TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM...TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.展开更多
TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of p...TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of pure Al matrix by 71.5% and 134% respectively However, the elongation is 20.36%, slightly lower than that of the Al matrix.展开更多
Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO...Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.展开更多
The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influenc...The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influences of contents and sizes of AlOon the structure and wearability were investigated.The results show that the wear resistance of the coating would be increased greatly by adding AlO,but the spray weldability decreases with increasing AlOcontent.So there is an optimal content of AlOpowder.The composite coating with AlOnano or sub-micron powder of 0.5% has the best abrasive resistance,while the optimal content of AlOmicron powder is 1 %.展开更多
Pure Al2O3-2SiO2 powders were prepared by sol-gel and coprecipitation methods, and their alkaliactivation reactivities were compared. The alkali-activation reactivity of the powder prepared by the so]-gel method was h...Pure Al2O3-2SiO2 powders were prepared by sol-gel and coprecipitation methods, and their alkaliactivation reactivities were compared. The alkali-activation reactivity of the powder prepared by the so]-gel method was higher than that of the powder prepared by the coprecipitation method. The powders were investigated by 27Al and 29Si magic-angle spinning nuclear magnetic resonance spectroscopy （MAS NMR） to understand the relationship between their structure and alkali-activation reactivity. The 27Al MAS NMR data showed that the five-coordinate AI content of the powder prepared by the sol-gel method was higher than that of the powder prepared by coprecipitation. The higher content of five-coordinate Al corresponded to higher alkali-activation reactivity. The 29Si MAS NMR data showed that for the powder prepared by the sol-gel method, silicon was replaced by aluminum at secondary coordination sites of the central Si atoms during calcination. However, for the powder prepared by single-batch coprecipitation, the main change was from a low degree of polycondensation to a high degree of polycondensation.展开更多
Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characte...Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.展开更多
文摘TiB2-Al2O3 composite powders were produced by self-propagating high-temperature synthesis（SHS） method with reductive process from B2O3-TiO2-AI system. X-ray diffraction（XRD） and scanning electron microscopy（SEM） analyses show the presence of TiB2 and Al2O3 only in the composite powders produced by SHS. The powders are uniform and free-agglomerate. Transmission electron microscopy （TEM） and high resolution electron microscopy （HREM） observation of microstructure of the composite powders indicate that the interfaces of the TiB2-Al2O3 bond well, without any interfacial reaction products. It is proposed that the good interfacial bonding of the composite powders can be resulted from the TiB2 particles crystallizing and growing on the Al2O3 particles surface with surface defects acting as nucleation centers.
文摘TiAl3 particle reinforced pure Al composite has been made by direct reaction among molten Al, TiO2 and a flux. The composite exhibits high Synthetically properties. The strength and hardness are higher than those of pure Al matrix by 71.5% and 134% respectively However, the elongation is 20.36%, slightly lower than that of the Al matrix.
文摘Al 2O 3-SiO 2-TiO 2-ZrO 2 supported membranes were prepar ed by Sol-Gel method. These composite ceramic membranes are level, even and no macro crack. There exist several crystalline phases such as Al 2O 3, TiO 2(a natase), Al 2SiO 5, and ZrO 2 in these membranes. Changing the molar ratio of Al∶Si∶Ti∶Zr,the kinds and content of crystal phases of composite membranes could be different, which may lead to a variety of microstructure of membranes. The surface nanoscale topography and microstructure of membranes were investiga ted by XRD,SEM,AFM,EPMA. The effects of additives and heat treatments on the sur face nanoscale topography and microstructure of composite ceramic membranes were also analyzed.
基金Item Sponsored by Provincial Natural Science Foundation of Jiangsu of China(BK2000012)
文摘The composite coating was prepared by thermal spray welding after making composite powder,which is composed of Ni-based self-melted alloy and AlOceramic powder including nano,sub-micron and micron powders.The influences of contents and sizes of AlOon the structure and wearability were investigated.The results show that the wear resistance of the coating would be increased greatly by adding AlO,but the spray weldability decreases with increasing AlOcontent.So there is an optimal content of AlOpowder.The composite coating with AlOnano or sub-micron powder of 0.5% has the best abrasive resistance,while the optimal content of AlOmicron powder is 1 %.
基金supported by the Chinese Natural Science Fund (Grant Nos.51262002 and 50962002)Guangxi Experiment Center of Science and Technology(Grant No.LGZXKF201202)+2 种基金Guangxi Natural Science Fund(Grant No.2014GXNSFAA118323)Research Project of the Education Department of Guangxi Government (Grant No.201204LX238)Opening Fund of Doctor Station Construction of Guangxi Teachers Education University
文摘Pure Al2O3-2SiO2 powders were prepared by sol-gel and coprecipitation methods, and their alkaliactivation reactivities were compared. The alkali-activation reactivity of the powder prepared by the so]-gel method was higher than that of the powder prepared by the coprecipitation method. The powders were investigated by 27Al and 29Si magic-angle spinning nuclear magnetic resonance spectroscopy （MAS NMR） to understand the relationship between their structure and alkali-activation reactivity. The 27Al MAS NMR data showed that the five-coordinate AI content of the powder prepared by the sol-gel method was higher than that of the powder prepared by coprecipitation. The higher content of five-coordinate Al corresponded to higher alkali-activation reactivity. The 29Si MAS NMR data showed that for the powder prepared by the sol-gel method, silicon was replaced by aluminum at secondary coordination sites of the central Si atoms during calcination. However, for the powder prepared by single-batch coprecipitation, the main change was from a low degree of polycondensation to a high degree of polycondensation.
基金supported by the National Natural Science Foundation of China (No.50574075)Program for New Century Excellent Talents in University(No.NCET-05-0873)Specialized Research Fund for the Doctoral Program of Higher Education (SRFDP 20060700011)
文摘Since Cu-Al powder characteristics have important effects on the preparation of Cu/Al2O3 composite, the apparent activation energy of Al internal oxidation reaction in Cu-Al pre-alloyed powders with different characteristics was calculated in the present investigation. The microstructure and properties of the synthesized Cu/Al2O3 were studied. The results show that high-energy milling can obviously promote internal oxidation of Al in Cu-Al powders in the same solid solubility. At the same milling conditions and internal oxidation parameters, the solid solution of Al in Cu either in low or high amount will result in the poor microstructure and properties of the Cu/Al2O3 composite. Subsequently, when high-energy milling and internal oxidation are synchronously used to prepare the Cu/Al2O3 composite, there should be an appropriate solubility and milling effect for the pre-alloyed powders.