COPOLYMERIZATION OF PROPYLENE WITH HINDERED PIPERIDINE MONOMER OVER A HIGH ACTIVITY SUPPORTED ZIEGLER-NATTA CATALYST

Copolymerization of propylene and hindered piperidine monomers was carried out over a high activity supported Ziegler-Natta catalyst, using Al(C2H5)(3) as cocatalyst. Factors which affect the copolymerization were studied, The copolymers exhibited high light stability without adding extra light stabilizers. A self-stabilized polypropylene was prepared.

EFFECTS OF EXTERNAL DONOR ON ACTIVE CENTER DISTRIBUTION OF SUPPORTED ZIEGLER-NATTA CATALYST

The composition distribution (CD) and microisotacticity distribution (ID) of propene/1-hexene copolymer synthesized by MgCl2/DIBP/TiCl4 (DIBP: diisobutyl phthalate) were determined by fractionating the copolymers according to crystallinity and characterizing the fractions by (CNMR)-C-13. The effects of two alkoxysilane donors, triethoxyphenylsilane (PTES) and dimethoxydi-tert-butylsilane (TBMS), on CD and ID of the copolymers were compared. Three main parts in the CD diagram of each copolymer were distinguished, which were correlated to active center distribution (ACD) based on three groups of different active centers. By studying the changes in l-hexene content, microisotacticity and reactivity ratio product of three typical fractions, the effects of external donor on ACD were better elucidated. It was found that TBMS shows much stronger effects on ACD than PTES. In the former system, most fractions were produced on active centers with relatively lower r(1)r(2), higher reactivity to I-hexene, and higher stereospecificity as compared to the system without external donor. It is concluded that the observed very extensive changes in ACD are mainly resulted by the formation of new types of active centers, possibly by coordination of external donor to certain positions on the catalyst.

STUDY ON 1-HEXENE POLYMERIZATION BASED ON ZIEGLER-NATTA CATALYSTS WITH DOPED SUPPORT

A series of Ti/Mg supported catalysts are prepared by using ball-milled mixtures of MgCl2-ethanol adducts and NaCl as supports, and 1-hexene polymerizations catalyzed by the novel catalysts are studied. It is found that the molecular weight distribution of poly(1-hexene) becomes apparently narrower when catalysts with doped supports are used, indicating that changing the structure of the support is an effective way to regulate the active center distribution of heterogeneous Ziegler-Natta catalyst.

Preparation of Ultra-High Molecular Weight Polypropylene Using Ziegler-Natta Catalyst via Combining Internal Electron Donor and Cocatalyst Loading

Due to the development of the new energy industry,polypropylene with ultra-high molecular weight plays a crucial role for battery isolation membrane.This work investigated the effect of internal electron donor of Ziegler-Natta catalyst system on the molecular weight of the obtained polypropylene.The scanning electron microscope(SEM)and Canon camera were used to characterize the surface morphologies of catalyst particles and polymer particles,respectively.Compared with the polypropylene particles featuring a spherical shape,these study results confirmed that the morphology duplication theory from the catalyst particle to the morphology of polymer particle was exhibited.The gel permeation chromatography(GPC)results revealed that the obtained polypropylene has a much higher average molecular weight than those prepared by conventional method.The Fourier transform infrared spectrometry(FT-IR)and X-ray photoelectron spectroscopy(XPS)revealed that the carbonyl oxygen atom on ester group was preferentially bound to Mg and Ti,as compared to the ether oxygen atom.The XPS results showed that the ratio of Ti^(3+)/Ti^(4+)could be changed by internal electron donors.When Ti3+content was nearly 99%in the Ziegler-Natta catalyst system,isotactic polypropylene with an ultra-high molecular weight of up to 1.42×10^(6)g/mol was obtained by Cat.3.This result implied that internal electron donor ID3 could reduce theβ-hydride elimination reaction to further increase the molecular weight of the obtained polymer.

