded to aluminum 1230 were investigated in this study. Experimental investigations were performed by optical microscopy, scanning electron microscopy, and microhardness and shear tensile strength testing. Prior to heat treatment, increasing the stand-off distance between samples from 1 to 2.5 mm caused their interface to become wavy and the thickness of intermetallic layers to increase from 3.5 to 102.3 μm. The microhardness increased from HV 766 in the sample prepared at a stand-off distance of 1 mm to HV 927 in the sample prepared at a stand-off distance of 2.5 mm; in addition, the sample strength increased from 103.2 to 214.5 MPa. Heat treatment at 450°C for 6 h increased the thickness of intermetallic compound layers to 4.4 and 118.5 μm in the samples prepared at stand-off distances of 1 and 2.5 mm, respectively. These results indicated that increasing the duration and temperature of heat treatment decreased the microhardness and strength of the interface of explosively welded stainless steel 321-Al 1230 and increased the thickness of the intermetallic region.

Effects of heat treatment process on stress corrosion cracking and microstructures of 7A05 Al alloy plate

In order to improve the stress corrosion cracking(SCC) resistance of 7A05Al alloy, four different heat treatment processes were performed. After the heat treatments, the stress corrosion cracking resistance, mechanical properties and microstructures of 7A05A1 alloys were studied. The results show that the retrogression and reaging(RRA) treated specimens possess the highest SCC resistance with slightly reduced strength compared with the other specimens. Thus RRA is the best process in terms of the optimal combination of SCC resistance and strength. Further TEM observation reveals that the RRA treated specimens are characterized by the fine equiaxed grains, dispersed second phase and wide PFZ. The pre-aging treated specimens show lower SCC resistance but higher strength as compared with the RRA treated ones. Equiaxed grains are also observed in the pre-aging treated samples by TEM, indicating that the anisotropy is eliminated. However, the dual aging and deformation plus aging treated specimens are demonstrated by large anisotropy.

Weldability and liquation cracking behavior of ZhS6U superalloy during electron-beam welding

The weldability of the ZhS6U nickel-based superalloy, which is prone to solidification cracking during electron-beam welding(EBW) repair processes, was investigated. The effects of two different pre-weld heat-treatment cycles on the final microstructure before and after welding were examined. Welds were made on flat coupons using an EBW machine, and the two heat-treatment cycles were designed to reduce γ′ liquation before welding. Microstructural features were also examined by optical and scanning electron microscopy. The results showed that the change in the morphology and size of the γ′ precipitates in the pre-weld heat-treatment cycles changed the ability of the superalloy to release the tensile stresses caused by the matrix phase cooling after EBW. The high hardness in the welded coupons subjected to the first heat-treatment cycle resulted in greater resistance to stress release by the base alloy, and the concentration of stress in the base metal caused liquation cracks in the heat-affected zone and solidification cracks in the weld area.

Experimental Study of Inducing Compressive Stress by Anti-welding Heating Treatment in a Thin Plate Weldment with Variant Temperatures

Significant compressive stress may be induced in thin plate weldment by anti-welding heating treatment (AWHT) with a temperature difference above 350℃, and an interesting phenomenon of obvious residual stress reduction on non-treated surface was discovered. The method of AWHT has no great effect on the mechanical properties including hardness, strength and toughness of the metal material. The results in the paper prompt a possibility application in shipbuilding industry.

Finite Element Simulation of Processes Involving Moving Heat Sources. Application to Welding and Surface Treatment

A wide range of welding and surface treatment processes involve the use of a heat source which is moving at a constant speed over the component. The numerical simulation of such processes implies a transient analysis using a very refined mesh in order to follow properly the path of the heat source. The 3D-mesh size can be very large if one consider the welds length or the heat-treated surface size in industrial components. To reduce the computational time to acceptable values, several techniques have been investigated. The first type is to use analytical methods such as Rosenthal equations. The second type of solutions consists in performing a transient analysis using adaptive meshing. But, for a large proportion of the involved processes, practical experience demonstrates the existence of quasi steady state conditions over the major part of the heat source path. Numerical algorithms have therefore been developed to directly compute the steady temperature, metallurgical phase proportion and stress distributions. This paper gives a general overview of the different numerical methods used to simulate welding and surface treatment processes with a special emphasis on the steady state calculation. The benefits and limitations of each of them are discussed and applications are presented.

Effects of heat treatment on microstructure and microhardness of linear friction welded dissimilar Ti alloys

A detailed investigation for the influence of post weld heat treatment （PWHT） on the microstructure of TC4 and TC17 dissimilar joints was analyzed. The fully transformed microstructure in the as-welded zone indicated that the peak temperature exceeded theβ-transus temperature at the weld interface during linear friction welding. TC4 side was mainly composed of martensiteα′phase with random distribution and it was singleβfor that of TC17. In the thermomechanically affected zones of TC4 and TC17, the structure undergoes severe plastic deformation and re-orientation, yet without altering the phase fractions. After PWHT, in the weld zone of TC4 alloy, the phase transformationα′→α＋βoccurred and the acicularαwas coarsened, which resulted in a decrease in hardness. In the weld zone of TC17 alloy, fineαphase precipitated at the grain boundary and withinβgrains, which resulted in a sharp increase in hardness.

