Wood plastic biocomposites of biodegradable poly（butylene succinate） （PBS） and Padauk sawdust was successfully pre- pared by using a twin screw extruder and an injection molding machine. The effects of water absor...Wood plastic biocomposites of biodegradable poly（butylene succinate） （PBS） and Padauk sawdust was successfully pre- pared by using a twin screw extruder and an injection molding machine. The effects of water absorption and sunlight exposure on some properties of the composites were investigated. Water absorption of PBS composites was found to follow the Fick＇s law of diffusion, while the diffusion coefficient increased with increasing wood content. Maximum water absorption of around 4.5% was observed at 30 wt.% sawdust. Optical micrograph indicated the swelling of wood particles by around 1% - 3% after 30 days of water immersion. The tensile and flexural strengths reduced slightly both under the water immersion and sunlight exposure. After 90 days of exposure, the composites clearly looked paler than the non-weathered ones. Thermal scan indicated the re- duction of crystalline region due to the plasticization effect derived from water molecules.展开更多
In order to solve the problem of poor thermal insulation in the current wood-plastic building,two kinds of structural wood wall integrated with wood plastic composite(WPC)are designed,and the thermal insulation perfor...In order to solve the problem of poor thermal insulation in the current wood-plastic building,two kinds of structural wood wall integrated with wood plastic composite(WPC)are designed,and the thermal insulation performances of the walls are studied.The results show that the WPC integrated wall with frame-shear structure has a good stability,and the excellent performance of the WPC can be fully realized.Wall studs and wall panels are important factors affecting the thermal performance of the walls.Wood plastic materials can meet the thermal performance requirements of the walls.The single-layer frame walls and double-layer frame walls integrated with the WPC both have a good thermal performance.According to‘Design Standard for Energy Efficiency of Public Buildings(GB 50189-2015)’,the heat transfer coefficient of the single-layer frame wall integrated with 20 mm thick WPC wall boards and WPC wall studs is 0.414 W/(m^(2)•K),which can meet the standard of wall thermal levelⅡt and is suitable for cold areas.The heat transfer coefficient of the double-layer frame wall integrated with 50 mm thick WPC wall panel and WPC wall studs is 0.207 W/(m^(2)•K),which can meet the standard of wall thermal levelⅠt and is suitable for severe cold areas.展开更多
The sound insulation performance is an important technical index for evaluating the physical property of the building wall.Three kinds of structural wood walls integrated with wood plastic composite(WPC)were designed....The sound insulation performance is an important technical index for evaluating the physical property of the building wall.Three kinds of structural wood walls integrated with wood plastic composite(WPC)were designed.And the sound insulation performance of the walls was studied.The results showed that for the wall that constructed by the WPC as the wall studs,compared with the one that constructed by the pine wood as the wall studs,the deviation of their sound insulation was lower than±3 dB.The wall’s external panel material had significant effect on the wall’s sound insulation property,and the contribution of the wood-plastic panel to the sound insulation was much higher than that of the polyvinyl chloride(PVC)plastic hanging board.The surrounding sealing quality of the wall’s external panel material had an important influence on the sound insulation effect of the building wall,and the panel of the wood plastic interior wall had less influence on the sound insulation performance of the wall.Taking the sound-absorbing cotton or non-woven fabric as elastic strips was an effective technical measure to improve the sound insulation performance of the walls.The sound insulation was improved by 2.4 dB and 3.1dB respectively after the correction of pink noise spectrum,and increased by 2.8 dB and 3.6 dB respectively after the correction of traffic noise spectrum.展开更多
文摘Wood plastic biocomposites of biodegradable poly（butylene succinate） （PBS） and Padauk sawdust was successfully pre- pared by using a twin screw extruder and an injection molding machine. The effects of water absorption and sunlight exposure on some properties of the composites were investigated. Water absorption of PBS composites was found to follow the Fick＇s law of diffusion, while the diffusion coefficient increased with increasing wood content. Maximum water absorption of around 4.5% was observed at 30 wt.% sawdust. Optical micrograph indicated the swelling of wood particles by around 1% - 3% after 30 days of water immersion. The tensile and flexural strengths reduced slightly both under the water immersion and sunlight exposure. After 90 days of exposure, the composites clearly looked paler than the non-weathered ones. Thermal scan indicated the re- duction of crystalline region due to the plasticization effect derived from water molecules.
文摘In order to solve the problem of poor thermal insulation in the current wood-plastic building,two kinds of structural wood wall integrated with wood plastic composite(WPC)are designed,and the thermal insulation performances of the walls are studied.The results show that the WPC integrated wall with frame-shear structure has a good stability,and the excellent performance of the WPC can be fully realized.Wall studs and wall panels are important factors affecting the thermal performance of the walls.Wood plastic materials can meet the thermal performance requirements of the walls.The single-layer frame walls and double-layer frame walls integrated with the WPC both have a good thermal performance.According to‘Design Standard for Energy Efficiency of Public Buildings(GB 50189-2015)’,the heat transfer coefficient of the single-layer frame wall integrated with 20 mm thick WPC wall boards and WPC wall studs is 0.414 W/(m^(2)•K),which can meet the standard of wall thermal levelⅡt and is suitable for cold areas.The heat transfer coefficient of the double-layer frame wall integrated with 50 mm thick WPC wall panel and WPC wall studs is 0.207 W/(m^(2)•K),which can meet the standard of wall thermal levelⅠt and is suitable for severe cold areas.
基金This work was supported by Anhui Sentai WPC Group Co.Ltd.and Priority Academic Development Program of Jiangsu High Education Institutions(PAPD).
文摘The sound insulation performance is an important technical index for evaluating the physical property of the building wall.Three kinds of structural wood walls integrated with wood plastic composite(WPC)were designed.And the sound insulation performance of the walls was studied.The results showed that for the wall that constructed by the WPC as the wall studs,compared with the one that constructed by the pine wood as the wall studs,the deviation of their sound insulation was lower than±3 dB.The wall’s external panel material had significant effect on the wall’s sound insulation property,and the contribution of the wood-plastic panel to the sound insulation was much higher than that of the polyvinyl chloride(PVC)plastic hanging board.The surrounding sealing quality of the wall’s external panel material had an important influence on the sound insulation effect of the building wall,and the panel of the wood plastic interior wall had less influence on the sound insulation performance of the wall.Taking the sound-absorbing cotton or non-woven fabric as elastic strips was an effective technical measure to improve the sound insulation performance of the walls.The sound insulation was improved by 2.4 dB and 3.1dB respectively after the correction of pink noise spectrum,and increased by 2.8 dB and 3.6 dB respectively after the correction of traffic noise spectrum.