EFFECTS OF REACTION AND PROCESSING PARAMETERS ON ETHYLENE POLYMERIZATION USING DIFFERENT ZIEGLER-NATTA CATALYSTS:EMPLOYMENT OF TAGUCHI EXPERIMENTAL DESIGN AND RESPONSE SURFACE METHOD

Different Ziegler-Natta catalysts were employed to polymerize ethylene. To investigate the influences of reaction parameters, namely Al/Ti molar ratio, hydrogen and processing parameters, i.e. ethylene pressure and temperature, a Taguchi experimental design was worked out. An L27 orthogonal array was chosen to take the above-mentioned parameters and relevant interactions into account. Response surface method was the tool used to analyze the experimental design results. Al/Ti, ethylene pressure and temperature were selected as experimental design factors, and catalyst activity and polymerization yield were the response parameters. Increasing pressure, due to an increment in monomer accessibility, and rising Al/Ti, because of higher reduction in the catalysts, cause an increase in both polymerization yield and catalyst activity. Nonetheless, a higher temperature, thanks to reducing ethylene solubility in the slurry medium and partially catalyst destruction, lead to a reduction in both response parameters. A synergistic effect was also observed between temperature and pressure. All catalyst activities will reduce in the presence of hydrogen. Molecular weight also shows a decline in the presence of hydrogen as a transfer agent. However, the polydispersity index remains approximately intact. Using SEM, various morphologies, owing to different catalyst morphologies, were seen for the polyethylene.

DEPENDENCE OF THE DISTRIBUTION OF ACTIVE CENTERS ON MONOMER IN SUPPORTED ZIEGLER-NATTA CATALYSTS

Distribution of active centers(ACD)of ethylene or 1-hexene homopolymerization and ethylene-1-hexene copolymerization with a MgCl_2/TiCl_4 type Z-N catalyst were studied by deconvolution of the polymer molecular weight distribution into multiple Flory components.Each Flory component is thought to be formed by a certain type of active center. ACD of ethylene-1-hexene copolymer with very low 1-hexene incorporation was compared with that of ethylene homopolymer to see the effect of introducingα-olefin on ethyle...

POISONING OF ACTIVE SITES ON ZIEGLER-NATTA CATALYST FOR PROPYLENE POLYMERIZATION

The effects of poisoning materials on catalytic activity and isospecificity of the supported Ziegler-Natta catalyst were investigated.A minor amount of simple structure of Lewis base,i.e.,methanol,acetone,ethyl acetate,was introduced into the catalyst slurry for partial poisoning catalytic active centers.It was found that the variations in deactivation power were in the order of methanol>acetone>ethyl acetate.The kinetic investigation via stopped-flow polymerization showed that poisoning compounds cau...

Study of a Novel Fourth-generation Supported Ziegler-Natta Catalyst for Propylene Polymerization: Relationship between Catalyst Structure and Polymerization Properties

This article presents a detailed structural study of a new spherical Mg Cl2-supported Ti Cl4 Ziegler-Natta catalyst for isotactic propylene polymerization, and researches on the relationship between catalyst structure and polymer properties. The spherical support with the chemical composition of CH3CH2 OMg OCH(CH2Cl)2 has been synthesized from a new dispersion system and is used as the supporting material to prepare Ziegler-Natta catalyst. The XRD analysis indicates that the catalyst is fully activated with δ-Mg Cl2 in the active catalyst. The far-IR spectrometric results confirm again the presence of δ-Mg Cl2 in the active catalyst. Textural property of the active catalyst exhibits high surface area coupled with high porosity. The high activity in propylene polymerization is mainly ascribed to the full activation and the porous structure of the catalyst. Scanning electron microscopy/energy dispersive spectrometer mapping results indicate a uniform titanium distribution throughout the catalyst particles. Particle size analysis shows that the catalyst has a narrow particle size distribution. The perfect spherical shape, uniform titanium distribution and narrow particle size distribution of the catalyst confirm the advantage of polymer particles production with less fines. The solid state 13 C NMR and mid-IR spectroscopic analyses indicate that there exists strong complexation between diisobutyl phthalate and Mg Cl2, which leads to the high isotacticity of polypropylene.

