ZnO whiskers with a length of 30-40μm and a diameter of about 1μm were synthesized by co-precipitation of ZnSO 4 and Na2CO3 solution at room temperature followed by hydrothermal treatment of the as-prepared Zn5(CO3)...ZnO whiskers with a length of 30-40μm and a diameter of about 1μm were synthesized by co-precipitation of ZnSO 4 and Na2CO3 solution at room temperature followed by hydrothermal treatment of the as-prepared Zn5(CO3)2(OH)6 precursor at 160 ℃for 6 h.The increase of the initial solution pH promotes the hydrothermal conversion of the particulate Zn5(CO3)2(OH)6 to ZnO whiskers.The presence of minor amount of EDTA in the hydrothermal solution promotes the one dimensional growth of ZnO whiskers,leading to the formation of ZnO whiskers with a length of 50-60μm and a diameter of 1-2μm.展开更多
Calcium aluminate cement(CAC)bonded corundum based castables were prepared using tabular corundum and activated alumina as the starting materials,CAC as the binder,zinc hydroxide(Zn(OH)_(2))and basic zinc carbonate(BZ...Calcium aluminate cement(CAC)bonded corundum based castables were prepared using tabular corundum and activated alumina as the starting materials,CAC as the binder,zinc hydroxide(Zn(OH)_(2))and basic zinc carbonate(BZC)as the ZnO precursors.The effects of the two ZnO precursors on the phase composition and the microstructure of the CAC bonded corundum based castable matrix specimens were analyzed,and the reasons affecting the hot performance of the castables were studied.The results show that Zn(OH)_(2) with a smaller particle size(d_(50)=1.26μm)is prone to agglomerate during sample preparation and generates ZnAl_(2)O_(4) spinel grains after firing,hindering the growth of CA_(6),thus decreasing the mechanical strength of the castables.BZC with a larger particle size(d_(50)=2.91μm),which shows a sound dispersity,in-situ generates nano-sized ZnO after firing,and ZnO or Zn^(2+)diffuses into calcium aluminates,promoting the sintering of CA_(2) and CA_(6),thereby enhancing the hot properties of the CAC-bonded corundum based castables.展开更多
CdTe@Zn5（CO3）2（OH）G composites were synthesized by a hydrothermal method. CdTe@Zn5（CO3）2（OH）6 composite nanospheres were characterized via X-ray diffraction, scanning electron microscopy, energy- dispersive X-...CdTe@Zn5（CO3）2（OH）G composites were synthesized by a hydrothermal method. CdTe@Zn5（CO3）2（OH）6 composite nanospheres were characterized via X-ray diffraction, scanning electron microscopy, energy- dispersive X-ray spectroscopy, and photoluminescence （PL）. The hydrothermal reaction time and the mole ratios of Zn/Te played important roles in the growth and fluorescence intensity of CdTe@Zn5（CO3）2（OH）6 composites. The composite powders showed peak PL at 578 nm at 1.6 times the intensity of powdered CdTe QDs. CdTe@Zn5（CO3）2（OH）6 exhibited a strong yellow fluorescence emission, and its preparation method was easy and economical. Therefore, CdTe@Zn5（CO3）2（OH）6 offers potential applications in biological markers and light-emitting diodes.展开更多
基金Project(50874066) supported by the National Natural Science Foundation of China
文摘ZnO whiskers with a length of 30-40μm and a diameter of about 1μm were synthesized by co-precipitation of ZnSO 4 and Na2CO3 solution at room temperature followed by hydrothermal treatment of the as-prepared Zn5(CO3)2(OH)6 precursor at 160 ℃for 6 h.The increase of the initial solution pH promotes the hydrothermal conversion of the particulate Zn5(CO3)2(OH)6 to ZnO whiskers.The presence of minor amount of EDTA in the hydrothermal solution promotes the one dimensional growth of ZnO whiskers,leading to the formation of ZnO whiskers with a length of 50-60μm and a diameter of 1-2μm.
文摘Calcium aluminate cement(CAC)bonded corundum based castables were prepared using tabular corundum and activated alumina as the starting materials,CAC as the binder,zinc hydroxide(Zn(OH)_(2))and basic zinc carbonate(BZC)as the ZnO precursors.The effects of the two ZnO precursors on the phase composition and the microstructure of the CAC bonded corundum based castable matrix specimens were analyzed,and the reasons affecting the hot performance of the castables were studied.The results show that Zn(OH)_(2) with a smaller particle size(d_(50)=1.26μm)is prone to agglomerate during sample preparation and generates ZnAl_(2)O_(4) spinel grains after firing,hindering the growth of CA_(6),thus decreasing the mechanical strength of the castables.BZC with a larger particle size(d_(50)=2.91μm),which shows a sound dispersity,in-situ generates nano-sized ZnO after firing,and ZnO or Zn^(2+)diffuses into calcium aluminates,promoting the sintering of CA_(2) and CA_(6),thereby enhancing the hot properties of the CAC-bonded corundum based castables.
基金supported by grants from the Science Foundation of Guangxi Province (No.2015GXNSFAA139025)the Students Innovation and Entrepreneurship Training Program of Guangxi University (No.201610593040)
文摘CdTe@Zn5（CO3）2（OH）G composites were synthesized by a hydrothermal method. CdTe@Zn5（CO3）2（OH）6 composite nanospheres were characterized via X-ray diffraction, scanning electron microscopy, energy- dispersive X-ray spectroscopy, and photoluminescence （PL）. The hydrothermal reaction time and the mole ratios of Zn/Te played important roles in the growth and fluorescence intensity of CdTe@Zn5（CO3）2（OH）6 composites. The composite powders showed peak PL at 578 nm at 1.6 times the intensity of powdered CdTe QDs. CdTe@Zn5（CO3）2（OH）6 exhibited a strong yellow fluorescence emission, and its preparation method was easy and economical. Therefore, CdTe@Zn5（CO3）2（OH）6 offers potential applications in biological markers and light-emitting diodes.