This paper describes a general model for the mechanical behavior studying of general wire rope strand. An exact solution of the deformation characteristics was given when the strands is under tensile and torsional loa...This paper describes a general model for the mechanical behavior studying of general wire rope strand. An exact solution of the deformation characteristics was given when the strands is under tensile and torsional loads. The theoretical results are useful in evaluating the extensional and torsional moduli of rigidity for the strands. Finally, a simple design criterion is establised for the nonrotating ropes.展开更多
通过调整炼钢成分(质量分数),将V含量由0.09%降低到≤0.005%,Cr含量由0.28%降低到≤0.05%,Mn含量由0.85%降低到0.70%,在降低了合金元素情况下,通过调整连铸轻压下工艺、在线热处理技术(吐丝温度890~910℃、盐槽温度510~520℃)生产的Φ15...通过调整炼钢成分(质量分数),将V含量由0.09%降低到≤0.005%,Cr含量由0.28%降低到≤0.05%,Mn含量由0.85%降低到0.70%,在降低了合金元素情况下,通过调整连铸轻压下工艺、在线热处理技术(吐丝温度890~910℃、盐槽温度510~520℃)生产的Φ15 mm YL82B-QM高强钢绞线盘条,平均抗拉强度达到1227 MPa,断面收缩率39.3%,索氏体化率98%,同圈强度在40 MPa范围内,晶界渗碳体和心部马氏体≤1.0级;与传统的Cr、V合金化Φ15 mm YL82B-V风冷盘条相比,盘条性能更加优良,降低了合金成分的加入量,且不需要风机冷却,极大的降低了能源消耗,做到了绿色环保工业生产,该盘条用于生产Φ10 mm 1570 MPa级轨枕钢丝,经过客户验证,钢丝抗拉强度、延伸率、弯折等重要指标均符合标准要求。展开更多
文摘This paper describes a general model for the mechanical behavior studying of general wire rope strand. An exact solution of the deformation characteristics was given when the strands is under tensile and torsional loads. The theoretical results are useful in evaluating the extensional and torsional moduli of rigidity for the strands. Finally, a simple design criterion is establised for the nonrotating ropes.
文摘通过调整炼钢成分(质量分数),将V含量由0.09%降低到≤0.005%,Cr含量由0.28%降低到≤0.05%,Mn含量由0.85%降低到0.70%,在降低了合金元素情况下,通过调整连铸轻压下工艺、在线热处理技术(吐丝温度890~910℃、盐槽温度510~520℃)生产的Φ15 mm YL82B-QM高强钢绞线盘条,平均抗拉强度达到1227 MPa,断面收缩率39.3%,索氏体化率98%,同圈强度在40 MPa范围内,晶界渗碳体和心部马氏体≤1.0级;与传统的Cr、V合金化Φ15 mm YL82B-V风冷盘条相比,盘条性能更加优良,降低了合金成分的加入量,且不需要风机冷却,极大的降低了能源消耗,做到了绿色环保工业生产,该盘条用于生产Φ10 mm 1570 MPa级轨枕钢丝,经过客户验证,钢丝抗拉强度、延伸率、弯折等重要指标均符合标准要求。