Study on the distribution of active centers in novel low Ti-loading MgCl2-supported Ziegler-Natta catalyst

Novel MgCl2-supported Ziegler-Natta (Z-N) catalysts prepared using a new one-pot ball milling method can effectively control the amounts of Ti-loading in the catalysts. Complex GPC data on polypropylene synthesized by these novel catalysts were analyzed using the method of fitting the molecular weight distribution (MWD) curves with a multiple Flory-Schulz function. It was found that multiple active centers exist in these novel catalysts. Detailed study of the effects of the Ti-loadings in the catalysts on the distribution of the active centers showed that the Ti-loadings in the novel MgCl2-supported Z-N catalysts might affect the proportion of each type of active centers; and might be the main factor responsible for the effect of the Ti-loadings on the microstructure, the molecular weight and molecular weight distribution width of the resultant polymer, the catalytic activity and polymerization kinetics.

SUPPORTED ZIEGLER-NATTA CATALYSTS FOR ETHYLENE SLURRY POLYMERIZATION AND CONTROL OF MOLECULAR WEIGHT DISTRIBUTION OF POLYETHYLENE

The effect of chemical composition of highly active supported Ziegler-Natta catalysts with controlled morphology on the MWD of PE has been studied.It was shown the variation of transition metal compound in the MgCl_2-supported catalyst affect of MWD of PE produced in broad range:Vanadium-magnesium catalyst(VMC)produce PE with broad and bimodal MWD(M_w/M_n=14-21).MWD of PE,produced over titanium-magnesium catalyst(TMC)is narrow or medium depending on Ti content in the catalyst(M_w/M_n=3.1-4.8).The oxidation ...

Synthesis of PE with Broad MWD Catalyzed by Supported Ziegler-Natta Catalyst Consisting of Cycloalkoxy Silane as IED

Two kinds of cycloalkoxy silane compounds were synthesized and used as the internal electron donors(IEDs) of supported Ziegler-Natta catalyst for ethylene polymerization to produce polyethylene with broader molecular weight distribution(MWD). The effect of the structure and the amount of these IEDs on the polymerization performance was investigated. The results implied that the molecular weight distribution of the obtained polyethylene could be adjusted by the incorporation of IEDs. SEM result showed that the morphology of catalyst particle was spherical and uniform in size distribution. The titanium content of these catalysts was higher, the active TiCl4 species were easily anchored on the support than that without adding IED, which was determined by ICP. The GPC result confirmed that the polyethylene with broader molecular weight distribution in the range of from 23.4 to 25.6 was obtained using triethoxy-(-cyclopentyloxy)-silane(ED1) and triethoxy-(-cyclohexyloxyl)- silane(ED2) as the internal electron donors.

Supported Ziegler-Natta catalysts from MgCl_(2)·nROH precursors and its catalytic behaviors for diene copolymerization

Heterogeneous TiCl4/MgCl_(2) type Ziegler-Natta(Z-N)catalysts with unique advantages like low cost,high activity,high stereoregularity and pretty particle morphology,contribute to more than 130 Mt polyolefin large-scale production.However,most researches related with heterogeneous Z-N catalysts focused onα-olefin polymerizations like ethylene,propylene,etc.

