Well-Migned Zn1-xMnxO nanorods have been synthesized successfully on bare silicon substrates by a simple evaporation method without using any catalyst. X-ray diffraction and electron microscopy studies demonstrate tha...Well-Migned Zn1-xMnxO nanorods have been synthesized successfully on bare silicon substrates by a simple evaporation method without using any catalyst. X-ray diffraction and electron microscopy studies demonstrate that the as-grown nanorods are of single wurtzite phase with a preferential growth direction along their c- axes, Quantitative energy-dispersive spectrum analysis reveals that the concentration of manganese is around 4 at,%, Magnetic measurements show the single-phase Zn1-xMnxO nanorod arrays exhibiting the paramagnetic behaviour. Photolumlnescence spectra demonstrate that the Zn1-xMnxO nanorods preserve ultraviolet emission at room temperature.展开更多
基金Supported by the National Natural Science Foundation of China under Grant No 50502005, and Beijing Natural Science Foundation under Grant No 1062008.
文摘Well-Migned Zn1-xMnxO nanorods have been synthesized successfully on bare silicon substrates by a simple evaporation method without using any catalyst. X-ray diffraction and electron microscopy studies demonstrate that the as-grown nanorods are of single wurtzite phase with a preferential growth direction along their c- axes, Quantitative energy-dispersive spectrum analysis reveals that the concentration of manganese is around 4 at,%, Magnetic measurements show the single-phase Zn1-xMnxO nanorod arrays exhibiting the paramagnetic behaviour. Photolumlnescence spectra demonstrate that the Zn1-xMnxO nanorods preserve ultraviolet emission at room temperature.