Microstructure characteristics and solidification behavior of wrought aluminum alloy 2024 rheo-diecast with self-inoculation method

One important problem in casting wrought aluminum alloys is the high tendency to the formation of hot tears in the solidification process.By using semi-solid metal(SSM) processing,the hot tearing tendency of alloys can be minimized during casting.In the present research,the semi-solid slurry of wrought aluminum alloy 2024 was firstly prepared with a novel self-inoculation method(SIM),and then the microstructure characteristics of the semi-solid slurry and the rheo-diecastings cast with the semi-solid slurry were investigated.The results indicate that finer and more uniform globular primary α-Al particles can be obtained when the semi-solid slurry are isothermally held for a short period within the semi-solid temperature range,and the primary α-Al particles without entrapped liquid are uniformly fine,globular grains in the rheo-diecastings.The holding temperature and time affect the solid fraction,particle size,and shape factor.After the semi-solid slurry is held at 625 ℃ for 3 min and 5 min,the optimal values for the average equivalent diameter are 70.80 μm and 74.15 μm,and for the shape factor are 1.32 and 1.42,respectively.The solidification process of the rheo-diecastings is composed of the following two distinct stages:primary solidification process and secondary solidification process.The secondary solidification process consists further of the following three stages:(1) direct growth of secondary primary(α 2) phase from the surface of the primary α-Al phase particles without re-nucleation,(2) independent nucleation and growth of α 3 phase from the residual liquid,and(3) eutectic reaction at the end.

Solidification behavior of 6061 wrought aluminum alloy during rheo-diecasting process with self-inoculation method

The semisolid slurry of the 6061 wrought aluminum alloy was prepared by the self-inoculation method（SIM）. The effects of the isothermal holding parameters on microstructures of rheo-diecastings were investigated, and the solidification behavior of 6061 wrought aluminum alloy during the rheo-diecasting process was analyzed using OM, SEM, EDS and EBSD. The results indicate that the isothermal holding process during slurry preparation has great effect on primary α（Al） particles（α1）, but has little effect on the microstructure of secondary solidification in the process of thin-walled rheo-diecasting. Nucleation is expected to take place in the entire remaining liquid when the remaining liquid fills the die cavity, and the secondary solidification particles（α2） are formed after the process of stable growth, unstable growth and merging. The solute concentration of remaining liquid is higher than that of the original alloy due to the existence of α1 particles, hence the contents of Mg and Si in α2 particles are higher than those in α1 particles.

Effects of solution treatment and aging process on microstructure refining of semi-solid slurry of wrought aluminum alloy 7A09

A new method was exploited using solution treatment and aging process as a pretreatment in preparing semi-solid slurry with fine microstructure before isothermal treatment of wrought aluminum alloy 7A09.Parameters of pretreatment were optimized by orthogonal experiment design and proper precursor was prepared.The evolution of microstructure of semi-solid slurry during isothermal treatment was analyzed and the mechanism of microstructure refining was discussed.The result of orthogonal experiment design shows that the optimum parameters are 462 ℃for solution temperature,40min for solution time,132 ℃for aging temperature and 14 h for aging time.Microstructure of isothermal treatment is fine,homogenous,with globular solid grains and a solid fraction between 50%and 70%,which is qualified for later semi-solid forming process.Mechanism of microstructure evolution includes the agglomeration ofα-phase and Ostwald ripening.Precipitations prepared by solution and aging treatment prevent the grains from coarsening and promote the grain ripening to globular shape.

SEMI-SOLID MICROSTRUCTURE AND ITS EVOLUTION OF WROUGHT ALUMINUM ALLOY BY DIRECTLYHEATING-ISOTHERMAL TREATMENT

Microstructure evolution of wrought aluminum alloy extruded rods and the mechanism of liquid phase formation during reheating were investigated. And the relation between the volume fraction of liquid phase and the recrystallization microstructure was proposed. The results show that increase in reheating temperature and time can augment the volume fraction of liquid phase and accelerate the grain spheroidization, as a result of which the requirement of semi-solid forming can be satisfied. Due to the higher aberration energy of grain boundary, the melting point is lowered as a result of the easy diffusion of atoms. At higher reheating temperature the grain boundary melts, the growth of the recrystallized grain is inhibited and the grain is refined. The composition of the low melt-point phase along the recrystallized grains was determined using EDS. It can be seen from the experimental results that when the extrusion rod of the wrought aluminum alloy is reheated at 610℃ for 20min, perfect fine equiaxial grains can be obtained, the average grain size is about 66.34μm and the volume fraction of solid phase is about 68%.

Examining the effect of the aging state on strength and plasticity of wrought aluminum alloys

A general rule of strength and plasticity was proposed for three typical wrought Al alloys(2xxx,6xxx,and 7xxx)subjected to different aging times.Investigations of the work-hardening processes and dislocation configurations in tensile and compressive testing reveal that this general rule arises because there is a common mechanism for these three kinds of wrought alloys whereby the tendency for cross-slip increases monotonously with aging time.By analyzing the strain hardening exponent and the stacking fault energy,it is demonstrated that the change in the dislocation slip mode is attributed mainly to the formation of second phases rather than to the matrix composition.Accordingly,a new work-hardening model was proposed for wrought Al alloys containing second phases and this explains the interaction between dislocations and second phases and other relevant experimental phenomena.This work is therefore beneficial for quantitatively investigating and optimizing the strength and plasticity of wrought aluminum alloys.