Effects of Electron Beam Local Postweld Heat Treatment on Microstructure and Properties of 30CrMnSiNi2A Steel Welded Joints

To improve the microstructure and properties of the electron beam welded joints, the vacuum or furnace whole post weld heat treatment (FWPWHT) usually should be done on it. The electron beam local post weld heat treatment (EBLPWHT) is a rather new heat treatment procedure that provides the advantages of high precision, flexibility and efficiency, energy saving and higher productivity. In this paper, the microstructure, mechanical properties, fracture toughness and fatigue properties of electron beam welded joints of 30CrMnSiNi2A steel in as-welded (AW) and EBLPWHT conditions have been investigated respectively. The results show that the microstructures of different zones of joints in as-welded condition are changed by EBLPWHT procedure, in which the welds from coarse needle martensite into lath-shaped martensite; the main structures of heat affected zones (HAZ) from lath-shaped martensite into lower bainite. The properties of welded joints can be improved by the EBLPWHT in some extent, especially the fracture toughness of the welds and the fatigue crack resistance of welded joints can be sufficiently improved. However, more appropriate heat treatment parameters of the EBLPWHT have to be studied in order to increase the mechanical properties of base metal near by the HAZ.

Effect of post-weld heat treatment on microstructure and mechanical properties of welded joints of 6061-T6 aluminum alloy

6061 aluminum alloy T-joints were welded by double-pulsed MIG welding process. Then, the post-weld heat treatment was performed on the welded T-joints. The weld microstructure under different aging temperature and time was investigated by transmission electron microscopy and scanning electron microscopy. The mechanical properties were examined by hardness test and tensile test. The results showed that the micro-hardness was sensitive to heat treatment temperature and time. Increasing temperature was beneficial to the shortening of peak aging time. There were a large number of dislocations and few precipitates in the welded joints. With the increase of post-weld heat treatment temperature and time, the density of dislocation decreased. Meanwhile, the strengthening phase precipitated and grew up gradually. When the post-weld heat treatment temperature increased up to 200℃, large Q' phases were observed. And they were responsible for the peak value of the micro-hardness in the welded joints.

Effect of Post-weld Heat Treatment on Microstructure and Mechanical Properties of Friction Stir Welded SSM7075 Aluminium Alloy

7XXX series aluminium alloys generally present low weldability by fusion welding methods because of the sensitivity to weld solidification cracking, vaporization of strengthening alloys and other defects in the fusion zone. Friction stir welding（FSW） can be deployed successfully with aluminium alloys. We presented the effect of post-weld heat treatment（PWHT） on the microstructure and mechanical properties of SSM7075 joints. Semi solid plates were butt-welded by FSW at a rotation speed of 1110 r/min, welding speeds of 70 and 110 mm/min. Solution treatment, artificial aging, and T6（solution treatment and artificial aging combined） were applied to the welded joints, each with three samples. It was found that the T6 joints at the speed of 70 mm/min yielded the highest tensile strength of 459.23 MPa. This condition best enhanced the mechanical properties of FSW SSM7075 aluminium alloy joints.

Microstructure characterization of electron beam welded joints of Ti_3Al after post-weld heat treatment

The effect of post-weld heat treatment on the microstructure characterization of electron beam welded(EBW) joints of Ti3Al-Nb was investigated.The results show that the microstructure of the weld is predominantly metastable,the columnar crystal metastructure of B2 phase.The microstructure morphology of the weld is significantly influenced by the method of the heat treatment.The microstructure of the weld is laminar structure(Widmanstaten structure) consisted of interphase α2 and B2 after post-weld heat treatment of 1000 ℃/2 h.The mechanism of the post-weld heat treatment makes the hardness distribution of joints homogeneous,but makes the whole joint somehow softened.

Effect of post-weld heat treatment on joint properties of dissimilar friction stir welded 2024-T4 and 7075-T6 aluminum alloys

The effect of post-weld heat treatment on dissimilar friction stir welded AA7075 and AA2024 joints was studied. After welding in constant parameters, solution heat treatment and various aging treatments were given to the welded joints. Microstructural and phase characterizations were done using optical microscope, SEM, FE-SEM, XRD and EDS techniques. Finally, mechanical properties of post-weld heat treated joints were evaluated and compared with as-welded joints. Results show that both 2024-T6 and 7075-T6 post-weld heat treatment procedures considerably improve the mechanical strength of the welded joint, with higher strength obtained for the 7075-T6 procedure, in comparison with the as-welded joint. This is explained by the formation of fine precipitates during the aging process, despite the abnormal grain growth. Fracture occurs at the interface between thermo-mechanical affected zone（TMAZ） and heat affected zone（HAZ） on the retreating side（AA7075） of as-welded joint, while by applying post-weld heat treatment fracture location shifts towards the stir zone（SZ） of the welded joint. Also, for post-weld heat treated samples, fracture surface is predominantly inter-granular, while in as-weld joint, fracture surface is mostly trans-granular. This is explained by dissolution and coarsening of precipitates within grains in post-weld heat treated joints.

