The silk fabrics were matching dyed with three natural edible pigments(red rice red,ginger yellow and gardenia blue).By investigating the dyeing rates and lifting properties of these pigments,it was observed that thei...The silk fabrics were matching dyed with three natural edible pigments(red rice red,ginger yellow and gardenia blue).By investigating the dyeing rates and lifting properties of these pigments,it was observed that their compatibilities were excellent in the dyeing process:dye dosage 2.5%(omf),mordant alum dosage 2.0%(omf),dyeing temperature 80℃and dyeing time 40 min.The silk fabrics dyed with secondary colors exhibited vibrant and vivid color owing to the remarkable lightness and chroma of ginger yellow.However,gardenia blue exhibited multiple absorption peaks in the visible light range,resulting in significantly lower lightness and chroma for the silk fabrics dyed with tertiary colors,thus making it suitable only for matte-colored fabrics with low chroma levels.In addition,the silk fabrics dyed with these three pigments had a color fastness that exceeded grade 3 in resistance to perspiration,soap washing and light exposure,indicating acceptable wearing properties.The dyeing process described in this research exhibited a wide range of potential applications in matching dyeing of protein-based textiles with natural colorants.展开更多
Synthetic dyes in the aqueous media have been commonly used for textile dyeing, resulting in resource and environmental pressure arising from consumption of water and environmentally unfriendly chemicals. In this stud...Synthetic dyes in the aqueous media have been commonly used for textile dyeing, resulting in resource and environmental pressure arising from consumption of water and environmentally unfriendly chemicals. In this study, an eco-friendly process of dyeing polyamide 6, 6(PA66) fabrics with natural Monascus pigments in decamethylcyclopentasiloxane(D5) solvent has been developed to minimize water consumption and effluent generation. The influence of processing parameters including dyeing temperature, dyebath pH and dyeing time on dyeing effects was explored. It was shown that color strength and color fastness of the samples dyed in D5 media were higher than those of the samples dyed in the aqueous media. Moreover, PA66 fabrics exhibited the highest color strength, good color fastness and a bacteriostatic rate of 53.6% against Staphylococcus aureus when it was dyed at pH of 3.5 and temperature of 80 ℃ for 30 min.展开更多
Aiming at improving the permeability of the pigment dyed fabrics,two kinds of hydrophilic polymers(polyvinyl pyrrolidone(PVP),and polyethylene glycol(PEG)were fed into the styrene-butyl acrylate(St-BuA)copolymer latex...Aiming at improving the permeability of the pigment dyed fabrics,two kinds of hydrophilic polymers(polyvinyl pyrrolidone(PVP),and polyethylene glycol(PEG)were fed into the styrene-butyl acrylate(St-BuA)copolymer latex binder respectively to prepare films with macropores.The effects of the post-added polymers on the latex film formation process and film structures were studied and the performance of the dyed fabrics was evaluated.It was found that the drying process could still be divided into three stages even after the addition of PVP and PEG.And the water evaporation rate during the first and last stage remained the same as usual.However,after the addition of PVP,the onset of the second stage was delayed to high volume fraction,and PVP formed into spherical dispersion phase with 300 nm in diameter.It provided a great deal of interface between the latex polymer and the PVP phase,which led to an increase in the water evaporation rate during the second stage.A different case was found after the feeding of PEG.Firstly,the first stage ended at low volume fraction and a decreased evaporation rate was observed in the second stage.Secondly,the PEG dispersion appeared as finger-like structure in the transmission electron microscopy(TEM)images with 9μm in length.After rinsing,pores were found only in the films formerly containing PVP or PEG,and the shapes and the sizes were closely correlated with the initial morphologies of the PVP or PEG domains.However,the shade of color,the abrasion fastness,and the permeability of the dyed fabric were independent of the type of the post-added hydrophilic polymer.展开更多
基金Fujian External Cooperation Project of Natural Science Foundation,China(No.2022I0042)。
文摘The silk fabrics were matching dyed with three natural edible pigments(red rice red,ginger yellow and gardenia blue).By investigating the dyeing rates and lifting properties of these pigments,it was observed that their compatibilities were excellent in the dyeing process:dye dosage 2.5%(omf),mordant alum dosage 2.0%(omf),dyeing temperature 80℃and dyeing time 40 min.The silk fabrics dyed with secondary colors exhibited vibrant and vivid color owing to the remarkable lightness and chroma of ginger yellow.However,gardenia blue exhibited multiple absorption peaks in the visible light range,resulting in significantly lower lightness and chroma for the silk fabrics dyed with tertiary colors,thus making it suitable only for matte-colored fabrics with low chroma levels.In addition,the silk fabrics dyed with these three pigments had a color fastness that exceeded grade 3 in resistance to perspiration,soap washing and light exposure,indicating acceptable wearing properties.The dyeing process described in this research exhibited a wide range of potential applications in matching dyeing of protein-based textiles with natural colorants.
基金Fujian Provincial Department of Education,China(No.JAT190528)Quanzhou Science and Technology Project,China(No.2019C014R)。
文摘Synthetic dyes in the aqueous media have been commonly used for textile dyeing, resulting in resource and environmental pressure arising from consumption of water and environmentally unfriendly chemicals. In this study, an eco-friendly process of dyeing polyamide 6, 6(PA66) fabrics with natural Monascus pigments in decamethylcyclopentasiloxane(D5) solvent has been developed to minimize water consumption and effluent generation. The influence of processing parameters including dyeing temperature, dyebath pH and dyeing time on dyeing effects was explored. It was shown that color strength and color fastness of the samples dyed in D5 media were higher than those of the samples dyed in the aqueous media. Moreover, PA66 fabrics exhibited the highest color strength, good color fastness and a bacteriostatic rate of 53.6% against Staphylococcus aureus when it was dyed at pH of 3.5 and temperature of 80 ℃ for 30 min.
基金Science Foundation of Zhejiang Province,China(No.Y4080375)Program for Changjiang Scholars and Innovative Research Teamin University,China(No.IRT0654)
文摘Aiming at improving the permeability of the pigment dyed fabrics,two kinds of hydrophilic polymers(polyvinyl pyrrolidone(PVP),and polyethylene glycol(PEG)were fed into the styrene-butyl acrylate(St-BuA)copolymer latex binder respectively to prepare films with macropores.The effects of the post-added polymers on the latex film formation process and film structures were studied and the performance of the dyed fabrics was evaluated.It was found that the drying process could still be divided into three stages even after the addition of PVP and PEG.And the water evaporation rate during the first and last stage remained the same as usual.However,after the addition of PVP,the onset of the second stage was delayed to high volume fraction,and PVP formed into spherical dispersion phase with 300 nm in diameter.It provided a great deal of interface between the latex polymer and the PVP phase,which led to an increase in the water evaporation rate during the second stage.A different case was found after the feeding of PEG.Firstly,the first stage ended at low volume fraction and a decreased evaporation rate was observed in the second stage.Secondly,the PEG dispersion appeared as finger-like structure in the transmission electron microscopy(TEM)images with 9μm in length.After rinsing,pores were found only in the films formerly containing PVP or PEG,and the shapes and the sizes were closely correlated with the initial morphologies of the PVP or PEG domains.However,the shade of color,the abrasion fastness,and the permeability of the dyed fabric were independent of the type of the post-added hydrophilic polymer.