Ziegler-Natta催化剂活性中心的研究进展

Ziegler-Natta(Z-N)催化剂活性中心对催化剂和聚合物的性能具有重要影响,开展活性中心结构的研究将为催化剂结构和性能关系、催化机理等提供更深入的认识,是目前聚烯烃催化剂领域中的研究热点。介绍了不同谱学手段对活性中心的表征及对活性中心结构变化的原位监测,综述了通过构建模型催化剂并结合表面分析对活性中心结构进行模拟的研究,以及基于氯化镁晶体模型对活性中心结构的密度泛函理论计算研究,并对Z-N催化剂活性中心结构研究的发展方向进行了展望。

醇镁加合物载体在Ziegler-Natta催化剂中的应用进展

基于醇镁加合物载体(简称醇镁载体)的Ziegler-Natta(Z-N)催化剂具有颗粒形貌优良、活性高等特点,醇镁载体的特性对催化剂和聚合物的综合性能有显著影响,是目前聚烯烃领域中的研究热点。介绍了氯化镁载体的发展历程以及醇镁载体的制备方法,分析了不同醇镁比、醇种类对醇镁载体结构的影响,综述了醇镁载体在Z-N催化剂中的应用,并对烯烃聚合用醇镁载体的开发提出了展望。

光学体表成像设备Catalyst的故障维修案例及日常保养方法

本文介绍了光学体表成像设备Catalyst HD的工作原理,以及处理常见的硬件和软件故障的方法,并提供了日常维护保养方法。其中,对于硬件故障,利用Catalyst HD系统的MutilZsn软件来判断Catalyst投影器和摄像头故障,对于软件故障方面,探讨了Catalyst HD系统在医用直线加速器上常见的Authorization Pending联锁问题的触发原因。本文为科室更好地开展光学体表引导放疗技术,高效地运用好设备提供参考意见。

两种丙烯聚合用球形Ziegler-Natta催化剂的性能研究

采用扫描电子显微镜、激光粒度仪、密度仪和熔体流动速率仪(MFR)等研究了2种丙烯聚合用球形齐格勒-纳塔(Ziegler-Natta)催化剂(记为1#和2#)的性能。结果表明:与2#相比,1#的平均粒径更小,粒径分布更宽,活性更高,对氢气更敏感,且所得聚丙烯(PP)堆积密度更高,但PP颗粒粒径较小。不同外给电子体对丙烯聚合的影响不同。采用二环戊基二甲氧基硅烷为外给电子体时,2种催化剂活性均最高,所得PP的MFR均最小。

Single-atom catalysts for the electrochemical reduction of carbon dioxide into hydrocarbons and oxygenates

The electrochemical reduction of carbon dioxide offers a sound and economically viable technology for the electrification and decarbonization of the chemical and fuel industries.In this technology,an electrocatalytic material and renewable energy-generated electricity drive the conversion of carbon dioxide into high-value chemicals and carbon-neutral fuels.Over the past few years,single-atom catalysts have been intensively studied as they could provide near-unity atom utilization and unique catalytic performance.Single-atom catalysts have become one of the state-of-the-art catalyst materials for the electrochemical reduction of carbon dioxide into carbon monoxide.However,it remains a challenge for single-atom catalysts to facilitate the efficient conversion of carbon dioxide into products beyond carbon monoxide.In this review,we summarize and present important findings and critical insights from studies on the electrochemical carbon dioxide reduction reaction into hydrocarbons and oxygenates using single-atom catalysts.It is hoped that this review gives a thorough recapitulation and analysis of the science behind the catalysis of carbon dioxide into more reduced products through singleatom catalysts so that it can be a guide for future research and development on catalysts with industry-ready performance for the electrochemical reduction of carbon dioxide into high-value chemicals and carbon-neutral fuels.

The regulation of ferrocene-based catalysts on heat transfer in highpressure combustion of ammonium perchlorate/hydroxyl-terminated polybutadiene/aluminum composite propellants