Effect of post weld heat treatment on microstructure and mechanical properties of gas tungsten arc welded AA6061-T6 alloy

Double-V butt TIG welding process was performed on two plates of AA6061-T6 using ER5356 filler. The microstructure,mechanical and nanomechanical properties of the joint were evaluated in as-welded and after post weld heat treatment (PWHT) usingXRD, FESEM, EBSD, nanoindentation and tensile tests. The results show that PWHT led to microstructural recovery of the heataffected zone (HAZ) in addition to the appearance of β-phase (Al3Mg2) at the grain boundaries of weld zone. The hardness (Hnano) inall zones increased after PWHT while the elastic modulus (Enano) was improved from 69.93 GPa to 81 GPa in weld area. All resultsindicate that PWHT has created a homogenous microstructure in the weld zone in addition to outstanding improvement inmechanical properties for the weld zone which surpass the base metal.

Effect of post weld heat treatment on properties of variable polarity TIG welded AA2219 aluminium alloy joints

AA2219 aluminium alloy joints were fabricated by variable polarity tungsten inert gas （VPTIG） welding process and the effects of post weld heat treatment （PWHT） on the tensile properties, microstructure and fatigue behaviour of the welded joints were investigated. The VPTIG welding process was adopted because it could meet the need of cathode cleaning and meanwhile it could reduce the deterioration of tungsten electrode furthest. The welded samples were divided into as-welded （AW） sample and PWHT sample. The PWHT method used on the samples was solution treatment （535 ℃, 30 rain）, water quenching and artificial aging （175 ℃, 12 h）. The experimental results show that, compared with the AW samples, the microstructure characteristics and mechanical properties of the AA2219 joints after PWHT were significantly improved. The improvement of yield strength, ultimate tensile strength, and fatigue strength are 42.6%, 43.1% and 18.4%, respectively.

A new post-weld heat treatment to improve toughness of 9Cr-1Mo steel weld metals

9Cr-1Mo ferritic steels have been used in the conventional power generation plants due to their excellent creep resistance. However, one of the main obstacles in welding 9Cr-1Mo steels is the formation of undesirable coarse columnar grains in weld metal whieh ean severely compromise the toughness. A new post-weld heat treatment （PWHT） is developed in the present work. Unlike the conventional processes in which the post-weld heat treatment is carried out below Ac1 , the use of temperatures above the Ac1 of 9Cr-1Mo alloy is considered. The new PWHT at a temperature above Ac1 improves the toughness of 9Cr-1Mo weld metals effectively. The improvement in toughness is mainly due to refinement and homogenization of mierostruetures. Key words

Effect of welding heat input and post-weld aging time on microstructure and mechanical properties in dissimilar friction stir welded AA7075-AA5086

The effects of welding heat input and post-weld heat treatment on the mechanical and microstructural aspects of dissimilarfriction stir welds of age-hardened AA7075-T6and strain hardenable AA5086-H32aluminium alloys were investigated.X-raydiffraction(XRD)residual stress analysis and tensile testing together with optical metallography and transmission electronmicroscopy(TEM)were performed to assess the effects of process parameters on welded joints.It was discovered that jointsproduced without heat sink exhibited more homogeneous stir zones than other joints.Of the natural aging time studied,higheramount of solid solution during rapid cooling of welds produced higher driving force for increase in hardness in the AA7075sideduring natural aging.Natural aging within stirring zone and thermo-mechanical affected zone of AA7075side resulted in a10to25MPa reduction in the residual stress in these zones;its effect decreased considerably in the welds performed without heat sink.Inaddition,natural aging had no noticeable effect on the joint strength.

Effect of postweld heat treatment on interface microstructure and metallurgical properties of explosively welded bronze–carbon steel

The effects of postweld heat treatment on the microstructure and metallurgical properties of a bronze–carbon steel(st37)explosively bonded interface were studied.Explosive welding was done under 1.5-and 2-mm standoff distances and different conditions of explosive charge.Samples were postweld heat treated for 4 and 16 h in the furnace at 250°C and 500°C and then air cooled.Laboratory studies using optical microscopy,scanning electron microscopy,and microhardness testing were used to evaluate the welded samples.Microstructural examinations showed that by increasing the standoff distance and the explosive charge,the interface of bronze to steel became wavier.The microhardness test result showed that the hardness of the samples was higher near the joint interface compared with other areas because of the intensive plastic deformation,which was caused by the explosion force.The results show that increasing the heat treatment temperature and time caused the intermetallic compounds’layer thickness to increase,and,because of the higher diffusion of copper and tin,the iron amount in the intermetallic compounds decreased.Also,because of the increase in heat treatment temperature and time,internal stresses were released,and the interface hardness decreased.