The regulation of the burning rate pressure exponent for the ammonium perchlorate/hydroxylterminated polybutadiene/aluminum(AP/HTPB/Al)composite propellants under high pressures is a crucial step for its application in high-pressure solid rocket motors.In this work,the combustion characteristics of AP/HTPB/Al composite propellants containing ferrocene-based catalysts were investigated,including the burning rate,thermal behavior,the local heat transfer,and temperature profile in the range of 7-28 MPa.The results showed that the exponent breaks were still observed in the propellants after the addition of positive catalysts(Ce-Fc-MOF),the burning rate inhibitor((Ferrocenylmethyl)trimethylammonium bromide,Fc Br)and the mixture of Fc Br/catocene(GFP).However,the characteristic pressure has increased,and the exponent decreased from 1.14 to 0.66,0.55,and 0.48 when the addition of Ce-FcMOF,Fc Br and Fc Br/GFP in the propellants.In addition,the temperature in the first decomposition stage was increased by 7.50℃ and 11.40℃ for the AP/Fc Br mixture and the AP/Fc Br/GFP mixture,respectively,compared to the pure AP.On the other hand,the temperature in the second decomposition stage decreased by 48.30℃ and 81.70℃ for AP/Fc Br and AP/Fc Br/GFP mixtures,respectively.It was also found that Fc Br might generate ammonia to cover the AP surface.In this case,a reaction between the methyl in Fc Br and perchloric acid caused more ammonia to appear at the AP surface,resulting in the suppression of ammonia desorption.In addition,the coarse AP particles on the quenched surface were of a concave shape relative to the binder matrix under low and high pressures when the catalysts were added.In the process,the decline at the AP/HTPB interface was only exhibited in the propellant with the addition of Ce-Fc-MOF.The ratio of the gas-phase temperature gradient of the propellants containing catalysts was reduced significantly below and above the characteristic pressure,rather than 3.6 times of the difference in the blank propellant.Overall,the obtained results demonstrated that the pressure exponent could be effectively regulated and controlled by adjusting the propellant local heat and mass transfer under high and low pressures.

Catalytic effect in lithium metal batteries: From heterogeneous catalyst to homogenous catalyst

Lithium metal batteries are regarded as prominent contenders to address the pressing needs owing to the high theoretical capacity.Toward the broader implementation,the primary obstacle lies in the intricate multi-electron,multi-step redox reaction associated with sluggish conversion kinetics,subsequently giving rise to a cascade of parasitic issues.In order to smooth reaction kinetics,catalysts are widely introduced to accelerate reaction rate via modulating the energy barrier.Over past decades,a large amount of research has been devoted to the catalyst design and catalytic mechanism exploration,and thus the great progress in electrochemical performance has been realized.Therefore,it is necessary to make a comprehensive review toward key progress in catalyst design and future development pathway.In this review,the basic mechanism of lithium metal batteries is provided along with corresponding advantages and existing challenges detailly described.The main catalysts employed to accelerate cathode reaction with emphasis on their catalytic mechanism are summarized as well.Finally,the rational design and innovative direction toward efficient catalysts are suggested for future application in metal-sulfur/gas battery and beyond.This review is expected to drive and benefit future research on rational catalyst design with multi-parameter synergistic impacts on the activity and stability of next-generation metal battery,thus opening new avenue for sustainable solution to climate change,energy and environmental issues,and the potential industrial economy.

Facile molybdenum and aluminum recovery from spent hydrogenation catalyst

Industrial catalyst waste has emerged as a hazardous pollutant that requires safe and proper disposal after the unloading process.Finding a valuable and sustainable strategy for its treatment is a significant challenge compared to traditional methods.In this study,we present a facile method for the recovery of molybdenum and aluminum contents from spent Mo-Ni/Al_(2)O_(3) hydrogenation catalysts through crystallization separation and coprecipitation.Furthermore,the recovered molybdenum and aluminum are utilized as active metals and carriers for the preparation of new catalysts.Their properties were thoroughly analyzed and investigated using various characterization techniques.The hydrogenation activity of these newly prepared catalysts was evaluated on a fixed-bed small-scale device and compared with a reference catalyst synthesized from commercial raw reagents.Finally,the hydrogenation activity of the catalysts was further assessed by using the entire distillate oil of coal liquefaction as the raw oil,specifically focusing on denitrogenation and aromatic saturation.This work not only offers an effective solution for recycling catalysts but also promotes sustainable development.